Application of face centred cubic TiB powder as conductive filler for electrically conductive adhesives

Face centred cubic（FCC） TiB ceramic powder synthesized by Ti-boronizing method was used as conductive filler to make ceramic electrically conductive adhesives（ECAs） with the polymer matrix.Electrically conductive properties of the ceramic ECAs were studied.The bulk electrical resistivity varied with the powder content of the FCC-TiB in ECAs.The FCC-TiB filled ECAs also showed the percolation behavior that usually occurred for the metal-filled ECAs,the percolation threshold was located at the content of 60%FCC-TiB.A minimum value of 0.1 Ω·cm was obtained at a content of 75%FCC-TiB.In order to check the reliability of mechanical property,tensile test was done to measure the shear strength,and the shear strength dropped with increasing the content of FCC-TiB powders.It is about 12.26 MPa at the content of 70%TiB powders.The Cu filled ECAs were also prepared for comparison.The properties of the oxidation resistance of the two ECAs were evaluated.The results show that the ceramic ECAs have excellent oxidation resistance and better stability compared with the Cu filled ECAs.

Electrochemical migration behavior of Ag-plated Cu-filled electrically conductive adhesives

The electrochemical migration (ECM) behavior of the electrically conductive adhesives (ECAs) filled with pure Ag powder or Ag-plated Cu composite powder with varied Ag:Cu ratios was investigated under the condition of applying constant voltage and distilled water environment.ECM resistance was determined from the current-time curves.The microstructure and composition of ECM dendrite products were analyzed by SEM/EDS and XRD.It was found that the ECM resistance of Ag-plated Cu composite powder-filled ECAs was evidently higher than that of pure Ag powder-filled ECAs.The Ag:Cu ratio of composite powder in ECAs had notable influence on ECM resistance,which was enhanced with the decrease of Ag:Cu ratios.The composition of dendrites formed between cathode and anode during ECM process was not uniform for Ag-plated Cu-filled ECAs.An ECM inhibiting mechanism of Ag-plated Cu composite powder was proposed according to analysis of the electrochemical impedance spectroscopy,Tafel plot and dendrite composition.

Application of silver nanoparticles in electrically conductive adhesives with silver micro flakes

This study has been conducted to evaluate the application of silver nanoparticles(NPs)in Electrically Conductive Adhesives(ECAs),filled with hybrid silver flakes and NPs,and silver flakes as a control sample,at a filler loading of 78 wt.%,83 wt.%and 88 wt.%and cured at 150℃and 180℃,respectively.The results show that the electrical and thermal conductivities of ECAs were improved with the increasing of filler loading and curing temperature.Adding silver NPs in silver flakes negatively affected the electrical and thermal conductivities of ECAs at a low filler mass fraction of 78 wt.%,because the segregation of NPs enlarged the average distance of silver flakes;while it positively influenced the electrical and thermal conductivities of ECAs at a loading ratio of 88 wt.%,probably due to NPs filling in the gaps between silver flakes or even sintering together with each other or with silver flakes,especially when curing at high temperature of 180℃.

Thermoelectric Behavior of Isotropically Conductive Adhesive

The paper deals with unusual use of one kind of ECA （electrically conductive adhesive）---the ICA （isotropic conductive adhesive）. The main sphere of ECA application is electronic assembly, e.g., it is bonding of semiconductor microchips on printed circuits boards. In this sphere, the ECA compete with soft solder. In spite of this fact, the author utilized of two main ECA characteristics--good electrical conductivity and excellent adhesion to material surfaces to make the fiat thermocouples. Both the design of thermocouples and the measuring device and the measuring workplace arrangement are described. The measured data of thermoelectric voltages are plotted. The thermoelectric （Seebeck＇s） coefficients were calculated from obtained dependences of thermoelectric voltage versus the temperature differences.

Crack initiation rate of brittle rock under thermal-hydro-mechanical coupling condition

A calculation formula of thermal-hydro-mechanical(THM)coupling crack initiation rate for brittle rock was derived based on the energy conservation law.The self-designed THM coupling fracture test with conductive adhesive electrical measurement method was applied to measuring the THM coupling crack propagation rate of brittle rock continuously.Research results show that both calculation and test results of crack initiation rate increased with increase of the temperature and the hydraulic pressure.They are almost in good agreement,which can prove validity of the calculation formula of THM coupling crack initiation rate.