Al-7graphite composite was processed using Al-7graphite mushy prepared by electromagnetic-mechanical stirring method, and the influence of solid fraction on the distributing of graphite particles in ingot was studied....Al-7graphite composite was processed using Al-7graphite mushy prepared by electromagnetic-mechanical stirring method, and the influence of solid fraction on the distributing of graphite particles in ingot was studied. The results shows that the relationship between solid fraction and stirring temperature of mushy is: f(s) = 591.5-0.897 t (where f(s) is the solid fraction, t is the stirring temperature). For Al-7graphite composite, with the increasing of solid fraction, the aggregation extent of graphite particles reduced gradually, and when solid fraction was larger than 30%, graphite particles could distribute evenly in ingot.展开更多
The electromagnetic-mechanical stirring technology was employed for preparing QTi4.3-4 graghite composite slurry,and QTi4.3-4 graghite composite with uniform distribution of graphite particles was prepared uring the ...The electromagnetic-mechanical stirring technology was employed for preparing QTi4.3-4 graghite composite slurry,and QTi4.3-4 graghite composite with uniform distribution of graphite particles was prepared uring the semi-solid casting technology successfully.The structure of this QTi4.3-4graphite composite was studied and the condition for uniform distribution of graphite particles was got.The experimental results show that there exists a linear relationship between the solid fraction and the stirring temperature of QTi4.3-4graphite slurry.With the decreasing of stirring temperature,the solid fraction of QTi4.3-4 graghite slurry increases constantly.In casting,with the increasing of solid fraction of QTi4.3-4 graphite slurry.the agglomeration of graphite particles is removed gradually.When the solid fraction is higher than 40%,graphite particles can distribute evenly in QTi4.3-4 graghite composite.展开更多
基金China and Tsinghua-Zhongda Postdoctoral Science Foundation.]
文摘Al-7graphite composite was processed using Al-7graphite mushy prepared by electromagnetic-mechanical stirring method, and the influence of solid fraction on the distributing of graphite particles in ingot was studied. The results shows that the relationship between solid fraction and stirring temperature of mushy is: f(s) = 591.5-0.897 t (where f(s) is the solid fraction, t is the stirring temperature). For Al-7graphite composite, with the increasing of solid fraction, the aggregation extent of graphite particles reduced gradually, and when solid fraction was larger than 30%, graphite particles could distribute evenly in ingot.
文摘The electromagnetic-mechanical stirring technology was employed for preparing QTi4.3-4 graghite composite slurry,and QTi4.3-4 graghite composite with uniform distribution of graphite particles was prepared uring the semi-solid casting technology successfully.The structure of this QTi4.3-4graphite composite was studied and the condition for uniform distribution of graphite particles was got.The experimental results show that there exists a linear relationship between the solid fraction and the stirring temperature of QTi4.3-4graphite slurry.With the decreasing of stirring temperature,the solid fraction of QTi4.3-4 graghite slurry increases constantly.In casting,with the increasing of solid fraction of QTi4.3-4 graphite slurry.the agglomeration of graphite particles is removed gradually.When the solid fraction is higher than 40%,graphite particles can distribute evenly in QTi4.3-4 graghite composite.