Ta2O5 single crystals have been grown by the laser heated pedestal growth (LHPG) technique up to several centimeters length with diameter of 1.1 mm. The crystal, characterized by X-ray diffraction, dielectric measurem...Ta2O5 single crystals have been grown by the laser heated pedestal growth (LHPG) technique up to several centimeters length with diameter of 1.1 mm. The crystal, characterized by X-ray diffraction, dielectric measurement, and thermal expansion analysis, has Htri-Ta2O5 symmetry. Dielectric permittivity, loss tangent along [001] and [110] direction were investigated over the temperature range from -80 ℃ to 100 ℃. Large dielectric anisotropy in Ta2O5 single crystal was observed. At room temperature, the dielectric permittivities (1 MHz) along [001] and [110] are 33.2 and 231.9, respectively. The reason of dielectric enhancement in Ta2O5 crystal grown by LHPG was also discussed.展开更多
基金Instrument Developing Project of the Chinese Academy of Sciences(YJKYYQ20170019)International Partnership Program of Chinese Academy of Sciences(121631KYSB20180045)National Natural Science Foundation of China(51872309,U1832106)。
基金supported by the National Nature Science Foundation of China(No.10674041)the Funding Project for Academic Human Resources Development in Institutions of Higer Learning under the Jursdiction of Beijing Municipality
文摘Ta2O5 single crystals have been grown by the laser heated pedestal growth (LHPG) technique up to several centimeters length with diameter of 1.1 mm. The crystal, characterized by X-ray diffraction, dielectric measurement, and thermal expansion analysis, has Htri-Ta2O5 symmetry. Dielectric permittivity, loss tangent along [001] and [110] direction were investigated over the temperature range from -80 ℃ to 100 ℃. Large dielectric anisotropy in Ta2O5 single crystal was observed. At room temperature, the dielectric permittivities (1 MHz) along [001] and [110] are 33.2 and 231.9, respectively. The reason of dielectric enhancement in Ta2O5 crystal grown by LHPG was also discussed.