Alkyd coatings embedded with nano-TiO2 and nano-ZnO pigments were prepared. The effects of nano pigments on anticorrosion performance of alkyd coatings were investigated using electrochemical impedance spectrum （EIS...Alkyd coatings embedded with nano-TiO2 and nano-ZnO pigments were prepared. The effects of nano pigments on anticorrosion performance of alkyd coatings were investigated using electrochemical impedance spectrum （EIS）. For the sake of comparison, the corrosion protection of alkyd coatings with conventional TiO2 and ZnO was also studied. It was found that nano-TiO2 pigment improved the corrosion resistance as well as the hardness of alkyd coatings. The optimal amount of nano-TiO2 in a colored coating for corrosion resistance was 1%. The viscosities of alkyd coatings with nanometer TiO2 and ZnO and conventional TiO2 and ZnO pigments were measured and the relation between viscosity and anticorrosion performance was discussed.展开更多
TiO2 films were formed on metallic titanium substrates by the anodic oxidation method in H2SO4 solution under the 80V D.C..Phase component and microstructure were characterized by X-ray diffraction (XRD) and scanning ...TiO2 films were formed on metallic titanium substrates by the anodic oxidation method in H2SO4 solution under the 80V D.C..Phase component and microstructure were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM).Water contact angles on titanium oxide film surface were measured under both dark and sunlight illumination conditions.Corrosion tests were carried out in seawater under different illumination conditions by electrochemistry impedance spectrum (EIS) and polarization curves.The result showed that the TiO2 film prepared by the anodic oxidation method was anatase with a uniform structure and without obvious pores or cracks on its surface.The average water contact angle of the film was 116.4? in dark, in contrast to an angle of 42.7? under the UV illumination for 2 hours, which demonstrates good hydrophobic property.The anti-corrosion behavior of the TiO2 film was declining with the extended immersion time.Under dark conditions, however, the hydrophobic TiO2 film retarded the water infiltrating into the substrate.The impedance changed slowly and the corrosion current density was 2 orders of magnitude lower than that with the film illuminated by sunlight.All of those mentioned above indicate that the TiO2 film possesses much better performance under dark condition, and it can be applied as an engineering material under dark seawater environment.展开更多
基金the financial support from the National Natural Science Foundation of China(No.50499334).
文摘Alkyd coatings embedded with nano-TiO2 and nano-ZnO pigments were prepared. The effects of nano pigments on anticorrosion performance of alkyd coatings were investigated using electrochemical impedance spectrum （EIS）. For the sake of comparison, the corrosion protection of alkyd coatings with conventional TiO2 and ZnO was also studied. It was found that nano-TiO2 pigment improved the corrosion resistance as well as the hardness of alkyd coatings. The optimal amount of nano-TiO2 in a colored coating for corrosion resistance was 1%. The viscosities of alkyd coatings with nanometer TiO2 and ZnO and conventional TiO2 and ZnO pigments were measured and the relation between viscosity and anticorrosion performance was discussed.
文摘TiO2 films were formed on metallic titanium substrates by the anodic oxidation method in H2SO4 solution under the 80V D.C..Phase component and microstructure were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM).Water contact angles on titanium oxide film surface were measured under both dark and sunlight illumination conditions.Corrosion tests were carried out in seawater under different illumination conditions by electrochemistry impedance spectrum (EIS) and polarization curves.The result showed that the TiO2 film prepared by the anodic oxidation method was anatase with a uniform structure and without obvious pores or cracks on its surface.The average water contact angle of the film was 116.4? in dark, in contrast to an angle of 42.7? under the UV illumination for 2 hours, which demonstrates good hydrophobic property.The anti-corrosion behavior of the TiO2 film was declining with the extended immersion time.Under dark conditions, however, the hydrophobic TiO2 film retarded the water infiltrating into the substrate.The impedance changed slowly and the corrosion current density was 2 orders of magnitude lower than that with the film illuminated by sunlight.All of those mentioned above indicate that the TiO2 film possesses much better performance under dark condition, and it can be applied as an engineering material under dark seawater environment.