Cathode material LiFePO4 of lithium-ion battery was synthesized by microwave heating. The "carbon-included" LiFePO4 with improved conductivity was synthesized by the addition of graphite. And the influence o...Cathode material LiFePO4 of lithium-ion battery was synthesized by microwave heating. The "carbon-included" LiFePO4 with improved conductivity was synthesized by the addition of graphite. And the influence of microwave-heating time on structure, morphology and charge/discharge performance of the products was discussed. The results of XRD, SEM, XPS, CV and charge/discharge testing measurements showed that the LiFePO4 product after 9 min in microwave oven had more advantages than other products.展开更多
CuInS2 thin films have been prepared by ion layer gas reaction (ILGAR) using C2H5OH as solvent, CuC1and InCl3 as reagents and H2S gas as sulfuration source. The effects of cationic concentrations and numbers of cycle ...CuInS2 thin films have been prepared by ion layer gas reaction (ILGAR) using C2H5OH as solvent, CuC1and InCl3 as reagents and H2S gas as sulfuration source. The effects of cationic concentrations and numbers of cycle on the properties of CuInS2 film were investigated. The chemical composition, crystalline structure, surface topography, deposited rate, optical and electronic properties of the films were characterized by X-ray diffractrometry (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), ultraviolet-visible spectrometry (UV-Vis) and Hall System. The results show that the crystalline of CuInS2 thin films and the deposition rate have been improved with the increase of cationic concentration, while CuxS segregation phases appear with further increasing cationic concentration. The deposition rate is close to constant as cationic concentration is fixed.CuInS2 thin film derived form lower cationic concentration is uniform, compact and good in adhesion to the substrates. The absorption coefficient of CuInS2 thin films is larger than 104 cm^-1, and the band gap Eg is in the range of 1.30-1.40 eV. The dark resisitivity of the thin film decreases from 50 to 10 Ω·cm and the carrier concentration ranges are over 10^16 cm^-3.展开更多
文摘Cathode material LiFePO4 of lithium-ion battery was synthesized by microwave heating. The "carbon-included" LiFePO4 with improved conductivity was synthesized by the addition of graphite. And the influence of microwave-heating time on structure, morphology and charge/discharge performance of the products was discussed. The results of XRD, SEM, XPS, CV and charge/discharge testing measurements showed that the LiFePO4 product after 9 min in microwave oven had more advantages than other products.
文摘CuInS2 thin films have been prepared by ion layer gas reaction (ILGAR) using C2H5OH as solvent, CuC1and InCl3 as reagents and H2S gas as sulfuration source. The effects of cationic concentrations and numbers of cycle on the properties of CuInS2 film were investigated. The chemical composition, crystalline structure, surface topography, deposited rate, optical and electronic properties of the films were characterized by X-ray diffractrometry (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), ultraviolet-visible spectrometry (UV-Vis) and Hall System. The results show that the crystalline of CuInS2 thin films and the deposition rate have been improved with the increase of cationic concentration, while CuxS segregation phases appear with further increasing cationic concentration. The deposition rate is close to constant as cationic concentration is fixed.CuInS2 thin film derived form lower cationic concentration is uniform, compact and good in adhesion to the substrates. The absorption coefficient of CuInS2 thin films is larger than 104 cm^-1, and the band gap Eg is in the range of 1.30-1.40 eV. The dark resisitivity of the thin film decreases from 50 to 10 Ω·cm and the carrier concentration ranges are over 10^16 cm^-3.
