Modern manufacturing industry demands low cost and high efficient welding processes to remain competitiveness in the time of globalization. In this study, conventional gas metal arc welding （GMAW） was modified, a do...Modern manufacturing industry demands low cost and high efficient welding processes to remain competitiveness in the time of globalization. In this study, conventional gas metal arc welding （GMAW） was modified, a double-electrode GMAW （DE-GMAW） system is developed and DE-GMAW process is implemented through optimization of the design and process parameters and suitable selection of igniting sequence of double arcs. High speed welding tests were carried out to examine the effects of different factors on occurrence of weld formation defects. Through observing the weld bead appearance in DE-GMA W, the values of critical welding speed were determined under different levels of welding current and welding speed.展开更多
为获取AZ31B镁合金薄板非熔化极气体保护双弧焊(double-electrode gas metal arc welding,DE-GMAW)焊接残余应力场分布,用ANSYS软件对焊接过程进行数值模拟,探索焊前预热对镁合金残余应力的影响规律。建立双弧热源模型,通过热应力耦合法...为获取AZ31B镁合金薄板非熔化极气体保护双弧焊(double-electrode gas metal arc welding,DE-GMAW)焊接残余应力场分布,用ANSYS软件对焊接过程进行数值模拟,探索焊前预热对镁合金残余应力的影响规律。建立双弧热源模型,通过热应力耦合法,先计算焊接温度场进而计算应力场。获得焊件残余应力的分布规律,沿着焊缝纵向残余应力最大值约为41 MPa,焊缝两端即起弧和熄弧处受较大横向压应力作用,最大值达55.6 MPa;采用盲孔法进行试验测量,测量结果与模拟结果一致。通过实测数据与模拟结果分析,表明镁合金DE-GMAW焊接残余应力的分布特点;镁合金焊前预热温度为100℃时,能够有效降低焊件的残余应力。展开更多
实现铝钢良好连接的关键是有效控制焊接热输入,尽量降低中间层铝铁金属间化合物的厚度,一般认为中间层金属间化合物厚度小于10μm时铝钢接头质量良好。提出旁路耦合电弧熔钎焊方法,通过调节旁路电弧电流的大小来控制焊接热输入。在优化...实现铝钢良好连接的关键是有效控制焊接热输入,尽量降低中间层铝铁金属间化合物的厚度,一般认为中间层金属间化合物厚度小于10μm时铝钢接头质量良好。提出旁路耦合电弧熔钎焊方法,通过调节旁路电弧电流的大小来控制焊接热输入。在优化控制系统和工艺参数的基础上采用脉冲旁路耦合电弧焊方法将铝镁合金ER5356堆焊到304不锈钢板上,获得结合良好的焊缝。对焊接接头进行扫描电镜(Scanning electron microscope,SEM)、能量色散光谱仪(Energy dispersive spectrometry,EDS)分析,结果表明:铝与不锈钢焊接接头中间层金属间化合物平均厚度约为8μm,小于10μm的临界厚度;脉冲旁路耦合电弧焊方法能够实现铝钢的连接,是一种新型低成本低热输入电弧焊方法。展开更多
在介绍了双丝旁路耦合电弧熔化极气体保护焊(双丝旁路耦合电弧(Double-electrode gas metal arc welding,DE-GMAW))高效焊接工艺原理的基础之上,采用双闭环反馈解耦智能控制系统,进行双丝旁路耦合电弧GMAW高速焊接工艺试验,测量双丝旁...在介绍了双丝旁路耦合电弧熔化极气体保护焊(双丝旁路耦合电弧(Double-electrode gas metal arc welding,DE-GMAW))高效焊接工艺原理的基础之上,采用双闭环反馈解耦智能控制系统,进行双丝旁路耦合电弧GMAW高速焊接工艺试验,测量双丝旁路耦合电弧GMAW母材热输入,分析双丝旁路耦合电弧GMAW高效焊接工艺机理,并对双丝旁路耦合电弧GMAW高效焊接工艺方法进行改进,进一步研究混合气体保护下的双丝旁路耦合电弧GMAW及其熔滴过渡行为,且开发出单电源双丝旁路耦合电弧GMAW。研究表明:采用双闭环反馈解耦智能控制系统使双丝旁路耦合电弧GMAW焊接过程稳定性更好、精确度更高且响应速度更快;旁路分流是实现高效焊接的同时降低母材热输入的关键;采用混合气体保护下的双丝旁路耦合电弧GMAW能进一步提高焊接过程稳定性,单电源双丝旁路耦合电弧GMAW能形成良好的焊缝成形,且设备成本低。展开更多
基金The authors wish to thank the financial support for this research from the National Natural Science Foundation of China （Grant No. 50675119）.
文摘Modern manufacturing industry demands low cost and high efficient welding processes to remain competitiveness in the time of globalization. In this study, conventional gas metal arc welding （GMAW） was modified, a double-electrode GMAW （DE-GMAW） system is developed and DE-GMAW process is implemented through optimization of the design and process parameters and suitable selection of igniting sequence of double arcs. High speed welding tests were carried out to examine the effects of different factors on occurrence of weld formation defects. Through observing the weld bead appearance in DE-GMA W, the values of critical welding speed were determined under different levels of welding current and welding speed.
文摘为获取AZ31B镁合金薄板非熔化极气体保护双弧焊(double-electrode gas metal arc welding,DE-GMAW)焊接残余应力场分布,用ANSYS软件对焊接过程进行数值模拟,探索焊前预热对镁合金残余应力的影响规律。建立双弧热源模型,通过热应力耦合法,先计算焊接温度场进而计算应力场。获得焊件残余应力的分布规律,沿着焊缝纵向残余应力最大值约为41 MPa,焊缝两端即起弧和熄弧处受较大横向压应力作用,最大值达55.6 MPa;采用盲孔法进行试验测量,测量结果与模拟结果一致。通过实测数据与模拟结果分析,表明镁合金DE-GMAW焊接残余应力的分布特点;镁合金焊前预热温度为100℃时,能够有效降低焊件的残余应力。
文摘实现铝钢良好连接的关键是有效控制焊接热输入,尽量降低中间层铝铁金属间化合物的厚度,一般认为中间层金属间化合物厚度小于10μm时铝钢接头质量良好。提出旁路耦合电弧熔钎焊方法,通过调节旁路电弧电流的大小来控制焊接热输入。在优化控制系统和工艺参数的基础上采用脉冲旁路耦合电弧焊方法将铝镁合金ER5356堆焊到304不锈钢板上,获得结合良好的焊缝。对焊接接头进行扫描电镜(Scanning electron microscope,SEM)、能量色散光谱仪(Energy dispersive spectrometry,EDS)分析,结果表明:铝与不锈钢焊接接头中间层金属间化合物平均厚度约为8μm,小于10μm的临界厚度;脉冲旁路耦合电弧焊方法能够实现铝钢的连接,是一种新型低成本低热输入电弧焊方法。
文摘在介绍了双丝旁路耦合电弧熔化极气体保护焊(双丝旁路耦合电弧(Double-electrode gas metal arc welding,DE-GMAW))高效焊接工艺原理的基础之上,采用双闭环反馈解耦智能控制系统,进行双丝旁路耦合电弧GMAW高速焊接工艺试验,测量双丝旁路耦合电弧GMAW母材热输入,分析双丝旁路耦合电弧GMAW高效焊接工艺机理,并对双丝旁路耦合电弧GMAW高效焊接工艺方法进行改进,进一步研究混合气体保护下的双丝旁路耦合电弧GMAW及其熔滴过渡行为,且开发出单电源双丝旁路耦合电弧GMAW。研究表明:采用双闭环反馈解耦智能控制系统使双丝旁路耦合电弧GMAW焊接过程稳定性更好、精确度更高且响应速度更快;旁路分流是实现高效焊接的同时降低母材热输入的关键;采用混合气体保护下的双丝旁路耦合电弧GMAW能进一步提高焊接过程稳定性,单电源双丝旁路耦合电弧GMAW能形成良好的焊缝成形,且设备成本低。