Electroless Ni-P plating on Mg-Li alloy by two-step method

Pretreated Mg-Li alloy sheets were pre-plated in a NiCO3？2Ni（OH）2？4H2O solution to form a thin Ni-P alloy film and then plating in a NiSO4？6H2O solution was carried out to obtain a protective coating.The surface morphology,structure and corrosion resistance of the coating were studied.The results showed that a flat,bright and compact plating layer,which was integrated into the matrix metal,was obtained.The P content of the Ni-P coating reached 13.56%（mass fraction）.The hardness value of the Ni-P coating was about HV 549.The polarization curve showed that the corrosion potential of the Ni-P coating reached ？0.249 V（vs SCE）.A long passivation region was found on the polarization curve,and this phenomenon indicated that the coating has an excellent anti-corrosion property.

An in situ measure method to study deposition mechanism of electroless Ni-P plating on AZ31 magnesium alloy

An in situ method was designed to measure a continuous open circuit potential （OCP） curve of AZ31 magnesium alloy and to observe the morphology variation of Ni-P coating during the process of the electroless plating. The deposition mechanism of the electroless Ni-P plating on AZ31 Mg alloy was studied by OCP curve, scanning electron microscopy （SEM）, and energy dispersion spectroscopy （EDS）. The process of electroless Ni-P plating contains the coating formation stage and the coating growth stage. The formation stage includes three procedures, i.e., the nucleation and growth of Ni crystallites, the extension of the coating in two-dimensional （2D） direction and the coalescence of the coating along three-dimensional （3D） direction. SEM investigations demonstrate that the spherical nodules of the Ni-P coating are not only formed during the coating growth stage, but also generated in the initial deposition stage of electroless Ni-P plating. The variation of the coating rates at different deposition stages corresponds to the deposition mechanism of their respective deposition stage.

Effect of novel ternary ligand system on acidic electroless Ni-P plating on AZ91D magnesium alloy

The electroless Ni-P coatings on AZ91 D magnesium alloy substrate were prepared using the acidic hypophosphite-reduced electroless nickel bath containing the novel ternary ligand system. The results indicate that the deposition rate varies with the ternary ligand concentration in plating solution. The structural and morphological characteristics of the coatings were analyzed by XRD and SEM. The anticorrosion properties of the Ni-P coatings were evaluated in 3.5% NaCl solution by electrochemical impedance and potentiodynamic polarization methods. The amount of ternary ligands in electroless plating bath has an significant effect on the surface morphology and structure of Ni-P coatings. The decrease of crystallization temperature and increase of crystallization heat of all the deposits with an increase in ternary ligand concentration are found by DSC measurements. The coating obtained with 0.035 mol/L ternary ligand additive in plating bath can offer a better surface homogeneity and improve corrosion resistance.

Electroless plating and growth kinetics of Ni-P alloy film on SiC_p/Al composite with high SiC volume fraction

After Sn/Pd activating, the SiCp/Al composite with 65% SiC (volume fraction) was coated by electroless Ni?P alloy plating. Surface morphology of the composite and its effect on the Ni?P alloy depositing process and bonding action of Ni and P atoms in the Ni?P alloy were studied. The results show that inhomogeneous distribution of the Sn/Pd activating points results in preferential deposition of the Ni?P alloy particles on the Al alloy and rough SiC particle surfaces and in the etched caves. The Ni?P alloy film has an amorphous structure where chemical bonding between Ni and P atoms exists. After a continuous Ni?P alloy film formed, electroless Ni?P alloy plating is not affected by surface morphology and characteristics of the SiCp/Al composite any longer, but by the electroless plating process itself. The Ni?P alloy film follows linear growth kinetics with an activation energy of 68.44 kJ/mol.

Homogenization pretreatment and electroless Ni-P plating on AZ91D magnesium alloy

Electroless nickel plating on AZ91D substrate with a new and eco-friendly pretreatment process based on tuning an electrochemical homogeneous surface was investigated. The morphology, deposition process, chemical composition and microstructure of Ni-P coating were studied. It is indicated that β phases are selectively removed, producing a microstructural homogeneous surface and the subsequent uniform and compact Zn immersion layer. A defect-free and well adhesive Ni-P coating can be successfully obtained due to its uniform nucleation and growth based on such pretreatment. Potentiodynamic polarization and electrochemical impedance spectroscopy （EIS） tests reveal that Ni-P coating could significantly improve the corrosion resistance of AZ91D substrate.

Influence of pH values on electroless Ni-P-SiC plating on AZ91D magnesium alloy

A novel Ni-P-SiC composite coating was prepared by electroless plating in order to improve the corrosion capacity and wear resistance of AZ91D magnesium alloy.The influence of pH values on deposition rates and properties of the coatings was studied.The microstructure and phase structure of the Ni-P-SiC coatings were analyzed by scanning electron microscopy(SEM)and X-ray diffractometry(XRD).The corrosion and wear resistance performances of the coatings were also investigated through electrochemical technique and pin-on-disk tribometer,respectively.The results indicate that the composite coating is composed of Ni, P and SiC.It exhibits an amorphous structure and good adhesion to the substrate.The coatings have higher open circuit potential than that of the substrate.The composite coating obtained at pH value of 5.2 possesses optimal integrated properties,which shows similar corrosion resistance and ascendant wear resistance properties to the substrate.

Electrochemical behavior of Cu-Zn-Al shape memory alloy after surface modification by electroless plated Ni-P

The electrochemical behavior of Cu-Zn-Al shape memory alloy (SMA) with andwithout electroless plated Ni-P was investigated by electrochemical methods, in artificial Tyrode'ssolution. The results showed that Cu-Zn-Al SMA engendered dezincification corrosion in Tyrode'ssolution. The anodic active current densities as well as electrochemical dissolution sensitivity ofthe electroless plated Ni-P Cu-Zn-Al SMA increased with NaCl concentration rising, pH of solutiondecreasing and environmental temperature uprising. X-ray diffraction analysis indicated that aftersurface modification by electroless plated Ni-P, an amorphous plated film formed on the surface ofCu-Zn-Al SMA. This film can effectively isolate matrix metal from corrosion media and significantlyimprove the electrochemical property of Cu-Zn-Al SMA in artificial Tyrode's solution.

Corrosion and wear properties of electroless Ni-P plating layer on AZ91D magnesium alloy

A direct electroless Ni-P plating treatment was applied to AZ91D magnesium alloy for improving its corrosion resistance and wear resistance. Corrosion resistance of the Ni-P coatings was evaluated by potentiodynamic polarization and immersing experiments in 3.5% NaCl solution. The wear resistance of the coatings was investigated by the wear track and the mass change after ball-on-disk experiment. The results show that corrosion resistance and wear resistance of the AZ91D alloy are greatly improved after direct electroless Ni-P plating. No discoloration is noticed until 4 d of immersion in 3.5% NaCl solution. Potentiodynamic polarization experiments show that the free corrosion potential of magnesium alloy is shifted from -1 500 mV to -250 mV and passivation occurs at 1 350 mV after direct electroless plating. The friction coefficients and wear rates of Ni-P coating and Ni-P coating after tempering are 0.10-0.351, 9.038×10-3 mm3/m and 0.13-0.177, 3.056×10-4 mm3/m, respectively, at a load of 1.5 N with dry sliding. Although minor hurt on corrosion resistance was caused, significant improvement of wear resistance was obtained after tempering treatment of the coating.

Direct electroless Ni-P plating on AZ91D magnesium alloy

An electroless Ni-P plating treatment was applied on AZ91D magnesium alloy to improve its corrosion resistance. Optimum pretreatment conditions and optimum bath of electroless nickel plating for magnesium alloy were found through many experiments. In order to avoid bother of pre-plating medium layer, a set of procedure of direct electroless Ni-P under the acid condition was investigated. The properties of the coating with 10% phosphorus were investigated. The results show that a coating with high hardness, low porosity and good adhesive strength is obtained. X-ray diffraction patterns show that the structure of the coating is an amorphous phase. After annealing at 400℃, the amorphous phase of Ni-P is transformed to crystalline phases, and some intermetallics as Ni3P and Ni5P2 are deposited from Ni-P solid solution along with an enhancing hardness from Hv 450 to Hv 910.

Structure and effects of electroless Ni-Sn-P transition layer during acid electroless plating on magnesium alloys

An electroless ternary Ni-Sn-P transition layer with high corrosion resistance was applied for acid electroless nickel plating on magnesium alloys. The surface morphologies and microstructure of the traditional alkaline electroless Ni-P and novel Ni-Sn-P transition layers were compared by SEM and XRD, and the bonding strengths between the transition layers and AZ31 magnesium alloys were tested. The corrosion resistance of the samples was analyzed by porosity test, potentiodynamic polarization, electrochemical impedance spectroscopy（EIS） in acid electroless solution at p H 4.5 and immersion test in 10% HCl. The results indicate that the transition layer is essential for acid electroless plating Ni-P coatings on magnesium alloys. Under the same thin thickness（-6 μm）, the electroless Ni-Sn-P transition layer possesses superior properties to the traditional Ni-P transition layer, including high amorphization, smooth and dense surface without pores, enhanced bonding strength and corrosion resistance. Most importantly, acid electroless Ni-P coatings can be successfully deposited on magnesium alloys by using Ni-Sn-P transition layer.

Progress of electroplating and electroless plating on magnesium alloy

The current research processes of electroplating and electroless Ni-P alloy plating on magnesium alloys were reviewed. Theoretically,the reason for difficulties in electroplating and electroless plating on magnesium alloys was given.The zinc immersion, copper immersion,direct electroless Ni-P alloy plating and electroplating and electroless plating on magnesium alloys prepared by chemical conversion coating were presented in detail.Especially,the research development of magnesium alloy AZ91 and AZ31 was discussed briefly.Based on the analysis,the existing problems and future research directions were then given.

The study of electroless Ni-W-P alloy plating on glass fibers

Ni-W-P coatings were deposited on the surface of glass fibers by the electroless plating process. The bath was very stable through the palladium salt test. There was no phenomenon of peeling and blistering on the surface of the Ni-W-P alloy glass fibers in the thermal shock test. It showed that the deposit had high impact strength and good adhesion. The morphology of the coatings was observed by scanning electron microscope （SEM）. The elements and their contents were tested and analyzed by energy dispersion spectrometer （EDS）. The tungsten content reached up to 12.1 wt.%. The effects of the concentrations of NiSO4, Na2WO4, and NaH2PO2.H20 on the conductivity of the coatings were studied. The resistivity of the Ni-W-P alloy glass fibers reached 7.39 × 10^-3 Ωcm. The alloy coatings on glass fibers were analyzed by XRD. The results indicated that the deposit had an amorphous structure and good heat stability. The suitable work temperature range was lower than 190℃. Finally, the electromagnetic parameters of the Ni-W-P alloy glass fibers were tested and analyzed primarily. The magnetic loss reached 0.04023 and the dielectric loss reached -5.80239. The plated alloy is a kind of soft magnetic material.

Study of Electroless Ni-P-CNTs Composite Plating

The electroless Ni-P-carbon nanotubes composite plating was studied on the copper substrate. Metallurgical microscope, scanning electronic microscope, X-ray diffractometer and micro hardness tester were used to study the structure, constitution and performance of the electroless Ni-P-carbon nanotubes composite deposit. Experiential results show that, with the increment of carbon nanotubes content in electroless plating solution, the grain size on the sample surface decreases whereas the density of grains and the hardness for composite deposit increases. Moreover, adding carbon nanotubes not only improves the degree of crystallization for the composite deposit but also helps their transformation from the amorphous state to the nanocrystal state.

Effect of Heat Treatment on Structure and Magnetic Performance of Ni-Fe-P Alloy Obtained by Electroless Plating

The electroless deposition of Ni68-Fe10.5-P21.5 alloy has been investigated. The crystallization behavior of the deposit was comparatively studied by using differential scanning calorimetry and X-ray diffractometry. The deposit transforms into a square Ni3P phase at 380. 0 ℃, then changes into a cubic FeNi3 phase at 490. 0 ℃. The microhardness, the size of the formed grains and the magnetic performance of the deposit increase with the increase of the heat treatment temperature below 500 ℃, then they decrease after this temperature. The effect of heat treatment time at 500 ℃ on the surface micromorphology, the structure and the magnetic performance of the deposit were also studied. The resuits show that with the increase of heat treatment time, the extent of crystallization of the deposit increases and the size of the formed grains becomes uniform. The results also show that the magnetic performance of the deposit under heat treatment for 40 min is maximal and then decreases with the increase of heat treatment time. The property change of the deposit is related to the crystal structure and the size of the formed grains of the deposit.

Pretreatment-free Ni-P plating on magnesium alloy at low temperatures

Electrochemically promoted electroless plating(EPEP)was used for the application of pretreatment-free Ni-P coating on AM60B magnesium alloy at low temperatures and the obtained coating was characterized by SEM,AFM,EDS and XRD techniques.Compact,uniform,and medium-phosphorus Ni-P coating with mixed crystalline-amorphous microstructure was obtained by applying a cathodic current density of4mA/cm^2at50℃.Also,island-like nickel clusters were deposited on the alloy surface under the same plating condition but without applying the cathodic current.In addition,the durability of the magnesium alloy against corrosion was strongly improved after plating via EPEP technique which was revealed by electrochemical examinations in3.5%NaCl(mass fraction)corrosive electrolyte.The results of the electrochemical examinations were confirmed by microscopic observations.Thickness,microhardness,porosity and adhesive strength of the deposits were also qualified.

Corrosion protection and mechanical properties of the electroless Ni-P-MOF nanocomposite coating on AM60B magnesium alloy

Al-based MIL-53 MOF nanostructure was synthesized hydrothermally and then co-deposited in the electroless nickel coating on AM60B magnesium alloy using Zr pretreatment as an eco-friendly underlayer.The MIL-53(Al)nanostructure was synthesized in the form of layered semi-cube crystals with the surface area and mean pore diameter of 985.72 m^(2)g^(-1) and 2.00 nm,respectively.The SEM images captured with two various zooming scales from the surface of the plain and MOF containing electroless layers showed cauliflower-like morphology with even distribution of nodule size.Also,the sub-grains of the plain coating disappeared after incorporation of the MOF.Although,both the normal and nanostructure-containing electroless layers have crystalline-amorphous structure,but the nanocomposite coating showed less crystallinity.The average surface roughness of the plain electroless coating was about 309 nm,which decreased to about 222 nm after incorporation of the MOF.The XRD patterns showed that the characteristic peak of Ni broadened after incorporation of the MOF,probably due to the decreasing of the crystallinity.For the heat-treated normal and MOF containing coatings at 200℃ no phase transition takes place,but new peaks appeared for heat-treated coatings at 400℃ due to the crystallization and second-phase precipitation.The results of the EIS tests showed an increase in the amount of the charge transfer resistance(from 19 to 29 kΩcm^(2))after addition of the MOF,which means an improvement in the corrosion resistance.Also,low Jcorrof the composite coating represents its higher corrosion resistance with respect to the plain coating.The micro-hardness values of the composite coating before and after the heat treatment were higher than the plain coating.Also,the Ni-P-MOF coating has a lower wear rate both before and after the heat treatment due to an improvement in its micro-hardness.

High-temperature tribological properties of Ni-P alloy coatings deposited by electro-brush plating

High-temperature tribological properties of Ni-P alloy coatings processed by electro-brush plating on 20CrMo steel have been investigated. A baU-on-disc configuration was employed and 4 mm diameter Si3N4 balls were used as static counterpart. All the wear tests were carried out at 450℃ for 180 rain without lubricants. The electro-brush plating Ni-P coating is amorphous in as-deposited condition, and it becomes polycrystalline with the formation of Ni and Ni3P after heat treatment at 450℃for 1 h. The friction coefficient of the Ni-P coating is just 50% of that of the 20CrMo steel at the friction temperature of 450℃. A mild adhesive wear mechanism was found for the electro-brush plating Ni-P coating tested at 450℃, whereas for the 20CrMo steel at the same temperature a mixed adhesive and abrasive wear mechanism was observed.

Microstructure and electrical conductivity of electroless copper plating layer on magnesium alloy micro-arc oxidation coating

In order to impart electrical conductivity to the magnesium alloy micro-arc oxidation(MAO)coating,the electroless copper plating was performed.Effects of plating temperature and complexing agent concentration on the properties of the electroless copper plating layers were studied by measuring their microstructure,corrosion resistance and electrical conductivity.It was found that the optimized plating temperature was 60°C,and the most suitable value of the complexing agent concentration was 30 g/L.Under this condition,a complete and dense plating layer could be obtained.The formation mechanism of the plating layer on magnesium alloy MAO coating was analyzed.A three-stage model of the plating process was proposed.The square resistance of the plated specimen was finally reduced to 0.03Ω/□after the third stage.Through electroless copper plating,the MAO coated sample obtained excellent electrical conductivity without significantly reducing its corrosion resistance.

PRIMARY STUDY FOR THE TECHNOLOGY OF ELECTROLESS PLATING Fe-Al-P ALLOYS

Manuscript received 24 June 1999 The Fe Al P alloy deposits were plated on copper sheets by electroless plating. The change law of the deposition rate, composition, surface appearance and structure for the deposits was studied by changing the metallic salt ratios (AlCl 3/AlCl 3+FeSO 4), the concentration of metallic salt AlCl 3 and reductant NaH 2PO 2. The optimum plating bath was obtained. It was found that the choices of ligand and reductant were the key of increasing Al content for the deposits.

Evaluation of residual stress and corrosion behaviour of electroless plated Ni-P/Ni-Mo-P coatings

Single Ni-P and Ni-Mo-P coatings as well as duplex Ni-P/Ni-Mo-P coatings with the same compositions were prepared by electroless plating.The residual stresses of the coatings on the surface and cross sections were measured by nanoindentation and AFM analysis,and the corrosion behaviour of the coatings in10%HCl solution was evaluated by electrochemical methods,to establish the correlation between the residual stresses and corrosion behaviour of the coatings.The results showed that the single Ni-P and duplex Ni-P/Ni-Mo-P coatings presented residual compressive stresses of241and206MPa respectively,while the single Ni-Mo-P coating exhibited a residual tensile stress of257MPa.The residual compressive stress impeded the growth of the pre-existing porosity in the coatings,protecting the integrity of the coating.The duplex Ni-P/Ni-Mo-P coatings had better corrosion resistance than their respective single coating.In addition,the stress states affect the corrosive form of coatings.