Macrosegregation is a critical factor that limits the mechanical properties of materials.The impact of equiaxed crystal sedimentation on macrosegregation has been extensively studied,as it plays a significant role in ...Macrosegregation is a critical factor that limits the mechanical properties of materials.The impact of equiaxed crystal sedimentation on macrosegregation has been extensively studied,as it plays a significant role in determining the distribution of alloying elements and impurities within a material.To improve macrosegregation in steel connecting shafts,a multiphase solidification model that couples melt flow,heat transfer,microstructure evolution,and solute transport was established based on the volume-averaged Eulerian-Eulerian approach.In this model,the effects of liquid phase,equiaxed crystals,columnar dendrites,and columnar-to-equiaxed transition(CET)during solidification and evolution of microstructure can be considered simultaneously.The sedimentation of equiaxed crystals contributes to negative macrosegregation,where regions between columnar dendrites and equiaxed crystals undergo significant A-type positive macrosegregation due to the CET.Additionally,noticeable positive macrosegregation occurs in the area of final solidification in the ingot.The improvement in macrosegregation is beneficial for enhancing the mechanical properties of connecting shafts.To mitigate the thermal convection of molten steel resulting from excessive superheating,reducing the superheating during casting without employing external fields or altering the design of the ingot mold is indeed an effective approach to control macrosegregation.展开更多
Two kinds of argon shroud protection devices with two different basic structures were designed and investigated. Industrial experiments and numerical simulations were used to examine the protection effect, and the mec...Two kinds of argon shroud protection devices with two different basic structures were designed and investigated. Industrial experiments and numerical simulations were used to examine the protection effect, and the mechanism of air entrapment during the casting of steel ingots was analyzed. The influence of the structure of the argon shroud protection device on the protection effect was investigated. An argon shroud protection device mounted to the nozzle holder on the bottom of the ladle does not provide a good protection effect because air can easily flow into the teeming system and cause reoxidation of molten steel during teeming. By contrast, an argon shroud protection device seated on the top of the central trumpet provides an excellent protection effect, where air has little chance of flowing into the teeming system during casting. The feasibilities of the argon shroud protection devices are discussed.展开更多
During the ingot casting process, the parametric changes of the molten steel pouring process often cause both ingot surface and internal quality defects. With the increasingly wide application of computers in industri...During the ingot casting process, the parametric changes of the molten steel pouring process often cause both ingot surface and internal quality defects. With the increasingly wide application of computers in industrial technology ,numerical simulations of the molten steel pouring process enable predictions of the defects that will arise during the pouring and solidification process, especially for the molten steel flow during the early stages of casting. In addition,using a computer to simulate the casting process of a 40 t ingot and solidification can prevent many defects. The simulation results indicate that controlling the pouring speed to less than 80 kg/s, hanging the casting powder in a mold with the hanging height maintained at 100-150 mm, and controlling the taper angle of the mold brick outlet to a suitable level can reduce the probability of slag entrapment and improve the internal and surface quality of the ingot.展开更多
A two-phase model for the prediction of macrosegregation formed during solidification is presented. This model incorporates the descriptions of heat transfer, melt convection, solute transport, and solid movement on t...A two-phase model for the prediction of macrosegregation formed during solidification is presented. This model incorporates the descriptions of heat transfer, melt convection, solute transport, and solid movement on the system scale with microscopic relations for grain nucleation and growth. Then the model is used to simulate the solidification of a benchmark industrial 3.3-t steel ingot. Simulations are per- formed to investigate the effects of grain motion and pipe shrinkage formation on the final macrosegregation pattern. The model predictions are compared with experimental data and numerical results from literatures. It is demonstrated that the model is able to express the overall macrosegregation patterns in the ingot. Furthermore, the results show that it is essential to consider the motion of equiaxed grains and the formation of pipe shrinkage in modelling. Several issues for future model improvements are identified.展开更多
The metallurgical effect of a round tundish used to cast heavy steel ingots in machine works at present was evaluated through water modeling experiments. The flow control devices of the improved oval tundish, which wa...The metallurgical effect of a round tundish used to cast heavy steel ingots in machine works at present was evaluated through water modeling experiments. The flow control devices of the improved oval tundish, which was used instead of the round tundish, had been optimized. The results show that the residence time of the round tundish is short, its inclusion removal efficiency is too low, and it has more dead zones and an unreasonable flow field. Compared with the round tundish, the improved oval tundish with the optimized weir and dam has a better effect: its minimum residence time is prolonged by 38.1 s, the average residence time is prolonged by 233.4 s, its dead volume fraction decreases from 26% to 15%, and the ratio of plug volume fraction to dead volume fraction increases from 0.54 to 1.27. The inclusion removal efficiency also increases by 17.5%.展开更多
Achieving a uniform structure with few defects in heavy steel ingot is of high commercial importance. In this present work, in order to verify the potential of pulsed magneto-oscillation(PMO) applied in the production...Achieving a uniform structure with few defects in heavy steel ingot is of high commercial importance. In this present work, in order to verify the potential of pulsed magneto-oscillation(PMO) applied in the production of heavy ingot, an induction coil was located at the hot top of the steel ingot to develop a novel technique, named hot top pulsed magneto oscillation(HPMO). The influences of HPMO on the solidification structure, macro segregation and compactness of a cylindrical medium carbon steel ingot with the weight of 160 kg were systematically investigated by optical microscope(OM) and laser induced breakdown spectroscopy original position metal analyzer(LIBSOPA-100). The results show that HPMO not only causes significant grain refinement and promotes the occurrence of columnar to equiaxed transition(CET) but also can homogenize the carbon distribution and enhance the compactness of the steel ingot. Therefore, HPMO technique has the potential to be applied in the production of heavy steel ingots on an industrial scale.展开更多
The method based on transient heat transfer model is adopted to simulate electro-slag remelting process. The calculated results of the model show that the process is in the quasi-steady state, and the shape of pool re...The method based on transient heat transfer model is adopted to simulate electro-slag remelting process. The calculated results of the model show that the process is in the quasi-steady state, and the shape of pool remains unchanged when the height of ingot is approximately 2.5-3 times the thickness of slab ingot. The change in the shape of pool is found to be strongly dependent on the pattern of melting rate, and hence, the power input; the depth of the molten pool increases with the increase in melting speed. It is concluded that a transient heat transfer model has to be used to obtain reliable input information for the entire, operatina time.展开更多
In this paper,a large-sized ingot of Mg–9Gd–3Y–1.5Zn–0.5Zr(wt%) alloy with a diameter of 600 mm was successfully prepared by the semi-continuous casting method.The alloy was subsequently annealed at a relatively l...In this paper,a large-sized ingot of Mg–9Gd–3Y–1.5Zn–0.5Zr(wt%) alloy with a diameter of 600 mm was successfully prepared by the semi-continuous casting method.The alloy was subsequently annealed at a relatively low temperature of 430°C for 12 h as a homogenization treatment.The microstructure and room-temperature mechanical properties of the alloy were investigated systematically.The results show that the as-cast alloy contained a mass of discontinuous lamellar-shaped 18 R long-period stacking ordered(LPSO) phases with a composition of Mg10 Zn Y and an α-Mg matrix,along with net-shaped Mg5(Y,Gd) eutectic compounds at the grain boundaries.Most of the eutectic compounds dissolved after the homogenization treatment.Moreover,the amount and dimensions of the lamellar-shaped LPSO phase obviously increased after the homogenization treatment.The structure of the phase transformed into 14H-type LPSO with composition Mg12Zn(Y,Gd).The mechanical properties of the heat-treated large-sized alloy ingot are uniform.The ultimate tensile strength(UTS) and tensile yield strength(TYS) of the alloy reached 207.2 MPa and 134.8 MPa,respectively,and the elongation was 3.4%.The high performances of the large-sized alloy ingot after the homogenization treatment is attributed to the strengthening of the α-Mg solid solution and to the plentiful LPSO phase distributed over the α-Mg matrix.展开更多
Shrinkage cavities and large inclusions are serious internal defects of heavy steel ingot and influence the quality of subsequent forgings. In order to remove these two types of defects, a 70 t 12Cr2Mo1 heavy ingot fa...Shrinkage cavities and large inclusions are serious internal defects of heavy steel ingot and influence the quality of subsequent forgings. In order to remove these two types of defects, a 70 t 12Cr2Mo1 heavy ingot fabricated by vacuum carbon de-oxidation process was sectioned and investigated by means of structure observation and EDS analysis. To further study the forming mechanism of shrinkage and inclusion defects and find possible solutions, simulation on pouring and solidification processes was also carried out using Fluent and ProCAST software, respectively. Results show that the shrinkage defects do not appear in the middle-upper part of the ingot. The critical value of shrinkage cavity criterion is ascertained as 0.013 on the basis of sectioning investigation and simulation results, which can be used in computer simulation to predict and avoid shrinkage defects in production of 12Cr2Mo1 ingots with different weights. However, large inclusions are found at the bottom of the ingot body. The bad thermal conditions of the ingot surface and large amount of entrained slag are the main origin of the large inclusions. The simulation result of the pouring process shows that large inclusions may be eliminated by combined measures of improving the top thermal condition and controlling the height of rudimental molten steel in the ladle to above 300 mm.展开更多
P91 is a new kind of heat-resistant and high-tensile steel. It can be extruded after ingot casting and can be widely used for different pipes in power plants. However, due to its mushy freezing characteristics, a lack...P91 is a new kind of heat-resistant and high-tensile steel. It can be extruded after ingot casting and can be widely used for different pipes in power plants. However, due to its mushy freezing characteristics, a lack of feeding in the ingot center often generates many defects, such as porosity and crack. A six-ton P91 ingot was cast and sliced, and a representative part of the longitudinal section was inspected in more detail. The morphology of crack-like defects was examined by X-ray high energy industrial CT and reconstructed by 3D software. There are f ive main portions of defects larger than 200 mm^3, four of which are interconnected. These initiated from continuous liquid f ilm, and then were torn apart by excessive tensile stress within the brittle temperature range(BTR). The 3D FEM analysis of thermo-mechanical simulation was carried out to analyze the formation of porosity and internal crack defects. The results of shrinkage porosity and Niyama values revealed that the center of the ingot suffers from inadequate feeding. Several criteria based on thermal and mechanical models were used to evaluate the susceptibility of hot crack formation. The Clyne and Davies' criterion and Katgerman's criterion successfully predicted the high hot crack susceptibility in the ingot center. Six typical locations in the longitudinal section had been chosen for analysis of the stresses and strains evolution during the BTR. Locations in the defects region showed the highest tensile stresses and relative high strain values, while other locations showed either low tensile stresses or low strain values. In conclusion, hot crack develops only when stress and strain exceed a threshold value at the same time during the BTR.展开更多
A mathematical model coupling the momentum, energy and species conservation equa-tions was proposed to calculate the macro--segregation of Fe--C alloy ingot during solid-ification. The corresponding simulation softwar...A mathematical model coupling the momentum, energy and species conservation equa-tions was proposed to calculate the macro--segregation of Fe--C alloy ingot during solid-ification. The corresponding simulation software which concurrently solves the macro-scopic mass, momentum, energy and species conservation equations has been developedby applying the SIMPLE algorithm.The thermo--solutal convection in a NH_4 Cl--H_2O ingot is verified and the result showsgood agreement with that reported. Then macro--segregation in a steel ingot is simu-lated by using the developed program. The steel ingot is in a rectangular mold with ariser. The fluid flow is mainly induced by the temperature field and the solid fraction.The macro--segregation pattern is mainly affected by the thermo--induced convectionin the mushy zone. The negative segregation forms along the walls of the casting.The positive segregation forms at the top center of the casting into the riser. Thespecies concentration reaches the peak in the center of the ingot where solidificationends lastly.展开更多
A ladle-tundish-mould transportation model considering the entire multiple pouring(MP) process is proposed. Numerical simulation is carried out to study the carbon distribution and variation in both the tundish and th...A ladle-tundish-mould transportation model considering the entire multiple pouring(MP) process is proposed. Numerical simulation is carried out to study the carbon distribution and variation in both the tundish and the mould for making a 292 t steel ingot. Firstly, the fluid flow as well as the heat and mass transfer of the molten steel in the tundish is simulated based on the multiphase transient turbulence model. Then, the carbon mixing in the mould is calculated by using the species concentration at the tundish outlet as the inlet condition during the teeming process. The results show a high concentration of carbon at the bottom and a low concentration of carbon at the top of the mould after a MP process with carbon content high in the first ladle and low in the last ladle. Such carbon concentration distribution would help reduce the negative segregation at the bottom and the positive segregation at the top of the solidified ingot.展开更多
Pulse Electric Discharging (PED) is a novel technique that can modify solidifying structure and reduce grain size. ItS effectsapplied to the high carbon liquid steel were presented here. The macrostructure and microst...Pulse Electric Discharging (PED) is a novel technique that can modify solidifying structure and reduce grain size. ItS effectsapplied to the high carbon liquid steel were presented here. The macrostructure and microstructure of the high carbon alloy steel werealso observed. Results show that (1 ) the length of columnar crystal at the edge of ingot without PED treatment is much longer than thatwith PED, and (2) the perlite lamellae of steel billets after deposed by PED are twisted and shortened. An explanation of those experimental results is given.展开更多
The influence and signification of casting parameters on the solidification process of steel ingot were discussed based on the finite element method (FEM) results by orthogonal experiment method. The range analysis, a...The influence and signification of casting parameters on the solidification process of steel ingot were discussed based on the finite element method (FEM) results by orthogonal experiment method. The range analysis, analysis of variance (ANOVA) and optimization project were used to investigate the FEM results. In order to decrease the ingot riser head and improve the utilization ratio of ingot, the casting parameters involved casting temperature, pouring velocity and interface heat transfer were optimized to decrease shrinkage pore and microporosity. The results show that the heat transfer coefficient between melt and heated board is a more sensitive factor. It is favor to decrease the shrinkage pore and microporosity under the conditions of low temperature, high pouring velocity and high heat transfer between melt and mold. If heat transfer in the ingot body is quicker than that in the riser, the position of shrinkage pore and microporosity will be closer to riser top. The results of optimization project show that few of shrinkage pore and microporosity reach into ingot body with the rational parameters, so the riser size can be reduced.展开更多
Macrosegregation is the major defect in large steel ingots caused by solute partitioning and melt convection during casting.In this study,a three-phase(liquid,columnar dendrites,and equiaxed grains)model is proposed t...Macrosegregation is the major defect in large steel ingots caused by solute partitioning and melt convection during casting.In this study,a three-phase(liquid,columnar dendrites,and equiaxed grains)model is proposed to simulate macrosegregation in a 36-t steel ingot.A supplementary set of conservation equations are employed in the model such that two types of equiaxed grains,either settling or adhering to the solid shell,are well simulated.The predicted concentration agrees quantitatively with the experimental value.A negative segregation cone was located at the bottom owing to the grain settlement and solute-enriched melt leaving from the mushy zone.The interdendritic liquid flow was carefully analyzed,and the formation of A-type segregations in the mid-height of the ingot is discussed.Negative segregation was observed near the riser neck due to the specific relationship between flow direction and temperature gradient.Additionally,the as-cast macrostructure of the ingot is presented,including the grain size distribution and columnar–equiaxed transition.展开更多
In order to avoid contamination from the crucible and to modify the structures,a new solidification method based on cold crucible technology was used to prepare silicon ingots.A silicon ingot with square cross section...In order to avoid contamination from the crucible and to modify the structures,a new solidification method based on cold crucible technology was used to prepare silicon ingots.A silicon ingot with square cross section was directionally solidified with a cold crucible.The mechanism of the cold crucible directional solidification of silicon ingot was revealed.Due to the induction heat that was released in the surface layer and the incomplete contact between the crucible and the melt,the lateral heat loss was reduced and the silicon ingot was directionally solidified.The structures,dislocation defects and the grain growth orientation of the ingot were determined.The results show that neither intergranular nor intragranular precipitates are found in the ingot,except for the top part that was the last to solidify.The average dislocation density is about 1 to 2×106 cm-2.The grains are preferentially <220> orientated.展开更多
The influence of ingot segregation on quenching distortion of gear steel was investigated in this paper. The results show that the shape of ingot segregation of rod steel depends on the shape of continuous casting (C...The influence of ingot segregation on quenching distortion of gear steel was investigated in this paper. The results show that the shape of ingot segregation of rod steel depends on the shape of continuous casting (CC) molds ,and that the distortion of gear steel with square ingot segregation is uniform, while that of gear steel with rectangular ingot segregation is anisotropic. After quenching,the outer circle of the ring sample with a large rectangular segregation area is distorted into an oval shape. No obvious element segregation has been found in the rod steel produced through the rectangular CC mold. Obvious difference in density has been detected at the cross section of rod steel. It suggests that center porosity may be the main reason for the strong impact of segregation on heat treatment distortion of gear steel.展开更多
The effect of electromagnetic stirring on the inner quality of K417 superalloy ingots is studied with EPMA and optical microscope.The results show that while an electromagnetic stirring with 50Hz frequency and 80A cur...The effect of electromagnetic stirring on the inner quality of K417 superalloy ingots is studied with EPMA and optical microscope.The results show that while an electromagnetic stirring with 50Hz frequency and 80A current is imposed,the equiax crystals of K417 superalloy ingots can be effectively refined and increased,and the central shrinkage porosity and the dendritic segregation of K417 superalloy ingots are greatly reduced,so the inner quality of K417 superalloy ingots is obviously improved.展开更多
Bulk metallic glass matrix composites (BMGMC) are unique materials of future having excellent mechanical properties (such as high hardness, strength and profound elastic strain limit). However, they exhibit poor ducti...Bulk metallic glass matrix composites (BMGMC) are unique materials of future having excellent mechanical properties (such as high hardness, strength and profound elastic strain limit). However, they exhibit poor ductility and suffer from catastrophic failure on the application of force. The reasons behind this are still not very well understood. In this study, an effort has been made to overcome this pitfall by solidification processing. Zr based BMGMCs are produced in the form of “as cast” wedges using vacuum arc melting and suction casting button furnace. The idea is to study the effect of cooling rate and inoculation on formability during solidification. Adjustment, manipulation and proper control of processing parameters are observed to reflect upon the quality of ingots such as improved castability, proper mold filling and defect free casting as characterized by NDT. Further, thermal analysis, optical microscopy and hardness measurement confirmed the formation and evolution of in-situcomposite structure. This is first footprint of pathway towards sustainable manufacturing of these alloys in future.展开更多
With the continuous improvement of product quality and function,the quality control of mold steel is becoming increasingly stricter. Argon protection is essential for ensuring casting quality during ingot casting. The...With the continuous improvement of product quality and function,the quality control of mold steel is becoming increasingly stricter. Argon protection is essential for ensuring casting quality during ingot casting. The development of argon protection in ingot casting and the production process of enclosed argon protection in 40 t line is discussed,w ith particular focus given the factors affecting the flow of oxygen in the argon protection cover are discussed. The influence of some related factors on the oxygen content is analyzed. On the basis of the online measurements of the oxygen content,the optimized operational approaches for improving the effect of argon protection are developed. This can decrease the liquid steel via secondary oxidation,and improve the quality of the ingots.展开更多
基金supported by the National Key Research and Development Program of China(2021YFB3702005)the National Natural Science Foundation of China(52304352)+3 种基金the Central Government Guides Local Science and Technology Development Fund Projects(2023JH6/100100046)2022"Chunhui Program"Collaborative Scientific Research Project(202200042)the Doctoral Start-up Foundation of Liaoning Province(2023-BS-182)the Technology Development Project of State Key Laboratory of Metal Material for Marine Equipment and Application[HGSKL-USTLN(2022)01].
文摘Macrosegregation is a critical factor that limits the mechanical properties of materials.The impact of equiaxed crystal sedimentation on macrosegregation has been extensively studied,as it plays a significant role in determining the distribution of alloying elements and impurities within a material.To improve macrosegregation in steel connecting shafts,a multiphase solidification model that couples melt flow,heat transfer,microstructure evolution,and solute transport was established based on the volume-averaged Eulerian-Eulerian approach.In this model,the effects of liquid phase,equiaxed crystals,columnar dendrites,and columnar-to-equiaxed transition(CET)during solidification and evolution of microstructure can be considered simultaneously.The sedimentation of equiaxed crystals contributes to negative macrosegregation,where regions between columnar dendrites and equiaxed crystals undergo significant A-type positive macrosegregation due to the CET.Additionally,noticeable positive macrosegregation occurs in the area of final solidification in the ingot.The improvement in macrosegregation is beneficial for enhancing the mechanical properties of connecting shafts.To mitigate the thermal convection of molten steel resulting from excessive superheating,reducing the superheating during casting without employing external fields or altering the design of the ingot mold is indeed an effective approach to control macrosegregation.
基金supported by the National Natural Science Foundation of China(Grant No.51404018)the State Key Laboratory of Advanced Metallurgy Foundation(No.41614014)
文摘Two kinds of argon shroud protection devices with two different basic structures were designed and investigated. Industrial experiments and numerical simulations were used to examine the protection effect, and the mechanism of air entrapment during the casting of steel ingots was analyzed. The influence of the structure of the argon shroud protection device on the protection effect was investigated. An argon shroud protection device mounted to the nozzle holder on the bottom of the ladle does not provide a good protection effect because air can easily flow into the teeming system and cause reoxidation of molten steel during teeming. By contrast, an argon shroud protection device seated on the top of the central trumpet provides an excellent protection effect, where air has little chance of flowing into the teeming system during casting. The feasibilities of the argon shroud protection devices are discussed.
文摘During the ingot casting process, the parametric changes of the molten steel pouring process often cause both ingot surface and internal quality defects. With the increasingly wide application of computers in industrial technology ,numerical simulations of the molten steel pouring process enable predictions of the defects that will arise during the pouring and solidification process, especially for the molten steel flow during the early stages of casting. In addition,using a computer to simulate the casting process of a 40 t ingot and solidification can prevent many defects. The simulation results indicate that controlling the pouring speed to less than 80 kg/s, hanging the casting powder in a mold with the hanging height maintained at 100-150 mm, and controlling the taper angle of the mold brick outlet to a suitable level can reduce the probability of slag entrapment and improve the internal and surface quality of the ingot.
基金supported by the National Science and Technology Major Project of China (No.2011ZX04014-052)the National Basic Research Priorities Program of China (No.2011CB012900)
文摘A two-phase model for the prediction of macrosegregation formed during solidification is presented. This model incorporates the descriptions of heat transfer, melt convection, solute transport, and solid movement on the system scale with microscopic relations for grain nucleation and growth. Then the model is used to simulate the solidification of a benchmark industrial 3.3-t steel ingot. Simulations are per- formed to investigate the effects of grain motion and pipe shrinkage formation on the final macrosegregation pattern. The model predictions are compared with experimental data and numerical results from literatures. It is demonstrated that the model is able to express the overall macrosegregation patterns in the ingot. Furthermore, the results show that it is essential to consider the motion of equiaxed grains and the formation of pipe shrinkage in modelling. Several issues for future model improvements are identified.
基金financially supported by the Key Special Project in the National Science & Technology Program during the Eleventh Five-Year Plan Period (No.2009ZX04014-061-7)
文摘The metallurgical effect of a round tundish used to cast heavy steel ingots in machine works at present was evaluated through water modeling experiments. The flow control devices of the improved oval tundish, which was used instead of the round tundish, had been optimized. The results show that the residence time of the round tundish is short, its inclusion removal efficiency is too low, and it has more dead zones and an unreasonable flow field. Compared with the round tundish, the improved oval tundish with the optimized weir and dam has a better effect: its minimum residence time is prolonged by 38.1 s, the average residence time is prolonged by 233.4 s, its dead volume fraction decreases from 26% to 15%, and the ratio of plug volume fraction to dead volume fraction increases from 0.54 to 1.27. The inclusion removal efficiency also increases by 17.5%.
基金financially supported by the National Natural Science Foundation of China(Granted No.U1760204,51504048)the National Key Research Program of China(Granted No.2017YFB0701800)
文摘Achieving a uniform structure with few defects in heavy steel ingot is of high commercial importance. In this present work, in order to verify the potential of pulsed magneto-oscillation(PMO) applied in the production of heavy ingot, an induction coil was located at the hot top of the steel ingot to develop a novel technique, named hot top pulsed magneto oscillation(HPMO). The influences of HPMO on the solidification structure, macro segregation and compactness of a cylindrical medium carbon steel ingot with the weight of 160 kg were systematically investigated by optical microscope(OM) and laser induced breakdown spectroscopy original position metal analyzer(LIBSOPA-100). The results show that HPMO not only causes significant grain refinement and promotes the occurrence of columnar to equiaxed transition(CET) but also can homogenize the carbon distribution and enhance the compactness of the steel ingot. Therefore, HPMO technique has the potential to be applied in the production of heavy steel ingots on an industrial scale.
文摘The method based on transient heat transfer model is adopted to simulate electro-slag remelting process. The calculated results of the model show that the process is in the quasi-steady state, and the shape of pool remains unchanged when the height of ingot is approximately 2.5-3 times the thickness of slab ingot. The change in the shape of pool is found to be strongly dependent on the pattern of melting rate, and hence, the power input; the depth of the molten pool increases with the increase in melting speed. It is concluded that a transient heat transfer model has to be used to obtain reliable input information for the entire, operatina time.
基金supported by the Youth Science Fund Project of the National Natural Science Fund of China(No.51401070)the Program for New Century Excellent Talents in Universities(No.NCET-12-0849)the Fundamental Research Funds for the Central Universities(No.2014ZZD03)
文摘In this paper,a large-sized ingot of Mg–9Gd–3Y–1.5Zn–0.5Zr(wt%) alloy with a diameter of 600 mm was successfully prepared by the semi-continuous casting method.The alloy was subsequently annealed at a relatively low temperature of 430°C for 12 h as a homogenization treatment.The microstructure and room-temperature mechanical properties of the alloy were investigated systematically.The results show that the as-cast alloy contained a mass of discontinuous lamellar-shaped 18 R long-period stacking ordered(LPSO) phases with a composition of Mg10 Zn Y and an α-Mg matrix,along with net-shaped Mg5(Y,Gd) eutectic compounds at the grain boundaries.Most of the eutectic compounds dissolved after the homogenization treatment.Moreover,the amount and dimensions of the lamellar-shaped LPSO phase obviously increased after the homogenization treatment.The structure of the phase transformed into 14H-type LPSO with composition Mg12Zn(Y,Gd).The mechanical properties of the heat-treated large-sized alloy ingot are uniform.The ultimate tensile strength(UTS) and tensile yield strength(TYS) of the alloy reached 207.2 MPa and 134.8 MPa,respectively,and the elongation was 3.4%.The high performances of the large-sized alloy ingot after the homogenization treatment is attributed to the strengthening of the α-Mg solid solution and to the plentiful LPSO phase distributed over the α-Mg matrix.
基金financially supported by the Program of National Technological Cooperation and Communication(Project 2010 DFR 70640)Chinese National S&T Major Project(2011ZX06004-016)
文摘Shrinkage cavities and large inclusions are serious internal defects of heavy steel ingot and influence the quality of subsequent forgings. In order to remove these two types of defects, a 70 t 12Cr2Mo1 heavy ingot fabricated by vacuum carbon de-oxidation process was sectioned and investigated by means of structure observation and EDS analysis. To further study the forming mechanism of shrinkage and inclusion defects and find possible solutions, simulation on pouring and solidification processes was also carried out using Fluent and ProCAST software, respectively. Results show that the shrinkage defects do not appear in the middle-upper part of the ingot. The critical value of shrinkage cavity criterion is ascertained as 0.013 on the basis of sectioning investigation and simulation results, which can be used in computer simulation to predict and avoid shrinkage defects in production of 12Cr2Mo1 ingots with different weights. However, large inclusions are found at the bottom of the ingot body. The bad thermal conditions of the ingot surface and large amount of entrained slag are the main origin of the large inclusions. The simulation result of the pouring process shows that large inclusions may be eliminated by combined measures of improving the top thermal condition and controlling the height of rudimental molten steel in the ladle to above 300 mm.
基金financially supported by the National Basic Research Program of China(No.2011CB012900)the National Science NSFC-Liaoning Joint Fund(U1508215)
文摘P91 is a new kind of heat-resistant and high-tensile steel. It can be extruded after ingot casting and can be widely used for different pipes in power plants. However, due to its mushy freezing characteristics, a lack of feeding in the ingot center often generates many defects, such as porosity and crack. A six-ton P91 ingot was cast and sliced, and a representative part of the longitudinal section was inspected in more detail. The morphology of crack-like defects was examined by X-ray high energy industrial CT and reconstructed by 3D software. There are f ive main portions of defects larger than 200 mm^3, four of which are interconnected. These initiated from continuous liquid f ilm, and then were torn apart by excessive tensile stress within the brittle temperature range(BTR). The 3D FEM analysis of thermo-mechanical simulation was carried out to analyze the formation of porosity and internal crack defects. The results of shrinkage porosity and Niyama values revealed that the center of the ingot suffers from inadequate feeding. Several criteria based on thermal and mechanical models were used to evaluate the susceptibility of hot crack formation. The Clyne and Davies' criterion and Katgerman's criterion successfully predicted the high hot crack susceptibility in the ingot center. Six typical locations in the longitudinal section had been chosen for analysis of the stresses and strains evolution during the BTR. Locations in the defects region showed the highest tensile stresses and relative high strain values, while other locations showed either low tensile stresses or low strain values. In conclusion, hot crack develops only when stress and strain exceed a threshold value at the same time during the BTR.
基金This work was financially supported by the National NSFC BaoSteel Conjunct Foun dation(No.50174031).
文摘A mathematical model coupling the momentum, energy and species conservation equa-tions was proposed to calculate the macro--segregation of Fe--C alloy ingot during solid-ification. The corresponding simulation software which concurrently solves the macro-scopic mass, momentum, energy and species conservation equations has been developedby applying the SIMPLE algorithm.The thermo--solutal convection in a NH_4 Cl--H_2O ingot is verified and the result showsgood agreement with that reported. Then macro--segregation in a steel ingot is simu-lated by using the developed program. The steel ingot is in a rectangular mold with ariser. The fluid flow is mainly induced by the temperature field and the solid fraction.The macro--segregation pattern is mainly affected by the thermo--induced convectionin the mushy zone. The negative segregation forms along the walls of the casting.The positive segregation forms at the top center of the casting into the riser. Thespecies concentration reaches the peak in the center of the ingot where solidificationends lastly.
基金financially supported by the National Basic Research Program of China(No.2011CB012900)the National Science and Technology Major Project of the Ministry of Science and Technology of China(No.2012ZX04012011)
文摘A ladle-tundish-mould transportation model considering the entire multiple pouring(MP) process is proposed. Numerical simulation is carried out to study the carbon distribution and variation in both the tundish and the mould for making a 292 t steel ingot. Firstly, the fluid flow as well as the heat and mass transfer of the molten steel in the tundish is simulated based on the multiphase transient turbulence model. Then, the carbon mixing in the mould is calculated by using the species concentration at the tundish outlet as the inlet condition during the teeming process. The results show a high concentration of carbon at the bottom and a low concentration of carbon at the top of the mould after a MP process with carbon content high in the first ladle and low in the last ladle. Such carbon concentration distribution would help reduce the negative segregation at the bottom and the positive segregation at the top of the solidified ingot.
文摘Pulse Electric Discharging (PED) is a novel technique that can modify solidifying structure and reduce grain size. ItS effectsapplied to the high carbon liquid steel were presented here. The macrostructure and microstructure of the high carbon alloy steel werealso observed. Results show that (1 ) the length of columnar crystal at the edge of ingot without PED treatment is much longer than thatwith PED, and (2) the perlite lamellae of steel billets after deposed by PED are twisted and shortened. An explanation of those experimental results is given.
基金Projects(50435010 50705080 50675187) supported by the National Natural Science Foundation of China
文摘The influence and signification of casting parameters on the solidification process of steel ingot were discussed based on the finite element method (FEM) results by orthogonal experiment method. The range analysis, analysis of variance (ANOVA) and optimization project were used to investigate the FEM results. In order to decrease the ingot riser head and improve the utilization ratio of ingot, the casting parameters involved casting temperature, pouring velocity and interface heat transfer were optimized to decrease shrinkage pore and microporosity. The results show that the heat transfer coefficient between melt and heated board is a more sensitive factor. It is favor to decrease the shrinkage pore and microporosity under the conditions of low temperature, high pouring velocity and high heat transfer between melt and mold. If heat transfer in the ingot body is quicker than that in the riser, the position of shrinkage pore and microporosity will be closer to riser top. The results of optimization project show that few of shrinkage pore and microporosity reach into ingot body with the rational parameters, so the riser size can be reduced.
基金financially supported by the project to strengthen industrial development at the grassroots level of the Ministry of Industry and Information Technology (MIIT), China (No. TC160A310/21)
文摘Macrosegregation is the major defect in large steel ingots caused by solute partitioning and melt convection during casting.In this study,a three-phase(liquid,columnar dendrites,and equiaxed grains)model is proposed to simulate macrosegregation in a 36-t steel ingot.A supplementary set of conservation equations are employed in the model such that two types of equiaxed grains,either settling or adhering to the solid shell,are well simulated.The predicted concentration agrees quantitatively with the experimental value.A negative segregation cone was located at the bottom owing to the grain settlement and solute-enriched melt leaving from the mushy zone.The interdendritic liquid flow was carefully analyzed,and the formation of A-type segregations in the mid-height of the ingot is discussed.Negative segregation was observed near the riser neck due to the specific relationship between flow direction and temperature gradient.Additionally,the as-cast macrostructure of the ingot is presented,including the grain size distribution and columnar–equiaxed transition.
基金financially supported by the National Natural Science Foundation of China (No.50804012)the Natural Science Foundation of Hei Longjiang Province,China (No.E201002)
文摘In order to avoid contamination from the crucible and to modify the structures,a new solidification method based on cold crucible technology was used to prepare silicon ingots.A silicon ingot with square cross section was directionally solidified with a cold crucible.The mechanism of the cold crucible directional solidification of silicon ingot was revealed.Due to the induction heat that was released in the surface layer and the incomplete contact between the crucible and the melt,the lateral heat loss was reduced and the silicon ingot was directionally solidified.The structures,dislocation defects and the grain growth orientation of the ingot were determined.The results show that neither intergranular nor intragranular precipitates are found in the ingot,except for the top part that was the last to solidify.The average dislocation density is about 1 to 2×106 cm-2.The grains are preferentially <220> orientated.
文摘The influence of ingot segregation on quenching distortion of gear steel was investigated in this paper. The results show that the shape of ingot segregation of rod steel depends on the shape of continuous casting (CC) molds ,and that the distortion of gear steel with square ingot segregation is uniform, while that of gear steel with rectangular ingot segregation is anisotropic. After quenching,the outer circle of the ring sample with a large rectangular segregation area is distorted into an oval shape. No obvious element segregation has been found in the rod steel produced through the rectangular CC mold. Obvious difference in density has been detected at the cross section of rod steel. It suggests that center porosity may be the main reason for the strong impact of segregation on heat treatment distortion of gear steel.
文摘The effect of electromagnetic stirring on the inner quality of K417 superalloy ingots is studied with EPMA and optical microscope.The results show that while an electromagnetic stirring with 50Hz frequency and 80A current is imposed,the equiax crystals of K417 superalloy ingots can be effectively refined and increased,and the central shrinkage porosity and the dendritic segregation of K417 superalloy ingots are greatly reduced,so the inner quality of K417 superalloy ingots is obviously improved.
文摘Bulk metallic glass matrix composites (BMGMC) are unique materials of future having excellent mechanical properties (such as high hardness, strength and profound elastic strain limit). However, they exhibit poor ductility and suffer from catastrophic failure on the application of force. The reasons behind this are still not very well understood. In this study, an effort has been made to overcome this pitfall by solidification processing. Zr based BMGMCs are produced in the form of “as cast” wedges using vacuum arc melting and suction casting button furnace. The idea is to study the effect of cooling rate and inoculation on formability during solidification. Adjustment, manipulation and proper control of processing parameters are observed to reflect upon the quality of ingots such as improved castability, proper mold filling and defect free casting as characterized by NDT. Further, thermal analysis, optical microscopy and hardness measurement confirmed the formation and evolution of in-situcomposite structure. This is first footprint of pathway towards sustainable manufacturing of these alloys in future.
文摘With the continuous improvement of product quality and function,the quality control of mold steel is becoming increasingly stricter. Argon protection is essential for ensuring casting quality during ingot casting. The development of argon protection in ingot casting and the production process of enclosed argon protection in 40 t line is discussed,w ith particular focus given the factors affecting the flow of oxygen in the argon protection cover are discussed. The influence of some related factors on the oxygen content is analyzed. On the basis of the online measurements of the oxygen content,the optimized operational approaches for improving the effect of argon protection are developed. This can decrease the liquid steel via secondary oxidation,and improve the quality of the ingots.