A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer...A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer were investigated. The composite layer has graded microstructures and compositions, due to the fast melting followed by rapid solidification and cooling during laser cladding. The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The size of TiC dendrites decreases with increasing depth. Y2O3 fine particles distribute in the whole clad layer. The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380, which is 4 times higher than the initial hardness. The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.展开更多
xNi/10NiO-NiFe2O4 （x=5, 10, 17） cermets and those doped with 1% BaO （mass fraction） were prepared by cold isostatic pressing at 200 MPa and sintering in nitrogen atmosphere at 1 473 K. The effects of BaO addition ...xNi/10NiO-NiFe2O4 （x=5, 10, 17） cermets and those doped with 1% BaO （mass fraction） were prepared by cold isostatic pressing at 200 MPa and sintering in nitrogen atmosphere at 1 473 K. The effects of BaO addition on relative density, microstructure and electric conductivity of cermets were investigated. The results show that relative densities ofxNi/10NiO-NiFe2O4 cermets （x=5, 10, 17） doped with 1% BaO at 1 473 K in nitrogen atmosphere are increased by 0.49%, 1.45% and 2.99% compared with those of the undoped BaO cermets, respectively. Moreover, the electric conductivities （21.98, 28.37 and 50.10 S/cm） of xNi/10NiO-NiFe2O4 cermets （x=5, 10, 17） doped with 1% BaO at 1 233 K are improved compared with those （18.70, 22.79 and 39.58 S/cm） of xNi/lONiO-NiFe2O4 cermets （x=5, 10, 17）, respectively. This indicates that perhaps the addition of BaO or formation of BaFe204 and Ba2Fe2O5 has an active effect on electric conductivities ofxNi/10NiO-NiFe2O4 （x=5, 10, 17） cermets.展开更多
Carbon nanotubes (CNTs) of narrow size distribution can be abundantly produced in the catalytic decomposition of CH4 over pre-reduced LaNiO3, La4Ni3O10, La3Ni2O7 and La2NiO4. The CNTs obtained were characterized by m...Carbon nanotubes (CNTs) of narrow size distribution can be abundantly produced in the catalytic decomposition of CH4 over pre-reduced LaNiO3, La4Ni3O10, La3Ni2O7 and La2NiO4. The CNTs obtained were characterized by means of transmission electron microscopy (TEM). Thermal oxidation of CNTs in air was monitored thermogravimetrically (TG). The results revealed that a lower La/Ni ratio of the catalysts would lead to a wider diameter distribution and a higher degree of graphitic nature.展开更多
基金Projects (51101096, 51002093) supported by the National Natural Science Foundation of ChinaProject (1052nm05000) supported by Special Foundation of the Shanghai Science and Technology Commission for Nano-Materials ResearchProject (J51042) supported by Leading Academic Discipline Project of the Shanghai Education Commission, China
文摘A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer were investigated. The composite layer has graded microstructures and compositions, due to the fast melting followed by rapid solidification and cooling during laser cladding. The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The size of TiC dendrites decreases with increasing depth. Y2O3 fine particles distribute in the whole clad layer. The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380, which is 4 times higher than the initial hardness. The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.
基金Project(2005CB623703) supported by the National Basic Research Program of ChinaProject(50721003) supported by the National Natural Science Fund for Innovation Group of ChinaProject(2008AA030501) supported by the National High-Tech Research and Development Program of China
文摘xNi/10NiO-NiFe2O4 （x=5, 10, 17） cermets and those doped with 1% BaO （mass fraction） were prepared by cold isostatic pressing at 200 MPa and sintering in nitrogen atmosphere at 1 473 K. The effects of BaO addition on relative density, microstructure and electric conductivity of cermets were investigated. The results show that relative densities ofxNi/10NiO-NiFe2O4 cermets （x=5, 10, 17） doped with 1% BaO at 1 473 K in nitrogen atmosphere are increased by 0.49%, 1.45% and 2.99% compared with those of the undoped BaO cermets, respectively. Moreover, the electric conductivities （21.98, 28.37 and 50.10 S/cm） of xNi/10NiO-NiFe2O4 cermets （x=5, 10, 17） doped with 1% BaO at 1 233 K are improved compared with those （18.70, 22.79 and 39.58 S/cm） of xNi/lONiO-NiFe2O4 cermets （x=5, 10, 17）, respectively. This indicates that perhaps the addition of BaO or formation of BaFe204 and Ba2Fe2O5 has an active effect on electric conductivities ofxNi/10NiO-NiFe2O4 （x=5, 10, 17） cermets.
文摘Carbon nanotubes (CNTs) of narrow size distribution can be abundantly produced in the catalytic decomposition of CH4 over pre-reduced LaNiO3, La4Ni3O10, La3Ni2O7 and La2NiO4. The CNTs obtained were characterized by means of transmission electron microscopy (TEM). Thermal oxidation of CNTs in air was monitored thermogravimetrically (TG). The results revealed that a lower La/Ni ratio of the catalysts would lead to a wider diameter distribution and a higher degree of graphitic nature.