Glass-Ceramics with High Strength and High Transmittance Obtained by Multi-Factor Controlling

The presence of Li_(2)Si_(2)O_(5) and LiAlSi_(4)O_(10) could effectively improve the elastic modulus and transmittance of lithium disilicate(LD)glass-ceramics.Through synergistically modulation of the crystal content and grain size,we obtained high strength and high transmittance of LD glass-ceramics.The optimal sample had a high transmittance of 90.3%,the hardness was 7.72 GPa,the fracture toughness was 1.07 MPa·m^(1/2),and the elastic modulus was 103.1 GPa.

Properties of Ultra-low Thermal Expansion LAS Transparent Glass-ceramics Prepared by Spodumene

The glass-ceramics were prepared with the spodumene mineral as the main raw material,and the effects of ZrO_(2)replacing TiO_(2)on the samples were systematically investigated.The results show that the substitution of ZrO_(2)for TiO_(2)is not conductive to precipitate𝛽β-quartz solid solution phase,but can improve the transparency and flexural strength of glass-ceramics.And the glass-ceramic with the highest visible light transmittance(87%)and flexural strength(231.80 MPa)exhibits an ultra-low thermal expansion of-0.028×10^(-7)K^(-1)in the region of 30-700℃.

Preparation, Crystallization and Mechanical Properties of Potassium Aluminosilicate Glass-ceramics

In this study,transparent K_(2)O-Al_(2)O_(3)-SiO_(2)(KAS)glass-ceramics with leucite as the main crystalline phase were prepared by melting-quench method and two-step heat treatment.The effects of SiO_(2)/Al_(2)O_(3) ratio and heat treatment on crystallization and mechanical properties were studied.The crystallization kinetics and X-Ray Diffraction(XRD)results showed that SiO_(2)/Al_(2)O_(3) ratio and heat treatment system had a direct impact on the crystallization behavior of potassium aluminosilicate glass-ceramics.When heat-treated at 680℃/2 h and 780℃/1 h,cracks generated on the surface of the sample with the addition of SiO_(2)/Al_(2)O_(3)=4.8(in mol)due to the huge difference in the coefficient of thermal expansion between glass matrix and surface.When the addition of SiO_(2)/Al_(2)O_(3)(in mol)was 4,the sample with leucite as the main crystalline phase showed an excellent fracture toughness(1.46 MPa·m^(0.5))after the heat treatment of 680℃/2 h and 780℃/5 h.And there was a phase transformation from kaliophilite to leucite.The crystalline phases of the sample heat-treated at 680℃/8 h and 780℃/1 h were leucite and kaliophilite,which resulted in the visible light transmittance of 63%and the fracture toughness of 0.91 MPa·m^(0.5).Furthermore,after the heat treatment of 680℃/2 h and 780℃/5 h,the main crystalline phase of the sample with SiO_(2)/Al_(2)O_(3)=3.2(in mol)was still kaliophilite.Because leucite only grows on the surface of the sample and is hard to grow inward,it is hard to achieve the bulk crystallization of leucite in the sample with SiO_(2)/Al_(2)O_(3)=3.2(in mol).

Crystallization kinetics and temperature dependence of energy storage properties of niobate glass-ceramics

Glass-ceramic materials of strontium barium niobate system were prepared through a melt-quenching method. The effects of crystallization temperature on the mierostructure, dielectric property, breakdown strength and energy storage density of barium strontium niobate glass-ceramics were studied. The crystallization mechanism of the glass-ceramics was discussed and should be one-dimensional interfacial growth. The results indicate that the breakdown strength remarkably increases with the increase of crystallization temperature. The glass-ceramic heat treated at 900 ℃ was found to possess optimal properties with breakdown strength of 1300 kV/cm and energy storage density of 2.8 J/cm3, which is promising dielectric materials for high energy storage density dielectrics.

Influence of aluminium nitride as a foaming agent on the preparation of foam glass-ceramics from high-titanium blast furnace slag

To effectively reuse high-titanium blast furnace slag （TS）, foam glass-ceramics were successfully prepared by powder sintering at 1000℃. TS and waste glass were used as the main raw materials, aluminium nitride （AIN） as the foaming agent, and borax as the fluxing agent. The influence of the amount of A1N added （lwt%-5wt%） on the crystalline phases, microstructure, and properties of the produced foam glass-ceramics was studied. The results showed that the main crystal phases were perovskite, diopside, and augite. With increasing A1N content, a transformation from diopside to augite occurred and the crystallinity of the pyroxene phases slightly decreased. Initially, the aver- age pore size and porosity of the foam glass-ceramics increased and subsequently decreased; similarly, their bulk density and compressive strength decreased and subsequently increased. The optimal properties were obtained when the foam glass-ceramics were prepared by adding 4wt% AIN.

Effect of sintering temperature on the microstructure and properties of foamed glass-ceramics prepared from high-titanium blast furnace slag and waste glass

Foamed glass-ceramics were prepared via a single-step sintering method using high-titanium blast furnace slag and waste glass as the main raw materials The influence of sintering temperature(900–1060℃) on the microstructure and properties of foamed glass-ceramics was studied. The results show that the crystal shape changed from grainy to rod-shaped and finally turned to multiple shapes as the sintering temperature was increased from 900 to 1060℃. With increasing sintering temperature, the average pore size of the foamed glass-ceramics increased and subsequently decreased. By contrast, the compressive strength and the bulk density decreased and subsequently increased. An excessively high temperature, however, induced the coalescence of pores and decreased the compressive strength. The optimal properties, including the highest compressive strength(16.64 MPa) among the investigated samples and a relatively low bulk density(0.83 g/cm^3), were attained in the case of the foamed glass-ceramics sintered at 1000℃.

Nucleation and crystallization of tailing-based glass-ceramics by microwave heating

The effect of microwave radiation on the nucleation and crystallization of tailing-based glass-ceramics was investigated using a 2.45 GHz multimode microwave cavity. Tailing-based glass samples were prepared fi＇om Shandong gold tailings and Guyang iron tailings utilizing a conventional glass melting technique. For comparison, the tailing-based glass samples were crystallized using two different heat-treatment methods： conventional heating and hybrid microwave heating. The nucleation and crystallization temperatures were determined by performing a differential thermal analysis of the quenched tailing-based glass. The prepared glass-ceramic samples were further characterized by Fourier transform infrared spectroscopy, X-ray diffraction, Raman spectroscopy, thermal expansion coefficient measurements, and scanning electron microscopy. The results demonstrated that hybrid microwave heating could be successfully used to crystallize the tailing-based glass, reduce the processing time, and decrease the crystallization temperature. Furthermore, the results indicated that the nucleation and crystallization mechanism of the hybrid microwave heating process slightly differs fi＇om that of the conventional heating process.

Luminescence of Er^(3+) in Oxyfluoride Transparent Glass-Ceramics

Erbium doped silicate, germanate, and tellurium-germanate oxyfluoride glasses were prepared in a bulk form. Through appropriate heat treatment of the as-prepared glasses, transparent glass-ceramics （TGCs） were obtained with the formation of β-PbF2：Er^3＋ nanocrystals in the glass matrix were confirmed by X-ray diffraction.Well-defined diffraction peaks were observed in the samples after heat-treatment. The average crystal diameter of these precipitated crystals from full-width at half-maximum （FWHM） of the diffraction peak was estimated to be between 8 and 13 nm. Optical absorption, photoluminescence, and upconversion luminescence were measured on as-prepared glass and glass-ceramics. Luminescence spectra in the TGC samples revealed well-resolved, sharp stark-splitting peaks, which indicates that a majority of Er^3＋ ions has been incorporated into the crystalline phase of the nanocrystals. The intensity of the visible and near infrared luminescence mostly increases in TSG compared to that in the as-prepared glass. In 1.53 μm absorption and emission bands, the maximum absorption peak is blue-shifted from 1531 to 1507 nm, whereas the maximum emission peak is redshifted from 1535 to 1543 nm in TGC, as compared with that in glass. The bandwidth at half-maximum （BWHM） of the emission band is significantly broader in TGC than in glass, which is beneficial to the erbium-doped fiber amplifier （EDFA）. Upconversion luminescence was measured using 800 nm near-infrared light excitation. Drastically increased upconversion 1 was observed from the TGC as compared to that from their corresponding as-prepared glasses. In addition to a strong green emission centered at 545 nm because of ^4S3/2→^4I15/2 transition and a weaker red emission centered at 662 nm because of ^4F9/2→^4I15/2 transition, generally seen from the Er^3＋ doped glasses, two violet emissions centered at 410 nm because of ^2H9/2→^4I15/2 transition and centered at 379 nm because of ^4G11/2→^4I15/2 transition were also observed from the was attributed to the decreased effective phonon energy and the increased energy transfer between the excited ions when Er^3＋ ions were incorporated into the precipitated β-PbF2 nanocrystals. The results indicated two attractive spectroscopic properties of the Er^3＋ doped TGC samples, compared to glass samples, namely a reduced multiphonon decay rate and a reduced inhomogeneous broadening. In addition, these oxyfluoride TGC materials were robust,easy and flexibile to process, and possible to be fabricated in the fiber form for device applications.

Influence of CeO_2 addition on the preparation of foamed glass-ceramics from high-titanium blast furnace slag

Foamed glass-ceramics doped with cerium oxide（CeO_2）were successfully prepared from high-titanium blast furnace slag by one-step sintering.The influence of CeO_2 addition（1.5wt%–3.5wt%）on the crystalline phases,microstructure,and properties of foamed glass-ceramics was studied.Results show that CeO_2 improves the stability of the glass phase and changes the two-dimensional crystallization mechanism into three-dimensional one.XRD analysis indicates the presence of Ca（Mg,Fe）Si_2O_6 and Ca（Ti,Mg,Al）（Si,Al）_2O_（6 ）in all sintered samples.Added with CeO_2,Ti CeO_4 precipitates,and crystallinity increases,leading to increased thickness of pore walls and uniform pores.The comprehensive properties of foamed glass-ceramics are better than that of samples without CeO_2.In particular,the sample added with a suitable amount of CeO_2（2.5wt%）exhibits bulk density that is similar to and compressive strength（14.9 MPa）that is more than twice of foamed glass-ceramics without CeO_2.

Glass-ceramics made from arc-melting slag of waste incineration fly ash

Grate fly ash and fluidized bed fly ash mixed with glass cullet additive respectively were melted in the electronic arc-furnace. The product, arc-melting slag, was further treated by crushing, pressing and heat treatment in order to make the glass-ceramics. The crystallization behaviors of the produced glass-ceramics were examined by differential thermal analysis （DTA）, X-ray diffractometry （XRD） and scanning electron microscopy （SEM）. Results show that main crystalline phase of the glass-ceramics fi＇om grate fly ash is wollastonite （CaSiO3） with small amount of diopside （Ca（Mg,Al）（Si,Al）206）, and that from fluidized bed fly ash is diopside （Ca（Mg,Al）（Si,Al）206）. It is found that the glass-ceramics sintered at 850 ℃and 1 000℃ from grate fly ash and fluidized bed fly ash respectively have the optimal physical, mechanical and chemical characteristics. Glass-ceramics samples, produced from incinerator fly ash with desirable properties and the low leaching concentration of heavy metals, can be the substitute of nature materials such as marble, granite and porcelain tiles.

Effect of Water Washing Pre-treatment on the Properties of Glass-ceramics from Incinerator Fly Ash Using Electronic Arc Furnace

Production of glass-ceramics by sintering the molten slag obtained from electric arc furnace treatment of fly ash was investigated. The effect of washing pretreatment prior to melting the fly ash on the microstructure and properties of the glass-ceramics was examined. The results show that washing pretreatment of fly ash can decrease alkali metal chloride and increase network former in fly ash, which results in the increase of peak crystallization temperature of parent glass and strengthening of properties of bending strength and chemical stability of the glass-ceramics. The optimal heat treatment temperature for parent glass of washed fly ash is 1 173 K, at which the crystalline phase of glass-ceramics is composed of gelignite （Ca2A12SiO7） and akermanite （Ca2MgSi207）. Glass-ceramics produced at optimal heat treatment temperature are excellent in term of the physical and chemical properties and leaching characteristics, indicating attractive potential as substitute of nature materials.

Rubidium-modified bioactive glass-ceramics with hydroxyapatite crystals for bone regeneration

In order to study the influence of rubidium(Rb)addition on the phase composition,microstructure,mechanical properties and cell response of bioactive glass-ceramics,CaO−SiO2−Na2O−B2O3−MgO−ZnO−P2O5 glass system was designed with and without addition of Rb.The results show that hydroxyapatite(HA)and Mg−whitelockite(Ca18Mg2H2(PO4)14)crystalline phases are formed in the glass matrix without Rb.After the addition of Rb,only HA phase is detected.The grain size of the crystals in the glass-ceramics is larger with the addition of Rb than that of samples without Rb.Rb addition can improve the bending strength of glass-ceramics.The cultivation of human bone marrow mesenchymal stem cells(hBMSCs)on Rb-containing glass-ceramics demonstrates enhanced cell adhesion,proliferation and ALP activity.In conclusion,Rb-modified glass-ceramics exhibit good mechanical property,excellent bioactivity and biocompatibility,which have potential for bone regeneration application.

Study of the material removal mechanism of glass-ceramics based on consecutive incremental loading in ductile-regime grinding

Glass-ceramics have many excellent properties and are widely used in various fields. During the grinding process,the workpiece surface is typically subject to material removal by grit of incremental heights, which has rarely been the focus of research. As such, it is necessary to study the material removal mechanism of glass-ceramics under consecutive incremental loading, which more closely reflects the actual grinding process. In this paper,to analyze the plastic deformation and residual stress of lithium aluminosilicate(LAS) glass-ceramics, a finite element model is established based on the Drucker–Prager yield criterion for ductile regimes. A nano-scratch test was also conducted and the test results show that both the residual depth and residual stress increase with an increase in the number of increments, and that consecutive incremental loading promotes the plastic deformation of glass-ceramics and increases the residual stress of the material in the ductile-regime process. These findings provide guidance for achieving higher dimensional accuracy in the actual grinding of glass-ceramics parts.

The Crystallization and Fracture Toughness of Transparent Glass-ceramics with Various Al_(2)O_(3) Additions for Mobile Devices

Li_(2)O-Al_(2)O_(3)-SiO_(2)(LAS)glass-ceramics were prepared by a melting method.Effects of different Al_(2)O_(3)content on the structure,crystallization,transmittance and fracture toughness of LAS glassceramics were investigated by means of XRD,FESEM and other methods as well.The results showed that the glass transition temperature and crystallization temperature of samples increased as the content of Al_(2)O_(3)increased from 4.1 wt%to 13.1 wt%,which restrained the precipitation of lithium disilicate crystals.The main crystalline phase of glass-ceramics transformed from lithium disilicate and petalite to silicon dioxide,which reduced the fracture toughness of glass-ceramics.When the Al_(2)O_(3)content was 7.1 wt%,the specimen had outstanding transmittance and fracture toughness.The transmittance was 90.32%.The fracture toughness was 1.13 MPa•m^(1/2).Compared with high-alumina glass,the fracture toughness of the glass-ceramic was greatly improved,and it could be used as a new type of protective material for mobile devices.

Fabrication and Characterization of Glass-Ceramics Doped with Rare Earth Oxide and Heavy Metal Oxide

Cordierite-based glass-ceramics with non-stoichiometric composition doped with rare earth oxide (REO_2) and heavy metal oxide (M_2O_3) respectively were fabricated from glass powders. After sintering and crystallization heat treatment, various physical properties, including compact density and apparent porosity, were examined to evaluate the sintering behavior of cordierite-based glass-ceramics. Results show that the additives both heavy metal oxide and rare earth oxide promote the sintering and lower the phase temperature from μ- to α-cordierite as well as affect the dielectric properties of sintered glass-ceramics. The complete-densification temperature for samples is as low as 900 ℃. The materials have a low dielectric constant (≈5), a low thermal expansion coefficient ((2.80～3.52)×10^(-6) ℃^(-1)) and a low dissipation factor (≤0.2%) and can be co-fired with high conductivity metals such as Au, Cu, Ag/Pd paste at low temperature (below 950 ℃), which makes it to be a promising material for low-temperature co-fired ceramic substrates.

Luminescence property of Eu-doped fluorochlorozirconate glass-ceramics

A series of Eu2＋-doped fluorochlorozirconate glass-ceramics were prepared by solid state reaction method. X-ray diffraction, pho- toluminescence, photo-stimulated luminescence （PSL） and the turbidity of fluorozirconate glass containing BaCl2 nano- and micro-crystals were measured for the samples annealed at 290℃ for 10 rain The PSL was attributed to the characteristic emission of Eu2＋ in nano-crystallites of BaCI2, which formed in the glass upon annealing. The PSL efficiency of the glass ceramic was increased by increasing the concentration of BaCl2, which, however, resulted in the decreasing in the transparency of the sample. The sample turned to a semi-transparent glass ceramic or even an opaque and milky white one from a near-transparent glass. The trade-off between optical transparency and PSL intensity over different concentrations of BaCl2 for X-ray imaging plate applications was briefly discussed.

Influence of Nucleation Agents Concentration on Crystallization Structure and Properties of Glass-ceramics

Deep color glass-ceramics is prepared by using gold tailings as the main raw material, and Cr2O3 is added as nucleation agent. Influence of different Cr2O3 additions on crystallization structure and properties of CaO-MgO-Al2O3-SiO2 glass-ceramics has been discussed so as to select optimum additions. DTA is employed to determine optimum crystallization and nucleation temperatures; XRD and SEM are used to characterize microstructure of each sample; and performance indexes, such as water absorption, bulk density, flexural strength and so on, are also determined. Experimental results show that when 3wt% Cr2O3 is introduced, fine glass-ceramics with diopside as the main crystal and Ca-Fe diopside as the second-crystal is obtained, and its corresponding performance indexes are as follows： water absorption 0.12%, bulk density 2.56 g/cm^3, and flexural strength 70.01 Mpa.

RESEARCH ON FACTORS AFFECTING THE COLOURATION OF RED GLASS-CERAMICS

In this pater, effect of alkali, zinc oxide and colorants such as cadmiun sulfide and selenium powder on the colouration of the red glass-ceramic materials in the CaO-Al2O3-SiO2 system has been studied. The relevant laws have been presented and analyzed.

Effects of Nucleating Additives on Crystallization and Properties of CaO-B_2O_3-SiO_2 Glass-ceramics

ZrO2, TiO2 and P2O5 were doped in CaO-B2O3-SiO2 glass-ceramics as nucleating additives. Effects of different nucleating additives on the phase separation and crystalline behaviors were investigated by using gradient temperature furnace, DTA and XRD. Then, sintering process of the glass-ceramics was investigated by testing sintering shrinkage, dielectric constant and loss. The experimental results shows that the glass-ceramics doped with nucleating additives represents higher crystallization, with ZrO2 as an exceptional effective dopant to promote the precipitation of wollastonite crystal. Finally, ZrO2 containing glass-ceramics was chosen to study the influence of sintering temperature and soaking time with the help of X-ray diffraction analysis and density measurement. The glass-ceramics can be well consolidated at 850 ℃ for 10 min, with low dielectric constant （5.87） and loss （3.21×10^-4）, which is desirable for LTCC application.

Preparation and crystallization action of SiO_2 -Al_2O_3 -CaO-ZnO-R_2O porous glass-ceramics

Using powder-sintering method,SiO2-Al2O3-CaO-ZnO-R2O porous glass-ceramics were produced for analysis. Five samples with different SiO2 /CaO ratios were used in the research. The mechanical properties, microstructures and textures of porous glass-ceramics are investigated by using differential thermogravimetric analysis/differential thermal analysis ( TGA/SDTA) ,X-ray diffraction ( XRD) ,and scanning electron microsco- py ( SEM) . The activity energy of crystallization ( E) and crystallization kinetics parameter ( k) were calculated based on the modified JMA equation. The Avrami parameter n was obtained according to Augis-Bennett function. The results show that the k value of No. 1 sample ( SiO2 /CaO = 61∶ 18) is the largest among all samples, which tends to crystallize more easily,and crystallization processes of all samples are observed bulk crystallization. The main crystal phase observed is parawollastonite ( clinorhombic system) with puncheon shape. Poreforming agents decomposed at 100 - 500 ℃ form a large number of closed pores with micron dimension and several semi-open pores distribute uniformly in the glass-ceramics matrix. This work may be expected to be favorable for industrial scale applications of porous glass-ceramics in the field of building thermal insulation.