In this study, electrorheological （ER） behavior of suspensions prepared from 3.0 and 9.0 μm diatomite particulate, dispersed in insulating silicone oil （SO） medium was investigated. Sedimentation stabilities of s...In this study, electrorheological （ER） behavior of suspensions prepared from 3.0 and 9.0 μm diatomite particulate, dispersed in insulating silicone oil （SO） medium was investigated. Sedimentation stabilities of suspensions （c = 5 wt%） prepared using these diatomite powders were determined to be 32 days （d = 3 μm） and 24 days （d = 9 μm）, respectively. ER activity of all the suspensions was observed to increase with increasing electric field strength, concentration and decreasing shear rate. Shear stress of diatomite suspensions increased linearly with increasing concentrations of the particles and with the applied electric field strength. Electric field viscosity of all the suspensions decreased sharply with increasing shear rate and particle size, showing a typical shear thinning non-Newtonian visco-elastic behavior. Effects of high temperature and polar promoter onto ER activity ofdiatomite/SO system were also investigated.展开更多
In this study, the electrorheological （ER） behavior of suspensions prepared from d50 = 2.4 lam talc powder, dispersed in insulating silicone oil （SO） medium was investigated. Sedimentation stabilities of suspensio...In this study, the electrorheological （ER） behavior of suspensions prepared from d50 = 2.4 lam talc powder, dispersed in insulating silicone oil （SO） medium was investigated. Sedimentation stabilities of suspensions （c = 5 wt%） prepared using these talc powder powders were determined to be 78 days. The ER activity of all the suspensions was observed to increase with increasing electric field strength, concentration and decreasing shear rate. The shear stress of talc powder suspensions increased linearly with increasing concentrations of the particles and with the applied electric field strength. Electric field viscosity of all the suspensions decreased sharply with increasing shear rate and showed a typical shear thinning non-Newtonian visco-elastic behavior. Effects of frequency on the ER activity of talc powder/SO system were also investigated.展开更多
Molecularly imprinted polymers using 2,4-dichlorophenoxyacetic acid （2,4-D） as templates were prepared by suspension polymerization in silicon oil. The polymer particles exhibited regular shape in the micro-scale ra...Molecularly imprinted polymers using 2,4-dichlorophenoxyacetic acid （2,4-D） as templates were prepared by suspension polymerization in silicon oil. The polymer particles exhibited regular shape in the micro-scale range. The adsorbing experiments indicated that the imprinted polymer particles possessed higher affinity to 2,4-D than the non-imprinted polymer particles.展开更多
文摘In this study, electrorheological （ER） behavior of suspensions prepared from 3.0 and 9.0 μm diatomite particulate, dispersed in insulating silicone oil （SO） medium was investigated. Sedimentation stabilities of suspensions （c = 5 wt%） prepared using these diatomite powders were determined to be 32 days （d = 3 μm） and 24 days （d = 9 μm）, respectively. ER activity of all the suspensions was observed to increase with increasing electric field strength, concentration and decreasing shear rate. Shear stress of diatomite suspensions increased linearly with increasing concentrations of the particles and with the applied electric field strength. Electric field viscosity of all the suspensions decreased sharply with increasing shear rate and particle size, showing a typical shear thinning non-Newtonian visco-elastic behavior. Effects of high temperature and polar promoter onto ER activity ofdiatomite/SO system were also investigated.
基金This work was supported by the Omya Mining Co of Istanbul and Harran University.
文摘In this study, the electrorheological （ER） behavior of suspensions prepared from d50 = 2.4 lam talc powder, dispersed in insulating silicone oil （SO） medium was investigated. Sedimentation stabilities of suspensions （c = 5 wt%） prepared using these talc powder powders were determined to be 78 days. The ER activity of all the suspensions was observed to increase with increasing electric field strength, concentration and decreasing shear rate. The shear stress of talc powder suspensions increased linearly with increasing concentrations of the particles and with the applied electric field strength. Electric field viscosity of all the suspensions decreased sharply with increasing shear rate and showed a typical shear thinning non-Newtonian visco-elastic behavior. Effects of frequency on the ER activity of talc powder/SO system were also investigated.
基金supported by the National Natural Science Foundation of China(No 20274052).
文摘Molecularly imprinted polymers using 2,4-dichlorophenoxyacetic acid （2,4-D） as templates were prepared by suspension polymerization in silicon oil. The polymer particles exhibited regular shape in the micro-scale range. The adsorbing experiments indicated that the imprinted polymer particles possessed higher affinity to 2,4-D than the non-imprinted polymer particles.