Hydro-sodalites are zeolitic materials with a wide variety of applications.Fly ash is an abundant industrial solid waste,rich in silicon and aluminum,from which hydro-sodalite can be synthesized.However,traditional hy...Hydro-sodalites are zeolitic materials with a wide variety of applications.Fly ash is an abundant industrial solid waste,rich in silicon and aluminum,from which hydro-sodalite can be synthesized.However,traditional hydrothermal synthesis methods are complex and cannot produce high-purity products.Therefore,there is a demand for processing routes to obtain high-purity hydro-sodalites.In the present study,high-purity hydro-sodalite(90.2 wt%)was prepared from fly ash by applying a hydrothermal method to a submolten salt system.Samples were characterized by powder X-ray diffraction(XRD),scanning electron microscopy(SEM),thermogravimetry and differential thermal analysis(TG–DTA),and Fourier transform infrared spectroscopy(FTIR)to confirm and quantify conversion of the raw material into the product phase.Purity of the samples prepared with an H2O/Na OH mass ratio of 1.5 and an H2O/fly ash mass ratio of 10 was calculated and the conversion process of the product phase was studied.Crystallinity of the product was influenced more by the Na OH concentration,less by the H2O/fly ash mass ratio.The main reaction process of the system is that the Si O ions produced by dissolution of the vitreous body in the fly ash and Na+ions in the solution reacted on the destroyed mullite skeleton to produce hydro-sodalite.This processing route could help mitigate processing difficulties,while producing high-purity hydro-sodalite from fly ash.展开更多
According to the chemical and mineral composition characteristics of the fly ash,alumina can be extracted from fly ash through the calcining method by using sodium carbonate and calcium carbonate additives.The effects...According to the chemical and mineral composition characteristics of the fly ash,alumina can be extracted from fly ash through the calcining method by using sodium carbonate and calcium carbonate additives.The effects on leaching rate of alumina have been investigated. The results showed that the fly ash can be activated effectively and the leaching rate of alumina can be improved to more than 92% through this method. The best process parameters were the ratio of raw materials,i. e. the material weight ratio of fly ash,calcium carbonate and sodium carbonate was 1. 0∶1. 2∶0. 9. The activating temperature was 850℃-900℃,activating time was 3 h. This process has a potential application prospect and improves the value of comprehensive utilization of fly ash.展开更多
基金financially supported by the National Natural Science Foundation of China (No. 51474028)the National Key Research and Development Program of China (No. 2017YFC0210301)+1 种基金China Postdoctoral Science Foundation (No. 2017M621034)the Science and Technology Benefiting Citizens Program of Ningbo, China (No. 2015C50058)
文摘Hydro-sodalites are zeolitic materials with a wide variety of applications.Fly ash is an abundant industrial solid waste,rich in silicon and aluminum,from which hydro-sodalite can be synthesized.However,traditional hydrothermal synthesis methods are complex and cannot produce high-purity products.Therefore,there is a demand for processing routes to obtain high-purity hydro-sodalites.In the present study,high-purity hydro-sodalite(90.2 wt%)was prepared from fly ash by applying a hydrothermal method to a submolten salt system.Samples were characterized by powder X-ray diffraction(XRD),scanning electron microscopy(SEM),thermogravimetry and differential thermal analysis(TG–DTA),and Fourier transform infrared spectroscopy(FTIR)to confirm and quantify conversion of the raw material into the product phase.Purity of the samples prepared with an H2O/Na OH mass ratio of 1.5 and an H2O/fly ash mass ratio of 10 was calculated and the conversion process of the product phase was studied.Crystallinity of the product was influenced more by the Na OH concentration,less by the H2O/fly ash mass ratio.The main reaction process of the system is that the Si O ions produced by dissolution of the vitreous body in the fly ash and Na+ions in the solution reacted on the destroyed mullite skeleton to produce hydro-sodalite.This processing route could help mitigate processing difficulties,while producing high-purity hydro-sodalite from fly ash.
文摘According to the chemical and mineral composition characteristics of the fly ash,alumina can be extracted from fly ash through the calcining method by using sodium carbonate and calcium carbonate additives.The effects on leaching rate of alumina have been investigated. The results showed that the fly ash can be activated effectively and the leaching rate of alumina can be improved to more than 92% through this method. The best process parameters were the ratio of raw materials,i. e. the material weight ratio of fly ash,calcium carbonate and sodium carbonate was 1. 0∶1. 2∶0. 9. The activating temperature was 850℃-900℃,activating time was 3 h. This process has a potential application prospect and improves the value of comprehensive utilization of fly ash.