A series of blue long afterglow mixed halide-phosphate phosphors Sr5 （PO4）3 FxCll-x：Eu2＋,Gd3＋ were synthesized in air by traditional solid-state reaction routte. The crystal structures, photoluminescence, thermol...A series of blue long afterglow mixed halide-phosphate phosphors Sr5 （PO4）3 FxCll-x：Eu2＋,Gd3＋ were synthesized in air by traditional solid-state reaction routte. The crystal structures, photoluminescence, thermolurninescenee properties and afterglow proper- ties of the phosphors were characterized systematically using X-ray diffraction （XRD）, luminescence spectrophotometer, microcom- puter thermoluminescence dosimeter and single photon counter, respectively. Under 280 nm excitation, the broadband emissions of Eu2＋ ions were observed at 445 nm （blue） due to the 4f7→4f65d transition. It was demonstrated that there existed the self-reduction of the Eu3＋ to Eu2＋ ions in this special halide-phosphate matrix in air condition. The addition of Gd3＋ ions obviously enhanced the after- glow properties of the single doped Eu2＋ ions in the halide-phosphate phosphors. And the content of the fluoride anions also had sig- nificant influence on the afterglow properties. All results indicated that Srs （PO4）3 FxCI1-x：Eu2＋,Gd3＋ might be potential phosphors for long lasting phosphorescence （LLP） materials.展开更多
基金Project supported by Cooperation Project in Industry, Education and Research of Guangdong Province and Ministry of Education of China （2012B09110044）, and the Guangdong Provincial Natural Science Foundation of China （9151009001000052 ）
文摘A series of blue long afterglow mixed halide-phosphate phosphors Sr5 （PO4）3 FxCll-x：Eu2＋,Gd3＋ were synthesized in air by traditional solid-state reaction routte. The crystal structures, photoluminescence, thermolurninescenee properties and afterglow proper- ties of the phosphors were characterized systematically using X-ray diffraction （XRD）, luminescence spectrophotometer, microcom- puter thermoluminescence dosimeter and single photon counter, respectively. Under 280 nm excitation, the broadband emissions of Eu2＋ ions were observed at 445 nm （blue） due to the 4f7→4f65d transition. It was demonstrated that there existed the self-reduction of the Eu3＋ to Eu2＋ ions in this special halide-phosphate matrix in air condition. The addition of Gd3＋ ions obviously enhanced the after- glow properties of the single doped Eu2＋ ions in the halide-phosphate phosphors. And the content of the fluoride anions also had sig- nificant influence on the afterglow properties. All results indicated that Srs （PO4）3 FxCI1-x：Eu2＋,Gd3＋ might be potential phosphors for long lasting phosphorescence （LLP） materials.