Magnesium alloys,the lightest structural metal,are used in the field of aeronautics and astronautics more and more,however they are still limited for the poor corrosion resistant and high temperature property.In order...Magnesium alloys,the lightest structural metal,are used in the field of aeronautics and astronautics more and more,however they are still limited for the poor corrosion resistant and high temperature property.In order to satisfy the need of long time store and short time operation at elevated temperature,coating with excellent corrosion resistance and thermal resistance was prepared on the surface of Mg alloy AZ31B.The cathodic electrophoretic deposition was applied for the preparation of coating.The bonding of organic electrophoretic deposition coating with substrate was improved using silane pretreatment.Nano-ZrO_(2) powder treated by silane was added into electrophoretic deposition solution.The corrosion resistance property of electrophoretic coating was evaluated using Machu test,and thermal characteristic using the thermal shock experiment and DTA respectively.The morphology of the coating was examined by SEM.It is found that both the corrosion resistant and thermal shock resistant properties can be improved by modifying the Mg specimen with APS silane,while adding nano-ZrO_(2)powder treated by GPS silane to the coating has the optimal effect.And the results also show that the main reason of the coating damage after thermal shock at 400°C or 500°C is mainly for the thermal stress.展开更多
Coated capillary columns were prepared by sol-gel technology and used in the separation of basic proteins with capillary zone electrophoresis. The results indicated that a significant decrease in protein adsorption wa...Coated capillary columns were prepared by sol-gel technology and used in the separation of basic proteins with capillary zone electrophoresis. The results indicated that a significant decrease in protein adsorption was obtained and EOF was also diminished to zero in the pH range of 3-10.展开更多
The application of Mg alloys is always accompanied by various coating technology, but a reliable model predicting the service life of coatings on Mg alloys is lacking but urgent. In this work, a semi-mechanistic model...The application of Mg alloys is always accompanied by various coating technology, but a reliable model predicting the service life of coatings on Mg alloys is lacking but urgent. In this work, a semi-mechanistic model was proposed to predict the service life of plasma electrolytic oxidation (PEO) coating/electrophoretic coatings on a VW63Z Mg alloy;the model was decomposed into three parts: a first part depicting the degradation time of organic coating (L_(1)) and the diffusion time of electrolyte in the inorganic coating (L_(2)), respectively;a second part interpreting the breakdown of coatings due to the corrosion process (L_(3));a final part establishing an algorithm converting the accelerated tests into the real service environment (α);the effect of structural stress and dissimilar metal joints on the service life of coatings was also considered. Based on the ongoing accelerated experiments, the semi-mechanistic model could be able to predict the service life of both PEO coatings and composite coatings on VW63Z Mg alloy with a satisfiable precision.展开更多
文摘Magnesium alloys,the lightest structural metal,are used in the field of aeronautics and astronautics more and more,however they are still limited for the poor corrosion resistant and high temperature property.In order to satisfy the need of long time store and short time operation at elevated temperature,coating with excellent corrosion resistance and thermal resistance was prepared on the surface of Mg alloy AZ31B.The cathodic electrophoretic deposition was applied for the preparation of coating.The bonding of organic electrophoretic deposition coating with substrate was improved using silane pretreatment.Nano-ZrO_(2) powder treated by silane was added into electrophoretic deposition solution.The corrosion resistance property of electrophoretic coating was evaluated using Machu test,and thermal characteristic using the thermal shock experiment and DTA respectively.The morphology of the coating was examined by SEM.It is found that both the corrosion resistant and thermal shock resistant properties can be improved by modifying the Mg specimen with APS silane,while adding nano-ZrO_(2)powder treated by GPS silane to the coating has the optimal effect.And the results also show that the main reason of the coating damage after thermal shock at 400°C or 500°C is mainly for the thermal stress.
文摘Coated capillary columns were prepared by sol-gel technology and used in the separation of basic proteins with capillary zone electrophoresis. The results indicated that a significant decrease in protein adsorption was obtained and EOF was also diminished to zero in the pH range of 3-10.
基金support from the National Natural Science Foundation of China(No.52201066)the National Program for the Young Top-notch Professionals.
文摘The application of Mg alloys is always accompanied by various coating technology, but a reliable model predicting the service life of coatings on Mg alloys is lacking but urgent. In this work, a semi-mechanistic model was proposed to predict the service life of plasma electrolytic oxidation (PEO) coating/electrophoretic coatings on a VW63Z Mg alloy;the model was decomposed into three parts: a first part depicting the degradation time of organic coating (L_(1)) and the diffusion time of electrolyte in the inorganic coating (L_(2)), respectively;a second part interpreting the breakdown of coatings due to the corrosion process (L_(3));a final part establishing an algorithm converting the accelerated tests into the real service environment (α);the effect of structural stress and dissimilar metal joints on the service life of coatings was also considered. Based on the ongoing accelerated experiments, the semi-mechanistic model could be able to predict the service life of both PEO coatings and composite coatings on VW63Z Mg alloy with a satisfiable precision.