The effect of back-diffusion of Mg dopants on optoelectronic characteristics of InGaN-based green light-emitting diodes (LEDs) is investigated. The LEDs with less Mg back-diffusion show blue shifts of longer wavelen...The effect of back-diffusion of Mg dopants on optoelectronic characteristics of InGaN-based green light-emitting diodes (LEDs) is investigated. The LEDs with less Mg back-diffusion show blue shifts of longer wavelengths and larger wavelengths with the increasing current, which results from the Mg-dopant-related polarization screening. The LEDs show enhanced efficiency with the decreasing Mg back-diffusion in the lower current region. Light outputs follow the power law L α I^m, with smaller parameter m in the LEDs with less Mg back-diffusion, indicating a lower density of trap states. The trap-assisted tunneling current is also suppressed by reducing Mg- defect-related nonradiative centers in the active region. Furthermore, the forward current-voltage characteristics are improved.展开更多
TiO2 nano powders with Mn concentration of 0 at%-12 at% were synthesized by the sol-gel process, and were annealed at 500 ℃ and 800 ℃ in air for 2 hrs. X-ray diffraction (XRD) measurements indicate that the Mn-TiO...TiO2 nano powders with Mn concentration of 0 at%-12 at% were synthesized by the sol-gel process, and were annealed at 500 ℃ and 800 ℃ in air for 2 hrs. X-ray diffraction (XRD) measurements indicate that the Mn-TiO2 nano powders with Mn concentration of 1 at% and 2 at% annealed at 500 and 800 ℃ are of pure anatase and rutile, respectively. The scanning electron microscope (SEM) observations reveal that the crystal grain size increases with the annealing temperature, and the high resolution transmission electron microscopy (HRTEM) investigations further indicate that the samples are well crystallized, confirming that Mn has doped into the TiO2 crystal lattice effectively. The room temperature ferromagnetism, which could be explained within the scope of the bound magnetic polaron (BMP) theory, is detected in the Mn-TiO2 samples with Mn concentration of 2 at%, and the magnetization of the powders annealed at 500 ℃ is stronger than that of the sample treated at 800 ℃. The UV-VIS diffuse reflectance spectra results demonstrate that the absorption of the TiO2 powders could be enlarged by the enhanced trapped electron absorption caused by Mn doping.展开更多
Acoustic structure study always is the academic research interest. Diffusion ab?sorbing structure(DiflFsorber) has good research value because it has both diflFusion property and sound absorption property. Quadrati...Acoustic structure study always is the academic research interest. Diffusion ab?sorbing structure(DiflFsorber) has good research value because it has both diflFusion property and sound absorption property. Quadratic residue diffusers(QRD) structure which had good diffusion property was combined with the perforated panel which had good sound absorption property in this study. According to standard AES-4id-2001, the diffusion experiments were carried out to study QRD structure and ones composited with perforated-panels which had1 mm-thickness and perforated percentage of 3%, 5%, 8% respectively. The polar coordinate diagrams of different structure were analyzed to derive the diffusion coefficients. Results showed that the composite structure still had good diffusion performance in the frequency range from100 Hz to 800 Hz. The reflection sound energy of composite structure reduced obviously in the perforated panel resonance frequency range where there was about 2 dB reduction averagely.The study result can provide the reference for the design and development of diifsorber.展开更多
Similar diffusion bonding of 1Cr11Ni2W2MoV stainless steel was conducted at different bonding tem- peratures. The interface characteristics and mechanical properties of joints were examined, and the evolution of inter...Similar diffusion bonding of 1Cr11Ni2W2MoV stainless steel was conducted at different bonding tem- peratures. The interface characteristics and mechanical properties of joints were examined, and the evolution of interracial void morphology was analyzed in detail The results showed that there were four typical interfacial void shapes generating sequentially: the large scraggly voids, penny-shaped voids, ellipse voids and rounded voids. The variation of interracial void shape was dominated by surface diffusion, while the reduction of void volume was ascribed to the combined effects of plastic flow of materials around voids, interface diffusion and volume diffusion. Owing to the elimination of void from the bonding interface, the sound joint obtained could exhibit nearly full interracial contact, and present excellent mechanical properties, in which the microhardness and shear strength of joint matched those of base material.展开更多
基金Supported by the National Natural Science Foundation of China under Grant Nos 61505197 and 61334009the National High-Technology Research and Development Program of China under Grant No 2014AA032604
文摘The effect of back-diffusion of Mg dopants on optoelectronic characteristics of InGaN-based green light-emitting diodes (LEDs) is investigated. The LEDs with less Mg back-diffusion show blue shifts of longer wavelengths and larger wavelengths with the increasing current, which results from the Mg-dopant-related polarization screening. The LEDs show enhanced efficiency with the decreasing Mg back-diffusion in the lower current region. Light outputs follow the power law L α I^m, with smaller parameter m in the LEDs with less Mg back-diffusion, indicating a lower density of trap states. The trap-assisted tunneling current is also suppressed by reducing Mg- defect-related nonradiative centers in the active region. Furthermore, the forward current-voltage characteristics are improved.
基金Project supported by the Innovation Foundation of BUAA for PhD Graduates (Grant No. 292122)Equipment Research Foundation of China
文摘TiO2 nano powders with Mn concentration of 0 at%-12 at% were synthesized by the sol-gel process, and were annealed at 500 ℃ and 800 ℃ in air for 2 hrs. X-ray diffraction (XRD) measurements indicate that the Mn-TiO2 nano powders with Mn concentration of 1 at% and 2 at% annealed at 500 and 800 ℃ are of pure anatase and rutile, respectively. The scanning electron microscope (SEM) observations reveal that the crystal grain size increases with the annealing temperature, and the high resolution transmission electron microscopy (HRTEM) investigations further indicate that the samples are well crystallized, confirming that Mn has doped into the TiO2 crystal lattice effectively. The room temperature ferromagnetism, which could be explained within the scope of the bound magnetic polaron (BMP) theory, is detected in the Mn-TiO2 samples with Mn concentration of 2 at%, and the magnetization of the powders annealed at 500 ℃ is stronger than that of the sample treated at 800 ℃. The UV-VIS diffuse reflectance spectra results demonstrate that the absorption of the TiO2 powders could be enlarged by the enhanced trapped electron absorption caused by Mn doping.
基金supported by the National Natural Science Foundation of China(11004133)open project of China communication and transportation industry key laboratory of environmental technology
文摘Acoustic structure study always is the academic research interest. Diffusion ab?sorbing structure(DiflFsorber) has good research value because it has both diflFusion property and sound absorption property. Quadratic residue diffusers(QRD) structure which had good diffusion property was combined with the perforated panel which had good sound absorption property in this study. According to standard AES-4id-2001, the diffusion experiments were carried out to study QRD structure and ones composited with perforated-panels which had1 mm-thickness and perforated percentage of 3%, 5%, 8% respectively. The polar coordinate diagrams of different structure were analyzed to derive the diffusion coefficients. Results showed that the composite structure still had good diffusion performance in the frequency range from100 Hz to 800 Hz. The reflection sound energy of composite structure reduced obviously in the perforated panel resonance frequency range where there was about 2 dB reduction averagely.The study result can provide the reference for the design and development of diifsorber.
基金supported by the National Natural Science Foundation of China (No. 51505386 and No. 51275416)the China Postdoctoral Science Foundation (No. 2014M562447)the Research Fund of the State Key Laboratory of Solidification Processing (NWPU), China (16-BZ-2015)
文摘Similar diffusion bonding of 1Cr11Ni2W2MoV stainless steel was conducted at different bonding tem- peratures. The interface characteristics and mechanical properties of joints were examined, and the evolution of interracial void morphology was analyzed in detail The results showed that there were four typical interfacial void shapes generating sequentially: the large scraggly voids, penny-shaped voids, ellipse voids and rounded voids. The variation of interracial void shape was dominated by surface diffusion, while the reduction of void volume was ascribed to the combined effects of plastic flow of materials around voids, interface diffusion and volume diffusion. Owing to the elimination of void from the bonding interface, the sound joint obtained could exhibit nearly full interracial contact, and present excellent mechanical properties, in which the microhardness and shear strength of joint matched those of base material.