通钢通过65 t Consteel电弧炉-65 t LF-150 mm×150 mm方坯连铸流程生产40Cr合金钢。检验结果表明,通过LF精炼,40Cr钢水中的氧含量由精炼前227×10-6降至35×10-6;而连铸时中间包钢中的氧含量增加至51×10-6,铸坯的氧...通钢通过65 t Consteel电弧炉-65 t LF-150 mm×150 mm方坯连铸流程生产40Cr合金钢。检验结果表明,通过LF精炼,40Cr钢水中的氧含量由精炼前227×10-6降至35×10-6;而连铸时中间包钢中的氧含量增加至51×10-6,铸坯的氧含量为54×10-6。因此,进一步预防钢水从钢包至中间包及中间包内钢水的二次氧化和去除钢中大型夹杂物,是提高钢水洁净度和降低[O]的关键步骤。展开更多
Reducing steel slag （RSS） was mainly acquired from five electric-arc furnace （EAF） steelmaking plants （among them, the products of two plants were carbon steel and those of other plants were stainless steel） for...Reducing steel slag （RSS） was mainly acquired from five electric-arc furnace （EAF） steelmaking plants （among them, the products of two plants were carbon steel and those of other plants were stainless steel） for research tests. The chemical properties, compound compositions, activities and contents of main expansive compounds were tested. The results showed that the field sampled RSS had a very high crystallinity and hydraulicity with main chemical compositions close to those of Portland cement. It can be known from the study that in case of C/S ratio higher than 2.0, the main compound compositions are C2S, C3S, C2F and f-CaO. However, after the RSS was stored for six months, an obvious variation occurred with potential pre-hydration in RSS, where the SO3 content was slightly reduced and the compressive activity index was obviously higher than that at the 28th day.展开更多
This study analyzes the feasibility of using stainless steel electric arc furnace （EAF） slag as composite cement admixture and the risk of leaching-out of heavy metals. The results show that the stainless steel EAF ...This study analyzes the feasibility of using stainless steel electric arc furnace （EAF） slag as composite cement admixture and the risk of leaching-out of heavy metals. The results show that the stainless steel EAF slag, mainly made up of Ca2 SiO4, Ca3 Mg （ SiO4 ） 2, some Cr-containing minerals and in small particle size, is easily ground and has cementitious activity. EAF slag, when used as cement admixture, can be added with a maximum percentage of 32%. It can meet the strength requirements of the standard P · C 32.5 cement. When the mixing percentage is decreased to 25 % , the strength of the cement can be increased to that of P · C 42.5 cement. Other main quality indexes of composite cement, such as the setting time and stability, also satisfy standard requirements. The results also show that most of the heavy metals in the stainless steel EAF slag exist in a stable speciation. The concentration of heavy metals that leach out from the stainless steel EAF slag and the composite cement products is far lower than the standard limit of hazardous wastes. The main heavy metal, chromium, exists as less hazardous trivalent chromium. Therefore, the risk of heavy metals leaching out from the stainless steel EAF slag is low. The internal exposure index （IRa） and the external exposure index （Iγ） of the stainless steel EAF slag are both lower than 1.0, satisfying the standard requirements of the state for the radionuclides of building materials. Therefore, stainless steel EAF slag can be safely used as admixture to produce composite cement.展开更多
This paper presents the improvements on equipment and process technologies of Baosteel EAF Bloom Caster Production Line.By using the new VOD equipment,super low carbon super 13Cr was successfully made;By applying and ...This paper presents the improvements on equipment and process technologies of Baosteel EAF Bloom Caster Production Line.By using the new VOD equipment,super low carbon super 13Cr was successfully made;By applying and developing the Soft Reduction technology,very good results were achieved on high quality steel grades such as tire cord steel,bear steel,hi-alloy steel;the ladle Anti-Slag Detector is normally applied,based on the detail analysis during the performance test period,the Detector gives out slag entrapment alarms 7-9 s average before slag flows into tundish.By optimizing production control points of each key process,great achievements are realized on high quality steel grades such as tire cord steel,bear steel,hi-alloy steel and hi-S/Al steel,etc.Some achievements and technical indices are presented,too.展开更多
通过LF加石灰,控制LF末期铝含量,RH过程喷80CaO-20CaF_2粉,RH终点喂铝线,RH结束后喂硅钙线等操作生产≤0.003%S的12MnV钢。根据脱硫数据表明,在110 t EAF-LF-RH-CC流程中LF平均脱硫率达88%,RH平均脱硫率不足30%;铝脱氧钢的冶炼过程中,...通过LF加石灰,控制LF末期铝含量,RH过程喷80CaO-20CaF_2粉,RH终点喂铝线,RH结束后喂硅钙线等操作生产≤0.003%S的12MnV钢。根据脱硫数据表明,在110 t EAF-LF-RH-CC流程中LF平均脱硫率达88%,RH平均脱硫率不足30%;铝脱氧钢的冶炼过程中,在不喂铝丝的情况下,随S含量降低,钢中Al含量降低;在RH前钢中应有足够的Al脱除钢中的氧,以利于RH脱硫。展开更多
26CrMoNbTiB钢由45 t EAF-LF(VD)-Φ80～180mm管坯HCC流程冶炼。该钢各工序的洁净度试验结果表明,LF-VD后钢中氧含量为(8～18)×10^(-6),平均夹杂物数量最低为2.31个/mm^2,连铸坯平均夹杂物数量为3.66个/mm^2,≥50μm大型夹杂物平...26CrMoNbTiB钢由45 t EAF-LF(VD)-Φ80～180mm管坯HCC流程冶炼。该钢各工序的洁净度试验结果表明,LF-VD后钢中氧含量为(8～18)×10^(-6),平均夹杂物数量最低为2.31个/mm^2,连铸坯平均夹杂物数量为3.66个/mm^2,≥50μm大型夹杂物平均含量为4.08 mg/10 kg。加强钢包到中间包长水口的密封保护和采用钢包下渣检测装置,提高中间包容量和采用挡渣墙是进一步提高铸坯洁净度的关键工艺措施。展开更多
文摘通钢通过65 t Consteel电弧炉-65 t LF-150 mm×150 mm方坯连铸流程生产40Cr合金钢。检验结果表明,通过LF精炼,40Cr钢水中的氧含量由精炼前227×10-6降至35×10-6;而连铸时中间包钢中的氧含量增加至51×10-6,铸坯的氧含量为54×10-6。因此,进一步预防钢水从钢包至中间包及中间包内钢水的二次氧化和去除钢中大型夹杂物,是提高钢水洁净度和降低[O]的关键步骤。
文摘Reducing steel slag （RSS） was mainly acquired from five electric-arc furnace （EAF） steelmaking plants （among them, the products of two plants were carbon steel and those of other plants were stainless steel） for research tests. The chemical properties, compound compositions, activities and contents of main expansive compounds were tested. The results showed that the field sampled RSS had a very high crystallinity and hydraulicity with main chemical compositions close to those of Portland cement. It can be known from the study that in case of C/S ratio higher than 2.0, the main compound compositions are C2S, C3S, C2F and f-CaO. However, after the RSS was stored for six months, an obvious variation occurred with potential pre-hydration in RSS, where the SO3 content was slightly reduced and the compressive activity index was obviously higher than that at the 28th day.
文摘This study analyzes the feasibility of using stainless steel electric arc furnace （EAF） slag as composite cement admixture and the risk of leaching-out of heavy metals. The results show that the stainless steel EAF slag, mainly made up of Ca2 SiO4, Ca3 Mg （ SiO4 ） 2, some Cr-containing minerals and in small particle size, is easily ground and has cementitious activity. EAF slag, when used as cement admixture, can be added with a maximum percentage of 32%. It can meet the strength requirements of the standard P · C 32.5 cement. When the mixing percentage is decreased to 25 % , the strength of the cement can be increased to that of P · C 42.5 cement. Other main quality indexes of composite cement, such as the setting time and stability, also satisfy standard requirements. The results also show that most of the heavy metals in the stainless steel EAF slag exist in a stable speciation. The concentration of heavy metals that leach out from the stainless steel EAF slag and the composite cement products is far lower than the standard limit of hazardous wastes. The main heavy metal, chromium, exists as less hazardous trivalent chromium. Therefore, the risk of heavy metals leaching out from the stainless steel EAF slag is low. The internal exposure index （IRa） and the external exposure index （Iγ） of the stainless steel EAF slag are both lower than 1.0, satisfying the standard requirements of the state for the radionuclides of building materials. Therefore, stainless steel EAF slag can be safely used as admixture to produce composite cement.
文摘This paper presents the improvements on equipment and process technologies of Baosteel EAF Bloom Caster Production Line.By using the new VOD equipment,super low carbon super 13Cr was successfully made;By applying and developing the Soft Reduction technology,very good results were achieved on high quality steel grades such as tire cord steel,bear steel,hi-alloy steel;the ladle Anti-Slag Detector is normally applied,based on the detail analysis during the performance test period,the Detector gives out slag entrapment alarms 7-9 s average before slag flows into tundish.By optimizing production control points of each key process,great achievements are realized on high quality steel grades such as tire cord steel,bear steel,hi-alloy steel and hi-S/Al steel,etc.Some achievements and technical indices are presented,too.
文摘通过LF加石灰,控制LF末期铝含量,RH过程喷80CaO-20CaF_2粉,RH终点喂铝线,RH结束后喂硅钙线等操作生产≤0.003%S的12MnV钢。根据脱硫数据表明,在110 t EAF-LF-RH-CC流程中LF平均脱硫率达88%,RH平均脱硫率不足30%;铝脱氧钢的冶炼过程中,在不喂铝丝的情况下,随S含量降低,钢中Al含量降低;在RH前钢中应有足够的Al脱除钢中的氧,以利于RH脱硫。
文摘26CrMoNbTiB钢由45 t EAF-LF(VD)-Φ80～180mm管坯HCC流程冶炼。该钢各工序的洁净度试验结果表明,LF-VD后钢中氧含量为(8～18)×10^(-6),平均夹杂物数量最低为2.31个/mm^2,连铸坯平均夹杂物数量为3.66个/mm^2,≥50μm大型夹杂物平均含量为4.08 mg/10 kg。加强钢包到中间包长水口的密封保护和采用钢包下渣检测装置,提高中间包容量和采用挡渣墙是进一步提高铸坯洁净度的关键工艺措施。