By using an Ar+ ion laser, a tunable Rh 6G dye laser(Linewidth: 0.5 cm -1) and a Coherent 899-21 dye laser as light sources and using a monochromator and a phase-locking amplifier, the optical properties of Eu 3+∶Y_2...By using an Ar+ ion laser, a tunable Rh 6G dye laser(Linewidth: 0.5 cm -1) and a Coherent 899-21 dye laser as light sources and using a monochromator and a phase-locking amplifier, the optical properties of Eu 3+∶Y_2SiO_5 crystal were detected. Persistent spectral hole burning (PSHB) were also observed in 5D_0-7F_0 transition in the crystal at the temperature of 16 K. For 15 mW dye laser (Wavelength: 579.62 nm) burning the crystal for 0.1 s a spectral hole with about 80 MHz hole width were detected and the hole can been keep for longer than 10 h.展开更多
A new aluminate host material Ca3ZnAl4O10 doped with Eu2+ was prepared by a high-temperature solid-state reaction method, and a pure crystalline phase of Ca3ZnAl4O10 was confirmed with X-ray powder diffraction (XRD) m...A new aluminate host material Ca3ZnAl4O10 doped with Eu2+ was prepared by a high-temperature solid-state reaction method, and a pure crystalline phase of Ca3ZnAl4O10 was confirmed with X-ray powder diffraction (XRD) measurement. The luminescent property was investigated with excitation and emission spectra. The phosphor could be excited by UV light from 220 nm to 400 nm and emitted a blue luminescence peaked at 450 nm, which corresponded to the 4f65d1→4f7 transition of Eu2+ ions. The dependence of luminesce...展开更多
文摘By using an Ar+ ion laser, a tunable Rh 6G dye laser(Linewidth: 0.5 cm -1) and a Coherent 899-21 dye laser as light sources and using a monochromator and a phase-locking amplifier, the optical properties of Eu 3+∶Y_2SiO_5 crystal were detected. Persistent spectral hole burning (PSHB) were also observed in 5D_0-7F_0 transition in the crystal at the temperature of 16 K. For 15 mW dye laser (Wavelength: 579.62 nm) burning the crystal for 0.1 s a spectral hole with about 80 MHz hole width were detected and the hole can been keep for longer than 10 h.
基金Project supported by the Korea Science and Engineering Foundation (KOSEF) grant funded by the Korea government (Ministry of Education, Science and Technology, MEST, 2009-0078682)
文摘A new aluminate host material Ca3ZnAl4O10 doped with Eu2+ was prepared by a high-temperature solid-state reaction method, and a pure crystalline phase of Ca3ZnAl4O10 was confirmed with X-ray powder diffraction (XRD) measurement. The luminescent property was investigated with excitation and emission spectra. The phosphor could be excited by UV light from 220 nm to 400 nm and emitted a blue luminescence peaked at 450 nm, which corresponded to the 4f65d1→4f7 transition of Eu2+ ions. The dependence of luminesce...