FeCrAl fiber-reinforced hydroxyapatite（HA） biocomposites（FeCrAl（f）/HA） were fabricated by the hot pressing technique.The metallographic microscopy,X-ray diffractometry,scanning electron microscopy（SEM） and ene...FeCrAl fiber-reinforced hydroxyapatite（HA） biocomposites（FeCrAl（f）/HA） were fabricated by the hot pressing technique.The metallographic microscopy,X-ray diffractometry,scanning electron microscopy（SEM） and energy dispersive spectroscopy（EDS） were used to observe and analyze the microstructure and composition of FeCrAl（f）/HA composites,respectively.The mechanical properties of FeCrAl（f）/HA composites were measured by the three-point-bending test.The results show that the composite can be reinforced by FeCrAl fiber and enhanced gradually,and then declined with the increase of the content of FeCrAl fiber（0-11%,volume fraction） in the whole range of experiments.Both the HA matrix and FeCrAl fiber integrate very tightly and bit into each other very deeply and counter-diffusion takes place to some extent at two-phase interface.The optimum parameters of FeCrAl（f）/HA composite are diameter of 22 μm,length of 1-2 mm and of volume faction of about 7% for FeCrAl fibers.展开更多
在分析光纤陀螺的噪声特性的基础上,研究光纤陀螺信号滤波的方法,采用基于S te in无偏似然估计原理,对光纤陀螺信号进行小波阈值除噪,从而达到抑制光纤陀螺中存在的1/fr噪声和白噪声的目的。实验结果表明,小波滤波的方法对于抑制光纤陀...在分析光纤陀螺的噪声特性的基础上,研究光纤陀螺信号滤波的方法,采用基于S te in无偏似然估计原理,对光纤陀螺信号进行小波阈值除噪,从而达到抑制光纤陀螺中存在的1/fr噪声和白噪声的目的。实验结果表明,小波滤波的方法对于抑制光纤陀螺中的噪声,提高信噪比具有良好的效果。展开更多
基金Project(50774096) supported by the National Natural Science Foundation of ChinaProject(2011QNZT046) supported by the Fundamental Research Funds of the Central South University,ChinaProject supported by the Postdoctoral Science Foundation of Central South University,China
文摘FeCrAl fiber-reinforced hydroxyapatite（HA） biocomposites（FeCrAl（f）/HA） were fabricated by the hot pressing technique.The metallographic microscopy,X-ray diffractometry,scanning electron microscopy（SEM） and energy dispersive spectroscopy（EDS） were used to observe and analyze the microstructure and composition of FeCrAl（f）/HA composites,respectively.The mechanical properties of FeCrAl（f）/HA composites were measured by the three-point-bending test.The results show that the composite can be reinforced by FeCrAl fiber and enhanced gradually,and then declined with the increase of the content of FeCrAl fiber（0-11%,volume fraction） in the whole range of experiments.Both the HA matrix and FeCrAl fiber integrate very tightly and bit into each other very deeply and counter-diffusion takes place to some extent at two-phase interface.The optimum parameters of FeCrAl（f）/HA composite are diameter of 22 μm,length of 1-2 mm and of volume faction of about 7% for FeCrAl fibers.