Electrodeposition of chitosan/graphene oxide conduit to enhance peripheral nerve regeneration

Currently available commercial nerve guidance conduits have been applied in the repair of peripheral nerve defects.However,a conduit exhibiting good biocompatibility remains to be developed.In this work,a series of chitosan/graphene oxide(GO)films with concentrations of GO varying from 0-1 wt%(collectively referred to as CHGF-n)were prepared by an electrodeposition technique.The effects of CHGF-n on proliferation and adhesion abilities of Schwann cells were evaluated.The results showed that Schwann cells exhibited elongated spindle shapes and upregulated expression of nerve regeneration-related factors such as Krox20(a key myelination factor),Zeb2(essential for Schwann cell differentiation,myelination,and nerve repair),and transforming growth factorβ(a cytokine with regenerative functions).In addition,a nerve guidance conduit with a GO content of 0.25%(CHGFC-0.25)was implanted to repair a 10-mm sciatic nerve defect in rats.The results indicated improvements in sciatic functional index,electrophysiology,and sciatic nerve and gastrocnemius muscle histology compared with the CHGFC-0 group,and similar outcomes to the autograft group.In conclusion,we provide a candidate method for the repair of peripheral nerve defects using free-standing chitosan/GO nerve conduits produced by electrodeposition.

Effects of laser energy on the surface quality and properties of electrodeposited zinc-nickel-molybdenum coatings

As a substitute for toxic cadmium coatings in the aerospace industry,zinc-nickel coatings have excellent application prospects,and their properties can be improved by adding molybdenum.In this study,laser-assisted electrodeposition is used to improve the surface quality and properties of Zn–Ni–Mo coatings,with investigation of how laser energy in the range of 0–21.1μJ affects their element content,surface morphology,crystal phase,microhardness,residual internal stress,and corrosion resistance.The laser irradiation accelerates the electrodeposition,refines the grain size,improves the hydrogen adsorption,and reduces the residual tensile stress,and a laser energy of 15.4μJ gives the highest Ni and Mo contents and the lowest Zn content,as well as the optimum surface morphology,microhardness,residual internal stress,and corrosion resistance of the coating.

Effect of Electrodeposition Methods of Cuprous Oxide on Antibacterial Properties of Concrete

Three types of electrodeposition,DC electrodeposition,low-frequency pulsed electrodeposition and high-frequency pulsed electrodeposition,were used to deposit cuprous oxide on the concrete surface to improve the antibacterial properties of concrete.The effects of pulse deposition frequency on the antibacterial property of concrete were studied using sulfate-reducing bacteria(SRB)and Escherichia coli(E.coli)as model bacteria.The bacterial concentration and the antibacterial rate were measured to evaluate the antibacterial performance of concrete.The effects of different deposition methods on the elemental content of copper and the amount of copper ions exuded were studied.XRD and SEM were used to analyze the microstructure of the deposited layers.The experimental results show that the concrete treated by electrodeposition exhibited good antibacterial properties against SRB and E.coli.The antibacterial effect of cuprous oxide deposited on concrete by pulse method was better than that by direct current(DC)method.The antibacterial rate of concrete was positively correlated with the exudation rate of copper ion.As the pulse frequency increased,the deposits content on the surface was increased with an accompanying improvement in the antibacterial property.Besides,the pulsed current had an indiscernible effect on the composition of the sediments,which were all mainly composed of Cu_(2)O,but the morphology of the Cu_(2)O differed greatly.Cubic octahedral cuprous oxide had better antibacterial properties with the highest copper ion leaching rate compared with cubic and spherical cuprous oxide.

Inverse-opal structured TiO_(2) regulating electrodeposition behavior to enable stable lithium metal electrodes

Lithium metal anode is almost the ultimate choice for high-energy density rechargeable batteries, but its uneven electrochemical dissolution-deposition characteristics lead to poor cycle stability and lithium dendrites safety problems. The fundamental solution to the problems is to interfere electrodeposition process of lithium metal so that it can be carried out reversibly and stably. In this work, an inverse-opal structured TiO2membrane with a thickness of only ~1 μm is designed to regulate the electrodeposition behavior of lithium metal, in which the ordered channels homogenize mass transfer process, the anatase TiO_(2)walls of the ion channels reduce desolvation barrier of solvated lithium-ions, and the spherical cavities with a diameter of ~300 nm confine migration of the adsorbed lithium atoms during electrocrystallization to diminish overpotential of lithium. These systematic effects cover and essentially change the whole process of electrodeposition of lithium metal and eliminate the possibility of lithium dendrite formation. The as-obtained lithium metal electrode delivers a Coulombic efficiency of 99.86% in the 100th cycle, and maintains a low deposition overpotential of 0.01 V for 800 h.

Three-dimensional structural Cu^(6)Sn_(5)/carbon nanotubes alloy thin-film electrodes fabricated by in situ electrodeposition from the leaching solution of waste-printed circuit boards

Tin-based materials are very attractive anodes because of their high theoretical capacity,but their rapid capacity fading from volume expansions limits their practical applications during alloying and dealloying processes.Herein,the improved binder-free tin-copper intermetallic/carbon nanotubes(Cu6Sn5/CNTs)alloy thin-film electrodes are directly fabricated through efficient in situ electrodeposition from the leaching solution of treated waste-printed circuit boards(WPCBs).The characterization results show that the easily agglomerated Cu6Sn5 alloy nanoparticles are uniformly dispersed across the three-dimensional network when the CNTs concentration in the electrodeposition solution is maintained at 0.2 g·L−1.Moreover,the optimal Cu6Sn5/CNTs-0.2 alloy thin-film electrode can not only provide a decent discharge specific capacity of 458.35 mAh·g^(−1)after 50 cycles at 100 mA·g^(−1)within capacity retention of 82.58%but also deliver a relatively high reversible specific capacity of 518.24,445.52,418.18,345.33,and 278.05 mAh·g^(−1)at step-increased current density of 0.1,0.2,0.5,1.0,and 2.0 A·g^(−1),respectively.Therefore,the preparation process of the Cu6Sn5/CNTs-0.2 alloy thin-film electrode with improved electrochemical performance may provide a cost-effective strategy for the resource utilization of WPCBs to fabricate anode materials for lithium-ion batteries.

Electrodeposited 3D hierarchical NiFe microflowers assembled from nanosheets robust for the selective electrooxidation of furfuryl alcohol

A robust and green strategy for the selective upgrading of biomass-derived platform chemicals towards highly valuable products is important for the sustainable development.Herein,the efficient electrocatalytic oxidation of biomass-derived furfuryl alcohol(FFA)into furoic acid(FurAc)catalyzed by the electrodeposited non-precious NiFe microflowers was successfully reached under the low temperature and ambient pressure.The 3D hierarchical NiFe microflowers assembled from ultrathin nanosheets were controllably synthesized by the electrodeposition method and uniformly grown on carbon fiber paper(CFP).Electrochemical analysis confirmed that NiFe nanosheets more preferred in the selective oxidation of FFA(FFAOR)than oxygen evolution reaction(OER).The linear sweep voltammetry(LSV)in FFAOR displayed a clear decrease towards lower potential,resulting in 30 mV reduction of overpotential at 20 mA cm^(-2) compared with that of OER.The optimal catalyst Ni_(1)Fe_(2) nanosheets exhibited the highest selectivity of FurAc(94.0%)and 81.4%conversion of FFA within 3 h.Besides,the influence of various reaction parameters on FFAOR was then explored in details.After that,the reaction pathway was investigated and rationally proposed.The outstanding performance for FFAOR can be ascribed to the unique structure of 3D flower-like NiFe nanosheets and oxygen vacancies,resulting in large exposure of active sites,faster electron transfer and enhanced adsorption of reactants.Our findings highlight a facile and convenient mean with a promising green future,which is promising for processing of various biomass-derived platform chemicals into value-added products.

Triboelectric nanogenerator based on electrodeposited Ag octahedral nano-assemblies

The tremendous potential of triboelectric generators-TENGs for converting mechanical energy into electrical energy places them as one of the most promising energy harvesting technologies. In this work, the fabrication of enhanced performance TENGs using Ag octahedron nano-assemblies on ITO as electrodes significantly increases the electric charge collection of the induced tribocharges. Thereby, nanostructured electrical contacts coated with Ag macroscale nano-assemblies with octahedral features were obtained by the electrodeposition technique on flexible PET/ITO substrates. Consequently, the nanostructured triboelectric generator-TENG exhibited 65 times more maximum output power, and almost 10 times more open circuit output voltage than that of a TENG with non-nanostructured contacts passing from μW to m W capabilities, which was attributed to the increment of intrinsic interface states due to a higher effective contact area in the former. Likewise, output performances of TENGs also displayed an asymptotic behavior on the output voltage as the operating frequency of the mechanical oscillations increased, which is attributed to a decrement in the internal impedance of the device with frequency. Furthermore, it is shown that the resulting electrical output power can successfully drive low power consumption electronic devices. On that account, the present research establishes a promising platform which contributes in an original way to the development of the TENGs technology.

Developing high photocatalytic antibacterial Zn electrodeposited coatings through Schottky junction with Fe3+-doped alkalized g-C_(3)N_(4) photocatalysts

Pure Zn coatings easily lose their protective performance after biofouling because they have no antibacterial effect under visible light.In this study,we fabricate a new antibacterial Zn composite coating using electrodeposition to couple Fe3+-doped alkalized g-C_(3)N_(4)(AKCN-Fe)into an existing Zn coating and show that the AKCN-Fe enhances antibacterial property of the Zn coating under visible light.We attribute this enhancement to the high photocatalytic performance,high loading content,and good dispersion of AKCN-Fe.In addition,the photocatalytic antibacterial mechanism of the composite coating is supported by scavenger experiments and electron paramagnetic resonance(EPR)measurements,suggesting that superoxide(·O_(2)^(-))and hydroxyl radical(·OH)play main and secondary roles,respectively.

Properties of electrodeposited amorphous Fe-Ni-W alloy deposits

A new technique of electroplating amorphous Fe-Ni-W alloy deposits was proposed.The structure and morphology o Fe-Ni-W alloy deposit were detected by XRD and SEM.The friction and wear behavior of Fe-Ni-W alloy deposit were studied and compared with that of chromium deposit.The corrosion properties against 5% sodium chloride,5% sulfuric acid and 5% sodium hydroxide were also discussed.The experimental results indicate that Fe-Ni-W alloy deposits have superior properties against wea than hard chromium deposits under dry sliding condition.Under oil sliding condition,except their better wear resistance,the deposits can protect their counterparts against wear.The deposits plated on brass and AISI 1045 steel show good behavior against corrosion o 5% sodium chloride,5% sulfuric acid and 5% sodium hydroxide.The bath of electroplating amorphous Fe-Ni-W alloy deposits is environmentally friendly and would find widely use in industry.

MICROSTRUCTURE OF ELECTRODEPOSITED Ni-W-P-SiC COMPOSITE COATINGS

ＭＩＣＲＯＳＴＲＵＣＴＵＲＥＯＦＥＬＥＣＴＲＯＤＥＰＯＳＩＴＥＤＮｉＷＰＳｉＣＣＯＭＰＯＳＩＴＥＣＯＡＴＩＮＧＳ①ＧｕｏＺｈｏｎｇｃｈｅｎｇ，ＹａｎｇＸｉａｎｗａｎ，ＬｉｕＨｏｎｇｋａｎｇＤｅｐａｒｔｍｅｎｔｏｆＭｅｔａｌｕｒｇｙ，Ｋｕｎｍｉｎ...

Electrodeposition of aluminium and aluminium-copper alloys from a room temperature ionic liquid electrolyte containing aluminium chloride and triethylamine hydrochloride

The electrodeposition of A1 and A1-Cu binary alloys on to gold substrates from a room temperature ionic liquid electrolyte containing A1C13-EtaNHC1 was studied. The electrochemical behavior of the electrolyte and the mechanism of deposition were investigated through cyclic voltammetry （CV）, and the properties of deposits obtained were assessed by scanning electron microscopy with energy dispersive X-ray spectroscopy （SEM-EDS） and X-ray diffraction （XRD）. A1 of 70μm in thickness and an A1-Cu alloy of 30μm in thickness with 8at% copper were deposited from the electrolyte. SEM images of the deposits indicate that the A1 deposit was smooth and uniform, whereas the Al-Cu deposit was nodular. The average crystalline size, as determined by XRD patterns, was found to be （30±5） and （29±5） nm, respectively, for A1 and A1-Cu alloys. Potentiodynamic polarization （Tafel plots） and electrochemical impedance spectroscopic （EIS） measurements showed that Al-Cu alloys are more corrosion resistant than Al.

Electrochemical behaviors of Zn-Fe alloy and Zn-Fe-TiO_2 composite electrodeposition

Electrochemical behaviors of Zn-Fe alloy and Zn-Fe-TiO2 composite electrodeposition in alkaline zincatesolutions were studied respectively by the methods of linear potential sweep and cyclic voltammetry. From the re-sults it can be concluded that Zn shows under potential deposition, Zn-Fe alloy codeposition is anomalous codeposi-tion and Zn-Fe alloy cathode polarization is increased with the introduction of additive. From the view point of elec-trochemistry, the reasons that the content of Fe in the Zn-Fe coating changes with the composition of the electrolyteand the process conditions altering and the relationship between the content of Fe and the appearance of the coatingare interpreted. The cathode polarization of Zn-Fe alloy codeposition is enhanced obviously with addition of additive.In the course of composite electrodeposition, TiO2 has less promotion to electrodeposition of zinc ions than to iron i-ons, while the electrodeposition of iron ions improves the content of TiO2 in composite coating, which is inagreement with the results of process experiments.

Direct electrodeposition of ionic liquid-based template-free Sn Co alloy nanowires as an anode for Li-ion batteries

Sn Co alloy nanowires were successfully electrodeposited from Sn Cl2-Co Cl2-1-ethyl-3-methylimidazolium chloride(EMIC) ionic liquid without a template. The nanowires were obtained from the molar ratio of 5:40:60 for Sn Cl2(25)Co Cl2(25)EMIC at-0.55 V and showed a minimum diameter of about 50 nm and lengths of over 20 μm. The as-fabricated SnCo nanowires were about 70 nm in diameter and featured a Sn/Co weight ratio of 3.85:1, when used as an anode for a Li-ion battery, they presented respective specific capacities of 687 and 678 m Ah·g^(-1) after the first charge and discharge cycle and maintained capacities of about 654 m Ah·g^(-1) after 60 cycles and 539 m Ah·g^(-1) after 80 cycles at a current density of 300 m A·g^(-1). Both the nanowire structure and presence of elemental Co helped buffer large volume changes in the Sn anode during charging and discharging to a certain extent, thereby improving the cycling performance of the Sn anode.

Effect of the current density on electrodepositing alpha-lead dioxide coating on aluminum substrate

The α-PbO2 electrodes are prepared by anodic electrodeposition on Al/conductive coating electrode from alkaline plumbite solutions in order to investigate the effect of the different current densities on the properties of α-PbO2 electrodes. The physic- ochemical properties of the α-PbO2 electrodes are analyzed by using SEM, EDS, XRD, Tafel plot, linear sweep voltammetry （LSV） and A.C. impedance. A compact and uniform layer of lead dioxide ：）vas obtained at the current density of 3 mA.cm-2. A further increase in current density results in smaller particles with high porosity. EDS and XRD analyses have shown that the PbO2 deposited in alkaline conditions is highly non stoichiometric, and the PbO impurities are formed on the surface layer besides the α-PbO2. The corrosion resistance of α-PbO2 at the low current density is superior to that of the high current density. It can be attributed to a porous layer of deposited films at high current densities in aqueous Zn2＋ 50 g·L^-1, H2SO4 150 When used as anodes for oxygen evolution g·L^-1, the Al/conductive coating/α-PbO2 exhibits lower potential compared to Pb electrode. Al/conductive coating/α-PbO2 electrode with the best electrocatalytic activity was obtained at current density of 1 mA·cm^-2. The lowest roughnest factor was obtained at 1 mA·cm^-2.

Electrodeposition of Rare Earth Metals and Their Alloys in Organic Electrolytes

Ｔｈｅｆｉｌｍｓｏｆｒａｒｅｅａｒｔｈｓｈａｖｅｍａｎｙｆｕｎｃｔｉｏｎａｌｐｅｒｆｏｒｍａｎｃｅｓａｎｄｈａｖｅｂｅｅｎｗｉｄｅｌｙａｐｐｌｉｅｄｉｎｍａｇｎｅｔｉｃ，ｏｐｔｉｃａｌ，ｎｕｃｌｅａｒ，ｓｕｐｅｒｃｏｎｄｕｃｔｉｎｇｍａｔｅｒｉ...

Corrosion resistance of electrodeposited RE-Ni-W-P-SiC composite coating

Immersion experiment results show that corrosion rate of the as deposited RE Ni W P SiC composite coating in HCl solutions increases with the rise of HCl concentration. On the contrary, the corrosion rate of the composite coating after heat treatment decreases with increasing HCl concentration. The corrosion rates of the composite coatings in as deposited state and after heat treatment in H 2SO 4 and H 3PO 4 solutions respectively decrease with the rise of H 2SO 4 and H 3PO 4 concentrations. The corrosion rate of the composite coating as deposited in FeCl 3 solutions decreases with increasing FeCl 3 concentration, while the rate of the composite coating after heat treatment increases with the rise of FeCl 3 concentration. The corrosion rate of 316L stainless steel in the corrosion media of H 2SO 4, HCl, H 3PO 4 and FeCl 3 solutions at different concentrations increases with rising concentration. In addition, the corrosion rate of 316L stainless steel in the corrosion media of H 2SO 4, HCl, H 3PO 4 and FeCl 3 solutions respectively is much greater than that of the RE Ni W P SiC composite coating as deposited and after heat treatment in the same corrosion media. [

STUDY ON PROPERTIES OF PULSE ELECTRODEPOSITED RE-Ni-W-P-SiC COMPOSITE COATINGS

The effects of pulse frequency f and duty cycle r on the deposition rate, composition, morphology, and hardness of pulse electrodeposited RE （rare earth）-Ni-W-P-SiC composite coatings have been studied. The results indicate that pulse current can improve the deposition rate of RE-Ni-W-P-SiC composite coatings; W, P, and SiC contents in the coating decrease with the increase of pulse frequency and reach the lowest value at f = 33Hz, whereas the RE content in the composite coatings increases with the increase of pulse frequency. SiC content decreases with the increase of duty cycle, W content reaches the lowest value, and P content reaches the highest value at r = 0.4; pulse current and RE can lead to smaller size of the crystalline grains; however, the effects of different pulse frequency and duty cycle on the morphologies of RE-Ni-W-P-SiC composite coatings are not obvious. The hardness of RE-Ni-W-P-SiC composite coatings is the highest when the duty cycle is at 0.6 and 0.8 and pulse frequency is at 50Hz. At the same pulse frequency, the hardness of RE-Ni-W-P-SiC composite coatings at r= 0.8 is higher than that at r= 0.6.

Solid state interfacial reactions in electrodeposited Ni/Sn couples

Ni/Sn couples, prepared by sequentially electroplating Ni layers and Sn layers on metallized Si wafers, were employed to study the microstructures and growth kinetics of Ni-Sn intermediate phases, when the Ni/Sn couples were aged at room temperature or armealed at temperatures from 150 to 225℃ for various times. The results show that the NiSn phase and Ni3Sn4 phase are formed, respectively, in the aged couples and annealed couples. The Ni3Sn4 layer is continuously distributed between the Ni and Sn sides in the annealed Ni/Sn couples. The Ni3Sn4 growth follows parabolic growth kinetics with an apparent activation energy of 39.0 kJ/mol.

Hydrogen peroxide biosensor based on electrodeposition of zinc oxide nanoflowers onto carbon nanotubes film electrode

A new amperometric biosensor for hydrogen peroxide was developed based on adsorption of horseradish peroxidase at the glassy carbon electrode modified with zinc oxide nanoflowers produced by electrodeposition onto multi-walled carbon nanotubes （MWNTs） film. The morphology of the MWNTs/nano-ZnO electrode has been investigated by scanning electron microscopy （SEM）, and the electrochemical performance of the electrode has also been studied by amperometric method. The resulting electrode offered an excellent detection for hydrogen peroxide at -0.11 V with a linear response range of 9.9×10^-7 to 2.9×10^-3 mol/L with a correlation coefficient of 0.991, and response time 〈5 s. The biosensor displays rapid response and expanded linear response range, and excellent stability.

Ni nanocomposite films formed by Ni nanowires embedded in Ni matrix using electrodeposition

Ni nanocomposite films formed by Ni nanowires embedded in Ni matrix(Ni nanowire/Ni composite films)were fabricated by electrodeposition combined with supersonic stirring in a conventional Watts'bath containing Ni nanowires with diameter about 30 nm.The deposition temperature-dependent microstructure,crystal orientation,lattice constant and corrosion behavior of the Ni nanowire/Ni composite films were investigated by field emission scanning electron microscope,X-ray diffraction and potentiodynamic polarization tests,respectively.And the possible mechanism was discussed.It is found that to some extent,the deposition temperature has an impact on the microstructure,crystal orientation,lattice constant and corrosion property of the Ni nanowire/Ni composite films.The Ni nanowire/Ni composite films prepared at 50℃exhibit a novel inter-twisted-nanowire microstructure and have the best corrosion resistance.