The H6P2W18O62/TiO2composite catalyst was prepared by the combination of nonionic surfactant C18H37(OCH2CH2)10OH(Brij-76)as the template and the sol-gel method.As-synthesized composite was characterized by FT-TR,SEM,N...The H6P2W18O62/TiO2composite catalyst was prepared by the combination of nonionic surfactant C18H37(OCH2CH2)10OH(Brij-76)as the template and the sol-gel method.As-synthesized composite was characterized by FT-TR,SEM,N2 absorption-desorption and NH3-TPD.The results showed that the composite H6P2W18O62/TiO2 was mesoporous material(ca.3.3 nm),and large surface area(99.78 m2/g).Additionally,the aggregation of TiO2 particles was effectively inhibited,and the surface acidity was increased substantially.The photocatalytic elimination of monochlorobenzene was used as model reaction to evaluate the photocatalytic activity of the composite catalyst under visible light separately.Photocatalytic experimental results showed that the composite H6P2W18O62/TiO2 can effectively degradate monochlorobenzene.展开更多
利用水热合成法合成了分子组成为(C6H11NH3)5H(P2Mo5O23)4H2O的杂多化合物, 用单晶X-ray衍射方法测定了它的结构,该晶体属于单斜晶系,空间群P21/c, a = 12.830(3), b = 14.848(3), c = 25.258(5) ? b = 92.95(3), Mr = 1483.62, V = 48...利用水热合成法合成了分子组成为(C6H11NH3)5H(P2Mo5O23)4H2O的杂多化合物, 用单晶X-ray衍射方法测定了它的结构,该晶体属于单斜晶系,空间群P21/c, a = 12.830(3), b = 14.848(3), c = 25.258(5) ? b = 92.95(3), Mr = 1483.62, V = 4805.1(17) 3, Z = 4, Dc = 2.051 g/cm3, m = 1.431 mm-1, F(000) = 3000, I >2s(I) 的可观察衍射点4426个, 最终结构偏差因子R = 0.0464, wR = 0.0801, S = 0.731。在[P2Mo5O23]6-杂多阴离子中5个MoO6八面体通过共边和共角相连, 形成1个近似的五角平面骨架, 2个PO4四面体加在五角平面的两侧。热性质研究表明杂多阴离子骨架在547.4 ℃左右分解。展开更多
文摘The H6P2W18O62/TiO2composite catalyst was prepared by the combination of nonionic surfactant C18H37(OCH2CH2)10OH(Brij-76)as the template and the sol-gel method.As-synthesized composite was characterized by FT-TR,SEM,N2 absorption-desorption and NH3-TPD.The results showed that the composite H6P2W18O62/TiO2 was mesoporous material(ca.3.3 nm),and large surface area(99.78 m2/g).Additionally,the aggregation of TiO2 particles was effectively inhibited,and the surface acidity was increased substantially.The photocatalytic elimination of monochlorobenzene was used as model reaction to evaluate the photocatalytic activity of the composite catalyst under visible light separately.Photocatalytic experimental results showed that the composite H6P2W18O62/TiO2 can effectively degradate monochlorobenzene.
基金2013年国家级大学生创新创业训练计划项目(201313256001)湖北师范学院硕士研究生创新科研基金项目(1051320130216)+1 种基金National Undergraduate Training Programs for Innovation and Entrepreneurship(201313256001)Postgraduate Innovation Scientific Research Foundation of Hubei Normal University(1051320130216)