A Ni Fe_2O_4/expanded graphite(Ni Fe_2O_4/EG)nanocomposite was prepared via a simple and inexpensive synthesis method. Its lithium storage properties were studied with the goal of applying it as an anode in a lithium-...A Ni Fe_2O_4/expanded graphite(Ni Fe_2O_4/EG)nanocomposite was prepared via a simple and inexpensive synthesis method. Its lithium storage properties were studied with the goal of applying it as an anode in a lithium-ion battery. The obtained nanocomposite exhibited a good cycle performance, with a capacity of 601 m Ah g^(-1)at a current of 1 A g^(-1)after 800 cycles. This good performance may beattributed to the enhanced electrical conductivity and layered structure of the EG. Its high mechanical strength could postpone the disintegration of the nanocomposite structure,efficiently accommodate volume changes in the Ni Fe_2O_4-based anodes, and alleviate aggregation of Ni Fe_2O_4 nanoparticles.展开更多
CaCl_(2)·6H_(2)O/expanded vermiculite shape stabilized phase change materials(CEV)was prepared by atmospheric impregnation method.Using gold mine tailings as aggregate of cemented paste backfill(CPB)material,the ...CaCl_(2)·6H_(2)O/expanded vermiculite shape stabilized phase change materials(CEV)was prepared by atmospheric impregnation method.Using gold mine tailings as aggregate of cemented paste backfill(CPB)material,the CPB with CEV added was prepared,and the specific heat capacity,thermal conductivity,and uniaxial compressive strength(UCS)of CPB with different cement-tailing ratios and CEV addition ratios were tested,the influence of the above variables on the thermal and mechanical properties of CPB was analyzed.The results show that the maximum encapsulation capacity of expanded vermiculite for CaCl_(2)·6H_(2)O is about 60%,and the melting and solidification enthalpies of CEV can reach 98.87 J/g and 97.56 J/g,respectively.For the CPB without CEV,the specific heat capacity,thermal conductivity,and UCS decrease with the decrease of cement-tailing ratio.For the CPB with CEV added,with the increase of CEV addition ratio,the specific heat capacity increases significantly,and the sensible heat storage capacity and latent heat storage capacity can be increased by at least 10.74%and 218.97%respectively after adding 12%CEV.However,the addition of CEV leads to the increase of pores,and the thermal conductivity and UCS both decrease with the increase of CEV addition.When cement-tailing ratio is 1:8 and 6%,9%,and 12%of CEV are added,the 28-days UCS of CPB is less than 1 MPa.Considering the heat storage capacity and cost price of backfill,the recommended proportion scheme of CPB material presents cement-tailing ratio of 1:6 and 12%CEV,and the most recommended heat storage/release temperature cycle range of CPB with added CEV is from 20 to 40℃.This work can provide theoretical basis for the utilization of heat storage backfill in green mines.展开更多
Self expanding metalic stent(SEMS) application can cause serious problems up to one third of the patients and some studies reported negative effect of SEMSs on survival in patients with malignancy. The SEMS type espec...Self expanding metalic stent(SEMS) application can cause serious problems up to one third of the patients and some studies reported negative effect of SEMSs on survival in patients with malignancy. The SEMS type especially the rigid one like Wall-stent rather than more flexible type Ultraflex was also reported to have bad impact on the risk of perforation we believe that stent based management protocol for patients with non-perforating left sided obstructing colorectal cancer is a complex method that needs qualified medical and technical team.展开更多
应用有限元法,借助ANSYS软件分析液压马达中活塞和缸体间O形圈加密封环的组合密封和新型膨胀环密封2种典型密封结构,获得2种密封结构在不同工作压力下的变形以及密封圈接触面的应力分布规律,并对2种密封结构的密封效果进行了比较。分析...应用有限元法,借助ANSYS软件分析液压马达中活塞和缸体间O形圈加密封环的组合密封和新型膨胀环密封2种典型密封结构,获得2种密封结构在不同工作压力下的变形以及密封圈接触面的应力分布规律,并对2种密封结构的密封效果进行了比较。分析结果表明:随着油压的升高,2种密封结构的范.米塞斯(Von M ises)应力都随之增加,均具有很好的自适应能力,但膨胀环密封更优;2种密封都达到了密封的效果,新型膨胀环密封的密封性能要好于组合密封结构,即使膨胀环密封由于局部应力过高可能造成磨损,但楔形结构可保证其密封效果得到自动补偿。展开更多
基金support from the National Basic Research Program of China (2014CB239702)National Natural Science Foundation of China (Grant Nos. 21371121, 21506126 and 51502174)+1 种基金Shenzhen Science and Technology Research Foundation (Grant Nos. JCYJ20150324141711645,JCYJ20150324141711616 and JCYJ20150626090504916)China Postdoctoral Science Foundation (2015 M582401 and 2015 M572349)
文摘A Ni Fe_2O_4/expanded graphite(Ni Fe_2O_4/EG)nanocomposite was prepared via a simple and inexpensive synthesis method. Its lithium storage properties were studied with the goal of applying it as an anode in a lithium-ion battery. The obtained nanocomposite exhibited a good cycle performance, with a capacity of 601 m Ah g^(-1)at a current of 1 A g^(-1)after 800 cycles. This good performance may beattributed to the enhanced electrical conductivity and layered structure of the EG. Its high mechanical strength could postpone the disintegration of the nanocomposite structure,efficiently accommodate volume changes in the Ni Fe_2O_4-based anodes, and alleviate aggregation of Ni Fe_2O_4 nanoparticles.
基金supported by the National Natural Science Foundation of China(Nos.51974225,51874229,51674188,51904224,51904225)the Shaanxi Innovative Talents Cultivate Program-New-star Plan of Science and Technology,China(No.2018KJXX-083)+2 种基金the Natural Science Basic Research Plan of Shaanxi Province of China(Nos.2018JM 5161,2018JQ5183,2019JM-074)the Scientific Research Program funded by the Shaanxi Provincial Education Department,China(No.19JK0543)the Outstanding Youth Science Fund of Xi’an University of Science and Technology,China(No.2018YQ2-01)。
文摘CaCl_(2)·6H_(2)O/expanded vermiculite shape stabilized phase change materials(CEV)was prepared by atmospheric impregnation method.Using gold mine tailings as aggregate of cemented paste backfill(CPB)material,the CPB with CEV added was prepared,and the specific heat capacity,thermal conductivity,and uniaxial compressive strength(UCS)of CPB with different cement-tailing ratios and CEV addition ratios were tested,the influence of the above variables on the thermal and mechanical properties of CPB was analyzed.The results show that the maximum encapsulation capacity of expanded vermiculite for CaCl_(2)·6H_(2)O is about 60%,and the melting and solidification enthalpies of CEV can reach 98.87 J/g and 97.56 J/g,respectively.For the CPB without CEV,the specific heat capacity,thermal conductivity,and UCS decrease with the decrease of cement-tailing ratio.For the CPB with CEV added,with the increase of CEV addition ratio,the specific heat capacity increases significantly,and the sensible heat storage capacity and latent heat storage capacity can be increased by at least 10.74%and 218.97%respectively after adding 12%CEV.However,the addition of CEV leads to the increase of pores,and the thermal conductivity and UCS both decrease with the increase of CEV addition.When cement-tailing ratio is 1:8 and 6%,9%,and 12%of CEV are added,the 28-days UCS of CPB is less than 1 MPa.Considering the heat storage capacity and cost price of backfill,the recommended proportion scheme of CPB material presents cement-tailing ratio of 1:6 and 12%CEV,and the most recommended heat storage/release temperature cycle range of CPB with added CEV is from 20 to 40℃.This work can provide theoretical basis for the utilization of heat storage backfill in green mines.
文摘Self expanding metalic stent(SEMS) application can cause serious problems up to one third of the patients and some studies reported negative effect of SEMSs on survival in patients with malignancy. The SEMS type especially the rigid one like Wall-stent rather than more flexible type Ultraflex was also reported to have bad impact on the risk of perforation we believe that stent based management protocol for patients with non-perforating left sided obstructing colorectal cancer is a complex method that needs qualified medical and technical team.
文摘应用有限元法,借助ANSYS软件分析液压马达中活塞和缸体间O形圈加密封环的组合密封和新型膨胀环密封2种典型密封结构,获得2种密封结构在不同工作压力下的变形以及密封圈接触面的应力分布规律,并对2种密封结构的密封效果进行了比较。分析结果表明:随着油压的升高,2种密封结构的范.米塞斯(Von M ises)应力都随之增加,均具有很好的自适应能力,但膨胀环密封更优;2种密封都达到了密封的效果,新型膨胀环密封的密封性能要好于组合密封结构,即使膨胀环密封由于局部应力过高可能造成磨损,但楔形结构可保证其密封效果得到自动补偿。