With sol-gel method,nanometer La-Ti composite oxides were prepared.By means of atomic force microscope,the surface pattern,particle size distribution and specific surface area were studied.The newly prepared nanocryst...With sol-gel method,nanometer La-Ti composite oxides were prepared.By means of atomic force microscope,the surface pattern,particle size distribution and specific surface area were studied.The newly prepared nanocrystals of La-Ti composite oxides were used as the catalysts to catalyze the dehydration of external compensated lactic acid to lactide.The lactide product was measured by polarimeter and micropolariscope.The results demonstrate that the ratio between D-lactide and L-lactide will not be equal to 1-1 if nanocrystals of La-Ti composite oxides are used as the catalysts,which implies,that nanocrystals of La-Ti composite oxides may be potential catalysts with a good selectivity.展开更多
With sol-gel method, nanometer La-Ti composite oxide was successfully prepared at a low temperature (750～800C) using polyethylene glycol as dispersant. By means of atomic force microscope, the surface pattern, partic...With sol-gel method, nanometer La-Ti composite oxide was successfully prepared at a low temperature (750～800C) using polyethylene glycol as dispersant. By means of atomic force microscope, the surface pattern, particle size distribution, and specific surface area were studied. The compound particle surface appears as a smooth sheet, the mean size of the compound is 25.38 nm. On the specific surface, the particle erects at a height of 4.69 nm. The surface area is 58.90 nm2. The La-Ti composite oxide nanocrystal prefers to narrow and even particle size distribution and the homogeneity of surface topography.展开更多
By means of atomic force microscope, the surface pattern, particle size distribution, and specific surface area of La Ti composite oxide were studied. The compound particle surface appears as a smooth sheet, the even ...By means of atomic force microscope, the surface pattern, particle size distribution, and specific surface area of La Ti composite oxide were studied. The compound particle surface appears as a smooth sheet, the even size of the compound ranges from 19.85 nm to 25.38 nm. The particle seems smooth, which erects at a height from 4.69 nm to 5.88 nm.The surface area ranges from 58.90 nm 2 to 1 238.04 nm 2. The La Ti composite oxide nanocrystallines enjoy a narrow and even particle size distribution and accumulate closely.展开更多
The present study dealt with investigations on the effects of annealing on the hydrogen storage properties of La 1.6 Ti 0.4 MgNi 9 alloys.The experimental alloys were prepared by magnetic levitation melting followed b...The present study dealt with investigations on the effects of annealing on the hydrogen storage properties of La 1.6 Ti 0.4 MgNi 9 alloys.The experimental alloys were prepared by magnetic levitation melting followed by annealing treatment.For La 1.6 Ti 0.4 MgNi 9 alloys,LaNi 5,LaNi 3 and LaMg 2 Ni 9 were the main phases,Ti 2 Ni phase appeared at 900℃.Annealing not only enhanced the maximum and effective hydrogen storage capacity,improved the hydrogen absorption/desorption kinetics,but also increased the discharge capacity.The cyclic stability had been improved markedly by annealing,e.g.,when the discharge capacity reduced to 60% of maximum discharge capacity,the charge/discharge cycles increased from 66（as-cast） to 89（annealed at 800℃） and 127 times（annealed at 900℃）.La 1.6 Ti 0.4 MgNi 9 alloy annealed at 900℃ exhibited better electrochemical properties compared to the other two alloy electrodes.展开更多
基金Project(50174059)supported by the National Natural Science Foundation of ChinaProject(Y406469)supported by Natural Science Foundation of Zhejiang Province
文摘With sol-gel method,nanometer La-Ti composite oxides were prepared.By means of atomic force microscope,the surface pattern,particle size distribution and specific surface area were studied.The newly prepared nanocrystals of La-Ti composite oxides were used as the catalysts to catalyze the dehydration of external compensated lactic acid to lactide.The lactide product was measured by polarimeter and micropolariscope.The results demonstrate that the ratio between D-lactide and L-lactide will not be equal to 1-1 if nanocrystals of La-Ti composite oxides are used as the catalysts,which implies,that nanocrystals of La-Ti composite oxides may be potential catalysts with a good selectivity.
基金This project was supported by the National Natural Science Foundation of China (1972003).
文摘With sol-gel method, nanometer La-Ti composite oxide was successfully prepared at a low temperature (750～800C) using polyethylene glycol as dispersant. By means of atomic force microscope, the surface pattern, particle size distribution, and specific surface area were studied. The compound particle surface appears as a smooth sheet, the mean size of the compound is 25.38 nm. On the specific surface, the particle erects at a height of 4.69 nm. The surface area is 58.90 nm2. The La-Ti composite oxide nanocrystal prefers to narrow and even particle size distribution and the homogeneity of surface topography.
文摘By means of atomic force microscope, the surface pattern, particle size distribution, and specific surface area of La Ti composite oxide were studied. The compound particle surface appears as a smooth sheet, the even size of the compound ranges from 19.85 nm to 25.38 nm. The particle seems smooth, which erects at a height from 4.69 nm to 5.88 nm.The surface area ranges from 58.90 nm 2 to 1 238.04 nm 2. The La Ti composite oxide nanocrystallines enjoy a narrow and even particle size distribution and accumulate closely.
基金National Defense Industrial Technology Development Program(JCKY2018419C101)Project of Science and Technology Development of Henan Province(202102210073)Program of Science and Technology of Luoyang City(1901016A)。
基金supported by National Natural Science Foundation of China (50861003,51071054)Natural Science Foundation of Guangxi(2010GXNSFD013004,2012GXNSFBA053149)+1 种基金the Foundation of Key Laboratory of National Education Ministry for Nonferrous Metals and Materials Processing Technology (GXKFJ09-15)the Guangxi University Program for Science and Technology Research (XBZ110379)
文摘The present study dealt with investigations on the effects of annealing on the hydrogen storage properties of La 1.6 Ti 0.4 MgNi 9 alloys.The experimental alloys were prepared by magnetic levitation melting followed by annealing treatment.For La 1.6 Ti 0.4 MgNi 9 alloys,LaNi 5,LaNi 3 and LaMg 2 Ni 9 were the main phases,Ti 2 Ni phase appeared at 900℃.Annealing not only enhanced the maximum and effective hydrogen storage capacity,improved the hydrogen absorption/desorption kinetics,but also increased the discharge capacity.The cyclic stability had been improved markedly by annealing,e.g.,when the discharge capacity reduced to 60% of maximum discharge capacity,the charge/discharge cycles increased from 66（as-cast） to 89（annealed at 800℃） and 127 times（annealed at 900℃）.La 1.6 Ti 0.4 MgNi 9 alloy annealed at 900℃ exhibited better electrochemical properties compared to the other two alloy electrodes.