A synthesis of LaF3：0.04Yb^3＋,0.01Er^3＋ nanocrystals with oleic acid as a capping ligand was presemed. The X-Ray Diffraction （XRD） pattern indicated that the power was a single hexagonal phase. Transmission Elect...A synthesis of LaF3：0.04Yb^3＋,0.01Er^3＋ nanocrystals with oleic acid as a capping ligand was presemed. The X-Ray Diffraction （XRD） pattern indicated that the power was a single hexagonal phase. Transmission Electron Microscopy （TEM） demonstrated that the average size of the nanocrystals was less than 10 nm, with a narrow size distribution. The nanocrystals were dispersible in nonpolar solvents and form a fully transparent colloidal solution, and the solution was stable for several months without any aggregates. The Yb^3＋-Er^3＋ codoped nanocrystal colloidal solution exhibited a bright green upconversion fluorescence under 980 nm excitation from a diode laser. The nanocrystals were potentially applicable in biolabeling and bioimaging.展开更多
LaF3：Yb^3＋ , Er^＋ microcrystals were synthesized by a hydrothermal method, and then, the LaF3： Yb^3＋ , Er^＋ microcrystals were coated with silica. Phase identification of LaF3： Yb^3＋ , Er^＋ and LaF3： Yb^3＋ ...LaF3：Yb^3＋ , Er^＋ microcrystals were synthesized by a hydrothermal method, and then, the LaF3： Yb^3＋ , Er^＋ microcrystals were coated with silica. Phase identification of LaF3： Yb^3＋ , Er^＋ and LaF3： Yb^3＋ , Er^＋/SiO2 was performed via XRD. The TEM image showed that the size of LaF3： Yb^3＋ , Er^＋ was 150 nm and LaF3： Yb^3＋ , Er^＋/SiO2 presented clearly a core/shell structure with 20 nm shell thickness. The upconversion spectra of LaF3： Yb^3＋ , Er^＋ and LaF3： Yb^3＋ , Er^＋/SiO2 in solid state and in ethanol were studied with a 980 nm diode laser as the excitation source. The upconversion spectra showed that the silica shell had little effect on the properties of fluorescence of the LaF3：Yb^3＋ , Er^＋ microcrystals. At the same time, the green luminescence photo of LaF3： Yb3＋, Er3＋/SiO2 in the PBS buffer was obtained, which indicated that the LaF3： Yb^3＋ , Er^＋/SiO2 could be used in biological applications.展开更多
基金Project supported by the National Natural Science Foundation of China (10474096 50672030)
文摘A synthesis of LaF3：0.04Yb^3＋,0.01Er^3＋ nanocrystals with oleic acid as a capping ligand was presemed. The X-Ray Diffraction （XRD） pattern indicated that the power was a single hexagonal phase. Transmission Electron Microscopy （TEM） demonstrated that the average size of the nanocrystals was less than 10 nm, with a narrow size distribution. The nanocrystals were dispersible in nonpolar solvents and form a fully transparent colloidal solution, and the solution was stable for several months without any aggregates. The Yb^3＋-Er^3＋ codoped nanocrystal colloidal solution exhibited a bright green upconversion fluorescence under 980 nm excitation from a diode laser. The nanocrystals were potentially applicable in biolabeling and bioimaging.
基金Project supported by the National Natural Science Foundation of China (10474096 and 50672030)
文摘LaF3：Yb^3＋ , Er^＋ microcrystals were synthesized by a hydrothermal method, and then, the LaF3： Yb^3＋ , Er^＋ microcrystals were coated with silica. Phase identification of LaF3： Yb^3＋ , Er^＋ and LaF3： Yb^3＋ , Er^＋/SiO2 was performed via XRD. The TEM image showed that the size of LaF3： Yb^3＋ , Er^＋ was 150 nm and LaF3： Yb^3＋ , Er^＋/SiO2 presented clearly a core/shell structure with 20 nm shell thickness. The upconversion spectra of LaF3： Yb^3＋ , Er^＋ and LaF3： Yb^3＋ , Er^＋/SiO2 in solid state and in ethanol were studied with a 980 nm diode laser as the excitation source. The upconversion spectra showed that the silica shell had little effect on the properties of fluorescence of the LaF3：Yb^3＋ , Er^＋ microcrystals. At the same time, the green luminescence photo of LaF3： Yb3＋, Er3＋/SiO2 in the PBS buffer was obtained, which indicated that the LaF3： Yb^3＋ , Er^＋/SiO2 could be used in biological applications.