Cu/Al bar clad material was fabricated by a drawing process and a subsequent heat treatment.During these processes,intermetallic compounds have been formed at the interface of Cu/Al and have affected its bonding prope...Cu/Al bar clad material was fabricated by a drawing process and a subsequent heat treatment.During these processes,intermetallic compounds have been formed at the interface of Cu/Al and have affected its bonding property.Microstructures of Cu/Al interfaces were observed by OM,SEM and EDX Analyser in order to investigate the bonding properties of the material.According to the microstructure a series of diffusion layers were observed at the interface and the thicknesses of diffusion layers have increased with aging time as a result of the diffusion bonding.The interfaces were composed of 3-ply diffusion layers and their compositions were changed with aging time at 400 °C.These compositional compounds were revealed to be η2,(θ+η2),(α+θ) intermetallic phases.It is evident from V-notch impact tests that the growth of the brittle diffusion layers with the increasing aging time directly influenced delamination distance between the Cu sleeve and the Al core.It is suggested that the proper holding time at 400 °C for aging as post heat treatment of a drawn Cu/Al bar clad material would be within 1 h.展开更多
We report a new kagome quantum spin liquid candidate CuaZn（OH）6FBr, which does not experience any phase transition down to 50inK, more than three orders lower than the antiferromagnetic Curie-Weiss temperature （-20...We report a new kagome quantum spin liquid candidate CuaZn（OH）6FBr, which does not experience any phase transition down to 50inK, more than three orders lower than the antiferromagnetic Curie-Weiss temperature （-200 K）. A clear gap opening at low temperature is observed in the uniform spin susceptibility obtained from 19F nuclear magnetic resonance measurements. We observe the characteristic magnetic field dependence of the gap as expected for fractionalized spin-1/2 spinon excitations. Our experimental results provide firm evidence for spin fractionalization in a topologically ordered spin system, resembling charge fraetionalization in the fractional quantum Hall state.展开更多
Two kinds of Nd 1+ x Ba 2- x Cu 3O 7- δ , the sintered samples and zone melted samples, were treated in pure Ar at 950 ℃. The substitution of Nd ions for Ba ions in the Nd 1+ x Ba 2- ...Two kinds of Nd 1+ x Ba 2- x Cu 3O 7- δ , the sintered samples and zone melted samples, were treated in pure Ar at 950 ℃. The substitution of Nd ions for Ba ions in the Nd 1+ x Ba 2- x Cu 3O 7- δ before and after the heat treatment was investigated by XRD. In order to know the effects of heat treatment, the T c and J c of samples with and without the heat treatment in Ar were comparatively studied. The results show that the substitution of Nd for Ba decreases, whereas T c and J c increase after the treatment. The Nd 1+ x Ba 2- x Cu 3O 7- δ samples were oxygenated in pure oxygen at 300 ℃ . Based on the XRD spectra it was found that the samples with x <0.4 can transform from tetragonal phase into orthorhombic phase after the oxygenation, whereas in the sample with x >0.4 no phase transition occurs even after a long time oxygenation.展开更多
Taking Au3Cu-type sublattice system as an example, three discoveries have been presented. First, the fourth barrier to hinder the progress of metal materials science is that today’s researchers do not understand that...Taking Au3Cu-type sublattice system as an example, three discoveries have been presented. First, the fourth barrier to hinder the progress of metal materials science is that today’s researchers do not understand that the Gibbs energy function of an alloy phase should be derived from Gibbs energy partition function constructed of alloy gene sequence and their Gibbs energy sequence. Second, the six rules for establishing alloy gene Gibbs energy partition function have been discovered, and it has been specially proved that the probabilities of structure units occupied at the Gibbs energy levels in the degeneracy factor for calculating configuration entropy should be degenerated as ones of component atoms occupied at the lattice points. Third, the main characteristics unexpected by today’s researchers are as follows. There exists a single-phase boundary curve without two-phase region coexisting by the ordered and disordered phases. The composition and temperature of the top point on the phase-boundary curve are far away from those of the critical point of the Au3Cu compound; At 0 K, the composition of the lowest point on the composition-dependent Gibbs energy curve is notably deviated from that of the Au3Cu compounds. The theoretical limit composition range of long range ordered Au3Cu-type alloys is determined by the first jumping order degree.展开更多
In order to eliminate the disadvantages of the keyhole in conventional friction stir spot welding joint and attain the highstrength lap joint of Al/Cu dissimilar metals,a novel welding technique,named as friction stir...In order to eliminate the disadvantages of the keyhole in conventional friction stir spot welding joint and attain the highstrength lap joint of Al/Cu dissimilar metals,a novel welding technique,named as friction stir spot riveting(FSSR),was proposed.A pinless tool and an extra filling stud were employed.The Al/Cu spot joints without keyhole defect were achieved by the FSSR.A Cu anchor-like structure was formed,which greatly increased the mechanical interlocking between the upper Al sheet and lower Cu sheet.The thin intermetallic compounds containing CuAl2 and CuAl at the Al/Cu interface strengthened the joining interface between the Al sheet and the Cu stud.Increasing rotating velocity increased frictional heat and plastic deformation and then eliminated the interfacial joining defects.The FSSR joint with the maximum tensile shear load of 3.50 kN was achieved at a rotating velocity of 1800 rpm and a dwell time of 20 s,whose fracture path passed through the softened region of upper Al sheet.In summary,the novel FSSR technique has the advantages of strong mechanical interlocking and metallurgical bonding between dissimilar materials,thereby attaining the high-strength spot joint.展开更多
基金Project supported by the Fundamental Materials Development funded by the Korean Ministry of Knowledge Economy
文摘Cu/Al bar clad material was fabricated by a drawing process and a subsequent heat treatment.During these processes,intermetallic compounds have been formed at the interface of Cu/Al and have affected its bonding property.Microstructures of Cu/Al interfaces were observed by OM,SEM and EDX Analyser in order to investigate the bonding properties of the material.According to the microstructure a series of diffusion layers were observed at the interface and the thicknesses of diffusion layers have increased with aging time as a result of the diffusion bonding.The interfaces were composed of 3-ply diffusion layers and their compositions were changed with aging time at 400 °C.These compositional compounds were revealed to be η2,(θ+η2),(α+θ) intermetallic phases.It is evident from V-notch impact tests that the growth of the brittle diffusion layers with the increasing aging time directly influenced delamination distance between the Cu sleeve and the Al core.It is suggested that the proper holding time at 400 °C for aging as post heat treatment of a drawn Cu/Al bar clad material would be within 1 h.
基金Supported by the National Key Research and Development Program of China under Grant Nos 2016YFA0300502,2016YFA0300503,2016YFA0300604,2016YF0300300 and 2016YFA0300802the National Natural Science Foundation of China under Grant Nos 11421092,11474330,11574359,11674406,11374346 and 11674375+3 种基金the National Basic Research Program of China(973 Program)under Grant No 2015CB921304the National Thousand-Young-Talents Program of Chinathe Strategic Priority Research Program(B) of the Chinese Academy of Sciences under Grant Nos XDB07020000,XDB07020200 and XDB07020300supported by DOE-BES under Grant No DE-FG02-04ER46148
文摘We report a new kagome quantum spin liquid candidate CuaZn（OH）6FBr, which does not experience any phase transition down to 50inK, more than three orders lower than the antiferromagnetic Curie-Weiss temperature （-200 K）. A clear gap opening at low temperature is observed in the uniform spin susceptibility obtained from 19F nuclear magnetic resonance measurements. We observe the characteristic magnetic field dependence of the gap as expected for fractionalized spin-1/2 spinon excitations. Our experimental results provide firm evidence for spin fractionalization in a topologically ordered spin system, resembling charge fraetionalization in the fractional quantum Hall state.
文摘Two kinds of Nd 1+ x Ba 2- x Cu 3O 7- δ , the sintered samples and zone melted samples, were treated in pure Ar at 950 ℃. The substitution of Nd ions for Ba ions in the Nd 1+ x Ba 2- x Cu 3O 7- δ before and after the heat treatment was investigated by XRD. In order to know the effects of heat treatment, the T c and J c of samples with and without the heat treatment in Ar were comparatively studied. The results show that the substitution of Nd for Ba decreases, whereas T c and J c increase after the treatment. The Nd 1+ x Ba 2- x Cu 3O 7- δ samples were oxygenated in pure oxygen at 300 ℃ . Based on the XRD spectra it was found that the samples with x <0.4 can transform from tetragonal phase into orthorhombic phase after the oxygenation, whereas in the sample with x >0.4 no phase transition occurs even after a long time oxygenation.
基金Project(51071181)supported by the National Natural Science Foundation of ChinaProject(2013FJ4043)supported by the Natural Science Foundation of Hunan Province,China
文摘Taking Au3Cu-type sublattice system as an example, three discoveries have been presented. First, the fourth barrier to hinder the progress of metal materials science is that today’s researchers do not understand that the Gibbs energy function of an alloy phase should be derived from Gibbs energy partition function constructed of alloy gene sequence and their Gibbs energy sequence. Second, the six rules for establishing alloy gene Gibbs energy partition function have been discovered, and it has been specially proved that the probabilities of structure units occupied at the Gibbs energy levels in the degeneracy factor for calculating configuration entropy should be degenerated as ones of component atoms occupied at the lattice points. Third, the main characteristics unexpected by today’s researchers are as follows. There exists a single-phase boundary curve without two-phase region coexisting by the ordered and disordered phases. The composition and temperature of the top point on the phase-boundary curve are far away from those of the critical point of the Au3Cu compound; At 0 K, the composition of the lowest point on the composition-dependent Gibbs energy curve is notably deviated from that of the Au3Cu compounds. The theoretical limit composition range of long range ordered Au3Cu-type alloys is determined by the first jumping order degree.
基金financially supported by the National Natural Science Foundation of China (Nos.51705339 and 51905355)。
文摘In order to eliminate the disadvantages of the keyhole in conventional friction stir spot welding joint and attain the highstrength lap joint of Al/Cu dissimilar metals,a novel welding technique,named as friction stir spot riveting(FSSR),was proposed.A pinless tool and an extra filling stud were employed.The Al/Cu spot joints without keyhole defect were achieved by the FSSR.A Cu anchor-like structure was formed,which greatly increased the mechanical interlocking between the upper Al sheet and lower Cu sheet.The thin intermetallic compounds containing CuAl2 and CuAl at the Al/Cu interface strengthened the joining interface between the Al sheet and the Cu stud.Increasing rotating velocity increased frictional heat and plastic deformation and then eliminated the interfacial joining defects.The FSSR joint with the maximum tensile shear load of 3.50 kN was achieved at a rotating velocity of 1800 rpm and a dwell time of 20 s,whose fracture path passed through the softened region of upper Al sheet.In summary,the novel FSSR technique has the advantages of strong mechanical interlocking and metallurgical bonding between dissimilar materials,thereby attaining the high-strength spot joint.