HNO 3 -pretreated CNTs were employed as supports, and a special ultrasound-assisted impregnation method was designed to prepare supported Cu-Co catalysts for higher-alcohol synthesis from syngas. The catalysts used in...HNO 3 -pretreated CNTs were employed as supports, and a special ultrasound-assisted impregnation method was designed to prepare supported Cu-Co catalysts for higher-alcohol synthesis from syngas. The catalysts used in this work were characterized by N 2 adsorption-desorption, TEM, XRD, H 2 -TPR, CO-TPD techniques. It was found that the pre-treatment procedure of CNTs remarkably promoted the catalytic properties of the Cu-Co/CNTs catalysts. For the Cu-Co catalyst supported on CNTs pre-treated by 68 wt% HNO 3 , some active components were introduced into the CNTs channels, their dispersions and the amount of strongly adsorbed CO-species were improved. The CO conversion and alcohol yield on the HNO 3 -pretreated Cu-Co/CNTs catalyst were increased by ～21% and ～69%, respectively, compared with those on the normal Cu-Co/CNTs catalyst.展开更多
在室温条件下,以不同浓度的HNO3溶液(质量分数分别为10,20,30 and 40%)为氧化介质处理沥青球,而后直接进行高温炭化处理,利用FT-IR、XPS、SEM和元素分析表征HNO3氧化沥青球及其炭化样的化学结构和表面形貌。结果表明:用30%HNO3氧化12h...在室温条件下,以不同浓度的HNO3溶液(质量分数分别为10,20,30 and 40%)为氧化介质处理沥青球,而后直接进行高温炭化处理,利用FT-IR、XPS、SEM和元素分析表征HNO3氧化沥青球及其炭化样的化学结构和表面形貌。结果表明:用30%HNO3氧化12h的沥青球在900℃高温炭化后能够保持良好的球形度和表面形貌;HNO3处理引入的-NO2官能团在400℃前转化为胺基,促进了沥青分子的交联,保证了沥青球炭化过程的顺利进行;当炭化温度为900℃时,胺基进一步发生了环化和芳构化反应,氮原子以吡啶氮和季氮形式存在。展开更多
基金supported by the Foundation of Shaanxi Educational Committee (2010JK608)the Research Foundation of XATU (204-000092)supported by the National Natural Science Foundation of China (205903603)
文摘HNO 3 -pretreated CNTs were employed as supports, and a special ultrasound-assisted impregnation method was designed to prepare supported Cu-Co catalysts for higher-alcohol synthesis from syngas. The catalysts used in this work were characterized by N 2 adsorption-desorption, TEM, XRD, H 2 -TPR, CO-TPD techniques. It was found that the pre-treatment procedure of CNTs remarkably promoted the catalytic properties of the Cu-Co/CNTs catalysts. For the Cu-Co catalyst supported on CNTs pre-treated by 68 wt% HNO 3 , some active components were introduced into the CNTs channels, their dispersions and the amount of strongly adsorbed CO-species were improved. The CO conversion and alcohol yield on the HNO 3 -pretreated Cu-Co/CNTs catalyst were increased by ～21% and ～69%, respectively, compared with those on the normal Cu-Co/CNTs catalyst.
基金Nature Science Foundation of China (50672025)Science and Technology Commission of Shanghai Municipality (065258033,06DZ22003)~~
文摘在室温条件下,以不同浓度的HNO3溶液(质量分数分别为10,20,30 and 40%)为氧化介质处理沥青球,而后直接进行高温炭化处理,利用FT-IR、XPS、SEM和元素分析表征HNO3氧化沥青球及其炭化样的化学结构和表面形貌。结果表明:用30%HNO3氧化12h的沥青球在900℃高温炭化后能够保持良好的球形度和表面形貌;HNO3处理引入的-NO2官能团在400℃前转化为胺基,促进了沥青分子的交联,保证了沥青球炭化过程的顺利进行;当炭化温度为900℃时,胺基进一步发生了环化和芳构化反应,氮原子以吡啶氮和季氮形式存在。