The ultrafine particles of a new style Fe-Cu-based catalysts for CO hydrogenation were prepared by impregnating the organic sol of Fe（OH）3 and Cu（OH）2 onto the activated Al2O3, in which the organic sol of Fe（OH）...The ultrafine particles of a new style Fe-Cu-based catalysts for CO hydrogenation were prepared by impregnating the organic sol of Fe（OH）3 and Cu（OH）2 onto the activated Al2O3, in which the organic sol of Fe（OH）3 and Cu（OH）2 were prepared in the microemulsion of dodecylbenzenesulfonic acid sodium（S）/n-butanol（A）/toluene（O）/water with V（A）/V（O） = 0.25 and W（A）/W（S） = 1.50. This catalyst was characterized by particle size analysis, XRD and TG. The results of particle size analysis showed that Fe（OH）3 particles with a mean size of 17.1 nm and Cu（OH）2 particles with an average size of 6.65 um were obtained. TG analysis and XRD patterns suggested that 673 K is the optimal calcination temperature. CO hydrogenation produced C＋OH with a high selectivity above 58 wt% by using the ultrafine particles as catalyst, and the total alcohol yield of 0.250 g·ml^-1 ·h^-1 was obtained when the contents of Al2O3 and K were 88.61 wt% and 1.60 wt%, respectively.展开更多
A series of Ni/SBA-15 catalysts with 5wt% to 15wt% Ni content as well as a series of 12.5%Ni/Cu/SBA-15 catalysts with 1% to 10% copper content were prepared by the impregnation method. The catalytic performance for pa...A series of Ni/SBA-15 catalysts with 5wt% to 15wt% Ni content as well as a series of 12.5%Ni/Cu/SBA-15 catalysts with 1% to 10% copper content were prepared by the impregnation method. The catalytic performance for partial oxidation of methane was investigated in a continuous flow microreactor under atmospheric pressure. The textural and chemical properties of the catalysts were characterized by XRD, TEM, BET and Hz-TPR techniques. The results indicated that the catalysts modified with Cu promoter showed better performance than those without modification. For the 12.5%Ni/2.5%/Cu/SBA-15 catalyst, at 850 ℃ the conversion of CH4 reached 97.9% and the selectivity of CO and H2 reached 98.0% and 96.0%, respectively. In XRD patterns of the Ni/Cu/SBA-15 catalyst with 7.5 to 10% Cu contents there were CuO characteristic peaks beside NiO characteristic peaks. The mesoporous structure of SBA-15 was retained in all of the catalysts. TPR analysis of the catalysts revealed that a strong interaction between Ni, Cu promoter and SBA-15 support may be existed. This interaction enhanced significantly the redox properties of the catalysts resulting in the higher catalytic activity.展开更多
Using solar energy to produce syngas via the endothermic reforming of methane has been extensively inves- tigated at the laboratory- and pilot plant-scales as a promising method of storing solar energy. One of the cha...Using solar energy to produce syngas via the endothermic reforming of methane has been extensively inves- tigated at the laboratory- and pilot plant-scales as a promising method of storing solar energy. One of the challenges to scaling up this process in a tubular reformer is to improve the reactor＇s performance, which is limited by mass and heat transfer issues. High thermal conductivity Cu foam was therefore used as a sub-strate to improve the catalyst＇s thermal conductivity during solar reforming. We also developed a method to coat the foam with the catalytically active component NiMg3AlOx. The Cu foam-based NiMg3AlOx performs better than catalysts supported on SiSiC foam, which is currently used as a substrate for solar-reforming cat- alysts, at high gas hourly space velocity （≥400,000 mL/（g.h）） or at low reaction temperatures （≤ 720 ℃）. The presence of a γ-Al2O3 intermediate layer improves the adhesion between the catalyst and substrate as well as the catalytic activity.展开更多
The copper-cobalt based catalysts were effective for higher alcohol synthesis, the surface state of the catalysts and the nature of the active sites were investigated by using XPS and XAES spectra, and some strong int...The copper-cobalt based catalysts were effective for higher alcohol synthesis, the surface state of the catalysts and the nature of the active sites were investigated by using XPS and XAES spectra, and some strong interactions were also observed, in each of the three cases, (after calcination, after reduction, and during the syngas reaction).展开更多
Various Cu/ZnO/Al2O3 catalysts have been synthesized by different aluminum emulsions as aluminum sources and their pertormances tor methanol synthesis from syngas have been investigated. The influences of preparation ...Various Cu/ZnO/Al2O3 catalysts have been synthesized by different aluminum emulsions as aluminum sources and their pertormances tor methanol synthesis from syngas have been investigated. The influences of preparation methods of aluminum emulsions on physicochemical and catalytic properties of catalysts were studied by XRD, SEM, XPS,N2 adsorption-desorption techniques and methanol synthesis from syngas. The preparation methods of aluminum emulsions were found to influence the catalytic activity, CuO crystallite size, surface area and Cu0 surface area and reduction process. The results show that the catalyst CN using the aluminum source prepared by addition the ammonia into the aluminum nitrate （NP） exhibited the best catalytic performance for methanol synthesis from syngas.展开更多
文摘The ultrafine particles of a new style Fe-Cu-based catalysts for CO hydrogenation were prepared by impregnating the organic sol of Fe（OH）3 and Cu（OH）2 onto the activated Al2O3, in which the organic sol of Fe（OH）3 and Cu（OH）2 were prepared in the microemulsion of dodecylbenzenesulfonic acid sodium（S）/n-butanol（A）/toluene（O）/water with V（A）/V（O） = 0.25 and W（A）/W（S） = 1.50. This catalyst was characterized by particle size analysis, XRD and TG. The results of particle size analysis showed that Fe（OH）3 particles with a mean size of 17.1 nm and Cu（OH）2 particles with an average size of 6.65 um were obtained. TG analysis and XRD patterns suggested that 673 K is the optimal calcination temperature. CO hydrogenation produced C＋OH with a high selectivity above 58 wt% by using the ultrafine particles as catalyst, and the total alcohol yield of 0.250 g·ml^-1 ·h^-1 was obtained when the contents of Al2O3 and K were 88.61 wt% and 1.60 wt%, respectively.
基金supported by the National Basic Research Program of China (Project No. 2005CB221405)the National "863" Project of China (No.2006AA10Z425)
文摘A series of Ni/SBA-15 catalysts with 5wt% to 15wt% Ni content as well as a series of 12.5%Ni/Cu/SBA-15 catalysts with 1% to 10% copper content were prepared by the impregnation method. The catalytic performance for partial oxidation of methane was investigated in a continuous flow microreactor under atmospheric pressure. The textural and chemical properties of the catalysts were characterized by XRD, TEM, BET and Hz-TPR techniques. The results indicated that the catalysts modified with Cu promoter showed better performance than those without modification. For the 12.5%Ni/2.5%/Cu/SBA-15 catalyst, at 850 ℃ the conversion of CH4 reached 97.9% and the selectivity of CO and H2 reached 98.0% and 96.0%, respectively. In XRD patterns of the Ni/Cu/SBA-15 catalyst with 7.5 to 10% Cu contents there were CuO characteristic peaks beside NiO characteristic peaks. The mesoporous structure of SBA-15 was retained in all of the catalysts. TPR analysis of the catalysts revealed that a strong interaction between Ni, Cu promoter and SBA-15 support may be existed. This interaction enhanced significantly the redox properties of the catalysts resulting in the higher catalytic activity.
基金supported by the CSIRO Energy Flagship and the Chinese Scholarship Council
文摘Using solar energy to produce syngas via the endothermic reforming of methane has been extensively inves- tigated at the laboratory- and pilot plant-scales as a promising method of storing solar energy. One of the challenges to scaling up this process in a tubular reformer is to improve the reactor＇s performance, which is limited by mass and heat transfer issues. High thermal conductivity Cu foam was therefore used as a sub-strate to improve the catalyst＇s thermal conductivity during solar reforming. We also developed a method to coat the foam with the catalytically active component NiMg3AlOx. The Cu foam-based NiMg3AlOx performs better than catalysts supported on SiSiC foam, which is currently used as a substrate for solar-reforming cat- alysts, at high gas hourly space velocity （≥400,000 mL/（g.h）） or at low reaction temperatures （≤ 720 ℃）. The presence of a γ-Al2O3 intermediate layer improves the adhesion between the catalyst and substrate as well as the catalytic activity.
文摘The copper-cobalt based catalysts were effective for higher alcohol synthesis, the surface state of the catalysts and the nature of the active sites were investigated by using XPS and XAES spectra, and some strong interactions were also observed, in each of the three cases, (after calcination, after reduction, and during the syngas reaction).
文摘Various Cu/ZnO/Al2O3 catalysts have been synthesized by different aluminum emulsions as aluminum sources and their pertormances tor methanol synthesis from syngas have been investigated. The influences of preparation methods of aluminum emulsions on physicochemical and catalytic properties of catalysts were studied by XRD, SEM, XPS,N2 adsorption-desorption techniques and methanol synthesis from syngas. The preparation methods of aluminum emulsions were found to influence the catalytic activity, CuO crystallite size, surface area and Cu0 surface area and reduction process. The results show that the catalyst CN using the aluminum source prepared by addition the ammonia into the aluminum nitrate （NP） exhibited the best catalytic performance for methanol synthesis from syngas.