Effect of temperature and reaction path interaction on fluidization reduction kinetics of iron ore powder

Due to the instability of FeO at temperatures below 843 K,the fuidization reduction pathway of iron ore powder changes with the reduction temperature.Thus,the effect of temperature and reaction pathway interaction on the kinetics of fuidization reduction of iron ore powder under low-temperature conditions ranging from 783 to 903 K was investigated to describe the fluidization reduction rate of iron ore powder from three aspects:microstructure change,reaction limiting link,and apparent activation energy of the reaction,exploring their internal correlation.The experimental results revealed that in a temperature range of 783-813 K,the formation of a dense iron layer hindered the internal diffusion of reducing gas,resulting in relatively high gas diffusion resistance.In addition,due to the differences in limiting links and reaction pathways in the intermediate stage of reduction,the apparent activation energy of the reaction varied.The apparent activation energy of the reaction ranged from 23.36 to 89.13 kJ/mol at temperature ranging from 783 to 813 K,while it ranged from 14.30 to 68.34 kJ/mol at temperature ranging from 873 to 903 K.

Characterization of fluidized reduction roasting of nickel laterite ore under CO/CO_(2)atmosphere

Fluidized reduction roasting is an efficient metallurgical technique.However,its application to nickel laterite ore has rarely been reported.In this paper,the effects of reduction temperature,reduction time,CO concentration,and material particle size on the roasting characteristics of ferronickel fluidization reduction were investigated.Combined with X-ray diffraction,scanning electron microscopy-energy dispersive spectrometry(SEM-EDS)characterization,the mineral phases and microscopic morphology of nickel laterite ore and its roasted ores were analyzed in depth.The results indicated that under the condition of a CO/CO_(2)ratio of 1:1,a reduction temperature of 800℃,and a reduction roasting time of 60 min,a nickel-iron concentrate with a nickel grade of 2.10%and an iron content of 45.96%was produced from a raw material with a nickel grade of 1.45%,achieving a remarkable nickel recovery rate of 46.26%.XRD and SEM-EDS analysis indicated that nickel in the concentrate mainly exists in the form of[Fe,Ni],while the unrecovered nickel in the tailings is primarily present in the form of[Fe,Ni]and Ni_(2)SiO_(4)in forsterite.This study established a theoretical foundation for further exploration of fluidized reduction roasting technology.

From laboratory research to industrial application:a green technology of fluidized mineral processing for manganese dioxide ore reduction

The efficient utilization of manganese dioxide(MnO_(2))ore is essential for the sustainable development of manganese(Mn)industry.Confronting the great challenge of chemical engineering scale-up,a commercial fluidized reduction project of MnO_(2)ore with the capacity of 200,000 t a^(-1)is carried out based on deep experimental investigation,extensive kilogram-scale test and detailed engineering design.Compared with other production technologies and equipment,it is proved that the fluidized process shows distinguished advantages of lower energy consumption,higher production efficiency,larger automation degree and less environmental pollution.The comprehensive studies of experiment,modeling,simulation and optimization are required for a more promising development of fluidization engineering in the future.