Commercially available 000Cr3OMo2 ferritic stainless steel and 4J33 ferromagnetic expansion alloy were di- rectly bonded to silicated graphite at 1180-1200℃ and 1100-1150℃, respectively, Intedacial microstructures w...Commercially available 000Cr3OMo2 ferritic stainless steel and 4J33 ferromagnetic expansion alloy were di- rectly bonded to silicated graphite at 1180-1200℃ and 1100-1150℃, respectively, Intedacial microstructures were examined by scanning electron microscopy, electron probe microanalysis, and X-ray diffraction. The results showed that transient liquid-phase present during bonding promoted the interracial reactions during bonding. Plenty of brittle chromium carbides, such as （Cr, Fe）7C3 and （Cr2.5Fe4.3Mo0.1）C3, were observed in 000Cr3OMo2/silicated graphite joints. Besides, transverse cracks were also found. In case of 4J33/silicated graphite system, well bonded joints free of defects Were obtained.展开更多
G/SiBCN ceramic composite was joined using Ni-19Cr-10Si （BNi5） and Ni-33Cr-24Pd-3.5Si-0.5B filler alloys at 1170 ℃ for 10 min. Two kinds of Ni-based filler alloys exhibited good wettability on the CdSiBCN com- posi...G/SiBCN ceramic composite was joined using Ni-19Cr-10Si （BNi5） and Ni-33Cr-24Pd-3.5Si-0.5B filler alloys at 1170 ℃ for 10 min. Two kinds of Ni-based filler alloys exhibited good wettability on the CdSiBCN com- posite, with a contact angle of 13° and 4°, respectively, The microstructures of the brazed joints were investigated by electron-probe microanalysis （EPMA）, and three-point bend test was conducted for the joints at room temperature. When being brazed with BNi5 filler alloy, no evident reaction layer was ob- served at the surface of the joined composite, and the joint microstructure was characterized by Ni2Si matrix with scatteringly distributing mixture compounds of Cr23C6, Ni2Si and CrB. While Ni-Cr-Pd（Si,B） brazing alloy was used, a Cr23C6 reaction layer with a thickness of 11 μm was formed at the surface of the base composite. In the central part of the brazed joint, the phases were composed of Ni（Cr, Si） solid solution and complex compounds including Pd2Si, （Ni,Pd）2Si and Ni-B. The strength of Cf/SiBCN joint brazed with BNi5 filler alloy was 62.9 MPa at room temperature, whereas that with Ni-Cr-Pd（Si,B） filler alloy was at the same level.展开更多
文摘Commercially available 000Cr3OMo2 ferritic stainless steel and 4J33 ferromagnetic expansion alloy were di- rectly bonded to silicated graphite at 1180-1200℃ and 1100-1150℃, respectively, Intedacial microstructures were examined by scanning electron microscopy, electron probe microanalysis, and X-ray diffraction. The results showed that transient liquid-phase present during bonding promoted the interracial reactions during bonding. Plenty of brittle chromium carbides, such as （Cr, Fe）7C3 and （Cr2.5Fe4.3Mo0.1）C3, were observed in 000Cr3OMo2/silicated graphite joints. Besides, transverse cracks were also found. In case of 4J33/silicated graphite system, well bonded joints free of defects Were obtained.
基金financially supported by the National Natural Science Foundation of China (Contract Nos. 59905022, 50475160 and 51275497)Aeronautical Science Foundation of China (Grant 2008 ZE21005)
文摘G/SiBCN ceramic composite was joined using Ni-19Cr-10Si （BNi5） and Ni-33Cr-24Pd-3.5Si-0.5B filler alloys at 1170 ℃ for 10 min. Two kinds of Ni-based filler alloys exhibited good wettability on the CdSiBCN com- posite, with a contact angle of 13° and 4°, respectively, The microstructures of the brazed joints were investigated by electron-probe microanalysis （EPMA）, and three-point bend test was conducted for the joints at room temperature. When being brazed with BNi5 filler alloy, no evident reaction layer was ob- served at the surface of the joined composite, and the joint microstructure was characterized by Ni2Si matrix with scatteringly distributing mixture compounds of Cr23C6, Ni2Si and CrB. While Ni-Cr-Pd（Si,B） brazing alloy was used, a Cr23C6 reaction layer with a thickness of 11 μm was formed at the surface of the base composite. In the central part of the brazed joint, the phases were composed of Ni（Cr, Si） solid solution and complex compounds including Pd2Si, （Ni,Pd）2Si and Ni-B. The strength of Cf/SiBCN joint brazed with BNi5 filler alloy was 62.9 MPa at room temperature, whereas that with Ni-Cr-Pd（Si,B） filler alloy was at the same level.