Improving corrosion resistance of additively manufactured WE43 magnesium alloy by high temperature oxidation for biodegradable applications

Laser powder bed fusion(L-PBF)has been employed to additively manufacture WE43 magnesium(Mg)alloy biodegradable implants,but WE43 L-PBF samples exhibit excessively rapid corrosion.In this work,dense WE43 L-PBF samples were built with the relativity density reaching 99.9%.High temperature oxidation was performed on the L-PBF samples in circulating air via various heating temperatures and holding durations.The oxidation and diffusion at the elevated temperature generated a gradient structure composed of an oxide layer at the surface,a transition layer in the middle and the matrix.The oxide layer consisted of rare earth(RE)oxides,and became dense and thick with increasing the holding duration.The matrix was composed ofα-Mg,RE oxides and Mg_(24)RE_(5) precipitates.The precipitates almost disappeared in the transition layer.Enhanced passivation effect was observed in the samples treated by a suitable high temperature oxidation.The original L-PBF samples lost 40%weight after 3-day immersion in Hank’s solution,and broke into fragments after 7-day immersion.The casted and solution treated samples lost roughly half of the weight after 28-day immersion.The high temperature oxidation samples,which were heated at 525℃ for 8 h,kept the structural integrity,and lost only 6.88%weight after 28-day immersion.The substantially improved corrosion resistance was contributed to the gradient structure at the surface.On one hand,the outmost dense layer of RE oxides isolated the corrosive medium;on the other hand,the transition layer considerably inhibited the corrosion owing to the lack of precipitates.Overall,high temperature oxidation provides an efficient,economic and safe approach to inhibit the corrosion of WE43 L-PBF samples,and has promising prospects for future clinical applications.

High Temperature Corrosion of Water Wall Materials T23 and T24 in Simulated Furnace Atmospheres

Candidate materials for water wall of supercritical and ultra-supercritical utility boilers,T23 and T24,were chosen as the experimental samples and exposed to oxidizing atmosphere,reducing atmosphere and oxidizing/reducing alternating atmosphere separately.The corrosion temperature was 450-550?C.The effects of oxygen con-tent and temperature on the corrosion in reducing atmosphere and alternating atmosphere were investigated.The scanning electron microscope(SEM) and energy dispersive spectrometer(EDS) were used to examine the corroded samples.The results show that the corrosion kinetics of T23 and T24 can be described by the double logarithmic equation and parabolic equation respectively.To describe the corrosion of materials accurately it is not sufficient to analyze the macro-mass gain and the macro-thickness of the corroded layer only,but the EDS should be applied to examine the migration depth of corrosive elements O and S.It is revealed that the corrosion becomes more severe when H2S is present in the corrosive gas.S is more active than O,and Cr can reduce the migration of oxygen but not S.The combination corrosion of S and O and pure [S] has a stronger corrodibility than pure H2S.T24 suffers the most severe corrosion at oxygen content of 0.8%.Corrosion is aggravated when the corrosion temperature is above 450 ℃ in the alternating atmosphere.T23 has better corrosion resistance than T24 and W contributes a lot to the corrosion resistance of T23.

Accelerated Corrosion of Pure Fe Induced by Gaseous ZnCl_2 at High Tempreratures

ZnCl2 is one of the dominant aggressive species in waste incinerators or other advanced combustion power generation systems. In this study, the influence of minor amount of gaseous ZnCl2 on the corrosion behavior of pure iron was examined at 600-800℃ in a pure oxygen environment. The corrosion rate usually increased markedly with increasing temperatures at a fixed ZnCl2 content or with increased ZnCl2 contents at a constant temperature. The corrosion products were composed of a thin outer layer of ZnFe2O4 spinel and an inner zone with a much thicker layer of Fe2O3, which exhibited a serious separation from the matrix. Moreover, a molten FeCl2 layer was observed at the scale substrate interface. The accelerated corrosion of pure iron was attributed to the existence of FeCl2 with low melting point on the metal surface, which destroyed the cohesion and adhesion of the oxide scale. The results are discussed in relation to the thermodynamic factors and the presence of volatile compounds in the reaction system.

Mechanical properties and damage constitutive model of sandstone after acid corrosion and high temperature treatments

Aiming at the problem of temperature-mechanics-chemical(T-M-C)action encountered by rocks in underground engineering,sandstone was selected as the sample for acid corrosion treatment at pH 1,3,5 and 7,the acid corrosion treated samples were then subjected to high-temperature experiments at 25,300,600,and 900℃,and triaxial compression experiments were conducted in the laboratory.The experimental results show that the superposition of chemical damage and thermal damage has a significant impact on the quality,wave velocity,porosity and compression failure characteristics of the rock.Based on the Lemaitre strain equivalent hypothesis theory,the damage degree of rock material was described by introducing damage variables,and the spatial mobilized plane(SMP)criterion was adopted.The damage constitutive model can well reflect the stress-strain characteristics of the rock triaxial compression process,which verified the rationality and reliability of the model parameters.The experiment and constitutive model analyzed the change law of mechanical properties of rock after chemical corrosion and high temperature thermal damage,which had certain practical significance for rock engineering construction.

CO_(2) High Temperature Corrosion and Its Prevention of Chromia Forming Fe-base Alloys

High temperature corrosion of chromia forming Fe-base alloys by CO_(2) produces not only oxidation but also carburisation.The corrosion kinetics in CO_(2)-rich gas is found to be increased compared with that in air or oxygen.As a result,higher alloy chromium levels are required to achieve protective chromia formation in CO_(2).Corrosion reaction mechanisms in CO_(2) are examined and the internal carburisation of alloys in low carbon activity CO_(2) gases are analysed based on the variation of pO_(2) at the interface of oxide and metal.Carbon penetration through chromia oxide scale has been revealed by atom probe tomography.The strategies to resist CO_(2) corrosion are reviewed by alloying of Si and/or Mn,forming additional diffusion barrier layers,and by adding sulphur to modify oxide grain boundaries to reduce carbon diffusion along the grain boundaries.

INFLUENCES OF SMALL AMOUNTS OF Y AND Ce ON HIGH TEMPERATURE CORROSION PROPERTIES OF M38 ALLOY

High temperature corrosion properties of M38 alloy with and without 0.04 wt-%Y and 0.05 wt-%Ce additions were studied in equilibrated S0_(2)+0_(2)gas mixtures at 850℃and 900℃.It was found that adding Y or Ce decreased the corrosion rate of M38 and changed considerably the surface morphologies and composition of corrosion products on M38.The effectiveness of Y and Ce were also discussed.

Investigation and Analysis of High Temperature Corrosion and Degradation of Marine Boiler Combustion Swirler

The present paper investigated and analyzed swirler material consisting of mild steel which was subjected to service for the period of one year in a 30 MW marine boiler. Due to the presence of high temperatures in the furnace coupled with the corrosive marine environment swirler material showed accelerated degradation and material wastage. An investigation into the feasibility of manufacturing the existing swirler with an alternate material or coating the swirler material with a thermal barrier coating was undertaken. Based on their properties and performance, SS 304 and SS 316 were proposed as the replacement materials for the swirler. The other alternative of coating the existing swirlers with a form thermal barrier coating to observe for any improvement in their performance at elevated temperatures was also tested. Stellite, which is a Ni-Co based coating, was carried out on the MS samples and the same were exposed to same temperatures mentioned above. The performance of the available options was evaluated with respect to the grain structure of the material, the hardness value of the materials and deterioration at elevated temperatures. Investigation showed the proposed materials/ coatings like SS 304, SS 316 and Stellite coating revealed that SS 316 is the material best suited for high temperature application.

IMPROVEMENT ON SUSCEPTIBILITY OF ULTAR-HIGH STRENGTH STEEL TO STRESS CORROSION CRACKING BY HIGH TEMPERATURE QUENCHING

The effect of quenching temperature on the stress corrosion cracking of 30Cr3SiNiMoV ultra-high strength steel in 3.5% NaCl aqueous solution has been studied.The threshold K_(ISCC) may continuously increase with the quenching temperature raised from 870 to 1200℃ . All of the fractures are intergranular.The analyses of the segregation along prior austenitic grain boundaries,grain size and other microstructural factors reveal that the inerease of K_(ISCC) is mainly due to the coarsening of prior austenitic grains.

Experimental study on the effect of H2S and SO2 on high temperature corrosion of 12Cr1MoV

Aiming at the high temperature corrosion in a coal-fired boiler,the effect of H2S and SO2 on the corrosion of 12 CrlMoV under the water wall condition has been investigated by experiments.The results indicate that H2 S can promote the corrosion significantly,and the coarse porous oxide film formed cannot stop the progress of corrosion.While SO2 presents little effect on the corrosion.The main composition of the surface of 12 CrlMoV corrosion products is Fe2 O3.With H2S in the atmosphere,the corrosion gradually develops into deeper layers by forming FeS,FeO and Fe2 O3 alternately.The corrosion rate is doubled for every 50℃ inerease in temperature at 400-500℃.

High temperature corrosion behavior of arc-sprayed aluminum coatings on steel

Aluminum coatings were sprayed on the substrate of steel Q235 by arc spraying. The test samples of Q235, Al coatings and Al coatings with seal coat were placed in box type electric resistance furnace at 400, 500,600, 650 ℃ when their oxidation behaviors were studied. And their oxidation kinetics curves were protracted. Microstructure, microhardness, bond strength and distribution of section elements were investigated by optical microscope(OM), Vickers microhardness instrument, electric tensile test machine and EPMA. Al coatings and Al coatings with seal coat can enhance the oxidation-resistance of substrate under 500 ℃. The latter has the best corrosion resistance. The coatings can't protect the substrate against oxidation above 600 ℃. After a long time corrosion there is enriched oxygen element at interface.

Microbiologically influenced corrosion resistance enhancement of coppercontaining high entropy alloy Fe_(x)Cu_(1−x)CoNiCrMn against Pseudomonas aeruginosa

To enhance the microbiologically influenced corrosion(MIC)resistance of FeCoNiCrMn high entropy alloy(HEAs),a series of Fe_(x)Cu_((1−x))CoNiCrMn(x=1,0.75,0.5,and 0.25)HEAs were prepared.Microstructural characteristics,corrosion behavior(morphology observation and electrochemical properties),and antimicrobial performance of Fe_(x)Cu_((1−x))CoNiCrMn HEAs were evaluated in a medium inoculated with typical corrosive microorganism Pseudomonas aeruginosa.The aim was to identify copper-containing FeCoNiCrMn HEAs that balance corrosion resistance and antimicrobial properties.Results revealed that all Fe_(x)Cu_((1−x))CoNiCrMn(x=1,0.75,0.5,and 0.25)HEAs exhibited an FCC(face centered cubic)phase,with significant grain refinement observed in Fe_(0.75)Cu_(0.25)CoNiCrMn HEA.Electrochemical tests indicated that Fe_(0.75)Cu_(0.25)CoNiCrMn HEA demonstrated lower corrosion current density(i_(corr))and pitting potential(E_(pit))compared to other Fe_(x)Cu_((1−x))CoNiCrMn HEAs in P.aeruginosa-inoculated medium,exhibiting superior resistance to MIC.Anti-microbial tests showed that after 14 d of immersion,Fe_(0.75)Cu_(0.25)CoNiCrMn achieved an antibacterial rate of 89.5%,effectively inhibiting the adhesion and biofilm formation of P.aeruginosa,thereby achieving resistance to MIC.

High-Temperature Corrosion of Protective Coatings for Boiler Tubes in Thermal Power Plants

High-temperature corrosion is a serious problem for the water-wall tubes of boilers used in thermal power plants. Oxidation, sulfidation and molten salt corrosion are main corrosion ways.Thereinto, the most severe corrosion occurs in molten salt corrosion environment. Materials rich in oxides formers, such as chromium and aluminum, are needed to resist corrosion in high-temperature and corrosive environment, but processability of such bulk alloys is very limited. High velocity electric arc spraying (HVAS) technology is adopted to produce coatings with high corrosion resistance. By comparison, NiCr (Ni-45Cr-4Ti) is recommended as a promising alloy coating for the water-wall tubes, which can even resist molten salt corrosion attack. In the study of corrosion mechanism, the modern material analysis methods, such as scanning electron microscopy (SEM), X-ray diffractometry (XRD) and energy dispersive spectrometry (EDS), are used. It is found that the corrosion resistances of NiCr and FeCrAI coatings are much better than that of 20g steel, that the NiCr coatings have the best anti-corrosion properties, and that the NiCr coatings have slightly lower pores than FeCrAI coatings.It is testified that corrosion resistance of coatings is mainly determined by chromium content, and the microstructure of a coating is as important as the chemical composition of the material. In addition, the fracture mechanisms of coatings in the cycle of heating and cooling are put forward. The difference of the thermal physical properties between coatings and base metals results in the thermal stress inside the coatings. Consequently, the coatings spall from the base metal.

Protective Effect of the Sputtered TiAlCrAg Coating on the High-Temperature Oxidation and Hot Corrosion Resistance of Ti-Al-Nb Alloy

The effect of a sputtered Ti-48AI-8Cr-2Ag (at. pct) coating on the oxidation resistance of the cast Ti-46.5AI-5Nb (at. pct) alloy was investigated in air at 1000-1100℃. Hot corrosion in molten 75 wt pct Na2SO4+25 wt pct K2SO4 was investigated at 900℃. The scale on the cast TiAINb tends to spall in air, while the scale on coating is very adherent. The sputtered Ti-48AI-8Cr-2Ag coating remarkably improved high temperature oxidation resistance of the cast Ti-46.5AI-5Nb alloy because of the formation of an adherent Al2O3 scale. Due to the inward diffusion of Cr, Kirkendall voids were found at the coating/substrate interface. TiAICrAg coating provided excellent hot corrosion resistance for TiAINb alloy in molten 75 wt pct Na2SO4+25 wt pct K2S04 at 900℃ due to the formation of a continuous Al_2O_3 scale.

Pitting corrosion and crevice corrosion behaviors of high nitrogen austenitic stainless steels

Pitting corrosion and crevice corrosion behaviors of high nitrogen austenitic stainless steels （HNSS） were investigated by electrochemical and immersion testing methods in chloride solution, respectively. The chemical constitution and composition in the depth of passive films formed on HNSS were analyzed by X-ray photoelectron spectrum （XPS）. HNSS has excellent pitting and crevice corrosion resistance compared to 316L stainless steel. With increasing the nitrogen content in steels, pitting potentials and critical pitting temperature （CPT） increase, and the maximum, average pit depths and average weight loss decrease. The CPT of HNSS is correlated with the alloying element content through the measure of alloying for resistance to corrosion （MARC）. The MARC can be expressed as an equation of CPT=2.55MARC-29. XPS results show that HNSS exhibiting excellent corrosion resistance is attributed to the enrichment of nitrogen on the surface of passive films, which forms ammonium ions increasing the local pH value and facilitating repassivation, and the synergistic effects of molybdenum and nitrogen.

Study of corrosion behavior of labeling medium on Fe-36%Ni cold-rolled strip used in LNG carriers in high-temperature and high-humidity environment

To fulfill the high-quality surface requirements of the Fe-36% Ni cold-rolled strip used in liquid natural gas carriers,corrosion tests were conducted on alloy surfaces using ink media with different composition in hightemperature and high-humidity conditions.The results show that the Cl^-content in ink is the main cause of surface corrosion of Fe-36%Ni alloy at 95%RH and 50℃ Cl^- penetrates the passivation film,causing pitting on the surface.This corrosive material primarily comprises elements Fe and O.After 120 h of high temperature and high humidity,pitting had occurred on the surface,which was characterized by irregularly distributed areas of bright red filamentous corrosion.With time,the corrosion gradually deepened and expanded to nearby areas.However,when the ink medium contained no Cl^-,no corrosion was found on the alloy surface.As such,during the production of Fe-36%Ni material and its application in LNG shipbuilding,care must be taken in the selection of the marker or medium that will come into contact with the strip surface to ensure that it contains no corrosive ions like Cl^-.

High-temperature corrosion-resistance performance of electro-thermal explosion spraying coating

As a new spraying technology used in the remanufacturing engineering, electro-thermal explosion spraying holds a lot of advantages. Electro-thermal explosion spraying coating aliquation phenomena are reduced and non-crystal, micro-crystal and millimicron-crystal and other microstructure are formed. The corrosion-resistance ability of electro-thermal explosion spraying coating in high temperature environment was surveyed respectively. SEM equipped with EDS was employed to analyze the microstructure of spraying coating before and after corrosion. The corrosion-resistance mechanism of the spraying coating was discussed.

Uniform corrosion behavior of FeCrAl alloys in borated and lithiated high temperature water

The uniform corrosion behavior of model FeCrAl alloys as well as commercial Zircaloy-4 as reference material were investigated in 360℃borated and lithiated water.The results reveal that FeCrAl alloys exhibited better corrosion resistance than Zircaloy-4.It is found that the oxide films formed on the FeCrAl alloys are composed of outer Fe_(3)O_(4)layer,inner layer consisting of compact spinel layer and porous spinel layer,and transition layer containing Al-Cr-rich oxides and matrix enriched with Fe°.The spinel oxides in the inner layer are FeFe_(2-x-y-z)Cr_(x)Al_(y)MozO_(4).The corrosion mechanism of FeCrAl alloys in high temperature water is discussed.

Effect of temperature on corrosion behavior of alloy 690 in high temperature hydrogenated water

The influence of temperature on the corrosion behavior of Alloy 690 is evaluated using potentiodynamic polarization curves, electrochemical impedance spectra （EIS）, scanning electron microscopy （SEM）, X- ray photoelectron spectroscopy （XPS） and transmission electron microscopy （TEM）. The corrosion rate of Alloy 690 reaches a local maximum at 250℃. The kinetic control step of the growth of oxide film changes from the diffusion process of aqueous-phase ions to the growth of Cr-rich barrier layer in the temperature range of 200-300 ℃. A modified double-layer model is proposed to describe the effect of temperature on the structure and composition of the oxide film.

Fabrication of high nitrogen austenitic stainless steels with excellent mechanical and pitting corrosion properties

A series of high nitrogen austenitic stainless steels were successfully developed with a pressurized electroslag remelting furnace. Nitride additives and deoxidizer were packed into the stainless steel pipes, and then the stainless steel pipes were welded on the surface of an electrode with low nitrogen content to prepare a compound electrode. Using Si3N4 as a nitrogen alloying source, the silicon contents in the ingots were prone to be out of the specification range, the electric current fluctuated greatly and the surface qualities of the ingots were poor. The surface qualities of the ingots were improved with FeCrN as a nitrogen alloying source. The sound and compact macrostructure ingot with the maximum nitrogen content of 1.21wt% can be obtained. The 18Cr18Mn2Mo0.9N high nitrogen austenitic stainless steel exhibits high strength and good ductility at room temperature. The steel shows typical ductile-brittle transition behavior and excellent pitting corrosion resistance properties.

Intergranular corrosion behavior of high nitrogen austenitic stainless steel

The intergranular corrosion （IGC） behavior of high nitrogen austenitic stainless steel （HNSS） sensitization treated at 650-950℃ was investigated by the double loop electrochemical potentiodynamic reactivation （DL-EPR） method. The effects of the electrolytes, scan rate, sensitizing temperature on the susceptibility to IGC of HNSS were examined. The results show that the addi-tion of NaCl is an effective way to improve the formation of the cracking of a passive film in chromium-depleted zones during the reactivation scan. Decreasing the scan rate exhibits an obvious effect on the breakdown of the passive film. A solution with 2 mol/L H2SO4＋1 mol/L NaCl＋0.01 mol/L KSCN is suitable to check the susceptibility to IGC of HNSS at a sensitizing temperature of 650-950℃ at a suitable scan rate of 1.667 mV/s. Chromium depletion of HNSS is attributed to the precipitation of Cr2N which results in the susceptibility to IGC. The synergistic effect of Mo and N is suggested to play an important role in stabilizing the passive film to prevent the attack of IGC.