A novel,facile method to prepare copolymers by virtue of the reinitiation of precursor containing isopropylthioxanthone(ITX) residues(ITXH) was reported.Using poly(maleic anhydride-co-vinyl acetate)(P(MAH-co-VAc)) wit...A novel,facile method to prepare copolymers by virtue of the reinitiation of precursor containing isopropylthioxanthone(ITX) residues(ITXH) was reported.Using poly(maleic anhydride-co-vinyl acetate)(P(MAH-co-VAc)) with incorporated ITX residues as a macroinitiator,polymerization of styrene was performed,and poly(maleic anhydride-co-vinyl acetate)-b-polystyrene(P(MAH-co-VAc)-b-PSt) was produced.Applying the resultant copolymer in a breath figure procedure,honeycomb structure films having pore size around 250...展开更多
Honeycomb composite films were prepared by breath figure method via a straightforward,one-step process by doping complex containing Eu or Sn into polystyrene-b-poly(acrylic acid) solution.Several key influencing facto...Honeycomb composite films were prepared by breath figure method via a straightforward,one-step process by doping complex containing Eu or Sn into polystyrene-b-poly(acrylic acid) solution.Several key influencing factors,such as the concentration of the block polymer solution,the relative humidity of the environment and the amount of complexes,were investigated to control micropore size and tune film surface properties.The characteristics of the composite films were studied by scanning electron microscopy(SEM),atomic force microscopy(AFM),X-ray diffraction(XRD),ultraviolet and emission spectra.Results indicate that composite films containing Eu have excellent optical performance,and micro-patterned bowl-like SnO_(2) microparticles could be fabricated from composite films containing Sn after being calcined at 600℃ for 5 h.This general approach for the fabrication of honeycomb composite films opens a convenient and effective route to the functional modification of honeycomb films and offers new prospects for the application in miniaturized sensors,micro-reactor and catalysis.展开更多
Double-layer honeycomb structure of 4-dodecylbenzenesulfonic acid(DBSA)-doped polyaniline(PANI) is fabricated in the humidity atmosphere by self-assembly method. The driving force of this procedure is capillary force(...Double-layer honeycomb structure of 4-dodecylbenzenesulfonic acid(DBSA)-doped polyaniline(PANI) is fabricated in the humidity atmosphere by self-assembly method. The driving force of this procedure is capillary force(self-assembly) and the water droplet plays the role as template.The morphology and electric property are studied by atomic force microscope and this honeycomb structure is proved to be electro-active. Additionally, the double layer′s formation mechanism is proposed in the systems while the density of organic solvents is higher than that of water.展开更多
基金supported by the programs for Changjiang Scholars & Innovative Research Team in Universities (PCSIRT,IRT0706)for Polymer Chemistry and Physics,Beijing Municipal Education Commission(BMEC, No.XK100100640)
文摘A novel,facile method to prepare copolymers by virtue of the reinitiation of precursor containing isopropylthioxanthone(ITX) residues(ITXH) was reported.Using poly(maleic anhydride-co-vinyl acetate)(P(MAH-co-VAc)) with incorporated ITX residues as a macroinitiator,polymerization of styrene was performed,and poly(maleic anhydride-co-vinyl acetate)-b-polystyrene(P(MAH-co-VAc)-b-PSt) was produced.Applying the resultant copolymer in a breath figure procedure,honeycomb structure films having pore size around 250...
基金financially supported by the National Natural Science Foundation of China (Nos.51403181, 51273172 and 21375116)。
文摘Honeycomb composite films were prepared by breath figure method via a straightforward,one-step process by doping complex containing Eu or Sn into polystyrene-b-poly(acrylic acid) solution.Several key influencing factors,such as the concentration of the block polymer solution,the relative humidity of the environment and the amount of complexes,were investigated to control micropore size and tune film surface properties.The characteristics of the composite films were studied by scanning electron microscopy(SEM),atomic force microscopy(AFM),X-ray diffraction(XRD),ultraviolet and emission spectra.Results indicate that composite films containing Eu have excellent optical performance,and micro-patterned bowl-like SnO_(2) microparticles could be fabricated from composite films containing Sn after being calcined at 600℃ for 5 h.This general approach for the fabrication of honeycomb composite films opens a convenient and effective route to the functional modification of honeycomb films and offers new prospects for the application in miniaturized sensors,micro-reactor and catalysis.
文摘Double-layer honeycomb structure of 4-dodecylbenzenesulfonic acid(DBSA)-doped polyaniline(PANI) is fabricated in the humidity atmosphere by self-assembly method. The driving force of this procedure is capillary force(self-assembly) and the water droplet plays the role as template.The morphology and electric property are studied by atomic force microscope and this honeycomb structure is proved to be electro-active. Additionally, the double layer′s formation mechanism is proposed in the systems while the density of organic solvents is higher than that of water.