Stannous oxalate was prepared efficiently and characterized by XRD and FT-IR. It exhibited higher catalytic activity and had profitable effect than tetrabutyl titanate and stannous octoate for the synthesis of polytri...Stannous oxalate was prepared efficiently and characterized by XRD and FT-IR. It exhibited higher catalytic activity and had profitable effect than tetrabutyl titanate and stannous octoate for the synthesis of polytrimethylene terephthalate （PTT） via esterification-route. Over this catalyst, the degree of esterification of pure terephthalic acid was up to 94.4% at 260 ℃ after 1.5 h,while the intrinsic viscosity and content of terminal carboxyl groups of the corresponding PTT polyester, polymerized at 260 ℃,60 Pa for 2 h, was 0.8950 dL/g and 15 mol/t, respectively. Stannous oxalate was a promising catalyst for the synthesis of PTT polyester.展开更多
文摘Stannous oxalate was prepared efficiently and characterized by XRD and FT-IR. It exhibited higher catalytic activity and had profitable effect than tetrabutyl titanate and stannous octoate for the synthesis of polytrimethylene terephthalate （PTT） via esterification-route. Over this catalyst, the degree of esterification of pure terephthalic acid was up to 94.4% at 260 ℃ after 1.5 h,while the intrinsic viscosity and content of terminal carboxyl groups of the corresponding PTT polyester, polymerized at 260 ℃,60 Pa for 2 h, was 0.8950 dL/g and 15 mol/t, respectively. Stannous oxalate was a promising catalyst for the synthesis of PTT polyester.