The glass transition behavior of La55A125-Ni10CU10 bulk metallic glass was investigated using elec-trical resistivity and differential-scanning calorimetry measurements. There are good agreements of the onset temperat...The glass transition behavior of La55A125-Ni10CU10 bulk metallic glass was investigated using elec-trical resistivity and differential-scanning calorimetry measurements. There are good agreements of the onset temperature （Tg-onset） and the end temperature （Tg-end） of the glass transition between the DSC curve and tempera-ture dependent electrical resistivity （TER） curve in the same heating rate. Kinetics of the glass transition is studied with the electrical resistivity data. The apparent activation energy of the glass transition （△Eg） is found to be 306.4 kJ.mol^-1. Fragility parameter D^＊ and VFT temper-ature To are 9.8 and 324.9 K, respectively.展开更多
The thin ribbons and the bulk cylindrical rods with diameters of 2 mm and 10 mm of the Vit1 metallic glass(MG)were prepared by the single roller melt spinning method and the copper mold injection casting method,respec...The thin ribbons and the bulk cylindrical rods with diameters of 2 mm and 10 mm of the Vit1 metallic glass(MG)were prepared by the single roller melt spinning method and the copper mold injection casting method,respectively.The cooling rates of the samples during melt solidification were evaluated.The glass transition behaviors of three groups of MG samples with different solidification cooling rates were studied by differential scanning calorimetry(DSC)at different heating rates.The effects of melt cooling rate on the glass transition kinetic parameters such as apparent activation energy(E)and fragility parameter(m)of the Vit1 MG were studied using the Kissinger and the Vogel-Fulcher-Tammann(VFT)equations.Additionally,the structural relaxation enthalpy(ΔHrel)of three groups of MG samples was quantitatively analyzed by DSC through multi-step temperature rise and fall measurements.Results show that the melt cooling rate(R)has a significant effect on the glass transition kinetics and the structural relaxation of the Vit1 MG.As R decreases in the order of magnitude,the glass transition temperature(Tg),E,m,andΔHrel of the Vit1 MG gradually decreases.Furthermore,in the range of the experimental cooling rates,E,m,andΔHrel all have an approximately linear relationship with lgR.展开更多
基金financially supported by the Fundamental Research Funds for the Central Universities(No.FRFTP-09-026B)the Program for Changjiang Scholars and Innovative Research Team in University,the Specialized Research Fund for the Doctoral Program of Higher Education(No.20100006110013)the National Natural Science Foundation of China(No.51010001)
文摘The glass transition behavior of La55A125-Ni10CU10 bulk metallic glass was investigated using elec-trical resistivity and differential-scanning calorimetry measurements. There are good agreements of the onset temperature （Tg-onset） and the end temperature （Tg-end） of the glass transition between the DSC curve and tempera-ture dependent electrical resistivity （TER） curve in the same heating rate. Kinetics of the glass transition is studied with the electrical resistivity data. The apparent activation energy of the glass transition （△Eg） is found to be 306.4 kJ.mol^-1. Fragility parameter D^＊ and VFT temper-ature To are 9.8 and 324.9 K, respectively.
基金supported by the National Key Research and Development Program of China(No.2019YFB2006501)。
文摘The thin ribbons and the bulk cylindrical rods with diameters of 2 mm and 10 mm of the Vit1 metallic glass(MG)were prepared by the single roller melt spinning method and the copper mold injection casting method,respectively.The cooling rates of the samples during melt solidification were evaluated.The glass transition behaviors of three groups of MG samples with different solidification cooling rates were studied by differential scanning calorimetry(DSC)at different heating rates.The effects of melt cooling rate on the glass transition kinetic parameters such as apparent activation energy(E)and fragility parameter(m)of the Vit1 MG were studied using the Kissinger and the Vogel-Fulcher-Tammann(VFT)equations.Additionally,the structural relaxation enthalpy(ΔHrel)of three groups of MG samples was quantitatively analyzed by DSC through multi-step temperature rise and fall measurements.Results show that the melt cooling rate(R)has a significant effect on the glass transition kinetics and the structural relaxation of the Vit1 MG.As R decreases in the order of magnitude,the glass transition temperature(Tg),E,m,andΔHrel of the Vit1 MG gradually decreases.Furthermore,in the range of the experimental cooling rates,E,m,andΔHrel all have an approximately linear relationship with lgR.