The unit cell of lanthanum chromate was constructed by calculating equivalent points. By means of calculation of the hole octahedrally surrounded by O^(2-) ions, it was considered that the sintered property of lanthan...The unit cell of lanthanum chromate was constructed by calculating equivalent points. By means of calculation of the hole octahedrally surrounded by O^(2-) ions, it was considered that the sintered property of lanthanum chromate and the stability of Cr-O octahedron might be promoted by mixing a little Ca^(2+) ions. The growth mechanism was discussed in terms of structural ledge observed by SEM, the surfaces of the structural ledges parallel to (001), (010) and (110) planes, respectively. The misfit between (110) and (001) planes is only 0.0021 on common atomic plane, and the interconnection of the structured ledge may occur during crystal growth.展开更多
The nano powders of LaCrO3 were prepared by a sol-gel route. The heat capacity of LaCrO3 nano powders from 350 to 550 K was measured by DSC method and expressed as： Cpa2CrO3） （±0.112） = 166.844 - 8.500 ×...The nano powders of LaCrO3 were prepared by a sol-gel route. The heat capacity of LaCrO3 nano powders from 350 to 550 K was measured by DSC method and expressed as： Cpa2CrO3） （±0.112） = 166.844 - 8.500 ×10^-3T- 1.022×10^6T^-2 （J/（mol.K）） （350-550 K）. An EMF measurement assembly was developed with CaF2 as an electrolyte for the galvanic cell. From measured EMF data of the reversible cell, （-） PL La2O3, LaF3, O2 （1 atm）lCaF2O2（1 atm）, LaF3, LaCrO3, Cr2O3, Pt（＋）, and the relevant value of Gibbs free energy, the Gibbs free energy of formation of LaCrO3 was calculated from 700 to 885 K： △G ФaLaCrO3 = -1555.364 ＋ 0.354T （kJ/mol） （700-885 K）. And the Gibbs free energy change of reaction from simple oxides La2O3 and Cr2O3 was calculated to be： AG f Oox（LaCrO3） = -94.758 ＋ 8.530×10^-2T（kJ/mol） （700-885 K）.展开更多
基金Project supported by the National"863"High Technology Project (2001AA327010) and the National Natural Science Founda tion of China (50362001)
文摘The unit cell of lanthanum chromate was constructed by calculating equivalent points. By means of calculation of the hole octahedrally surrounded by O^(2-) ions, it was considered that the sintered property of lanthanum chromate and the stability of Cr-O octahedron might be promoted by mixing a little Ca^(2+) ions. The growth mechanism was discussed in terms of structural ledge observed by SEM, the surfaces of the structural ledges parallel to (001), (010) and (110) planes, respectively. The misfit between (110) and (001) planes is only 0.0021 on common atomic plane, and the interconnection of the structured ledge may occur during crystal growth.
基金This project is financially supported by the National Natural Science Foundation of China (Nos. 50374009, 20331030, and 20571009)
文摘The nano powders of LaCrO3 were prepared by a sol-gel route. The heat capacity of LaCrO3 nano powders from 350 to 550 K was measured by DSC method and expressed as： Cpa2CrO3） （±0.112） = 166.844 - 8.500 ×10^-3T- 1.022×10^6T^-2 （J/（mol.K）） （350-550 K）. An EMF measurement assembly was developed with CaF2 as an electrolyte for the galvanic cell. From measured EMF data of the reversible cell, （-） PL La2O3, LaF3, O2 （1 atm）lCaF2O2（1 atm）, LaF3, LaCrO3, Cr2O3, Pt（＋）, and the relevant value of Gibbs free energy, the Gibbs free energy of formation of LaCrO3 was calculated from 700 to 885 K： △G ФaLaCrO3 = -1555.364 ＋ 0.354T （kJ/mol） （700-885 K）. And the Gibbs free energy change of reaction from simple oxides La2O3 and Cr2O3 was calculated to be： AG f Oox（LaCrO3） = -94.758 ＋ 8.530×10^-2T（kJ/mol） （700-885 K）.
