ZSM-5/MCM-41 composite molecular sieve was prepared by the nano-assembling method.The ZSM-5 molecular sieve,the MCM-41 molecular sieve,the ZSM-5/MCM-41 mechanical mixture and the ZSM-5/MCM-41 composite molecular sieve...ZSM-5/MCM-41 composite molecular sieve was prepared by the nano-assembling method.The ZSM-5 molecular sieve,the MCM-41 molecular sieve,the ZSM-5/MCM-41 mechanical mixture and the ZSM-5/MCM-41 composite molecular sieve were characterized by X-ray powder diffractometry,N_2 adsorption isotherms,temperature programmed desorption of ammonia and scanning electron microscopy and their properties were analyzed.Using FCC gasoline as the feed,activities of different molecular sieves for reducing olefin content were investigated in a continuous high-pressure micro-reactor unit under the following conditions:a reaction temperature of 400℃,a reaction time of 2 h,a weight hourly space velocity of 3h^(-1),and a reaction pressure of 2.0 MPa.The results showed that the HMCM-41 molecular sieve had low reaction performance,and the HZSM-5 molecular sieve demonstrated high aromatization activity,while the ZSM-5/MCM- 41 composite molecular sieve exhibited a best olefin-reducing performance because of its high isomerization activity and moderate aromatization activity.With a largest olefin-reducmg capability and a reasonable distribution of products,the composite molecular sieve was more suitable for FCC gasoline upgrading compared to other three catalysts.展开更多
In this study,various ZSM-5/MCM-41 micro/mesoporous zeolite composites have been prepared by alkalidesilication and surfactant-directed recrystallization of ZSM-5.The effects of particle size and Si/Al ratio of initia...In this study,various ZSM-5/MCM-41 micro/mesoporous zeolite composites have been prepared by alkalidesilication and surfactant-directed recrystallization of ZSM-5.The effects of particle size and Si/Al ratio of initial ZSM-5 zeolites on the structure and catalytic performance of ZSM-5/MCM-41 composites are studied.The results of XRD,TEM N_2-adsorption-desorption,NH_3-TPD and in situ FT-IR revealed that ordered hexagonal MCM-41 mesopores with 3-4 nm pore size were formed around ZSM-5 crystals,and the specific surface area and mesopore volume of composites increased with increasing the Si/Al ratio of initial ZSM-5.Catalytic cracking of n-dodecane(550℃,4 MPa) showed that the ZSM-5/MCM-41 composites obtained from the high Si/Al ratio and nano-sized initial ZSM-5 zeolites exhibited superior catalytic performance,with the improvement higher than 87%in the catalytic activities and 21%in the deactivation rate compared with untreated zeolites.This could be ascribed to their suitable pore structure,which enhanced the diffusion of reactant molecules in pores of catalysts.展开更多
文摘ZSM-5/MCM-41 composite molecular sieve was prepared by the nano-assembling method.The ZSM-5 molecular sieve,the MCM-41 molecular sieve,the ZSM-5/MCM-41 mechanical mixture and the ZSM-5/MCM-41 composite molecular sieve were characterized by X-ray powder diffractometry,N_2 adsorption isotherms,temperature programmed desorption of ammonia and scanning electron microscopy and their properties were analyzed.Using FCC gasoline as the feed,activities of different molecular sieves for reducing olefin content were investigated in a continuous high-pressure micro-reactor unit under the following conditions:a reaction temperature of 400℃,a reaction time of 2 h,a weight hourly space velocity of 3h^(-1),and a reaction pressure of 2.0 MPa.The results showed that the HMCM-41 molecular sieve had low reaction performance,and the HZSM-5 molecular sieve demonstrated high aromatization activity,while the ZSM-5/MCM- 41 composite molecular sieve exhibited a best olefin-reducing performance because of its high isomerization activity and moderate aromatization activity.With a largest olefin-reducmg capability and a reasonable distribution of products,the composite molecular sieve was more suitable for FCC gasoline upgrading compared to other three catalysts.
基金Supported by the National Natural Science Foundation of China(U123213421306132)the Doctoral Program of Higher Education(20120032120008)
文摘In this study,various ZSM-5/MCM-41 micro/mesoporous zeolite composites have been prepared by alkalidesilication and surfactant-directed recrystallization of ZSM-5.The effects of particle size and Si/Al ratio of initial ZSM-5 zeolites on the structure and catalytic performance of ZSM-5/MCM-41 composites are studied.The results of XRD,TEM N_2-adsorption-desorption,NH_3-TPD and in situ FT-IR revealed that ordered hexagonal MCM-41 mesopores with 3-4 nm pore size were formed around ZSM-5 crystals,and the specific surface area and mesopore volume of composites increased with increasing the Si/Al ratio of initial ZSM-5.Catalytic cracking of n-dodecane(550℃,4 MPa) showed that the ZSM-5/MCM-41 composites obtained from the high Si/Al ratio and nano-sized initial ZSM-5 zeolites exhibited superior catalytic performance,with the improvement higher than 87%in the catalytic activities and 21%in the deactivation rate compared with untreated zeolites.This could be ascribed to their suitable pore structure,which enhanced the diffusion of reactant molecules in pores of catalysts.