Effect of Reactivity of Quick Lime on the Properties of Hydrated Lime Sorbent for SO_2 Removal

The hydration of quick lime and the sulfation of hydrated lime were carried out for verification of relationship between the reactivity of quick lime and the properties of hydrated lime as a sorbent. The effect of reactivity of quick lime was investigated with the change of calcination temperature and time. Results obtained showed that the temperature rise during the hydration of quick limes varied from 31 to 69℃ with the variation of calcination temperature and time. The specific surface area and the sulfation ability of hydrated lime prepared by hydration of quick lime showed a proportional relationship with the reactivity of quick lime. The hydrated lime which was prepared by hydration of quick lime calcined at 1100℃ had the highest reactivity and showed 41.53 m^2/g of the specific surface area, 0.16 cm^3/g of the pore volume and 87% of the removal efficiency for SO2 removal,

Effect of Some Admixtures on the Hydration of Silica Fume and Hydrated Lime

The effects of sodium salt of naphthalene formaldehyde sulfonic acid and stearic acid on the hydration of silica fume and Ca(OH)2 have been investigated. The hydration was carried out at 60℃ and W/S ratio of 4 for various time intervals namely, 1, 3, 7 and 28 days and in the presence of 0, 2% and 5% superplasticizer and stearic acid. The results of the hydration kinetics show that both admixtures accelerate the hydration reaction of silica fume and calcium hydroxide during the first 7 days. Whereas, after 28 days hydration there is no significant effect. Generally, most of free calcium hydroxide seems to be consumed after 28 days. In addition, the phase composition as well as the microstructure of the formed hydrates was examined by using X-ray diffraction analysis (XRD) and scanning electron microscopy (SEM) respectively.

Biopolymer stabilization of clayey soil

This study investigates the efficacy of sodium alginate(SA),xanthan gum(XG),guar gum(GG)and chitosan(CS)d each applied at five different solid biopolymer-to-water mass ratios(or dosages)and cured for 7 d and 28 d d on the unconfined compressive strength(UCS)performance of a high plasticity clayey soil.Moreover,on identifying the optimum biopolymer-treatment scenarios,their performance was compared against conventional stabilization using hydrated lime.For a given curing time,the UCS for all biopolymers followed a riseefall trend with increasing biopolymer dosage,peaking at an optimum dosage and then subsequently decreasing,such that all biopolymer-stabilized samples mobilized higher UCS values compared to the unamended soil.The optimum dosage was found to be 1.5%for SA,XG and CS,while a notably lower dosage of 0.5%was deemed optimum for GG.Similarly,for a given biopolymer type and dosage,increasing the curing time from 7 d to 28 d further enhanced the UCS,with the achieved improvements being generally more pronounced for XG-and CS-treated cases.None of the investigated biopolymers was able to produce UCS improvements equivalent to those obtained by the 28-d soilelime samples;however,the optimum XG,GG and CS dosages,particularly after 28 d of curing,were easily able to replicate 7-d lime stabilization outcomes achieved with as high as twice the soil’s lime demand.Finally,the fundamental principles of clay chemistry,in conjunction with the soil mechanics framework,were employed to identify and discuss the clayebiopolymer stabilization mechanisms.

Effects of lime treatment on the microstructure and hydraulic conductivity of Héricourt clay

This study aims at evidencing the effects of lime treatment on the microstructure and hydraulic conductivityof a compacted expansive clay, with emphasis put on the effect of lime hydration and modification.For this purpose, evolutions of hydraulic conductivity were investigated for both lime-treatedand untreated soil specimens over 7 d after full saturation of the specimens and their microstructureswere observed at the end. Note that for the treated specimen, dry clay powder was mixed with quicklimeprior to compaction in order to study the effect of lime hydration. It is observed that lime hydration andmodification did not affect the intra-aggregate pores but increased the inter-aggregates pores size. Thisincrease gave rise to an increase of hydraulic conductivity. More precisely, the hydraulic conductivity oflime-treated specimen increased progressively during the first 3 d of modification phase and stabilisedduring the next 4 d which correspond to a short period prior to the stabilisation phase. The microstructureobservation showed that stabilisation reactions took place after 7 d. Under the effect of stabilisation,a decreasing hydraulic conductivity can be expected in longer time due to the formation ofcementitious compounds. 2014 Institute of Rock and Soil Mechanics, Chinese Academy of Sciences. Production and hosting byElsevier B.V. All rights reserved.