Effects of External Electric Field on AlN Precipitation and Recrystallization Texture of Deep-drawing 08Al Killed Steel Sheet

The effects of an electric field on AIN precipitation and recrystallization texture were investigated. Cold-rolled 08Al killed steel sheets were annealed at 550℃ according to the two-step processes, for various maintaining times, with and without applying an electric field. It was found that the electric field promotes the precipitation of the second phase （AlN particles）, strengthens the γ-fiber and weakens the α-fiber texture component in the recrystallized specimens. A possible explanation for the reinforcement of γ-fiber texture by the electric field is that the second phase AIN particle promotes the growth of γ-fiber at the expense of differently oriented grains.

Non-metallic Inclusions in Continuously Cast Aluminum Killed Steels

In aluminum killed steels, the size, shape, quantity and formation of non-metallic inclusions in ladle steel (before and after RH vacuum treatment) and in tundish as well as in slabs were studied by EPMA (Electron Probe Microanalysis) and by analyzing the total oxygen. The results showed that in the slabs the total oxygen was quite low and the inclusions discovered were mainly small-sized angular alumina inclusions. This indicates that most inclusions have been removed by floating out during the continuous casting process. In addition, the countermeasures were discussed to decrease the alumina inclusions in the slabs further.

Effect of intercritical annealing temperature and cooling rate on the microstructure and mechanical properties of low-carbon aluminum killed steel

In this study, the intercritical annealing process for a typical low-carbon aluminum killed steel is investigated. A cold-rolled sheet was annealed at intercfitical temperatures ranging from 730 ℃ to 770 ℃ and then cooled in air or water. The annealed steel was then baked at 210 ℃, and its mechanical properties and microstructures were analyzed in detail. It is shown that after the air-cooling process,the strength of steel decreased and ductility increased with an increase in the annealing temperature. However, after water-cooling, the strength and ductility both increased with the increase of annealing temperature. These results are attributed to the property- optimization of the steel.

Effect of continuous annealing temperature on the microstructure and mechanical property of an aluminum killed steel

The continuous annealing process of a typical aluminum killed steel was investigated. A cold rolled sheet was annealed continuously at holding temperature ranging from 580 to 760 ℃. The microstructures were analyzed in detail based on contiuous cooling transformation（ CCT） curves that were simulated with JM artP ro softw are. The results show ed that recrystallization and perlitic transformations caused a diversity of microstructures and mechanical properties. In comparison with annealed steel that was produced from insufficient recrystallization,annealed steel produced from sufficient recrystallization had more isometric grains and exhibited low er strength and higher ductility. Higher annealing temperatures than A_1 provided steel with lamellar pearlite zones,large ferrite grains,low strength,and high ductility. The results are attributed to the property optimization of the steel.

Control of Ultra Low Titanium in Ultra Low Carbon Al-Si Killed Steel

Titanium is the impurity in some special steel grades.The existence of titanium decreases the grain size,depresses the yield strength,and results in the low quality of these steels in various properties.Thus,titanium should be removed to the minimum.Based on the industrial production of ultra low carbon Al-Si killed steel,the physical-chemical behavior of titanium was investigated in vacuum degassing refining（RH）process with and without desulfurization.The influences of titanium content in hot metal,ladle slag composition,and ladle slag quantity,etc,on titanium content of refined liquid steel were discussed.The results showed that the partition ratio of titanium between ladle slag and liquid steel is in inverse proportion to the 4/3square of aluminum content.The maximum partition ratio of titanium between top slag and liquid steel can be obtained by adjusting an optimum slag composition including contents of FeOxand Al2O3and the slag basicity,and the suitable range of them should be controlled higher than 6%,less than 20%,and within 1.5to 3.0,respectively.Moreover,desulfurization refining by RH decreases the partition ratio of titanium between ladle slag and liquid steel significantly.To ensure the titanium content stably less than 15×10-6 in a 300tladle,the titanium content in hot metal must be less than 500×10-6 and the thickness of basic oxygen furnace（BOF）slag carrying over must be less than 50mm.

Research on the properties of laser welded joints of aluminum killed cold rolled steel

Aluminum killed cold rolled steel used for automobiles was welded in this paper by using CO 2 laser with wavelength 10.6μm.The experiment shows that high quality of welding can be realized at welding speed of 4 500mm/min by optimizing the parameters.The strength and hardness of laser welded joints for aluminum killed cold rolled steel increased compared to those of the base metal while the formability decreased.Forming limit diagram of joint material indicated that the laser weld seam should avoid the maximum deformation area of automobile parts during the designing period for the position of weld seam.

Analysis of thermodynamics and kinetics of titanium between top slag and liquid steel

： Titanium is an impurity element in some special steel grades. The existence of titanium decreases the grain size and lowers the yield strength ,resulting in low quality of these steels with regard to various properties. Thus, the titanium content should be reduced to the minimum. Based on the industrial production of ultra-low carbon A1-Si killed steel, this paper investigated the physical-chemical behaviors of titanium with and without desulfurization during RH refining. The influences of Ti content in hot metal, ladle slag composition, and ladle slag quantity, etc., on the Ti content in refined liquid steel were discussed. The results show that the partition ratio of titanium between ladle slag and liquid steel is inversely proportional to the AI content to the power of 4/3 ,and the empirical formula regressed from practical experience can be expressed as w（TiO2）/WTi=48/w[AI]4/3 Maximum partition ratio of titanium between top slag and liquid steel can be ensured W[Til WIAIIby an optimum slag composition including components of FeOx and A12 03 and an appropriate slag basicity. The contents of FetO and A1203 should be controlled above 6% and below 20% respectively and the slag basicity should be kept within 1.5 to 3.0. Moreover, desulfurization refining in the RH vacuum will decrease the partition ratio of titanium between ladle slag and liquid steel significantly. To keep the Ti content stably below 15 ×10 ^-4% in a 300 ton ladle ,the Ti content in hot metal must be lower than 500 × 10^-4% and the thickness of ladle slag carried over from BOF slag must be less than 50 ram.

Microstructure and texture evolution during recrystallization of low-carbon steel sheets

Aluminum killed low-carbon steel sheets were cold rolled at different reduction ratios and annealed using different temperatures and holding time.The Vickers hardness was examined.The results show that when cold rolling reduction ratios increase from 40% to 81%,recrystallization temperatures decrease from 602℃ to 572℃ during 4hisochronal annealing,as well recrystallization holding time decreases from 117 min to 5min during isothermal annealing at 610℃.All recrystallization temperatures and holding time can be calculated using the annealing experiment results.Microstructure was examined through electron backscattered diffraction（EBSD）.The results show that as rolling direction preferentially grows,equiaxed grains grow into cake-type during recrystallization.Cake-type grains are more beneficial to obtaining ideal〈111〉//ND（normal direcrtion）orientation texture.{111}orientation grains nucleate and grow up preferentially.Deformation grains of{111}〈110〉orientations grow into new recrystallization grains of{111}〈123〉and{111}〈112〉during recrystallization.Texture formation can be explained by directional nucleation.