The microstructure of a composite coating system, which was composed of an inner layer of Fe-Cr-Al and an outer layer of aluminum, was studied after it was respectively oxidized and sulfurdized at elevated temperature...The microstructure of a composite coating system, which was composed of an inner layer of Fe-Cr-Al and an outer layer of aluminum, was studied after it was respectively oxidized and sulfurdized at elevated temperatures. Apart from the Al2O3 scale formed on the surface, the microstructure of the composite coatings exposed at 900℃ in air for 4h was a three-layer structure. The first layer consisted of a solid solution of Cr and Fe in α aluminum and an intermetallic compound FeAl3 while the second layer was a single phase of the aluminide and the third layer still remained the same appearance as the original Fe-Cr-Al coating. The microstructural observation of the specimen tested at 850-900℃ at low oxygen pressure and high sulfur pressure for 576h revealed that the surface coatings of the specimen had transformed into a duplex structure containing an outer layer and a thicker aluminide layer beneath. X-ray diffraction results showed that the out layer was composed of Al2S3 and Al2O3 and that AlCrFee was the main phase composition of the aluminide layer, with a few of Al2S3 and Al2O3 accompanied.展开更多
The Fe-Al/WC intermetallic composite coatings have been prepared by high velocity arc spraying(HVAS) technology on 20G steel and the oxidation performance of Fe-Al/WC composite coatings has been studied by means of th...The Fe-Al/WC intermetallic composite coatings have been prepared by high velocity arc spraying(HVAS) technology on 20G steel and the oxidation performance of Fe-Al/WC composite coatings has been studied by means of thermogrativmetic analyzer. The results demonstrate that the kinetics curve of oxidation approximately follows the logarithmic law. The composition of the oxidized coating surface mainly is composed of A12O3, Fe2O3, Fe3O4 and FeO which distribute unevenly. The protective A12O3 film firstly forms and preserves the coatings from further oxidation.展开更多
Fe-Al intermetallics with remarkable high-temperature intensity and excellent erosion, high-temperature oxidation and sulfuration resistance are potential low cost high-temperature structural materials. But the room t...Fe-Al intermetallics with remarkable high-temperature intensity and excellent erosion, high-temperature oxidation and sulfuration resistance are potential low cost high-temperature structural materials. But the room temperature brittleness induces shape difficult and limits its industrial application. The Fe-Al intermetallic coatings were prepared by high velocity arc spraying technology with cored wire on 20G steel, which will not only obviate the problems faced in fabrication of these alloys into useful shapes, but also allow the effective use of their outstanding high-temperature performance. The Fe-Al/WC intermetallic composite coatings were prepared by high velocity arc spraying technology on 20G steel and the oxidation performance of Fe-Al/WC composite coatings was studied by means of thermogrativmetic analyzer at 450, 650 and 800℃. The results demonstrate that the kinetics curve of oxidation at three temperatures approximately follows the logarithmic law. The composition of the oxidized coating is mainly composed of Al2O3, Fe2O3, Fe3O4 and FeO. These phases distribute unevenly. The protective Al2O3 film firstly forms and preserves the coatings from further oxidation.展开更多
The effect of different regimes of heat treatment on the tensile strength of SiC coated composite of C fibers reinforced Al wires has been investigated.Their tensile strength may increase under treatment either at 500...The effect of different regimes of heat treatment on the tensile strength of SiC coated composite of C fibers reinforced Al wires has been investigated.Their tensile strength may increase under treatment either at 500℃ for 2h or 550℃ for 1h,but decrease over 600℃.After the strength tests of extracted fibers from composite wires,the SiC coating is an excellent protection to C fibers.EPMA and EDAX showed that the C/Al interface of the composite wires is stable under treatment below 600℃,but unstable at 650℃展开更多
The processes of mixed rare earth metal (REM) conversion coatings on 2024 alloy and Al6061/SiC p metal matrix composites (MMC) were introduced. The coatings were examined to be honeycomb like feature by scanning elect...The processes of mixed rare earth metal (REM) conversion coatings on 2024 alloy and Al6061/SiC p metal matrix composites (MMC) were introduced. The coatings were examined to be honeycomb like feature by scanning electron microscope. X ray diffraction analysis revealed that the coatings are amorphous structure. The results of X ray photoelectron spectroscopy indicated that the mixed REM conversion coatings consist predominantly of Ce and O, the contents of other rare earth elements (such as La, Pr) are relatively low, the coatings are about 2～4 μm thickness with excellent adhesion and wearability. The results of mass loss test showed that the mixed REM conversion coatings produce corrosion resistant surface of 2024 alloy and Al6061/SiC p. [展开更多
Nanostructured FeS-SiC coating was deposited by atmospheric plasma spraying（APS）.The microstructure and phase composition of the coating were characterized with SEM and XRD,respectively.In addition,the size distribu...Nanostructured FeS-SiC coating was deposited by atmospheric plasma spraying（APS）.The microstructure and phase composition of the coating were characterized with SEM and XRD,respectively.In addition,the size distribution of the reconstituted powders and the porosity of the coating have been measured.It was found that the reconstitiuted powers with sizes in the range of 20 to 80 μm had excellent flowability and were suitable for plasma spraying process.The as-sprayed FeS-SiC composite coating exhibited a bimodal distribution with small grains（30～80nm） and large grains（100～200nm）.The coating was mainly composed of FeS and SiC,a small quantity of Fe1-xS and oxide were also found.The porosity of the coating was approximately 19%.展开更多
文摘The microstructure of a composite coating system, which was composed of an inner layer of Fe-Cr-Al and an outer layer of aluminum, was studied after it was respectively oxidized and sulfurdized at elevated temperatures. Apart from the Al2O3 scale formed on the surface, the microstructure of the composite coatings exposed at 900℃ in air for 4h was a three-layer structure. The first layer consisted of a solid solution of Cr and Fe in α aluminum and an intermetallic compound FeAl3 while the second layer was a single phase of the aluminide and the third layer still remained the same appearance as the original Fe-Cr-Al coating. The microstructural observation of the specimen tested at 850-900℃ at low oxygen pressure and high sulfur pressure for 576h revealed that the surface coatings of the specimen had transformed into a duplex structure containing an outer layer and a thicker aluminide layer beneath. X-ray diffraction results showed that the out layer was composed of Al2S3 and Al2O3 and that AlCrFee was the main phase composition of the aluminide layer, with a few of Al2S3 and Al2O3 accompanied.
基金supports for this work by the National Natural Science Foundation of China(Project No.50235030)Foundation of state economy trade committee of China are grateful acknowledged.
文摘The Fe-Al/WC intermetallic composite coatings have been prepared by high velocity arc spraying(HVAS) technology on 20G steel and the oxidation performance of Fe-Al/WC composite coatings has been studied by means of thermogrativmetic analyzer. The results demonstrate that the kinetics curve of oxidation approximately follows the logarithmic law. The composition of the oxidized coating surface mainly is composed of A12O3, Fe2O3, Fe3O4 and FeO which distribute unevenly. The protective A12O3 film firstly forms and preserves the coatings from further oxidation.
文摘Fe-Al intermetallics with remarkable high-temperature intensity and excellent erosion, high-temperature oxidation and sulfuration resistance are potential low cost high-temperature structural materials. But the room temperature brittleness induces shape difficult and limits its industrial application. The Fe-Al intermetallic coatings were prepared by high velocity arc spraying technology with cored wire on 20G steel, which will not only obviate the problems faced in fabrication of these alloys into useful shapes, but also allow the effective use of their outstanding high-temperature performance. The Fe-Al/WC intermetallic composite coatings were prepared by high velocity arc spraying technology on 20G steel and the oxidation performance of Fe-Al/WC composite coatings was studied by means of thermogrativmetic analyzer at 450, 650 and 800℃. The results demonstrate that the kinetics curve of oxidation at three temperatures approximately follows the logarithmic law. The composition of the oxidized coating is mainly composed of Al2O3, Fe2O3, Fe3O4 and FeO. These phases distribute unevenly. The protective Al2O3 film firstly forms and preserves the coatings from further oxidation.
文摘The effect of different regimes of heat treatment on the tensile strength of SiC coated composite of C fibers reinforced Al wires has been investigated.Their tensile strength may increase under treatment either at 500℃ for 2h or 550℃ for 1h,but decrease over 600℃.After the strength tests of extracted fibers from composite wires,the SiC coating is an excellent protection to C fibers.EPMA and EDAX showed that the C/Al interface of the composite wires is stable under treatment below 600℃,but unstable at 650℃
文摘The processes of mixed rare earth metal (REM) conversion coatings on 2024 alloy and Al6061/SiC p metal matrix composites (MMC) were introduced. The coatings were examined to be honeycomb like feature by scanning electron microscope. X ray diffraction analysis revealed that the coatings are amorphous structure. The results of X ray photoelectron spectroscopy indicated that the mixed REM conversion coatings consist predominantly of Ce and O, the contents of other rare earth elements (such as La, Pr) are relatively low, the coatings are about 2～4 μm thickness with excellent adhesion and wearability. The results of mass loss test showed that the mixed REM conversion coatings produce corrosion resistant surface of 2024 alloy and Al6061/SiC p. [
基金Project (2012BAE06B01) supported by the Key Technology R&D Program During the 12th Five-Year Plan Period, ChinaProjects(21201030, 51272039, 51032007) supported by the National Natural Science Foundation of ChinaProject (1099043) supported by the Science and Technology in Guangxi Province, China
基金The authors would like to thank National Natural Science Foundation of China (No. 50375015) for supporting.
文摘Nanostructured FeS-SiC coating was deposited by atmospheric plasma spraying（APS）.The microstructure and phase composition of the coating were characterized with SEM and XRD,respectively.In addition,the size distribution of the reconstituted powders and the porosity of the coating have been measured.It was found that the reconstitiuted powers with sizes in the range of 20 to 80 μm had excellent flowability and were suitable for plasma spraying process.The as-sprayed FeS-SiC composite coating exhibited a bimodal distribution with small grains（30～80nm） and large grains（100～200nm）.The coating was mainly composed of FeS and SiC,a small quantity of Fe1-xS and oxide were also found.The porosity of the coating was approximately 19%.