Teroolymerization of enichlorohydrin（ECH）-maleic anhydride（MAn）-carbon dioxide（CO;） was carried out by using Y(P;);-Al（i-Bu）;as catalyst for the first time.The terpolymersobtained were characterized by IR and;...Teroolymerization of enichlorohydrin（ECH）-maleic anhydride（MAn）-carbon dioxide（CO;） was carried out by using Y(P;);-Al（i-Bu）;as catalyst for the first time.The terpolymersobtained were characterized by IR and;H-NMR.It was foundthat the composition of the teroolymer was influenced by theaddition mode,initial monomer charge ratio,etc.展开更多
Copolyesters having secondary and tertiary amine salt groups in the main and side chains are prepared by chemoselective polymerization. These copolyesters are soluble in a 10% aqueous solution of poly(vinyl alcohol) ...Copolyesters having secondary and tertiary amine salt groups in the main and side chains are prepared by chemoselective polymerization. These copolyesters are soluble in a 10% aqueous solution of poly(vinyl alcohol) (PVA) at 90 degree C and act as plasticizer in the blend films cast from the solution. Only a glass transition temperature is observed for all these blends indicating the formation of compatible blends from these polyesters with PVA. These blends exhibit manifold characteristics such as ionic conductivity, complex formation with metal ions, absorption of moisture and color changes. The electric conductivity of the copolyesters and blends is in the range of 10** minus **6 Scm** minus **1. The blends with PVA forms complexes with Cu**2** plus and Co**2** plus . The coordination structure with two chelate rings is suggested for these polymer blend/metal complexes. (Author abstract) 10 Refs.展开更多
Amphiphilic hydroxyl functioned polyester（HFP） can be used as compatibilizers for blends of starch and resins.We developed a synthetic method for effective preparation of HFPs.Water was removed by high flow rate N_2...Amphiphilic hydroxyl functioned polyester（HFP） can be used as compatibilizers for blends of starch and resins.We developed a synthetic method for effective preparation of HFPs.Water was removed by high flow rate N_2 rather than high vacuum during polycondensation of sebacic acid with xylitol,sorbitol,or mannitol in the presence of dehydrative condensation catalyst and the product is with[η]of 27.2 mL/g,M_n of 1903,M_w of 167,693,T_g of -30.5℃,T_m of 44.0℃.Weight loss is 1.73%under 200℃. The integral distributions of molecular weight are 43.6 wt%and 63.8 wt%over 10,000 and 3000,respectively.The results indicated that higher molecular weight HFP was economically synthesized.展开更多
文摘Teroolymerization of enichlorohydrin（ECH）-maleic anhydride（MAn）-carbon dioxide（CO;） was carried out by using Y(P;);-Al（i-Bu）;as catalyst for the first time.The terpolymersobtained were characterized by IR and;H-NMR.It was foundthat the composition of the teroolymer was influenced by theaddition mode,initial monomer charge ratio,etc.
文摘Copolyesters having secondary and tertiary amine salt groups in the main and side chains are prepared by chemoselective polymerization. These copolyesters are soluble in a 10% aqueous solution of poly(vinyl alcohol) (PVA) at 90 degree C and act as plasticizer in the blend films cast from the solution. Only a glass transition temperature is observed for all these blends indicating the formation of compatible blends from these polyesters with PVA. These blends exhibit manifold characteristics such as ionic conductivity, complex formation with metal ions, absorption of moisture and color changes. The electric conductivity of the copolyesters and blends is in the range of 10** minus **6 Scm** minus **1. The blends with PVA forms complexes with Cu**2** plus and Co**2** plus . The coordination structure with two chelate rings is suggested for these polymer blend/metal complexes. (Author abstract) 10 Refs.
基金the financial support of National Key Technology R&D Program(No.2006BAD07A06)National"863"Program Project of China(No.2006AA100216)
文摘Amphiphilic hydroxyl functioned polyester（HFP） can be used as compatibilizers for blends of starch and resins.We developed a synthetic method for effective preparation of HFPs.Water was removed by high flow rate N_2 rather than high vacuum during polycondensation of sebacic acid with xylitol,sorbitol,or mannitol in the presence of dehydrative condensation catalyst and the product is with[η]of 27.2 mL/g,M_n of 1903,M_w of 167,693,T_g of -30.5℃,T_m of 44.0℃.Weight loss is 1.73%under 200℃. The integral distributions of molecular weight are 43.6 wt%and 63.8 wt%over 10,000 and 3000,respectively.The results indicated that higher molecular weight HFP was economically synthesized.