LiFePO4-Li3V2（PO4）3 composites were synthesized by solid-hydrothermal method and by ball milling,respectively.The electrochemical performance of the solid-hydrothermally obtained materials（C-LFVP） was significantl...LiFePO4-Li3V2（PO4）3 composites were synthesized by solid-hydrothermal method and by ball milling,respectively.The electrochemical performance of the solid-hydrothermally obtained materials（C-LFVP） was significantly improved compared with LiFePO4（LFP） and Li3V2（PO4）3（LVP）,and it was also much better than that of the ball-milled LiFePO4-Li3V2（PO4）3（P-LFVP）.C-LFVP and P-LFVP both had four REDOX peaks（voltage plateaus）,which coincided with that of LFP and LVP.Some new trace substances were found in C-LFVP which had more perfect morphology,this was responsible for the better electrochemical performance of C-LFVP than P-LFVP.展开更多
The Li3V2（PO4）3/C composite cathode material was synthesized via sol-gel method using three different chelating agents （citric acid, salicylic acid and polyacrylic acid） at pH value of 3 or 7. The crystal structur...The Li3V2（PO4）3/C composite cathode material was synthesized via sol-gel method using three different chelating agents （citric acid, salicylic acid and polyacrylic acid） at pH value of 3 or 7. The crystal structure, morphology, specific surface area and electrochemical performance of the prepared samples were investigated by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, cyclic voltammetry （CV）, electrochemical impedance spectroscopy （EIS） and galvanostatic charge/discharge test. The results show that the effects of pH value on the performance of the prepared materials are greatly related to the chelating agents. With salicylic acid or polyacrylic acid as the chelating reagent, the structure, morphology and electrochemical performance of the samples are greatly influenced by the pH values. However, the structure of the materials with citric acid as the chelating agent does not change as pH value changes, and the materials own uniform particle size distribution and good electrochemical performance. It delivers an initial discharge capacity of 113.58 mA·h/g at 10C, remaining as high as 108.48 mA·h/g after 900 cycles, with a capacity retention of 95.51%.展开更多
Li3V2-2/3xMnx（PO4）3（0≤x≤0.12） powders were synthesized by sol-gel method. The effect of Mn2＋-doping on the structure and electrochemical performances of Li3V2（PO4）3/C was characterized by XRD, SEM, XPS, galva...Li3V2-2/3xMnx（PO4）3（0≤x≤0.12） powders were synthesized by sol-gel method. The effect of Mn2＋-doping on the structure and electrochemical performances of Li3V2（PO4）3/C was characterized by XRD, SEM, XPS, galvanostatic charge /discharge and electrochemical impedance spectroscopy（EIS）. The XRD study shows that a small amount of Mn2＋-doped does not alter the structure of Li3V2（PO4）3/C materials, and all Mn2＋-doped samples are of pure single phase with a monoclinic structure （space group P21/n）. The XPS analysis indicates that valences state of V and Mn are ＋3 and ＋2 in Li3V1.94Mn0.09（PO4）3/C, respectively, and the citric acid in raw materials was decomposed into carbon during calcination, and residual carbon exists in Li3V1.94Mn0.09（PO4）/C. The results of electrochemical measurements show that Mn2＋-doping can improve the cyclic stability and rate performance of these cathode materials. The Li3V1.94Mn0.09（PO4）3/C cathode material shows the best cyclic stability and rate performance. For example, at the discharge current density of 40 mA/g, after 100 cycles, the discharge capacity of Li3V1.94Mn0.09（PO4）3/C declines from initial 158.8 mA·h/g to 120.5 mA·h/g with a capacity retention of 75.9%; however, that of the Mn-undoed sample declines from 164.2 mA·h/g to 72.6 mA·h/g with a capacity retention of 44.2%. When the discharge current is increased up to 1C, the intial discharge capacity of Li3V1.94Mn0.09（PO4）3/C still reaches 146.4 mA·h/g, and the discharge capacity maintains at 107.5 mA·h/g after 100 cycles. The EIS measurement indicates that Mn2＋-doping with a appropriate amount of Mn2＋ decreases the charge transfer resistance, which is favorable for the insertion/extraction of Li＋.展开更多
2LiFe1-xCoxPO4-Li3V2（P04）3/C was synthesized using Fel-2xCo2xVO4 as precursor which was prepared by a simple co-precipitation method. 2LiFej-xCoxPO4-Li3V2（PO4）3/C samples were characterized by X-ray diffraction （...2LiFe1-xCoxPO4-Li3V2（P04）3/C was synthesized using Fel-2xCo2xVO4 as precursor which was prepared by a simple co-precipitation method. 2LiFej-xCoxPO4-Li3V2（PO4）3/C samples were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and electrochemical measurements. All 2LiFel-xCoxPOa-Li3V2（PO4）3/C composites are of the similar crystal structure. The XRD analysis and SEM images show that 2LiFe0.96Co0.04PO4-Li3V2（PO4）3/C sample has the best-ordered structure and the smallest particle size. The charge-discharge tests demonstrate that these powders have the best electrochemical properties with an initial discharge capacity of 144.1 mA.h/g and capacity retention of 95.6% after 100 cycles when cycled at a current density of 0.1C between 2.5 and 4.5 V.展开更多
以酚醛树脂为碳源,分别采用了固相法和溶胶凝胶法合成了锂离子电池正极材料Li3V2(PO4)3/C。结果表明,高分子材料酚醛树脂是一种优良的碳源材料,其热解后得到的导电网络能够有效的提高Li3V2(PO4)3的电化学性能;两种试样的充放电曲线和交...以酚醛树脂为碳源,分别采用了固相法和溶胶凝胶法合成了锂离子电池正极材料Li3V2(PO4)3/C。结果表明,高分子材料酚醛树脂是一种优良的碳源材料,其热解后得到的导电网络能够有效的提高Li3V2(PO4)3的电化学性能;两种试样的充放电曲线和交流阻抗图谱体现出了试样良好的可逆性,其极化程度很低,电荷转移电阻小;而相对于固相法来讲,溶胶凝胶法和表面活性剂CTAB(十六烷基三甲基溴化铵)的共同作用能够有效的将颗粒粒径控制在纳米级别。用这种方法合成的试样在15 C下充放电比容量也能高于90 m Ah/g,5 C倍率下循环50次比容量无衰减,证明了以酚醛树脂为碳源并采用溶胶凝胶法合成的试样具有很好的倍率性能与循环性能。展开更多
基金Project (2007BAQ01055) supported by the National Key Technology R&D Programs of ChinaProject (50574063) supported by theNational Natural Science Foundation of China
文摘LiFePO4-Li3V2（PO4）3 composites were synthesized by solid-hydrothermal method and by ball milling,respectively.The electrochemical performance of the solid-hydrothermally obtained materials（C-LFVP） was significantly improved compared with LiFePO4（LFP） and Li3V2（PO4）3（LVP）,and it was also much better than that of the ball-milled LiFePO4-Li3V2（PO4）3（P-LFVP）.C-LFVP and P-LFVP both had four REDOX peaks（voltage plateaus）,which coincided with that of LFP and LVP.Some new trace substances were found in C-LFVP which had more perfect morphology,this was responsible for the better electrochemical performance of C-LFVP than P-LFVP.
基金Project(2007BAQ01055)supported by the National Key Technology R&D Program of ChinaProject(2011SCU11081)supported by the Sichuan University Funds for Young Scientists,ChinaProject(20120181120103)supported by Ph.D.Programs Foundation of the Ministry of Education of China
文摘The Li3V2（PO4）3/C composite cathode material was synthesized via sol-gel method using three different chelating agents （citric acid, salicylic acid and polyacrylic acid） at pH value of 3 or 7. The crystal structure, morphology, specific surface area and electrochemical performance of the prepared samples were investigated by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, cyclic voltammetry （CV）, electrochemical impedance spectroscopy （EIS） and galvanostatic charge/discharge test. The results show that the effects of pH value on the performance of the prepared materials are greatly related to the chelating agents. With salicylic acid or polyacrylic acid as the chelating reagent, the structure, morphology and electrochemical performance of the samples are greatly influenced by the pH values. However, the structure of the materials with citric acid as the chelating agent does not change as pH value changes, and the materials own uniform particle size distribution and good electrochemical performance. It delivers an initial discharge capacity of 113.58 mA·h/g at 10C, remaining as high as 108.48 mA·h/g after 900 cycles, with a capacity retention of 95.51%.
基金Project (20771100) supported by the National Natural Science Foundation of China
文摘Li3V2-2/3xMnx（PO4）3（0≤x≤0.12） powders were synthesized by sol-gel method. The effect of Mn2＋-doping on the structure and electrochemical performances of Li3V2（PO4）3/C was characterized by XRD, SEM, XPS, galvanostatic charge /discharge and electrochemical impedance spectroscopy（EIS）. The XRD study shows that a small amount of Mn2＋-doped does not alter the structure of Li3V2（PO4）3/C materials, and all Mn2＋-doped samples are of pure single phase with a monoclinic structure （space group P21/n）. The XPS analysis indicates that valences state of V and Mn are ＋3 and ＋2 in Li3V1.94Mn0.09（PO4）3/C, respectively, and the citric acid in raw materials was decomposed into carbon during calcination, and residual carbon exists in Li3V1.94Mn0.09（PO4）/C. The results of electrochemical measurements show that Mn2＋-doping can improve the cyclic stability and rate performance of these cathode materials. The Li3V1.94Mn0.09（PO4）3/C cathode material shows the best cyclic stability and rate performance. For example, at the discharge current density of 40 mA/g, after 100 cycles, the discharge capacity of Li3V1.94Mn0.09（PO4）3/C declines from initial 158.8 mA·h/g to 120.5 mA·h/g with a capacity retention of 75.9%; however, that of the Mn-undoed sample declines from 164.2 mA·h/g to 72.6 mA·h/g with a capacity retention of 44.2%. When the discharge current is increased up to 1C, the intial discharge capacity of Li3V1.94Mn0.09（PO4）3/C still reaches 146.4 mA·h/g, and the discharge capacity maintains at 107.5 mA·h/g after 100 cycles. The EIS measurement indicates that Mn2＋-doping with a appropriate amount of Mn2＋ decreases the charge transfer resistance, which is favorable for the insertion/extraction of Li＋.
基金supported by the China Postdoctoral Science Foundation (2014M562322)Research Fund for the Doctoral Program of Higher Education, Ministry of Education of China (20120181120103)~~
基金Project(51072233) supported by National Natural Science Foundation of China
文摘2LiFe1-xCoxPO4-Li3V2（P04）3/C was synthesized using Fel-2xCo2xVO4 as precursor which was prepared by a simple co-precipitation method. 2LiFej-xCoxPO4-Li3V2（PO4）3/C samples were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and electrochemical measurements. All 2LiFel-xCoxPOa-Li3V2（PO4）3/C composites are of the similar crystal structure. The XRD analysis and SEM images show that 2LiFe0.96Co0.04PO4-Li3V2（PO4）3/C sample has the best-ordered structure and the smallest particle size. The charge-discharge tests demonstrate that these powders have the best electrochemical properties with an initial discharge capacity of 144.1 mA.h/g and capacity retention of 95.6% after 100 cycles when cycled at a current density of 0.1C between 2.5 and 4.5 V.
文摘以酚醛树脂为碳源,分别采用了固相法和溶胶凝胶法合成了锂离子电池正极材料Li3V2(PO4)3/C。结果表明,高分子材料酚醛树脂是一种优良的碳源材料,其热解后得到的导电网络能够有效的提高Li3V2(PO4)3的电化学性能;两种试样的充放电曲线和交流阻抗图谱体现出了试样良好的可逆性,其极化程度很低,电荷转移电阻小;而相对于固相法来讲,溶胶凝胶法和表面活性剂CTAB(十六烷基三甲基溴化铵)的共同作用能够有效的将颗粒粒径控制在纳米级别。用这种方法合成的试样在15 C下充放电比容量也能高于90 m Ah/g,5 C倍率下循环50次比容量无衰减,证明了以酚醛树脂为碳源并采用溶胶凝胶法合成的试样具有很好的倍率性能与循环性能。