Crystal characterization and optical spectroscopy of Eu^(3+)-doped CaGdAlO_4 single crystal fabricated by the floating zone method

A highly transparent Eu3＋-doped CaGdA104 （CGA） single crystal is grown by the floating zone method. The segregation coefficient, x ray diffraction, and x ray rocking curve are detected, and the results reveal that the single crystal is of high quality. The f-f transitions of Eu3＋ in the host lattice are discussed. The 5D0-7F2 emis- sion transition at 621 nm （red light） is dominant over the 5D0-7F1 emission transitions at 591 and 599 nm （orange light）, agreeing well with the random crystal environment of Eu3＋ ions in a CGA crystal. The decay time of Eu：5D0 is measured to be 1.02 ms. All the results show that the Eu：CGA crystal has good optical char- acterization and promises to be an excellent red- fluorescence material.

Floating zone growth and magnetic and specific heat properties of La0.67Ca0.33Mn1-xFexO3（x=0.00,0.04）single crystals

Single crystals of La0.67Ca0.33MnO3 and La0.67Ca0.33Mn0.96Fe0.04O3 were obtained by floating zone method. Laue diffraction pattern and rocking curve of the single crystals show that their quality is good. The magnetic behaviours of these compounds have been studied. Fe doping significantly depresses the magnetic contribution to the total specific heat Cp, but slightly influences the lattice contribution at temperatures above 50K. The peak of Cp shifts towards high temperatures with increasing magnetic field. Both single crystals exhibit the first-order magnetic transition around the Curie temperature.

Crystal growth,structure and optical properties of Pr^(3+)-doped yttria-stabilized zirconia single crystals

The development of blue semiconductor light-emitting diodes(LEDs)has produced potential applications for Prdoped materials that can absorb blue light,especially crystals,and we now report structure and optical properties for high-quality Pr-doped single crystals of yttria-stabilized zirconia(YSZ)grown by the optical floating zone(FZ)method.X-ray diffraction(XRD)and Raman spectroscopy showed that all of the single crystal samples were in the cubic phase,whereas the corresponding ceramic samples contained a mixture of monoclinic and cubic phases.X-ray photoelectron spectroscopy(XPS)and electron paramagnetic resonance(EPR)spectroscopy showed that Pr was present as the Pr^(3+)ion in ceramic rods and single crystals after heating to high temperatures.The absorption and photoluminescence excitation(PLE)spectra of the Pr-doped YSZ crystals measured at room temperature showed strong absorption of blue light,while their photoluminescence(PL)spectra showed five emission peaks at 565 nm,588 nm,614 nm,638 nm,and 716 nm under450 nm excitation.The optimum luminescence properties were obtained with the crystal prepared using 0.15 mol%Pr_(6)O_(11),and those with higher concentrations showed evidence of quenching of the luminescence properties.In addition,the color purity of Pr-doped YSZ single crystal reached 98.9%in the orange–red region.

Optical phonon behavior and magnetism of columbite Zn0.8Co0.2Nb2O6

Columbite Zn0.8Co0.2Nb2O6 crystals were grown by optical floating zone methods. The x-ray diffraction(XRD) was used to check the structure information of the grown Zn0.8Co0.2Nb2O6 crystal. The room temperature and temperature-dependent Raman spectra were tested to investigate the optical phonon behaviors of columbite Zn0.8Co0.2Nb2O6, which exhibited a temperature stable property. The magnetics properties of Zn0.8Co0.2Nb2O6, measured by a physical property measurement system(PPMS), were also presented in this work.

输运溶剂浮区法生长Bi_(2+x)Sr_(2-x)Ca_(n-1)Cu_nO_(2n+4+d)晶体

The growth of crystals of the high T c oxide superconductors has been hampe red by the complexities of the materials and their phase diagrams.The most common crys tal growth technique adopted for these oxides is the “flux”method,where the st arting materials are solved in a melt,which is usually formed by excess CuO and BaO or a KCl/NaCl mixture.The crystals are produced by slow cooling of the heate d solvent.This method,however,suffers from several disadvantages: (1) the crystals are contaminated with the crucible material, (2) the crystals are difficult to remove from the crucible, (3) the crystals contain flux inclusions.

White light luminescence in Dy/Tm co-doped yttria stabilized zirconia single crystals

A series of high quality Dy_(2)O_(3) and Tm_(2)O_(3)co-doped yttria stabilized zirconia(YSZ) single crystals was synthesized.These crystals have a single cubic structure,and exhibit the characteristic of Dy^(3+)(blue and yellow emissions) and Tm^(3+)(blue emission) under excitation with NUV light.Impo rtantly,the hue can be varied between blue and white by modifying the Tm^(3+)/Dy^(3+)ratio.The photoluminescence and decay curves are consistent with the existence of resonance-type energy transfer from Tm^(3+)to Dy^(3+)ions via an electric multipole interaction mechanism.Maximum luminescence intensity is observed in YSZ doped with 0.50 mol% Tm_(2)O_(3) and 0.75 mol% Dy_(2)O_(3),and this sample has CIE coordinates(x = 0.33,y = 0.33) in accordance with those for white chromaticity.Thus,the outstanding luminescence properties of these single crystals suggest potential applications in white light emission devices.