Model Transformer Evaluation of High-Permeability Grain-Oriented Electrical Steels

The dependence of transformer performance on the material properties was investigated using two laboratory-processed 0.23 mm thick grain-oriented electrical steels domain-refined with elec-trolytically etched grooves having different magnetic properties. The iron loss at 1.7 T, 50 Hz and the flux density at 800 A/m of material A were 0.73 W/kg and 1.89 T, respectively; and those of material B, 0.83 W/kg and 1.88 T. Model stacked and wound transformer core experiments using the tested materials exhibited performance well reflecting the material characteristics. In a three-phase stacked core with step-lap joints excited to 1.7 T, 50 Hz, the core loss, the exciting current and the noise level were 0.86 W/kg, 0.74 A and 52 dB, respectively, with material A; and 0.97 W/kg, 1.0 A and 54 dB with material B. The building factors for the core losses of the two materials were almost the same in both core configurations. The effect of higher harmonics on transformer performance was also investigated.

Opposite Relationship between Orientation Selection and Texture Memory in the Deformed Electrical Steel Sheets during α→γ→α Transformation

The undesired {111} texture component for the magnetic properties mainly exists in the sheets of electrical steels by the conventional process, whereas the sheets with the non-{111} texture can be obtained by α→γ→α transformation. In this paper, we mainly investigate the opposite relationship between orientation selection and texture memory in the deformed ultra-low carbon steel sheet during →→ transformation annealing. A 0.5 mm thick hot-rolled sheet is directly subjected to transformation. The result shows that the specific transformation textures are not possible to generate in the sheets without deformation. Besides, transformation annealing is conducted on the recrystallized sheets in hydrogen and vacuum, respectively. The near {100} and {110} grains have the growth advantage at the atmosphere/metal interface, and the initial ferrite textures are retained in vacuum. Cold-rolled sheets with different thicknesses are annealed for transformation in vacuum, hydrogen and nitrogen, respectively.The near {100} and {110} textures are still the preferential orientations at the atmosphere/metal interface. When the surface grains have sufficiently large growth advantage, the {111} grains developed by texture memory effect will be annexed. Otherwise, the {111} grains at the center layer of the sheets are hard to be replaced, and they are retained after α→γ→α transformation cycle. The results of deformed sheets annealed with different heating rates in hydrogen show that the growth of initial recrystallization grains has a great effect on variant selection.

The Electrical Control System PLC Transformation of The XA6132 Milling

For the electrical control system of XA6132 milling machine circuit complexity, reliability and flexibility, high failure rate. Mitsubishi FX2N-40MR programmable controller is used to improve the performance and efficiency of the entire electrical control system by technological transformation. Mitsubishi FX2N-d0MRPLC on electrical control system transformation can expand link to the technological transformation of the similar equipments.

The Electrical Control System PLC Transformation of The T68 Boring

T68 boring machine electric control system circuit is complex, its reliability and flexibility is poor with high failure rate. The mitsubishi FX2N-40MR Programmable controller for the technical innovation of electric control system improves the work performance of the whole electric control system and the work efficiency. This paper introduces the mitsubishi FX2N-40MR PLC in T68 boring machine electric control system, the application of the elaborated system＇s hardware and PLC program design can provide work for technical reform of similar equipment.