At first, a series of finite element method (FEM) simulation tests were used to find the critical forming conditions of hot-galvanized sheet steel during the rectangular box drawing processing when constant blank ho...At first, a series of finite element method (FEM) simulation tests were used to find the critical forming conditions of hot-galvanized sheet steel during the rectangular box drawing processing when constant blank holder forces were applied. According the test results, the reasonable alteration scope of initial variable blank holder force (VBHF) was as 1.9-2.3 T. Then, based on the test productions of blank holder force, 12 typical VBHF curves were applied to perform the simulation tests by the simulation software of DYNAFORM. The simulation test results showed that VBHF had great effects on drawing formability of hot-galvanized sheet steel during the rectangular box drawing. However, the different VBHF curves were applied to control the whole drawing and it would get great different effects. At the same tine, the VBHF had great effects on the maximum thick thinning ratio, but had little effect on the maximum thick incrassation ratio. So, reasonable application of the VBHF would greatly decrease the fractures. When the VBHF profile is taken as curve L, the best effect of drawing formability could be obtained. When curve I is used, contrary effect could be gotten. The other types of curves would cause effects between above two types of VBHF curves. Finally, the actual tests were applied to check the validity of the FEM simulation tests. The results show that the FEM simulation tests are good ways for predicting and optimizing the VBHF.展开更多
A probe test method was employed to detect the friction condition of the interfaces between tools and blank. At the same time a self-developed measurement apparatus to realize the probe test method was also presented....A probe test method was employed to detect the friction condition of the interfaces between tools and blank. At the same time a self-developed measurement apparatus to realize the probe test method was also presented. Based on the analysis of force, a correlative friction model was also given. With the self-developed measurement apparatus,the effects of three kinds of lubricating oils which were in common use during the process of sheet steel drawing were studied. By probing the friction coefficient values of different lubricating oils during the drawing process of the hot-galvanized sheet steel (steel brand: ST07Zn), we can see that the friction caused by PK oil was the lowest, so the effect of PK oil was the best. Then PK oil was used as the base lubricating oil and some solid additive powers was added into it to make a new type lubrication (named as L oil).The result of test proved that the new lubricating oil had remarkable effect on the drawing process of hot-galvanized sheet steel.展开更多
A full-frequency instant core-loss equation built from the induction physical model of magnetic materials, where the iron loss, eddy loss, and hysteresis loss no longer have an integral term, and this new equation pro...A full-frequency instant core-loss equation built from the induction physical model of magnetic materials, where the iron loss, eddy loss, and hysteresis loss no longer have an integral term, and this new equation provides high simulation accuracy and performs dynamic core loss analysis on non-sinusoidal or pulse magnetic fields. The simulation examples use a high-grade electrical steel sheet 65CS400 by Epstein experimental data covering magnetic field 0.1 - 1.8 T and frequency 50 - 5000 Hz, and the average error of the simulated core loss is less than 4%. Since the simulation is converged by magnetic physical parameters, so the physical relevance of the similar laminated materials can be compared with the coefficient results. .展开更多
Powdering/exfoliating of coatings and scratching galvanized steels and high strength steels (HSS), are the main forms of surface damage in the forming of which result in increased die maintenance cost and scrap rate...Powdering/exfoliating of coatings and scratching galvanized steels and high strength steels (HSS), are the main forms of surface damage in the forming of which result in increased die maintenance cost and scrap rate. In this study, a special rectangular box was developed to investigate the behavior and characteristics of surface damage in sheet metal forming (SMF) processes. U-channel forming tests were conducted to study the effect of tool hardness on surface damage in the forming of high strength steels and galvanized steels (hot-dip galvanized and galvannealed steels). Experimental results indicate that sheet deformation mode influences the severity of surface damage in SMF and surface damage occurs easily at the regions where sheet specimen deforms under the action of compressive stress. Die corner is the position where surface damage initiates. For HSS sheet, surface damage is of major interest due to high forming pressure. The HSS and hot-dip galvanized steels show improved ability of damage-resistance with increased hardness of the forming tool. However, for galvannealed steel it is not the forming tool with the highest hardness value that performs best.展开更多
The microstructural characteristics and formability at the edges of low carbon pickled steel sheets have been investigated based on the generation of earing and cracking defects while drawing. The microstructure of th...The microstructural characteristics and formability at the edges of low carbon pickled steel sheets have been investigated based on the generation of earing and cracking defects while drawing. The microstructure of the edge features coarse grains and mixed sized grains. The strength of the sheet edge is slightly lower than that at the center. Besides, the formability is obviously worsened. The plastic strain ratios along the longitudinal and transverse orientations are 0.31 and 0.6, respectively, with distinct anisotropy. The plastic strain ratio at the edge is obviously lower than that at the middle of the steel sheet. The observed microstructural characteristics and mechanical properties at the edge of the steel sheet can be attributed to the lower rolling temperature in the two-phase region of pro-eutectoid ferrite and austenite. These differences in microstructure and mechanical properties at the edge of the steel sheet lead to the generation of earing and cracking defects while drawing. The microstructure and mechanical properties at the edge of low carbon pickled steel sheets can be improved via the optimization of the rolling process and the adjustment of chemical composition.展开更多
The use of ultra-high strength steels through sheet metal forming process offers a practical solution to the lightweight design of vehicles.However,sheet metal forming process not only produces desirable changes in ma...The use of ultra-high strength steels through sheet metal forming process offers a practical solution to the lightweight design of vehicles.However,sheet metal forming process not only produces desirable changes in material properties but also causes material damage that may adversely influence the service performance of the material formed.Thus,an investigation is conducted to experimentally quantify such influence for a commonly used steel(the 22MnB5 steel) based on the hot and cold forming processes.For each process,a number of samples are used to conduct a uniaxial tensile test to simulate the forming process.After that,some of the samples are trimmed into a standard shape and then uniaxially extended until fracture to simulate the service stage.Finally,a microstructure test is conducted to analyze the microdefects of the remaining samples.Based on the results of the first two tests,the effect of material damage on the service performance of 22MnB5 steel is analyzed.It is found that the material damages of both the hot and cold forming processes cause reductions in the service performance,such as the failure strain,the ultimate stress,the capacity of energy absorption and the ratio of residual strain.The reductions are generally lower and non-linear in the former process but higher and linear in the latter process.Additionally,it is found from the microstructure analysis that the difference in the reductions of the service performance of 22MnB5 by the two forming processes is driven by the difference in the micro damage mechanisms of the two processes.The findings of this research provide a useful reference in terms of the selection of sheet metal forming processes and the determination of forming parameters for 22MnB5.展开更多
The process properties and interface behavior of CO_2 laser brazing with automatic wire feed for galvanized steel sheets were investigated, in which the brazing filler metal was CuSi3 and no flux was used. As to the a...The process properties and interface behavior of CO_2 laser brazing with automatic wire feed for galvanized steel sheets were investigated, in which the brazing filler metal was CuSi3 and no flux was used. As to the appearance quality of the brazing seams, the roles of the processing parameters, such as brazing speed, wire feeding rate, inclination and feeding direction of the wire, laser power, spot diameter and heating position, were assessed. The further investigation indicates that the behavior of the active elements Si, Mn and Zn are significantly influenced by energy input. At the interface, the microstructure of the base metal was composed of columnar crystals and the acicular α solid solution was found on the filler metal side.展开更多
Over the past several decades, the texture, properties and manufacture of quality silicon steels have been investigated for application in magnetic devices requiring magnetically soft materials, such as transformers, ...Over the past several decades, the texture, properties and manufacture of quality silicon steels have been investigated for application in magnetic devices requiring magnetically soft materials, such as transformers, inductive devices, etc. Most recently, the factors effecting the texture and magnetic properties, e.g. impurities, rolling process and annealing process, have been greatly studied. The benefits of this study are that low core loss silicon steels with stable high-performance can be obtained through an economic production process. This review is intended to summarize the recent developments in the texture, properties, manufacture and application of oriented silicon steel sheets.展开更多
Samples of the cross section microstructures of galvannealed steel sheets that lack alloying were analyzed. X-ray diffraction (XRD) tests were carried out. The study discovers that the deficit of alloying was higher...Samples of the cross section microstructures of galvannealed steel sheets that lack alloying were analyzed. X-ray diffraction (XRD) tests were carried out. The study discovers that the deficit of alloying was higher on both sides of the steel sheet when compared to the center and the thickness of the coating on the sides was also higher than the center. The results of the XRD tests demonstrate that the microstructure of the coating with a lack of alloy is mainly composed of zinc,ζ and δ. They also indicate that the lack of alloying is mainly due to a lower galvannealing temperature and thicker coating. It is shown by the optical micrographs of coating that the δ phase forms first in a discontinuous manner at the interface and then rapidly pushes towards the coating and enlarges.展开更多
In order to simplify production process and to decrease production cost of thicker cold-rolled iF steel sheets for deep drawing applications, a new hot-rolled IF steel sheet is developed through hot-rolling in or regi...In order to simplify production process and to decrease production cost of thicker cold-rolled iF steel sheets for deep drawing applications, a new hot-rolled IF steel sheet is developed through hot-rolling in or region. In this paper, properties, microstructures and precipitate morphology of hot-rolled iF steel sheets are described..展开更多
Four kinds of galvanized steel sheets having different surface roughness values were used to prepare the steel sheets with a self-lubricated coating. The effects of surface roughness on the surface lubrication perform...Four kinds of galvanized steel sheets having different surface roughness values were used to prepare the steel sheets with a self-lubricated coating. The effects of surface roughness on the surface lubrication performance of the steel sheets were examined using a friction coefficient tester. Results revealed large dynamic friction coefficients for the galvanized steel sheets, which increased remarkably with surface roughness. Once the self-lubricated coating was applied, significant drops in the dynamic friction coefficients were measured. After the first stage of the friction test,the coefficients were almost unchanged, which reflected a weak dependence on the surface roughness of the self-lubricated steel sheets. However, the dynamic friction coefficients gradually increased as the test progressed, where these increase clearly correlated with the surface roughness of the self-lubricated steel sheets.展开更多
Zn-Mg alloy coatings were obtained by physical vapor deposition (PVD) on electroplated steel sheets. Study on the formation of intermetallic phases in the coatings was conducted through the use of X-ray diffraction ...Zn-Mg alloy coatings were obtained by physical vapor deposition (PVD) on electroplated steel sheets. Study on the formation of intermetallic phases in the coatings was conducted through the use of X-ray diffraction (XRD) ,scanning electron microscope (SEM) and glow discharge optical emission spectrometry (GDOES). It is found that MgZn2 is the main Zn-Mg alloy phase formed after heat treatment. The formation of Mg-Zn intermetallic phases is controlled not only by thermodynamics, but also by kinetics. MgZn2 has different morphologies, such as laminar structure,porous structure and floc-like structure,which are mainly determined by the annealing temperature. Obvious diffusion of Mg starts at 350 ℃, and the diffusion of iron increases significantly when the temperature is elevated to 380℃.展开更多
A siliconizing process to manufacture 6.5% Si steel sheet has been developed. Electric components, such as transformers and reactors are made easily from 6.5% Si steel sheet. However, improved workability is desirable...A siliconizing process to manufacture 6.5% Si steel sheet has been developed. Electric components, such as transformers and reactors are made easily from 6.5% Si steel sheet. However, improved workability is desirable to increase the applications. Therefore the improvement of workability of 6.5% Si steel sheet was investigated, and the results were obtained as follows: (a) workability of 6.5% Si steel sheet is deteriorated by grain boundary oxidization, (b) grain boundary oxidization can be restrained by the addition of C. Workability and magnetic properties of 6.5% Si steel sheet with C addition are discussed. Furthermore, it was found that the workability of high Si steel sheet was improved remarkably by varying the Si content gradient along the thickness without deterioration of high frequency magnetic properties. This newly developed magnetic gradient high Si steel sheet is also discussed.展开更多
Commercial grain oriented silicon steel was cold rolled to thickness from 0.06 to 0.10 mm by cross shear rolling, then annealed in vacuum or a hydrogen atmosphere furnace. Deformation textures of the sheets were resea...Commercial grain oriented silicon steel was cold rolled to thickness from 0.06 to 0.10 mm by cross shear rolling, then annealed in vacuum or a hydrogen atmosphere furnace. Deformation textures of the sheets were researched by ODF method and reverse pole figure quantitative analyses. The results indicate that: in the condition of the cross shear rolling, the deformation texture of rolled sheet is generally similar to that of conventional rolled sheet, however, the texture distribution through the thickness is asymmetrical. With mismatch speed ratio increasing, the amount of Goss texture increases. With reduction ratio increasing, the intensity of γ-fiber becomes strong.展开更多
U-channel forming tests were performed to investigate the surface topography evolvement of hot-dip galvanized(GI) and galvannealed(GA) steels and the effects of die hardness on sheet metal forming(SMF). Experimental r...U-channel forming tests were performed to investigate the surface topography evolvement of hot-dip galvanized(GI) and galvannealed(GA) steels and the effects of die hardness on sheet metal forming(SMF). Experimental results indicate that the surface roughness values of the two galvanized steels increase with the number of forming,i.e.,the surface topographies of galvanized steels are roughened in SMF. Moreover,GI steel has a better ability of damage-resistance than GA steel. The mechanisms of topography evolvement are different in the forming of GI and GA steels. Scratch is the main form of surface damage in the forming of GI steels. The severity of scratch can be decreased by increasing die hardness. GA steel results in exfoliating of the coating firstly and then severe scratching. The surface topography of galvannealed steels can be improved by increasing die hardness. However,the hardness should not be too high.展开更多
Al coated steel sheets with excellent heat resistance,thermal reflection,and corrosion resistance are widely used in various applications.The laser weldability of the Al coated steel sheet for full penetration welding...Al coated steel sheets with excellent heat resistance,thermal reflection,and corrosion resistance are widely used in various applications.The laser weldability of the Al coated steel sheet for full penetration welding was reported.The phenomenon caused by intermixed aluminum and behavior of aluminum in the weld were investigated.Al coated steel sheets that have various thickness and coating mass were prepared for laser welding.The effects of parameters such as welding conditions and Al coating conditions were investigated.Al content mixed in the weld after laser welding was evaluated,and then a correlation between the mixed Al and mechanical properties was investigated.The results show that the Al-rich zones which have Fe-Al intermetallic compounds are found in the weld.The intermetallic compounds cause the decreased strength of the weld.展开更多
文摘At first, a series of finite element method (FEM) simulation tests were used to find the critical forming conditions of hot-galvanized sheet steel during the rectangular box drawing processing when constant blank holder forces were applied. According the test results, the reasonable alteration scope of initial variable blank holder force (VBHF) was as 1.9-2.3 T. Then, based on the test productions of blank holder force, 12 typical VBHF curves were applied to perform the simulation tests by the simulation software of DYNAFORM. The simulation test results showed that VBHF had great effects on drawing formability of hot-galvanized sheet steel during the rectangular box drawing. However, the different VBHF curves were applied to control the whole drawing and it would get great different effects. At the same tine, the VBHF had great effects on the maximum thick thinning ratio, but had little effect on the maximum thick incrassation ratio. So, reasonable application of the VBHF would greatly decrease the fractures. When the VBHF profile is taken as curve L, the best effect of drawing formability could be obtained. When curve I is used, contrary effect could be gotten. The other types of curves would cause effects between above two types of VBHF curves. Finally, the actual tests were applied to check the validity of the FEM simulation tests. The results show that the FEM simulation tests are good ways for predicting and optimizing the VBHF.
文摘A probe test method was employed to detect the friction condition of the interfaces between tools and blank. At the same time a self-developed measurement apparatus to realize the probe test method was also presented. Based on the analysis of force, a correlative friction model was also given. With the self-developed measurement apparatus,the effects of three kinds of lubricating oils which were in common use during the process of sheet steel drawing were studied. By probing the friction coefficient values of different lubricating oils during the drawing process of the hot-galvanized sheet steel (steel brand: ST07Zn), we can see that the friction caused by PK oil was the lowest, so the effect of PK oil was the best. Then PK oil was used as the base lubricating oil and some solid additive powers was added into it to make a new type lubrication (named as L oil).The result of test proved that the new lubricating oil had remarkable effect on the drawing process of hot-galvanized sheet steel.
文摘A full-frequency instant core-loss equation built from the induction physical model of magnetic materials, where the iron loss, eddy loss, and hysteresis loss no longer have an integral term, and this new equation provides high simulation accuracy and performs dynamic core loss analysis on non-sinusoidal or pulse magnetic fields. The simulation examples use a high-grade electrical steel sheet 65CS400 by Epstein experimental data covering magnetic field 0.1 - 1.8 T and frequency 50 - 5000 Hz, and the average error of the simulated core loss is less than 4%. Since the simulation is converged by magnetic physical parameters, so the physical relevance of the similar laminated materials can be compared with the coefficient results. .
基金supported by the National Natural Science Foundation of China under grant No. 50605043
文摘Powdering/exfoliating of coatings and scratching galvanized steels and high strength steels (HSS), are the main forms of surface damage in the forming of which result in increased die maintenance cost and scrap rate. In this study, a special rectangular box was developed to investigate the behavior and characteristics of surface damage in sheet metal forming (SMF) processes. U-channel forming tests were conducted to study the effect of tool hardness on surface damage in the forming of high strength steels and galvanized steels (hot-dip galvanized and galvannealed steels). Experimental results indicate that sheet deformation mode influences the severity of surface damage in SMF and surface damage occurs easily at the regions where sheet specimen deforms under the action of compressive stress. Die corner is the position where surface damage initiates. For HSS sheet, surface damage is of major interest due to high forming pressure. The HSS and hot-dip galvanized steels show improved ability of damage-resistance with increased hardness of the forming tool. However, for galvannealed steel it is not the forming tool with the highest hardness value that performs best.
文摘The microstructural characteristics and formability at the edges of low carbon pickled steel sheets have been investigated based on the generation of earing and cracking defects while drawing. The microstructure of the edge features coarse grains and mixed sized grains. The strength of the sheet edge is slightly lower than that at the center. Besides, the formability is obviously worsened. The plastic strain ratios along the longitudinal and transverse orientations are 0.31 and 0.6, respectively, with distinct anisotropy. The plastic strain ratio at the edge is obviously lower than that at the middle of the steel sheet. The observed microstructural characteristics and mechanical properties at the edge of the steel sheet can be attributed to the lower rolling temperature in the two-phase region of pro-eutectoid ferrite and austenite. These differences in microstructure and mechanical properties at the edge of the steel sheet lead to the generation of earing and cracking defects while drawing. The microstructure and mechanical properties at the edge of low carbon pickled steel sheets can be improved via the optimization of the rolling process and the adjustment of chemical composition.
基金Supported by National Natural Science Foundation of China(Grant No.51375201)CSAE(Beijing)Automotive Lightweight Technology Research Institute Development Fund Project of China
文摘The use of ultra-high strength steels through sheet metal forming process offers a practical solution to the lightweight design of vehicles.However,sheet metal forming process not only produces desirable changes in material properties but also causes material damage that may adversely influence the service performance of the material formed.Thus,an investigation is conducted to experimentally quantify such influence for a commonly used steel(the 22MnB5 steel) based on the hot and cold forming processes.For each process,a number of samples are used to conduct a uniaxial tensile test to simulate the forming process.After that,some of the samples are trimmed into a standard shape and then uniaxially extended until fracture to simulate the service stage.Finally,a microstructure test is conducted to analyze the microdefects of the remaining samples.Based on the results of the first two tests,the effect of material damage on the service performance of 22MnB5 steel is analyzed.It is found that the material damages of both the hot and cold forming processes cause reductions in the service performance,such as the failure strain,the ultimate stress,the capacity of energy absorption and the ratio of residual strain.The reductions are generally lower and non-linear in the former process but higher and linear in the latter process.Additionally,it is found from the microstructure analysis that the difference in the reductions of the service performance of 22MnB5 by the two forming processes is driven by the difference in the micro damage mechanisms of the two processes.The findings of this research provide a useful reference in terms of the selection of sheet metal forming processes and the determination of forming parameters for 22MnB5.
文摘The process properties and interface behavior of CO_2 laser brazing with automatic wire feed for galvanized steel sheets were investigated, in which the brazing filler metal was CuSi3 and no flux was used. As to the appearance quality of the brazing seams, the roles of the processing parameters, such as brazing speed, wire feeding rate, inclination and feeding direction of the wire, laser power, spot diameter and heating position, were assessed. The further investigation indicates that the behavior of the active elements Si, Mn and Zn are significantly influenced by energy input. At the interface, the microstructure of the base metal was composed of columnar crystals and the acicular α solid solution was found on the filler metal side.
文摘Over the past several decades, the texture, properties and manufacture of quality silicon steels have been investigated for application in magnetic devices requiring magnetically soft materials, such as transformers, inductive devices, etc. Most recently, the factors effecting the texture and magnetic properties, e.g. impurities, rolling process and annealing process, have been greatly studied. The benefits of this study are that low core loss silicon steels with stable high-performance can be obtained through an economic production process. This review is intended to summarize the recent developments in the texture, properties, manufacture and application of oriented silicon steel sheets.
文摘Samples of the cross section microstructures of galvannealed steel sheets that lack alloying were analyzed. X-ray diffraction (XRD) tests were carried out. The study discovers that the deficit of alloying was higher on both sides of the steel sheet when compared to the center and the thickness of the coating on the sides was also higher than the center. The results of the XRD tests demonstrate that the microstructure of the coating with a lack of alloy is mainly composed of zinc,ζ and δ. They also indicate that the lack of alloying is mainly due to a lower galvannealing temperature and thicker coating. It is shown by the optical micrographs of coating that the δ phase forms first in a discontinuous manner at the interface and then rapidly pushes towards the coating and enlarges.
基金The auLhors thank for the financial aid from Scienceamend of Shandong Province (No. Q98F05146)
文摘In order to simplify production process and to decrease production cost of thicker cold-rolled iF steel sheets for deep drawing applications, a new hot-rolled IF steel sheet is developed through hot-rolling in or region. In this paper, properties, microstructures and precipitate morphology of hot-rolled iF steel sheets are described..
文摘Four kinds of galvanized steel sheets having different surface roughness values were used to prepare the steel sheets with a self-lubricated coating. The effects of surface roughness on the surface lubrication performance of the steel sheets were examined using a friction coefficient tester. Results revealed large dynamic friction coefficients for the galvanized steel sheets, which increased remarkably with surface roughness. Once the self-lubricated coating was applied, significant drops in the dynamic friction coefficients were measured. After the first stage of the friction test,the coefficients were almost unchanged, which reflected a weak dependence on the surface roughness of the self-lubricated steel sheets. However, the dynamic friction coefficients gradually increased as the test progressed, where these increase clearly correlated with the surface roughness of the self-lubricated steel sheets.
文摘Zn-Mg alloy coatings were obtained by physical vapor deposition (PVD) on electroplated steel sheets. Study on the formation of intermetallic phases in the coatings was conducted through the use of X-ray diffraction (XRD) ,scanning electron microscope (SEM) and glow discharge optical emission spectrometry (GDOES). It is found that MgZn2 is the main Zn-Mg alloy phase formed after heat treatment. The formation of Mg-Zn intermetallic phases is controlled not only by thermodynamics, but also by kinetics. MgZn2 has different morphologies, such as laminar structure,porous structure and floc-like structure,which are mainly determined by the annealing temperature. Obvious diffusion of Mg starts at 350 ℃, and the diffusion of iron increases significantly when the temperature is elevated to 380℃.
文摘A siliconizing process to manufacture 6.5% Si steel sheet has been developed. Electric components, such as transformers and reactors are made easily from 6.5% Si steel sheet. However, improved workability is desirable to increase the applications. Therefore the improvement of workability of 6.5% Si steel sheet was investigated, and the results were obtained as follows: (a) workability of 6.5% Si steel sheet is deteriorated by grain boundary oxidization, (b) grain boundary oxidization can be restrained by the addition of C. Workability and magnetic properties of 6.5% Si steel sheet with C addition are discussed. Furthermore, it was found that the workability of high Si steel sheet was improved remarkably by varying the Si content gradient along the thickness without deterioration of high frequency magnetic properties. This newly developed magnetic gradient high Si steel sheet is also discussed.
基金National Natural Science Foundation of China!(No. 59671037).
文摘Commercial grain oriented silicon steel was cold rolled to thickness from 0.06 to 0.10 mm by cross shear rolling, then annealed in vacuum or a hydrogen atmosphere furnace. Deformation textures of the sheets were researched by ODF method and reverse pole figure quantitative analyses. The results indicate that: in the condition of the cross shear rolling, the deformation texture of rolled sheet is generally similar to that of conventional rolled sheet, however, the texture distribution through the thickness is asymmetrical. With mismatch speed ratio increasing, the amount of Goss texture increases. With reduction ratio increasing, the intensity of γ-fiber becomes strong.
基金Project(50605043) supported by the National Natural Science Foundation of China
文摘U-channel forming tests were performed to investigate the surface topography evolvement of hot-dip galvanized(GI) and galvannealed(GA) steels and the effects of die hardness on sheet metal forming(SMF). Experimental results indicate that the surface roughness values of the two galvanized steels increase with the number of forming,i.e.,the surface topographies of galvanized steels are roughened in SMF. Moreover,GI steel has a better ability of damage-resistance than GA steel. The mechanisms of topography evolvement are different in the forming of GI and GA steels. Scratch is the main form of surface damage in the forming of GI steels. The severity of scratch can be decreased by increasing die hardness. GA steel results in exfoliating of the coating firstly and then severe scratching. The surface topography of galvannealed steels can be improved by increasing die hardness. However,the hardness should not be too high.
文摘Al coated steel sheets with excellent heat resistance,thermal reflection,and corrosion resistance are widely used in various applications.The laser weldability of the Al coated steel sheet for full penetration welding was reported.The phenomenon caused by intermixed aluminum and behavior of aluminum in the weld were investigated.Al coated steel sheets that have various thickness and coating mass were prepared for laser welding.The effects of parameters such as welding conditions and Al coating conditions were investigated.Al content mixed in the weld after laser welding was evaluated,and then a correlation between the mixed Al and mechanical properties was investigated.The results show that the Al-rich zones which have Fe-Al intermetallic compounds are found in the weld.The intermetallic compounds cause the decreased strength of the weld.