Repeated-Batch and Continuous Production of L-Lactic Acid by Rhizopus oryzae Immobilized in Calcium Alginat Beads:ReactorPerformance and Kinetic Model

Repeated-batch and continuous production of L-lactic acid by immobilized Rhizopusoryzae with calcium alginate entrapment method in a three-phase fluidized-bed bioreactor was stud-ied.The operation conditions were optimized.The productivity based on total reactor volume wasabout 3 times higher than that with free cells in a traditional stirred tank bioreactor.A mathemat-ical model was proposed and the model predictions were in good agreement with the experimentaldat.

Synthesis of the Biomimetic Polymer: Aliphatic Diamine and RGDS Modified Poly(d,l-lactic acid)

A novel poly（d, /-lactic acid） （PDLLA） based biomimetic polymer was synthesized by grafting maleic anhydride, butanediamine and arg-gly-asp-ser （RGDS） peptides onto the backbone of PDLLA, aiming to overcome the acidity and auto-accelerating degradation of PDLLA during degradation and to improve its biospecificity and biocompatibility. The synthetic copolymer was characterized by FTIR, ^13C NMR and amino acid analyzer （AAA）.

L-LACTIC ACID FERMENTATION IN A ROTATING-DISC CONTACTOR WITH SIMULTANEOUS PRODUCT SEPARATION BY ION-EXCHANGE

A rotating disk contactor（RDC）was designed to perform L-lactic acid fermentation with afilamentous fungi,Rhizopus oryzae,which was immobilized on the surfaces of the rotating discs.Thebioreactor was operated using repeated-batch method as well as continuous feeding method.Ananionic resin,D354,slightly basic in nature and of high selectivity and capacity was chosen for lacticacid separation.A coupled process of L-lactic acid fermentation and ion-exchange separation wasevaluated experimentally.The results indicated that the pH value of the fermentation broth could bemaintained at about 3-3.5 without any addition of alkali.The conversion ratio of glucose to L-lacticacid was about 0.7 g·g-1 and the fermentation rate reached as high as 62.5 g·h-1·m-2.

Synthesis and Characterization of Chitosan-g-poly- (D, L-lactic acid) Copolymer

Biodegradable chitosan-g-poly (D, L-lactic acid) copolymers were prepared via two methods. (1) The lactide was grafted onto hydroxyl groups of chitosan by using macromolecular initiator sodium of trimethylsilyl-chitosan, (2) poly (D,L-lactic acid)(PLA) with low molecular weight can be linked to the amino group by coupling activated PLA to trimethylsilyl-chitosan. Two graft copolymers had hydrophilic-hydrophobic character and can be applied as carriers for drug delivery.

SURFACE OF GELATIN MODIFIED POLY(L-LACTIC ACID)FILM

In this paper, the surface structure of poly(L-lactic acid) (PLLA) film modified with gelatin was investigated. ThePLLA film specimens were treated directly with aqueous alkali solution to provide their surfaces with carboxyl groups, sothat these functional groups could become the reactive sites for gelatin immobilization. The functional groups of the PLLAfilms were identified by ATR-FTIR spectra and XPS spectra, the changes in surface morphology were observed by usingenvironmental scanning electron microscopy (ESEM), and the hydrophilicity of modified PLLA films was examined bywater contact angle measurement. Experimental results showed that the gelatin was immobilized with water-solublecarbodiimide (EDC) onto the PLLA film's surfaces, and the gelatin content on the polymer surface was related to carboxylicgroup formed in the controlled hydrolysis process. Rough surfaces caused by hydrolysis will predominantly favor the adhesion and growth of cell; and the hydrophilicity of these surfaces after the modification procedure is enhanced.

Preparation and Properties of Bio-Based Flame Retardant L-APP/Poly(L-lactic acid)Composites

Poly(L-lactic acid)(PLLA)is a thermoplastic material with complete degradability,high biocompatibility and excellent mechanical properties.It can replace petroleum-based polymers are currently being used in the fields of packaging,agriculture,textiles,medical and so on.However,PLLA’s extremely flammability greatly limits its wider application.An bio-based flame retardant L-APP/PLLA composites was prepared by melt blending of the L-APP and PLLA.The morphology,impact properties,thermal properties and flame retardant properties of composites were investigated by field emission scanning electron microscope(SEM),impact tester,differential scanning calorimeter(DSC),thermogravimetric analyzer(TGA),limiting oxygen indexer(LOI)and horizontalvertical burning tester.The results showed that the degree of crystallization(X_(c))and LOI of L-APP/PLLA composites increased as increasing of L-APP content.What’s more,the impact strength first increased and then decreased,the glass transition temperature(T_(g))and melting temperature(T_(m))do not changed significantly.The impact strength of composites was 9.1 kJ/m^(2) at a 5 wt%loading for L-APP,which was the highest level.When the content of L-APP was 20%,the LOI was 30.8%,the Xc was 42.3%and the UL-94 level was V-0.This research can promote the value-added utilization of lignin and the application of PLLA in the fields of flame retardant materials.

Chitosan——L-Lactic Acid Scaffold for the Regeneration of Peripheral Nerve and Its NGF Release Properties

Chitosan—L-lactic acid composite scaffold for the regeneration of peripheral nerve is obtained by grafting L-lactic acid onto the amino groups in chitosan with combined vacuum freezer drier. The composite scaffold was characterized by ATR-FTIR and SEM. The scaffold has a better graft efficiency and has a dense inner layer and a loose outer layer with porous structure, and the pore size is about 100 μm.The NGF release properties of the scaffold were investigated. The experimental results showed that, at the 1st day, 15.2 ng of NGF on average was released from the scaffold. From day 2 to day 10, the release rate obviously slowed down and 1.64 ng of NGF was released on average every day. After 10 days, the release rate was slower and 10.3 ng of NGF was released on average every day. After 60 days, NGF could also maintained a certain concentration. These properties show that the scaffold is a better carrier for NGF which can be more advantageous to the regeneration of the damaged peripheral nerve. As a result, this composite scaffold would be an ideal candidate for the regeneration of damaged peripheral nerve.

Composite Biomaterials Based on Poly(L-Lactic Acid)and Functionalized Cellulose Nanocrystals

The biocomposite films were prepared from poly(L-lactic acid)and cellulose nanocrystals.To improve interfacial compatibility of hydrophilic cellulose nanocrystals with hydrophobic matrix polymer as well as to provide the osteoconductive properties,cellulose was functionalized with poly(glutamic acid).The modified cellulose nanocrystals were better distributed and less aggregated within the matrix,which was testified by scanning electron,optical and polarized light microscopy.According to mechanical tests,composites filled with nanocrystals modified with PGlu demonstrated higher values of Young’s modulus,elongation at break and tensile strength.Incubation of composite materials in model buffer solutions for 30 weeks followed with staining of Ca^(2+)deposits with Alizarin Red S assay testified better mineralization of materials containing PGlu-modified cellulose nanocrystals as filler.As the result of in vivo experiment,the developed composite materials showed less level of inflammation in comparison with pure polymer matrix and composites filled with non-functionalized cellulose nanocrystals.

Preparation of Poly ( L-lactic acid ) / Vermiculites Composites by in situ Copolymerization of Lactic Acid and Hydroxylic Vermiculites

L-lactic acid (L-LA) based copolymer/hydroxylation vermiculites composites (PLLA-co-bis A/HVMTs) were prepared by in situ reaction among L-LA, adipic acid, and hydroxylation lamellar vermiculites (HVMTs) using bisphenol-A epoxy resin as chain extending agent. HVMTs were obtained by sulfuric acid-leaching of lamellar vermiculites (VMTs). The effects of sulfuric acid leaching on the VMTs structure were characterized by X-ray diffraction (XRD), 29Si magic-angle spinning nuclear magnetic resonance(29Si NMR), Fourier transform infrared spectroscopy (FTIR), field emission scanning electron microscopy (FE-SEM), and thermogravimetric analysis (TGA). FTIR, FE-SEM, and TGA were used to characterize the reaction activity of HVMTs. The results indicated that VMTs with increased hydroxyl groups had been successfully obtained and could react with -COOH of the reaction system. The amount of L-LA based copolymer grafted on the surface of HVMTs was more than 22%. The onset decomposition temperature of L-LA based copolymer grafted on the surface of HVMTs was 30℃ higher than that of free L-LA based copolymer.

Multi-porous electroactive poly(L-lactic acid)/ polypyrrole composite micro/nano fibrous scaffolds promote neurite outgrowth in PC12 cells

In this study, poly（L-lactic acid）/ammonium persulfate doped-polypyrrole composite fibrous scaffolds with moderate conductivity were produced by combining electrospinning with in situ polymerization. PC12 cells were cultured on these fibrous scaffolds and their growth following electrical stimulation （0-20.0 μA stimulus intensity, for 1-4 days） was observed using inverted light microscopy, and scanning electron microscopy coupled with the MTT cell viability test. The results demonstrated that the poly（L-lactic acid）/ammonium persulfate doped-polypyrrole fibrous scaffold was a dual multi-porous micro/nano fibrous scaffold. An electrical stimulation with a current intensity 5.0- 10.0 μAfor about 2 days enhanced neuronal growth and neurite outgrowth, while a high current intensity （over 15.0 μA） suppressed them. These results indicate that electrical stimulation with a moderate current intensity for an optimum time frame can promote neuronal growth and neurite outgrowth in an intensity- and time-dependent manner.

衣康酸小试发酵条件研究

对衣康酸产生菌（ＡｓｐｅｒｇｉｌｌｕｓＴｅｒｒｅｕｓＮＲＲＬ１９６０）在不同条件下的小试发酵进行了探讨。通过反复试验，确立了衣康酸最佳斜面培养基、发酵培养基和发酵条件。摇瓶培养７２ｈｒ后，残糖可降至０．１％Ａ右；产酸率平均为４８．６ｇ／Ｌ；对糖的转化率平均为５４．９％。

聚乳酸-聚乙醇酸共聚物的合成及其结构与性能研究

以左旋乳酸（ L－LA ）为原料，以氯化亚锡（SnCl2）和对甲苯磺酸（TSA）为复合催化剂直接熔融缩聚制备不同相对分子质量（ Mw ）的聚左旋乳酸（ PLLA）；将不同 Mw 的 PLLA 与 Mw 为4620的聚乙醇酸（PGA）按摩尔比为4：1，催化剂SnCl2：TSA摩尔比为1：1，在170℃，小于100 Pa的条件下反应4 h，制得PLLA－PGA共聚物（ PLGA）；通过用丙酮、三氯甲烷等多步溶解－离心沉淀进行分离，对PLGA的结构与性能进行表征。结果表明：共聚物为PLGA及PGA共混物；共聚物中PLGA组分的含量随着PLLA的 Mw 变化而变化，当PLLA的Mw 在20000左右时，共聚物中PLGA的质量分数大于90％，共聚物具有2个熔融峰，熔程分别为120．19～140．74℃，196．28～202．94℃，其热性能优于PLLA。

生活垃圾酸性发酵的产酸特性研究

本文研究了生活垃圾酸性发酵的特点 ,旨在为利用硫酸盐还原菌 (SRB)处理含硫酸盐的酸性矿山废水时寻找一种新的经济碳源。实验中采用小试规模的批量反应器和CSTR反应器 ,在温度35℃条件下研究了生活垃圾厌氧发酵产酸过程中 pH、挥发性脂肪酸 (VFA)和氧化还原电位的变化。在实验条件下 ,5种不同固体浓度 ( 6% ,9% ,12 % ,15 %和 2 0 % )批量运行结果表明 :所产生VFA浓度经过缓慢增加、快速增加和增加相对平缓 3个阶段 ,VFA浓度最后趋于稳定并达到一个最大值。 15 %的固体浓度是最佳固体浓度。在CSTR反应器实验中 ,5个不同的水力停留时间 ( 15 ,2 0 ,2 5 ,30和 35d)的实验结果表明 :最佳水力停留时间为 30d ,单位反应器容积的VFA产率为0 361gVFA/(L·d) ,单位重量垃圾的VFA产率为 2 2 5 4gVFA/(kg·d)。实验结果表明 :生活垃圾产酸发酵可以在较低的 pH值 ( 4 35～ 4 45 )和较高的氧化还原电位 ( +2 0 0～ +340mV)下进行。实验还测定了发酵液中乙酸、丙酸和丁酸的相对组成 ,3种短链VFA中乙酸的比例最大。

Microwave-assisted Polymerization of D,L-Lactide with Stannous Octanoate as Catalyst

Poly (lactic acid) (PLA) was synthesized by microwave-assisted ring-opening polymerization of D, L-lactide with stannous octanoate (SnOct(2)) as catalyst. Its weight-average molar mass (M-w) ranged from 39000 to 67000 and the polydispersity index from 1.3 to 1.7. The polymerization rate was much faster than that of the conventional thermal polymerization. A degradation of newly formed PLA in reaction mixture by microwave irradiation was observed.

Enhancement of L(+)-Lactic Acid Production of Immobilized Rhizoous Orvzae Imolanted by Ion Beams

Immobilized Rhizopus oryzae culturing may be a solution to the inhibited production of L（＋）-lactic acid in submerged fermentation, which is caused by aggregated mycelia floc. In the present study, a R. oryzae mutant （RL6041） with a 90% conversion rate of glucose into L-lactic acid was obtained by N＋ implantation under the optimized conditions of a beam energy of 15 keV and a dose of 2.6 ×10^15 ions/cm^2. Using polyurethane foam as the immobilization matrix, the optimal L-lactic acid production conditions were determined as 4 mm polyurethane foam, 150 r/min, 50 g/L ～ 80 g/L of initial glucose, 38℃ and pH 6.0. 15-cycle repeated productions of L-lactic acid by immobilized RL6041 were performed under the optimized culturing conditions and over 80% of the glucose was converted into L-lactic acid in 30 hours on average. The results show that immobilized RL6041 is a promising candidate for continuous L-lactic acid production.

微内核结构的测控系统软件

测控系统软件是测控系统重要组成部分,直接影响着测控系统的运行。提出了一种基于微内核结构的测控系统软件设计方法,该方法以消息数据处理为中心,通过统一的消息接口将测控任务插件化,利用受控的消息传递机制实现测控软件各个功能模块间的交互,并在微内核单元管理下进行HPFS-HRRN的测控任务调度;基于虚拟仪器技术,设计和实现了水平分层结构替代纵向层次结构的测控系统软件。实验测试表明,将该方法应用到L-乳酸发酵过程测控系统软件设计中,所构建的测控系统具有较高的可靠性、通用性和可扩展性。

In Vitro Characterizations of PLLA/β-TCP Porous Matrix Materials and RMSC-PLLA-β-TCP Composite Scaffolds

To develop a novel degradable poly (L-lactic acid)/β-tricalcium phosphate (PLLA/β-TCP) bioactive materials for bone tissueengineering, β-TCP powder was produced by a new wet process. Porous scaffolds were prepared by three steps, i.e. solventcasting, compression molding and leaching stage. Factors influencing the compressive strength and the degradation behaviorof the porous scaffold, e.g. weight fraction of pore forming agent-sodium chloride (NaCl), weight ratio of PLLA: β-TCP,the particle size of β-TCP and the porosity, were discussed in details. Rat marrow stromal cells (RMSC) were incorporatedinto the composite by tissue engineering approach. Biological and osteogenesis potential of the composite scaffold weredetermined with MTT assay, alkaline phosphatase (ALP) activity and bone osteocalcin (OCN) content evaluation. Resultsshow that PLLA/β-TCP bioactive porous scaffold has good mechanical and pore structure with adjustable compressive strengthneeded for surgery. RMSCs seeding on porous PLLA/β-TCP composite behaves good seeding efficacy, biocompatibility andosteoinductive potential. Osteoprogenitor cells could well penetrate into the material matrix and begin cell proliferation andosteogenic differentiation. Osseous matrix could be formed on the surface of the composite after culturing in vitro. It isexpected that the PLLA/β-TCP porous composites are promising scaffolds for bone tissue engineering in prosthesis surgery.

Preparation and Degradation Characteristics of Poly(d,1-laetide) Composite Films

PDLLA/CHI/β-TCP/NGF composite films were prepared by a solvent evaporation method. The degradation characteristics of the poly （d, l-lactide） composite films were studied in vitro and in vivo. The acidity produced by poly （d, l-lactide） materials was not obvious. Adding chitosan and β-TCP can relieve the acidity problem and improve strength performance of films. The NGF has influences on the degradation characteristics of films. It is verified that PDLLA/CHI/β-TCP/NGF composite films prepared by solvent evaporation method have excellent degradation characteristics. It can be used as a perfect biomaterial for repairing nerve injuries.