Fe-Al/Cr3C2 coatings were sprayed on low steel by high velocity arc spraying（HVAS） technology. The influences of oxides on erosion, corrosion and wear behavior for high velocity arc sprayed Fe-Al/Cr3C2 coatings were...Fe-Al/Cr3C2 coatings were sprayed on low steel by high velocity arc spraying（HVAS） technology. The influences of oxides on erosion, corrosion and wear behavior for high velocity arc sprayed Fe-Al/Cr3C2 coatings were studied. The results show that HVAS-sprayed Fe-Al/Cr3C2 coatings have good erosion, heat corrosion and wear resistance. The erosion resistance improves with the increase of the temperature. On one hand, the ferrous oxides are incompact, so they peel off the surface of the coatings easily during the high temperature erosion. On the other hand, compact Al2O3 films on the surface can protect the coatings.展开更多
Ceramic composites Al_2O_3/(W, Ti)C/Cr_3C_2 with different contents of Cr_3C_2 and (W, Ti)C particles, and with the additive Y_2O_3, were fabricated with hot-pressing technique at 1700 ℃ under 28 MPa pressure for 30 ...Ceramic composites Al_2O_3/(W, Ti)C/Cr_3C_2 with different contents of Cr_3C_2 and (W, Ti)C particles, and with the additive Y_2O_3, were fabricated with hot-pressing technique at 1700 ℃ under 28 MPa pressure for 30 min in N_2 atmosphere. The mechanical properties were tested, and the microstructure was investigated by environment scanning electron microscope (ESEM), transmission electron microscope (TEM), energy dispersive analysis using X-ray (EDAX) and optical microscope (OM). Results indicate that the incorporation of Cr_3C_2 and (W,Ti)C particles can suppress the grain growth of the others, and the toughening and strengthening effects mainly originate from nano-particles, dispersion toughening and solidification strengthening. The multiphase composite ceramic material Al_2O_3/10%Cr_3C_2/20%(W,Ti)C shows good mechanical properties, especially the fracture toughness increases from 4.0 MPa·m 1/2 (Monolithic Al_2O_3 ceramic) to 8.92 MPa·m 1/2, the flexural strength from 260～340 MPa (Monolithic Al_2O_3 ceramic) to 496 MPa, due to incorporation of the suitable contents of Cr_3C_2 and (W,Ti)C particles.展开更多
A new hardfacing process, reactive braze coating process (RBCC) was studied, and (TiC+Cr_3C_2)/Fe composite coatings were prepared by RBCC using carbon, Cr_3C_2, iron, ferrochromium and titanium powder as the raw mate...A new hardfacing process, reactive braze coating process (RBCC) was studied, and (TiC+Cr_3C_2)/Fe composite coatings were prepared by RBCC using carbon, Cr_3C_2, iron, ferrochromium and titanium powder as the raw materials in vacuum braze furnace. The results show that TiC is in-situ synthesized in the coatings. The methods of introducing Cr_3C_2 have great effects on the distribution of TiC. Adding Cr_3C_2 directly to the raw materials for coatings, fine TiC particles aggregate into discoids parallel to the coating surface, whereas, in-situ synthesizing Cr_3C_2 in coatings, the aggregations of TiC are lumpish. During braze coating, Cr_3C_2 particles directly added dissolve and precipitate to become needle-shaped. The coatings have an even and smooth surface and are combined with their mild steel substrates by a metallurgical bonding.展开更多
文摘Fe-Al/Cr3C2 coatings were sprayed on low steel by high velocity arc spraying（HVAS） technology. The influences of oxides on erosion, corrosion and wear behavior for high velocity arc sprayed Fe-Al/Cr3C2 coatings were studied. The results show that HVAS-sprayed Fe-Al/Cr3C2 coatings have good erosion, heat corrosion and wear resistance. The erosion resistance improves with the increase of the temperature. On one hand, the ferrous oxides are incompact, so they peel off the surface of the coatings easily during the high temperature erosion. On the other hand, compact Al2O3 films on the surface can protect the coatings.
文摘Ceramic composites Al_2O_3/(W, Ti)C/Cr_3C_2 with different contents of Cr_3C_2 and (W, Ti)C particles, and with the additive Y_2O_3, were fabricated with hot-pressing technique at 1700 ℃ under 28 MPa pressure for 30 min in N_2 atmosphere. The mechanical properties were tested, and the microstructure was investigated by environment scanning electron microscope (ESEM), transmission electron microscope (TEM), energy dispersive analysis using X-ray (EDAX) and optical microscope (OM). Results indicate that the incorporation of Cr_3C_2 and (W,Ti)C particles can suppress the grain growth of the others, and the toughening and strengthening effects mainly originate from nano-particles, dispersion toughening and solidification strengthening. The multiphase composite ceramic material Al_2O_3/10%Cr_3C_2/20%(W,Ti)C shows good mechanical properties, especially the fracture toughness increases from 4.0 MPa·m 1/2 (Monolithic Al_2O_3 ceramic) to 8.92 MPa·m 1/2, the flexural strength from 260～340 MPa (Monolithic Al_2O_3 ceramic) to 496 MPa, due to incorporation of the suitable contents of Cr_3C_2 and (W,Ti)C particles.
文摘A new hardfacing process, reactive braze coating process (RBCC) was studied, and (TiC+Cr_3C_2)/Fe composite coatings were prepared by RBCC using carbon, Cr_3C_2, iron, ferrochromium and titanium powder as the raw materials in vacuum braze furnace. The results show that TiC is in-situ synthesized in the coatings. The methods of introducing Cr_3C_2 have great effects on the distribution of TiC. Adding Cr_3C_2 directly to the raw materials for coatings, fine TiC particles aggregate into discoids parallel to the coating surface, whereas, in-situ synthesizing Cr_3C_2 in coatings, the aggregations of TiC are lumpish. During braze coating, Cr_3C_2 particles directly added dissolve and precipitate to become needle-shaped. The coatings have an even and smooth surface and are combined with their mild steel substrates by a metallurgical bonding.