Distribution behavior of Copper and Tin between FeO-rich slag and iron solution

The distribution behavior of residual elements copper and tin between FeO rich slag and iron solution was investigated under the condition of an induction furnace. The results indicate that a part of copper and tin is incidently oxidized when oxygen is blasted into bath to react with iron element. The distribution ratio of copper and tin between slag and metal is about 0.1. Phenomena of Cu and Sn elements segregation and accumulation in slag were observed by means of EPMA analysis. The distribution ratio of copper and tin between slag and metal may descend with increasing of CaO content in slag.

铜滴在富FeO熔渣中的电迁移行为

电场作用下通过熔渣中金属铜的电毛细迁移富集渣中铜是一种去除熔渣中铜的有效方法.本文叙述了富FeO熔渣体系的热力学性质,揭示了电场作用下铜滴的迁移行为,讨论了铜滴迁移的影响因素,并给出了电场作用下富FeO渣中金属铜的迁移富集的规律.

含铜和锡铁液渣化过程中富FeO熔渣的EPMA观察

在感应炉熔炼条件下,研究含铜、锡等元素的铁溶液的渣化过程,并对熔渣进行EPMA观察。结果表明,向熔池中 吹氧氧化铁的同时,有部分铜、锡等元素被氧化,由于金属渣间反应进行的不充分而使金属滞留于熔渣中。富FeO熔渣与铁溶液 的分离不好也是造成熔渣中铜、锡含量偏高的原因之一。在电子探针显微分析中观察到铜、锡等元素在熔渣中的偏析现象。

锡在富FeO熔渣中氧化溶解行为的研究

在1873K温度下对锡在富FeO熔渣中的氧化溶解行为进行了研究。结果表明:锡在富FeO熔渣中是以SnO形式存在。熔渣中的CaO含量对锡的氧化溶解影响不大,随着CaO含量的增加,锡的氧化溶解稍微有点下降。根据实验数据拟合曲线,得出γSnO与熔渣中CaO含量之间的关系为:γSnO=1.286+0.0021(CaO%)。

铜在富FeO熔渣中的氧化溶解行为

在1873K条件下对铜在富FeO熔渣中的氧化溶解行为进行了研究。结果表明铜氧化物在富FeO熔渣中以Cu2O的形式存在;熔渣中CaO的含量将对铜的氧化溶解产生影响,随着渣中CaO含量的增加,熔渣中的铜含量逐渐下降,但在不同温度下,这种影响的作用各不相同;当温度较高时,渣中CaO含量对铜的氧化溶解影响较大,且随着温度的降低,其影响作用明显变缓;反应体系的氧分压对铜的氧化溶解影响较大,在熔渣中γ(CuO0.5)不变的情况下,铜氧化物的溶解与体系氧分压的四分之一次方之间呈正线性关系。

铜锡在铁液与富FeO熔渣中分配行为的研究

研究了 1 0kg感应炉熔炼时铜、锡等钢中残存有害元素在铁液与富FeO熔渣中的分配行为。结果表明 :当向熔池中吹氧与铁元素反应时 ,有一部分铜、锡等元素被氧化 ,由于渣金间反应不完全而使其滞留于熔渣中 ,铜、锡在渣 金之间的分配比约为 0 .1 ;在电子探针显微分析 (EPMA)中观察到铜、锡元素在熔渣中的偏析和积聚现象 ;增加熔渣中CaO含量会降低铜、锡在渣