Nanometer powders of Al Fe alloy were prepared by gas evaporation. The formation regularity of the phases in the as prepared powders and the morphology of the particles were examined. The experimental results show tha...Nanometer powders of Al Fe alloy were prepared by gas evaporation. The formation regularity of the phases in the as prepared powders and the morphology of the particles were examined. The experimental results show that chemical composition of the master alloy is the key factor which controls the chemical composition of the compound phases in nanometer powders at given evaporating temperature, the compound phases with high Fe mole fraction will form with increasing of Fe content in master alloy. Only Al 13 Fe 4, FeAl 2 and Al 2Fe compound phases form in nanometer powders in present experiment, changing of the pressure of Ar can only alter relative amounts of the compound phases in the powders. Nanometer particles with inhomogeneous tissue were obtained, which is very different from that of pure Al and Fe nanometer particles. When mole fraction of Fe in particles increases, the inhomogeneity is enhanced. [展开更多
Al-4.9 Fe-4.9 Ni alloy powders have been synthesized by mechanical alloying. The rnechanically alloyed powders are consolidated by hot hydrostatic extrusion. The results show that extrusion tempereture. extrusion rati...Al-4.9 Fe-4.9 Ni alloy powders have been synthesized by mechanical alloying. The rnechanically alloyed powders are consolidated by hot hydrostatic extrusion. The results show that extrusion tempereture. extrusion ratio and lubricant have great effects on the quality of extruded rods and their mechanical properties, The mixture of graphite and glass powders as lubricant can prevent the oxidization of cold compacted billet by cladding the billet with this lubricant before heating. This technique greatly simplifies the conventional densification process of powders展开更多
采用机械合金化法制备Al V Fe纳米粉末 ,通过测定M ssbauer效应 ,研究了不同球磨能量对制备Al V Fe纳米粉末的影响·结果表明 ,振动球磨与高能球磨所制备的Al V Fe纳米粉末结构均由非晶和α Al纳米晶组成 ,其非晶含量随着球磨能量...采用机械合金化法制备Al V Fe纳米粉末 ,通过测定M ssbauer效应 ,研究了不同球磨能量对制备Al V Fe纳米粉末的影响·结果表明 ,振动球磨与高能球磨所制备的Al V Fe纳米粉末结构均由非晶和α Al纳米晶组成 ,其非晶含量随着球磨能量的增加而有所不同·展开更多
文摘Nanometer powders of Al Fe alloy were prepared by gas evaporation. The formation regularity of the phases in the as prepared powders and the morphology of the particles were examined. The experimental results show that chemical composition of the master alloy is the key factor which controls the chemical composition of the compound phases in nanometer powders at given evaporating temperature, the compound phases with high Fe mole fraction will form with increasing of Fe content in master alloy. Only Al 13 Fe 4, FeAl 2 and Al 2Fe compound phases form in nanometer powders in present experiment, changing of the pressure of Ar can only alter relative amounts of the compound phases in the powders. Nanometer particles with inhomogeneous tissue were obtained, which is very different from that of pure Al and Fe nanometer particles. When mole fraction of Fe in particles increases, the inhomogeneity is enhanced. [
文摘Al-4.9 Fe-4.9 Ni alloy powders have been synthesized by mechanical alloying. The rnechanically alloyed powders are consolidated by hot hydrostatic extrusion. The results show that extrusion tempereture. extrusion ratio and lubricant have great effects on the quality of extruded rods and their mechanical properties, The mixture of graphite and glass powders as lubricant can prevent the oxidization of cold compacted billet by cladding the billet with this lubricant before heating. This technique greatly simplifies the conventional densification process of powders
基金supported by the Key Laboratory of Micro-systems and Micro-structures Manufacturing of Ministry of Education,Harbin Institute of Technology,China(No.2020KM005)the Natural Science Foundation of Heilongjiang Province,China(No.YQ2020E030)。