Thick-film thermistor with negative temperature coefficient（NTC）, low room-temperature resistivity and modest thermistor constant was screen-printed on the alumina substrate by the combination of 30.94III0.04II0.02 ...Thick-film thermistor with negative temperature coefficient（NTC）, low room-temperature resistivity and modest thermistor constant was screen-printed on the alumina substrate by the combination of 30.94III0.04II0.02 B OBi Coa Co with Ba0.5Bi0.5Fe0.9Sn0.1O3. The electrical properties of the thick films were characterized by a digital multimeter, a Keithley 2400 and an impedance analyzer. The results show that with the Ba0.5Bi0.5Fe0.9Sn0.1O3 content increasing from 0.05 to 0.25, the values of room-temperature resistivity, thermistor constant and peak voltage of the thick films increases and are in the ranges of 1.47-26.5 ？·cm, 678-1345 K and 18.9-47.0 V, respectively. The corresponding current at the peak voltage of the thick films decreases and is in the range of 40-240 m A. The impedance spectroscopy measurement demonstrates that the as-prepared thick films show the abnormal electrical heterogeneous microstructure, consisting of high-resistive grains and less resistive grain boundary regions. It can be concluded that the addition of Ba0.5Bi0.5Fe0.9Sn0.1O3 into 30.94III0.04II0.02 Ba Co OBi Co improves the thermistor behavior and but also deteriorates the current characteristics.展开更多
A new binuclear Zn^Ⅱ coordination complex,Zn2（bta）（phen）2（Cl）3（1,Hbta = 2-（1Hbenzotriazol-1-yl）acetic acid and phen = 1,10-phenanthroline）,has been synthesized and characterized by single-crystal X-ray diff...A new binuclear Zn^Ⅱ coordination complex,Zn2（bta）（phen）2（Cl）3（1,Hbta = 2-（1Hbenzotriazol-1-yl）acetic acid and phen = 1,10-phenanthroline）,has been synthesized and characterized by single-crystal X-ray diffraction,IR spectroscopy,elemental,and photoluminescent analysis.Complex 1 crystallizes in triclinic system,space group P1 with a = 9.3040（19）,b = 10.694（2）,c =16.841（3） A°,α = 101.18（3）,β = 105.77（3）,γ = 91.72（3）°,V= 1575.8（5） A°3,C（32）H（22）Zn2Cl3N7O2,Mr =773.66,Dc = 1.631 g/cm^3,Z = 2,F（000） = 780,μ = 1.820 mm^-1,the final R = 0.1238 and wR =0.1131.X-ray diffraction analyses indicate that 1 displays two crystallographic independent Zn^Ⅱmetal centers with a distorted tetragonal pyramidal（ZnN4O） and a tetrahedral（ZnNCl3） geometries,respectively.The phen serves as a common N,N＇-bidentate ligand,and the bta^- as a unique N,O-bridged ligand in 1.In the crystal,1 forms a stable 3D supramolecular architecture by trifurcated hydrogen bonding C-H…C1 interactions and C-H…π,π…π stacking.1 showed photo-electric conversion properties.展开更多
A new 3-D nickel（Ⅱ） metal-organic framework（MOFs） with formula [Ni（bib）_2（SO_4）]_n（1）, where bib = 1,4-bis（imidazol-1-yl）benzene, has been synthesized and characterized by single-crystal X-ray diffraction...A new 3-D nickel（Ⅱ） metal-organic framework（MOFs） with formula [Ni（bib）_2（SO_4）]_n（1）, where bib = 1,4-bis（imidazol-1-yl）benzene, has been synthesized and characterized by single-crystal X-ray diffraction, IR spectroscopy, elemental analysis and surface photovoltage spectroscopy（SPS）. Complex 1 crystallizes in monoclinic system, space group C2/c with a = 19.5988（6）, b = 9.7531（3）, c = 11.8146（4） ？, β = 96.185（3）°, V = 2245.20（12） ？~3, C_（24）H_（20）N_8NiO_4S, M_r = 575.25, D_c = 1.702 g/cm^3, Z = 4, F（000） = 1184, μ = 1.011 mm-1, the final R = 0.0293 and w R = 0.0702. X-ray diffraction analyses indicated that the center Ni^（2＋） ion is six-coordinated with an O_2N_4 donor set of two μ_2-SO_4^（2–） and four bib ligands, resulting in an ideal octahedral geometry. Topological analysis on complex 1 considers each Ni^（2＋） as a 6-connected node, while bib and sulfate ion as linkers, giving an α-Po topology with short Schl？fli symbol 412·63. In the crystal packing, the components interact with pairs of intermolecular C–H×××O hydrogen bonds. The SPS of 1 indicates that there are positive response bands in the range of 300~600 nm showing photo-electric conversion properties.展开更多
目的研究丹参酮ⅡA磺酸钠(TSN)对家兔在体心房单相动作电位(AMAP)及短期快速心房起搏时电重构的影响,探讨其防治房颤的可能机制。方法家兔24只,随机分为对照组与TSN组各12只。将电极经颈内静脉置入右心房记录AMAP,观察基础状态下、给药...目的研究丹参酮ⅡA磺酸钠(TSN)对家兔在体心房单相动作电位(AMAP)及短期快速心房起搏时电重构的影响,探讨其防治房颤的可能机制。方法家兔24只,随机分为对照组与TSN组各12只。将电极经颈内静脉置入右心房记录AMAP,观察基础状态下、给药后0.5 h及以600次.m in-1心房快速起搏后0.5 h、8 h AMAP及其频率适应性的变化。结果与起搏前相比对照组AERP200 m s在起搏后0.5h缩短21.2 m s,起博后8h缩短21.6m s(P<0.05),且心房肌的频率适应性丧失。TSN在基础状态下对AMAPA、AMAPD无明显影响,但使AERP200 m s由(105.9±3.8)m s延长至(114.7±7.2)m s(P<0.05)。起搏后TSN组维持原有的心房肌频率适应性。结论快速心房起搏使心房肌的频率适应性丧失而致电重构,TSN能通过抑制L-型钙通道减轻短期快速心房起搏所致电重构。展开更多
基金Projects(5110205551462005)supported by the National Natural Science Foundation of China
文摘Thick-film thermistor with negative temperature coefficient（NTC）, low room-temperature resistivity and modest thermistor constant was screen-printed on the alumina substrate by the combination of 30.94III0.04II0.02 B OBi Coa Co with Ba0.5Bi0.5Fe0.9Sn0.1O3. The electrical properties of the thick films were characterized by a digital multimeter, a Keithley 2400 and an impedance analyzer. The results show that with the Ba0.5Bi0.5Fe0.9Sn0.1O3 content increasing from 0.05 to 0.25, the values of room-temperature resistivity, thermistor constant and peak voltage of the thick films increases and are in the ranges of 1.47-26.5 ？·cm, 678-1345 K and 18.9-47.0 V, respectively. The corresponding current at the peak voltage of the thick films decreases and is in the range of 40-240 m A. The impedance spectroscopy measurement demonstrates that the as-prepared thick films show the abnormal electrical heterogeneous microstructure, consisting of high-resistive grains and less resistive grain boundary regions. It can be concluded that the addition of Ba0.5Bi0.5Fe0.9Sn0.1O3 into 30.94III0.04II0.02 Ba Co OBi Co improves the thermistor behavior and but also deteriorates the current characteristics.
基金supported by Guangxi Provincial Department of Education(No.KY2015ZD130)the Natural Science Foundation of Guangxi Province(No.2013GXNSFBA019030)the financial support from the Natural Science Foundation of Qinzhou University(No.2014PY-GJ05)
文摘A new binuclear Zn^Ⅱ coordination complex,Zn2（bta）（phen）2（Cl）3（1,Hbta = 2-（1Hbenzotriazol-1-yl）acetic acid and phen = 1,10-phenanthroline）,has been synthesized and characterized by single-crystal X-ray diffraction,IR spectroscopy,elemental,and photoluminescent analysis.Complex 1 crystallizes in triclinic system,space group P1 with a = 9.3040（19）,b = 10.694（2）,c =16.841（3） A°,α = 101.18（3）,β = 105.77（3）,γ = 91.72（3）°,V= 1575.8（5） A°3,C（32）H（22）Zn2Cl3N7O2,Mr =773.66,Dc = 1.631 g/cm^3,Z = 2,F（000） = 780,μ = 1.820 mm^-1,the final R = 0.1238 and wR =0.1131.X-ray diffraction analyses indicate that 1 displays two crystallographic independent Zn^Ⅱmetal centers with a distorted tetragonal pyramidal（ZnN4O） and a tetrahedral（ZnNCl3） geometries,respectively.The phen serves as a common N,N＇-bidentate ligand,and the bta^- as a unique N,O-bridged ligand in 1.In the crystal,1 forms a stable 3D supramolecular architecture by trifurcated hydrogen bonding C-H…C1 interactions and C-H…π,π…π stacking.1 showed photo-electric conversion properties.
基金supported by the Guangxi Provincial Department of Education(No.KY2015ZD130,YB2014414)the Natural Science Foundation of Guangxi Province(No.2014GXNSFBA118040)+2 种基金The supports of the National Natural Science Foundation of China(No.51402158)are gratefully acknowledgedthe financial support by the Opening Project of Guangxi Colleges and Universities Key Laboratory of Beibu Gulf Oil and Natural Gas Resource Effective Utilization(No.2015KLOG09)the financial support from the Natural Science Foundation of Qinzhou University(No.2014PY-GJ05)
文摘A new 3-D nickel（Ⅱ） metal-organic framework（MOFs） with formula [Ni（bib）_2（SO_4）]_n（1）, where bib = 1,4-bis（imidazol-1-yl）benzene, has been synthesized and characterized by single-crystal X-ray diffraction, IR spectroscopy, elemental analysis and surface photovoltage spectroscopy（SPS）. Complex 1 crystallizes in monoclinic system, space group C2/c with a = 19.5988（6）, b = 9.7531（3）, c = 11.8146（4） ？, β = 96.185（3）°, V = 2245.20（12） ？~3, C_（24）H_（20）N_8NiO_4S, M_r = 575.25, D_c = 1.702 g/cm^3, Z = 4, F（000） = 1184, μ = 1.011 mm-1, the final R = 0.0293 and w R = 0.0702. X-ray diffraction analyses indicated that the center Ni^（2＋） ion is six-coordinated with an O_2N_4 donor set of two μ_2-SO_4^（2–） and four bib ligands, resulting in an ideal octahedral geometry. Topological analysis on complex 1 considers each Ni^（2＋） as a 6-connected node, while bib and sulfate ion as linkers, giving an α-Po topology with short Schl？fli symbol 412·63. In the crystal packing, the components interact with pairs of intermolecular C–H×××O hydrogen bonds. The SPS of 1 indicates that there are positive response bands in the range of 300~600 nm showing photo-electric conversion properties.
文摘目的研究丹参酮ⅡA磺酸钠(TSN)对家兔在体心房单相动作电位(AMAP)及短期快速心房起搏时电重构的影响,探讨其防治房颤的可能机制。方法家兔24只,随机分为对照组与TSN组各12只。将电极经颈内静脉置入右心房记录AMAP,观察基础状态下、给药后0.5 h及以600次.m in-1心房快速起搏后0.5 h、8 h AMAP及其频率适应性的变化。结果与起搏前相比对照组AERP200 m s在起搏后0.5h缩短21.2 m s,起博后8h缩短21.6m s(P<0.05),且心房肌的频率适应性丧失。TSN在基础状态下对AMAPA、AMAPD无明显影响,但使AERP200 m s由(105.9±3.8)m s延长至(114.7±7.2)m s(P<0.05)。起搏后TSN组维持原有的心房肌频率适应性。结论快速心房起搏使心房肌的频率适应性丧失而致电重构,TSN能通过抑制L-型钙通道减轻短期快速心房起搏所致电重构。