The purpose of this paper is to study large-sized copper billets refined with 5N ultrahigh purity after vacuum melting and directional solidifi-cation (VMDS). The precise impurity analysis of copper billets was carr...The purpose of this paper is to study large-sized copper billets refined with 5N ultrahigh purity after vacuum melting and directional solidifi-cation (VMDS). The precise impurity analysis of copper billets was carried out with a glow discharge mass spectrometer (GDMS). The re-sults demonstrate that the total concentration of twenty-two impurities is decreased by 63.1wt.%-66.5 wt.%. Ag, P, S, Na, Mg, Se, Zn, In and Bi are easy to be removed due to lgPimp - lgPCu 1.5, and they can be removed effectively under the vacuum condition of 1650-1700 K for 30 min. The electrical conductivity of 5N copper is higher than that of the raw material as the impurity concentrations decrease. The segrega-tion effect in directional solidification can be remarkable when the equilibrium distribution coefficient (k0) value is less than 0.65 due to the strong affinity of Cu for some metallic and non-metallic impurities.展开更多
Directional solidified turbine blades of Ni-based superalloy are widely used as key parts of the gas turbine engines.The mechanical properties of the blade are greatly influenced by the final microstructure and the gr...Directional solidified turbine blades of Ni-based superalloy are widely used as key parts of the gas turbine engines.The mechanical properties of the blade are greatly influenced by the final microstructure and the grain orientation determined directly by the grain selector geometry of the casting.In this paper,mathematical models were proposed for three dimensional simulation of the grain growth and microstructure evolution in directional solidification of turbine blade casting.Ray-tracing method was applied to calculate the temperature variation of the blade.Based on the thermo model of heat transfer,the competitive grain growth within the starter block and the spiral of the grain selector,the grain growth in the blade and the microstructure evolution were simulated via a modified Cellular Automaton method.Validation experiments were carried out,and the measured results were compared quantitatively with the predicted results.The simulated cooling curves and microstructures corresponded well with the experimental results.The proposed models could be used to predict the grain morphology and the competitive grain evolution during directional solidification.展开更多
Using a Bridgman vertical vacuum furnace,Ti-45Al-8Nb-(W,B,Y) (at.%) bars,which were prepared from a plasma arc melting (PAM) ingot,were directionally solidified at growth rates of 10,15,and 20 μm/s.Polysyntheti...Using a Bridgman vertical vacuum furnace,Ti-45Al-8Nb-(W,B,Y) (at.%) bars,which were prepared from a plasma arc melting (PAM) ingot,were directionally solidified at growth rates of 10,15,and 20 μm/s.Polysynthetic twinned (PST) crystal with an aligned lamellar microstructure was obtained at the growth rate of 15 μm/s because of high Nb addition.The principle of PST crystal growth and the effect of Nb element were discussed.The results of investigations on microstructure and micromechanical properties of the directionally solidified (DS) bars of Ti-45Al-8Nb-(W,B,Y) alloy are briefly summarized.展开更多
Phase field investigation reveals that the stability of the planar interface is related to the anisotropic intensity of surface tension and the misorientation of preferred crystallographic orientation with respect to ...Phase field investigation reveals that the stability of the planar interface is related to the anisotropic intensity of surface tension and the misorientation of preferred crystallographic orientation with respect to the heat flow direction. The large anisotropic intensity may compete to determine the stability of the planar interface. The destabilizing effect or the stabilizing effect depends on the misorientation. Moreover, the interface morphology of initial instability is also affected by the surface tension anisotropy.展开更多
As the key parts of an aero-engine,single crystal(SX)superalloy turbine blades have been the focus of much attention.However,casting defects often occur during the manufacturing process of the SX turbine blades.Modeli...As the key parts of an aero-engine,single crystal(SX)superalloy turbine blades have been the focus of much attention.However,casting defects often occur during the manufacturing process of the SX turbine blades.Modeling and simulation technology can help to optimize the manufacturing process of SX blades.Multiscale coupled models were proposed and used to simulate the physical phenomena occurring during the directional solidification(DS)process.Coupled with heat transfer(macroscale)and grain growth(meso-scale),3D dendritic grain growth was calculated to show the competitive grain growth at micro-scale.SX grain selection behavior was studied by the simulation and experiments.The results show that the geometrical structure and technical parameters had strong influences on the grain selection effectiveness.Based on the coupled models,heat transfer,grain growth and microstructure evolution of a complex hollow SX blade were simulated.Both the simulated and experimental results show that the stray grain occurred at the platform of the SX blade when a constant withdrawal rate was used in manufacturing process.In order to avoid the formation of the stray crystal,the multi-scale coupled models and the withdrawal rate optimized technique were applied to the same SX turbine blade.The modeling results indicated that the optimized variable withdrawal rate can achieve SX blade castings with no stray grains,which was also proved by the experiments.展开更多
The microstructure scales of dendrites, such as primary and secondary dendrite arm spacings, control the segregation profiles and the formation of secondary phases within interdendritic regions, which determine the pr...The microstructure scales of dendrites, such as primary and secondary dendrite arm spacings, control the segregation profiles and the formation of secondary phases within interdendritic regions, which determine the properties of solidified structures. Investigations on primary and secondary dendrite arm spacings of primary a-phase during directionally solidified Pb-26wt%Bi hypo-peritectic alloy were carried out in this research, and systematic studies were conducted using cylindrical samples with different diameters (Ф = 1.8 and 7.0 mm) in order to analyze the effects of sample diameter on the primary and secondary dendrite arm spacings. In this work, the dependence of dendrite arm spacings on growth velocity was established. In addition, the experimental data concerning the primary and secondary dendrite ann spacings were compared with the main predictive dendritic models from the literatures. A comparison between experimental results for dendrite arm spacings of the 1.8-mm-diameter sample and 7.0-ram-diameter sample was also conducted.展开更多
Bottomless electromagnetic cold crucible is a new apparatus for continuous melting and directional solidification;however,improving its power efficiency and optimizing the configuration are important for experiment an...Bottomless electromagnetic cold crucible is a new apparatus for continuous melting and directional solidification;however,improving its power efficiency and optimizing the configuration are important for experiment and production.In this study,a 3-D finite element (FE) method based on experimental verification was applied to calculate the magnetic flux density (Bz).The effects of the power parameters and the induction coil on the magnetic field distribution in the cold crucible were investigated.The results show that higher current intensity and lower frequency are beneficial to the increase of Bz at both the segment midpoint and the slit location.The induction coil with racetrack section can induce greater Bz,and a larger gap between the induction coil and the shield ring increases Bz.The mechanism for this effect is also discussed.展开更多
The intermetallic Ti-43Al-2Cr-2Nb(at.%) alloy was directionally solidified in an electromagnetic cold crucible with different withdrawal rates(V) ranging from 0.2 to 1.0 mm·min^(-1), at a constant temperature gra...The intermetallic Ti-43Al-2Cr-2Nb(at.%) alloy was directionally solidified in an electromagnetic cold crucible with different withdrawal rates(V) ranging from 0.2 to 1.0 mm·min^(-1), at a constant temperature gradients(G=18 K·mm^(-1)). Macrostructures of the alloy were observed by optical microscopy. Microstructures of the alloy were characterized by scanning electron microscopy(SEM) in back-scattered electron mode and transmission electron microscopy. Results showed that morphologies of macrostructure depend greatly on the applied withdrawal rate. Continuous columnar grains can be obtained under slow withdrawal rates ranging from 0.2 to 0.6 mm·min^(-1). The microstructure of the alloy was composed of α_2/γ lamellar structures and a small number of mixtures of B2 phases and blocky γ phases. The columnar grain size(d) and interlamellar spacing(λ) decrease with an increasing withdrawal rate. The effect of withdrawal rate on microhardness was also investigated. The microhardness of the directional y solidified Ti-43Al-2Cr-2Nb alloy increases with an increase in withdrawal rate. This is mainly attributed to the increase of B2 and α_2 phases as well as the refinement of lamellae.展开更多
Cold crucible directional solidification(CCDS)is a newly developed technique,which combines the advantages of the cold crucible and continuous melting.It can be applied to directionally solidify reactive,high purity a...Cold crucible directional solidification(CCDS)is a newly developed technique,which combines the advantages of the cold crucible and continuous melting.It can be applied to directionally solidify reactive,high purity and refractory materials.This paper describes the principle of CCDS and its characteristics;development of the measurement and numerical calculation of the magnetic field,flow field and temperature field in CCDS;and the CCDS of Ti based alloys.The paper also reviews original data obtained by some scholars,including the present authors,reported in separate publications in recent years.In Ti based alloys,Ti6Al4V,TiAl alloys and high Nb-containing TiAl alloys,have been directionally solidified in different cold crucibles.The crosssections of the cold crucibles include round,near rectangular and square with different sizes.Tensile testing results show that the elongation of directionally solidified Ti6Al4V can be improved to 12.7%from as cast5.4%.The strength and the elongation of the directionally solidified Ti47Al2Cr2Nb and Ti44Al6Nb1.0Cr2.0V are 650 MPa/3%and 602.5MPa/1.20%,respectively.The ingots after CCDS can be used to prepare turbine or engine blades,and are candidates to replace Ni super-alloy at temperatures of 700 to 900°C.展开更多
Straight plates, hollow columns, ear-like blade tips, twist plates withdirectional solidification microstructure made of Rene 95 superalloys were successfully fabricatedon Nickel-base superalloy and DD3 substrates, re...Straight plates, hollow columns, ear-like blade tips, twist plates withdirectional solidification microstructure made of Rene 95 superalloys were successfully fabricatedon Nickel-base superalloy and DD3 substrates, respectively. The processing conditions for productionof the parts with corresponding shapes were obtained. The fabrication precision was high and thecomponents were compact. The solidification microstructure of the parts was analyzed by opticalmicroscopy. The results show that the solidification microstructure is composed of columnardendrites, by epitaxial growth onto the directional solidification substrates. The crystallographyorientation of the parts was parallel to that of the substrates. The primary arm spacing was about10 mum, which is in the range of superfine dendrites, and the secondary arm was small or evendegenerated. It is concluded that the laser metal forming technique provides a method to manufacturedirectional solidification components.展开更多
This paper briefly reviews the recent research on the near rapid directional solidification and microstructure superfining. The morphology transitions and the corresponding mechanical properties are presented. The cri...This paper briefly reviews the recent research on the near rapid directional solidification and microstructure superfining. The morphology transitions and the corresponding mechanical properties are presented. The critical velocities relevant to the morphology transitions are comprehensively given. Meanwhile the solidification characteristics near absolute stability limit are studied.It can be clearly seen that the superfine microstructures possess extremely better properties compared with the conventional microstructures.展开更多
This paper considers the effect of the anisotropic surface tension on the morphological stability of the planar interface during directional solidification. When the expression exhibiting the four-fold symmetry is inc...This paper considers the effect of the anisotropic surface tension on the morphological stability of the planar interface during directional solidification. When the expression exhibiting the four-fold symmetry is included, the modified absolute stability criterion is obtained by employing the multi-variable expansion method. The linear stability analysis reveals that for the given temperature gradient, as the anisotropic surface tension parameter increases, the stability zone tends to decrease.展开更多
To further investigate the microstructure characteristic and solidification mechanism,so as to provide knowledge for the microstructure control of a NiTi-Al based high-temperature structural material,the microstructur...To further investigate the microstructure characteristic and solidification mechanism,so as to provide knowledge for the microstructure control of a NiTi-Al based high-temperature structural material,the microstructure of Ni-43Ti-4Al-2Nb-2Hf(at.%)alloy ingots prepared by conventional casting(arc-melting)and directional solidification (DS)at various drawing velocities(2 mm·min -1 ,18 mm·min -1 ,30 mm·min -1 and 60 mm·min -1 ,respectively)was investigated by means of electron probe microanalyses.Experimental results reveal that the microstructures are composed of NiTi matrix phase,β-Nb phase and Ti 2 Ni phase for samples obtained by both conventional casting and DS.Conventional casting has an equiaxial structure,while DS has a slender and acicular cellular structure which grows along the[001]orientation preferentially.Small amounts of whiteβ-Nb phase and black Ti 2 Ni phase co-exist at the grain boundaries or intercellular regions.With an increase in drawing velocity,the NiTi matrix phase is inclined to grow along(100)and(200)crystallographic planes,and the cellular arm spacing reduce gradually, but the directionality of the solidified structure weakens significantly.The homogeneous dispersion ofβ-Nb phase and the decrease of Ti2Ni phase in DS samples are beneficial to improving the mechanical properties.Solidification mechanism analysis indicates that the dark grey NiTi matrix phase initially precipitates from the liquid phase,and then the divorced eutectic reaction takes place,which produces the light gray matrix phase andβ-Nb phase.Finally, the peritectic reaction happens,which generates the black Ti2Ni phase.The complete solidified path of the alloy is L→NiTi+L→NiTi+β-Nb+L→NiTi+β-Nb+Ti 2 Ni.展开更多
In order to avoid contamination from the crucible and to modify the structures,a new solidification method based on cold crucible technology was used to prepare silicon ingots.A silicon ingot with square cross section...In order to avoid contamination from the crucible and to modify the structures,a new solidification method based on cold crucible technology was used to prepare silicon ingots.A silicon ingot with square cross section was directionally solidified with a cold crucible.The mechanism of the cold crucible directional solidification of silicon ingot was revealed.Due to the induction heat that was released in the surface layer and the incomplete contact between the crucible and the melt,the lateral heat loss was reduced and the silicon ingot was directionally solidified.The structures,dislocation defects and the grain growth orientation of the ingot were determined.The results show that neither intergranular nor intragranular precipitates are found in the ingot,except for the top part that was the last to solidify.The average dislocation density is about 1 to 2×106 cm-2.The grains are preferentially <220> orientated.展开更多
Directional solidification continuous casting (DSCC) process is a new manufacturing technology for metallic materials which combines advantages of both directional solidification technology and continuous casting tech...Directional solidification continuous casting (DSCC) process is a new manufacturing technology for metallic materials which combines advantages of both directional solidification technology and continuous casting technology. Unlimited long shaped metal with directionally solidifying microstructure can be produced by this process. It is experimentally shown that controlling condition of stable and continuous growth of single crystal structure means the precise control of the location of the S/L interface, which is affected and determined by seven process parameters. Moreover, these parameters are also interacted each other, so the disturbance of any parameters may cause the failure of controlling of S/L interface. In this paper, on the basis of analyzing the forming conditions of continuously directional microstructures in DSCC process, the control model of DSCC procedure by neural network control (NNC) method was proposed and discussed. Combining with the experiments, we first used the computer to simulate the effects of the solidification parameters on destination control variable (S/L interface) and the interactions among these parameters during DSCC procedure. Secondly many training samples necessary for neural network calculation can be obtained through the simulation. Moreover, these samples are inputted into neural network software (NNs) and trained, then the control model can be built up.展开更多
Zn-5wt% Al eutectic alloy was directionally solidified with different growth rates (5.32-250.0μm/s) at a constant temperature gradient of 8.50 K/mm using a Bridgman-type growth apparatus.The values of eutectic spac...Zn-5wt% Al eutectic alloy was directionally solidified with different growth rates (5.32-250.0μm/s) at a constant temperature gradient of 8.50 K/mm using a Bridgman-type growth apparatus.The values of eutectic spacing were measured from transverse sections of the samples.The dependences of the eutectic spacing and undercooling on growth rate are determined as λ=9.21V-0.53 and ΔT=0.0245V0.53,respectively.The results obtained in this work were compared with the Jackson-Hunt eutectic theory and the similar experimental results in the literature.Microhardness of directionally solidified samples was also measured by using a microhardness test device.The dependency of the microhardness on growth rate is found as Hv=115.64V0.13.Afterwards,the electrical resistivity (r) of the casting alloy changes from 40×10-9 to 108×10-9 Ω·m with the temperature rising in the range of 300-630 K.The enthalpy of fusion (ΔH) and specific heat (Cp) for the Zn-Al eutectic alloy are calculated to be 113.37 J/g and 0.309 J/(g·K),respectively by means of differential scanning calorimetry (DSC) from heating trace during the transformation from liquid to solid.展开更多
Microstructure Characteristic of Ni-Nb near eutectic alloy is systematically investigated during directional solidification with electron beam floating zone melting (EBFZM). The effect of the Zone melting rate on the ...Microstructure Characteristic of Ni-Nb near eutectic alloy is systematically investigated during directional solidification with electron beam floating zone melting (EBFZM). The effect of the Zone melting rate on the microstructure has also been studied.展开更多
The carbide growth behavior of MAR-M247 LC alloy was investigated by directional solidification and quench method. The carbide volume fraction, trapping and growth behavior were correlated with the growth rate.It was ...The carbide growth behavior of MAR-M247 LC alloy was investigated by directional solidification and quench method. The carbide volume fraction, trapping and growth behavior were correlated with the growth rate.It was found that the carbide volume fraction decreased at slower growth rate.This decreasing was caused by lower solidliquid interface trapping ability at slower growth rate.展开更多
A quantitative cellular automaton model is used to study the cell-to-dendrite transition(CDT) in directional solidification. We give a detailed description of the CDT by carefully examining the influence of the phys...A quantitative cellular automaton model is used to study the cell-to-dendrite transition(CDT) in directional solidification. We give a detailed description of the CDT by carefully examining the influence of the physical parameters, including:the Gibbs–Thomson coefficient Γ, the solute diffusivity Dl, the solute partition coefficient k0, and the liquidus slope ml. It is found that most of the parameters agree with the Kurz and Fisher(KF) criterion, except for k0. The intrinsic relations among the critical velocity Vcd, the cellular primary spacing λc,max, and the critical spacing λcd are investigated.展开更多
The effects of pulling velocity on the solidification behavior and microstructural parameters of A1Sil0Mg alloys prepared in a Bridgman-type directional solidification furnace were investigated. The microstructure, pa...The effects of pulling velocity on the solidification behavior and microstructural parameters of A1Sil0Mg alloys prepared in a Bridgman-type directional solidification furnace were investigated. The microstructure, particularly the secondary dendritic arm spacing (SDAS), and the Brinell hardness (BH) of the solidified A1Sil0Mg alloys were characterized for samples with cylindrical shapes and differ- ent conicities (θ = 0°, 5°, and 10°). Microstructural studies revealed an increased density of ct-A1 phase dendrites and a decreased interden- dritic distance with increasing pulling velocity. The dendrites were found to be preferentially oriented along the pulling direction for low pulling velocities. For larger pulling velocities, the dendrites grew first in the cooling direction but then broke as others nucleated and coars- ened. The HB values of the solidified samples increased as the pulling velocity increased. In regard to sample conicity, smaller dendrites were observed for an apex angle of θ = 5°, resulting in the largest HB value. This result was interpreted in terms of the favorable orientation of the dendrite along the pulling direction.展开更多
文摘The purpose of this paper is to study large-sized copper billets refined with 5N ultrahigh purity after vacuum melting and directional solidifi-cation (VMDS). The precise impurity analysis of copper billets was carried out with a glow discharge mass spectrometer (GDMS). The re-sults demonstrate that the total concentration of twenty-two impurities is decreased by 63.1wt.%-66.5 wt.%. Ag, P, S, Na, Mg, Se, Zn, In and Bi are easy to be removed due to lgPimp - lgPCu 1.5, and they can be removed effectively under the vacuum condition of 1650-1700 K for 30 min. The electrical conductivity of 5N copper is higher than that of the raw material as the impurity concentrations decrease. The segrega-tion effect in directional solidification can be remarkable when the equilibrium distribution coefficient (k0) value is less than 0.65 due to the strong affinity of Cu for some metallic and non-metallic impurities.
基金financially supported by the National Basic Research Program of China (No.2005CB724105,2011CB706801)National Natural Science Foundation of China (No.10477010)+1 种基金National High Technology Research,Development Program of China (No.2007AA04Z141)Important National Science & Technology Specific Projects (No.2009ZX04006-041,2011ZX04014-052)
文摘Directional solidified turbine blades of Ni-based superalloy are widely used as key parts of the gas turbine engines.The mechanical properties of the blade are greatly influenced by the final microstructure and the grain orientation determined directly by the grain selector geometry of the casting.In this paper,mathematical models were proposed for three dimensional simulation of the grain growth and microstructure evolution in directional solidification of turbine blade casting.Ray-tracing method was applied to calculate the temperature variation of the blade.Based on the thermo model of heat transfer,the competitive grain growth within the starter block and the spiral of the grain selector,the grain growth in the blade and the microstructure evolution were simulated via a modified Cellular Automaton method.Validation experiments were carried out,and the measured results were compared quantitatively with the predicted results.The simulated cooling curves and microstructures corresponded well with the experimental results.The proposed models could be used to predict the grain morphology and the competitive grain evolution during directional solidification.
基金supported by the National Natural Science Foundation of China (No. 50771013)
文摘Using a Bridgman vertical vacuum furnace,Ti-45Al-8Nb-(W,B,Y) (at.%) bars,which were prepared from a plasma arc melting (PAM) ingot,were directionally solidified at growth rates of 10,15,and 20 μm/s.Polysynthetic twinned (PST) crystal with an aligned lamellar microstructure was obtained at the growth rate of 15 μm/s because of high Nb addition.The principle of PST crystal growth and the effect of Nb element were discussed.The results of investigations on microstructure and micromechanical properties of the directionally solidified (DS) bars of Ti-45Al-8Nb-(W,B,Y) alloy are briefly summarized.
基金Project supported by the National Natural Science Foundation of China (Grant No. 50401013)the State Key Laboratory of Solidification Processing in Northwestern Polytechnical University of China (NWPU) (Grant No. KP200903)
文摘Phase field investigation reveals that the stability of the planar interface is related to the anisotropic intensity of surface tension and the misorientation of preferred crystallographic orientation with respect to the heat flow direction. The large anisotropic intensity may compete to determine the stability of the planar interface. The destabilizing effect or the stabilizing effect depends on the misorientation. Moreover, the interface morphology of initial instability is also affected by the surface tension anisotropy.
基金supported by the National Basic Research Program of China(No.2011CB706801)the National Natural Science Foundation of China(Nos.51171089 and 51374137)the National Science and Technology Major Project(Nos.2011ZX04014-052 and 2012ZX04012-011)
文摘As the key parts of an aero-engine,single crystal(SX)superalloy turbine blades have been the focus of much attention.However,casting defects often occur during the manufacturing process of the SX turbine blades.Modeling and simulation technology can help to optimize the manufacturing process of SX blades.Multiscale coupled models were proposed and used to simulate the physical phenomena occurring during the directional solidification(DS)process.Coupled with heat transfer(macroscale)and grain growth(meso-scale),3D dendritic grain growth was calculated to show the competitive grain growth at micro-scale.SX grain selection behavior was studied by the simulation and experiments.The results show that the geometrical structure and technical parameters had strong influences on the grain selection effectiveness.Based on the coupled models,heat transfer,grain growth and microstructure evolution of a complex hollow SX blade were simulated.Both the simulated and experimental results show that the stray grain occurred at the platform of the SX blade when a constant withdrawal rate was used in manufacturing process.In order to avoid the formation of the stray crystal,the multi-scale coupled models and the withdrawal rate optimized technique were applied to the same SX turbine blade.The modeling results indicated that the optimized variable withdrawal rate can achieve SX blade castings with no stray grains,which was also proved by the experiments.
基金supported by the China Postdoctoral Science Foundation (No. 20110491492)National Natural Science Foundation of China (No. 50765005)the Innovative Group of Science and Technology of College of Jiangxi Province,China (No. 00008713)
文摘The microstructure scales of dendrites, such as primary and secondary dendrite arm spacings, control the segregation profiles and the formation of secondary phases within interdendritic regions, which determine the properties of solidified structures. Investigations on primary and secondary dendrite arm spacings of primary a-phase during directionally solidified Pb-26wt%Bi hypo-peritectic alloy were carried out in this research, and systematic studies were conducted using cylindrical samples with different diameters (Ф = 1.8 and 7.0 mm) in order to analyze the effects of sample diameter on the primary and secondary dendrite arm spacings. In this work, the dependence of dendrite arm spacings on growth velocity was established. In addition, the experimental data concerning the primary and secondary dendrite ann spacings were compared with the main predictive dendritic models from the literatures. A comparison between experimental results for dendrite arm spacings of the 1.8-mm-diameter sample and 7.0-ram-diameter sample was also conducted.
基金financially supported by the National Basic Research Program of China (Grant No.2011CB605504)
文摘Bottomless electromagnetic cold crucible is a new apparatus for continuous melting and directional solidification;however,improving its power efficiency and optimizing the configuration are important for experiment and production.In this study,a 3-D finite element (FE) method based on experimental verification was applied to calculate the magnetic flux density (Bz).The effects of the power parameters and the induction coil on the magnetic field distribution in the cold crucible were investigated.The results show that higher current intensity and lower frequency are beneficial to the increase of Bz at both the segment midpoint and the slit location.The induction coil with racetrack section can induce greater Bz,and a larger gap between the induction coil and the shield ring increases Bz.The mechanism for this effect is also discussed.
基金supported by the National Natural Science Foundation of China(Grant No.51171053 and No.51471062)
文摘The intermetallic Ti-43Al-2Cr-2Nb(at.%) alloy was directionally solidified in an electromagnetic cold crucible with different withdrawal rates(V) ranging from 0.2 to 1.0 mm·min^(-1), at a constant temperature gradients(G=18 K·mm^(-1)). Macrostructures of the alloy were observed by optical microscopy. Microstructures of the alloy were characterized by scanning electron microscopy(SEM) in back-scattered electron mode and transmission electron microscopy. Results showed that morphologies of macrostructure depend greatly on the applied withdrawal rate. Continuous columnar grains can be obtained under slow withdrawal rates ranging from 0.2 to 0.6 mm·min^(-1). The microstructure of the alloy was composed of α_2/γ lamellar structures and a small number of mixtures of B2 phases and blocky γ phases. The columnar grain size(d) and interlamellar spacing(λ) decrease with an increasing withdrawal rate. The effect of withdrawal rate on microhardness was also investigated. The microhardness of the directional y solidified Ti-43Al-2Cr-2Nb alloy increases with an increase in withdrawal rate. This is mainly attributed to the increase of B2 and α_2 phases as well as the refinement of lamellae.
基金supported by the National Natural Science Foundation of China(51274076)the Program of New Century Excellent Talents in University(NCET-12-0153)the National Basic Research Program of China(2011CB605504)
文摘Cold crucible directional solidification(CCDS)is a newly developed technique,which combines the advantages of the cold crucible and continuous melting.It can be applied to directionally solidify reactive,high purity and refractory materials.This paper describes the principle of CCDS and its characteristics;development of the measurement and numerical calculation of the magnetic field,flow field and temperature field in CCDS;and the CCDS of Ti based alloys.The paper also reviews original data obtained by some scholars,including the present authors,reported in separate publications in recent years.In Ti based alloys,Ti6Al4V,TiAl alloys and high Nb-containing TiAl alloys,have been directionally solidified in different cold crucibles.The crosssections of the cold crucibles include round,near rectangular and square with different sizes.Tensile testing results show that the elongation of directionally solidified Ti6Al4V can be improved to 12.7%from as cast5.4%.The strength and the elongation of the directionally solidified Ti47Al2Cr2Nb and Ti44Al6Nb1.0Cr2.0V are 650 MPa/3%and 602.5MPa/1.20%,respectively.The ingots after CCDS can be used to prepare turbine or engine blades,and are candidates to replace Ni super-alloy at temperatures of 700 to 900°C.
基金This research was financially supported by the National High Technology Research and Development Program of China (No.2001AA337020)the Development Plan of State Key Fundamental Research of China (No. G2000067205-3)
文摘Straight plates, hollow columns, ear-like blade tips, twist plates withdirectional solidification microstructure made of Rene 95 superalloys were successfully fabricatedon Nickel-base superalloy and DD3 substrates, respectively. The processing conditions for productionof the parts with corresponding shapes were obtained. The fabrication precision was high and thecomponents were compact. The solidification microstructure of the parts was analyzed by opticalmicroscopy. The results show that the solidification microstructure is composed of columnardendrites, by epitaxial growth onto the directional solidification substrates. The crystallographyorientation of the parts was parallel to that of the substrates. The primary arm spacing was about10 mum, which is in the range of superfine dendrites, and the secondary arm was small or evendegenerated. It is concluded that the laser metal forming technique provides a method to manufacturedirectional solidification components.
文摘This paper briefly reviews the recent research on the near rapid directional solidification and microstructure superfining. The morphology transitions and the corresponding mechanical properties are presented. The critical velocities relevant to the morphology transitions are comprehensively given. Meanwhile the solidification characteristics near absolute stability limit are studied.It can be clearly seen that the superfine microstructures possess extremely better properties compared with the conventional microstructures.
基金Project supported by the National Basic Research Program of China (the Project 973) (Grant No 2006CB605205)the National Natural Science Foundation of China (Grant No 10672019)
文摘This paper considers the effect of the anisotropic surface tension on the morphological stability of the planar interface during directional solidification. When the expression exhibiting the four-fold symmetry is included, the modified absolute stability criterion is obtained by employing the multi-variable expansion method. The linear stability analysis reveals that for the given temperature gradient, as the anisotropic surface tension parameter increases, the stability zone tends to decrease.
基金supported by the Natural Science Foundation of China(Grant No.51101003)
文摘To further investigate the microstructure characteristic and solidification mechanism,so as to provide knowledge for the microstructure control of a NiTi-Al based high-temperature structural material,the microstructure of Ni-43Ti-4Al-2Nb-2Hf(at.%)alloy ingots prepared by conventional casting(arc-melting)and directional solidification (DS)at various drawing velocities(2 mm·min -1 ,18 mm·min -1 ,30 mm·min -1 and 60 mm·min -1 ,respectively)was investigated by means of electron probe microanalyses.Experimental results reveal that the microstructures are composed of NiTi matrix phase,β-Nb phase and Ti 2 Ni phase for samples obtained by both conventional casting and DS.Conventional casting has an equiaxial structure,while DS has a slender and acicular cellular structure which grows along the[001]orientation preferentially.Small amounts of whiteβ-Nb phase and black Ti 2 Ni phase co-exist at the grain boundaries or intercellular regions.With an increase in drawing velocity,the NiTi matrix phase is inclined to grow along(100)and(200)crystallographic planes,and the cellular arm spacing reduce gradually, but the directionality of the solidified structure weakens significantly.The homogeneous dispersion ofβ-Nb phase and the decrease of Ti2Ni phase in DS samples are beneficial to improving the mechanical properties.Solidification mechanism analysis indicates that the dark grey NiTi matrix phase initially precipitates from the liquid phase,and then the divorced eutectic reaction takes place,which produces the light gray matrix phase andβ-Nb phase.Finally, the peritectic reaction happens,which generates the black Ti2Ni phase.The complete solidified path of the alloy is L→NiTi+L→NiTi+β-Nb+L→NiTi+β-Nb+Ti 2 Ni.
基金financially supported by the National Natural Science Foundation of China (No.50804012)the Natural Science Foundation of Hei Longjiang Province,China (No.E201002)
文摘In order to avoid contamination from the crucible and to modify the structures,a new solidification method based on cold crucible technology was used to prepare silicon ingots.A silicon ingot with square cross section was directionally solidified with a cold crucible.The mechanism of the cold crucible directional solidification of silicon ingot was revealed.Due to the induction heat that was released in the surface layer and the incomplete contact between the crucible and the melt,the lateral heat loss was reduced and the silicon ingot was directionally solidified.The structures,dislocation defects and the grain growth orientation of the ingot were determined.The results show that neither intergranular nor intragranular precipitates are found in the ingot,except for the top part that was the last to solidify.The average dislocation density is about 1 to 2×106 cm-2.The grains are preferentially <220> orientated.
文摘Directional solidification continuous casting (DSCC) process is a new manufacturing technology for metallic materials which combines advantages of both directional solidification technology and continuous casting technology. Unlimited long shaped metal with directionally solidifying microstructure can be produced by this process. It is experimentally shown that controlling condition of stable and continuous growth of single crystal structure means the precise control of the location of the S/L interface, which is affected and determined by seven process parameters. Moreover, these parameters are also interacted each other, so the disturbance of any parameters may cause the failure of controlling of S/L interface. In this paper, on the basis of analyzing the forming conditions of continuously directional microstructures in DSCC process, the control model of DSCC procedure by neural network control (NNC) method was proposed and discussed. Combining with the experiments, we first used the computer to simulate the effects of the solidification parameters on destination control variable (S/L interface) and the interactions among these parameters during DSCC procedure. Secondly many training samples necessary for neural network calculation can be obtained through the simulation. Moreover, these samples are inputted into neural network software (NNs) and trained, then the control model can be built up.
基金supported by Erciyes University Scientific Research Project Unit (No.FBA-10-3376)
文摘Zn-5wt% Al eutectic alloy was directionally solidified with different growth rates (5.32-250.0μm/s) at a constant temperature gradient of 8.50 K/mm using a Bridgman-type growth apparatus.The values of eutectic spacing were measured from transverse sections of the samples.The dependences of the eutectic spacing and undercooling on growth rate are determined as λ=9.21V-0.53 and ΔT=0.0245V0.53,respectively.The results obtained in this work were compared with the Jackson-Hunt eutectic theory and the similar experimental results in the literature.Microhardness of directionally solidified samples was also measured by using a microhardness test device.The dependency of the microhardness on growth rate is found as Hv=115.64V0.13.Afterwards,the electrical resistivity (r) of the casting alloy changes from 40×10-9 to 108×10-9 Ω·m with the temperature rising in the range of 300-630 K.The enthalpy of fusion (ΔH) and specific heat (Cp) for the Zn-Al eutectic alloy are calculated to be 113.37 J/g and 0.309 J/(g·K),respectively by means of differential scanning calorimetry (DSC) from heating trace during the transformation from liquid to solid.
文摘Microstructure Characteristic of Ni-Nb near eutectic alloy is systematically investigated during directional solidification with electron beam floating zone melting (EBFZM). The effect of the Zone melting rate on the microstructure has also been studied.
文摘The carbide growth behavior of MAR-M247 LC alloy was investigated by directional solidification and quench method. The carbide volume fraction, trapping and growth behavior were correlated with the growth rate.It was found that the carbide volume fraction decreased at slower growth rate.This decreasing was caused by lower solidliquid interface trapping ability at slower growth rate.
基金Project supported by the National Natural Science Foundation of China(Grant Nos.51271213 and 51323008)the National Basic Research Program of China(Grant No.2011CB610402)+2 种基金the National High Technology Research and Development Program of China(Grant No.2013AA031103)the Specialized Research Fund for the Doctoral Program of Higher Education of China(Grant No.20116102110016)the China Postdoctoral Science Foundation(Grant No.2013M540771)
文摘A quantitative cellular automaton model is used to study the cell-to-dendrite transition(CDT) in directional solidification. We give a detailed description of the CDT by carefully examining the influence of the physical parameters, including:the Gibbs–Thomson coefficient Γ, the solute diffusivity Dl, the solute partition coefficient k0, and the liquidus slope ml. It is found that most of the parameters agree with the Kurz and Fisher(KF) criterion, except for k0. The intrinsic relations among the critical velocity Vcd, the cellular primary spacing λc,max, and the critical spacing λcd are investigated.
基金financially supported by the doctoral scholarship grant of the Algerian-MHESR
文摘The effects of pulling velocity on the solidification behavior and microstructural parameters of A1Sil0Mg alloys prepared in a Bridgman-type directional solidification furnace were investigated. The microstructure, particularly the secondary dendritic arm spacing (SDAS), and the Brinell hardness (BH) of the solidified A1Sil0Mg alloys were characterized for samples with cylindrical shapes and differ- ent conicities (θ = 0°, 5°, and 10°). Microstructural studies revealed an increased density of ct-A1 phase dendrites and a decreased interden- dritic distance with increasing pulling velocity. The dendrites were found to be preferentially oriented along the pulling direction for low pulling velocities. For larger pulling velocities, the dendrites grew first in the cooling direction but then broke as others nucleated and coars- ened. The HB values of the solidified samples increased as the pulling velocity increased. In regard to sample conicity, smaller dendrites were observed for an apex angle of θ = 5°, resulting in the largest HB value. This result was interpreted in terms of the favorable orientation of the dendrite along the pulling direction.