以柠檬酸为络合剂,聚乙二醇(PEG)为表面活性剂,偏钒酸铵、乙酸锰、磷酸二氢铵、氢氧化锂为原料,采用溶胶-凝胶法合成了xLiMnPO4·y Li3V2(PO4)3锂离子电池复合正极材料。采用X射线衍射(XRD)、扫描电镜(SEM)对其晶体结构和微观形貌...以柠檬酸为络合剂,聚乙二醇(PEG)为表面活性剂,偏钒酸铵、乙酸锰、磷酸二氢铵、氢氧化锂为原料,采用溶胶-凝胶法合成了xLiMnPO4·y Li3V2(PO4)3锂离子电池复合正极材料。采用X射线衍射(XRD)、扫描电镜(SEM)对其晶体结构和微观形貌进行表征,结果表明在700℃下烧结15 h合成的3LiMnPO4·Li3V2(PO4)3为结晶良好的两相结构,颗粒粒径相对较小且分布均匀。电化学性能研究表明,3LiMnPO4·Li3V2(PO4)3在室温0.2 C倍率下首次充放电容量分别为148.2 m Ah/g和141.5 m Ah/g,循环50次后放电容量为136.7 m Ah/g。展开更多
Lithium-ion battery cathode material Li3V2(PO4)3 was synthesized by sol-gel method using LiOH·H2O, NH4VO3, H3PO4 and citric acid as the raw materials. The samples were investigated by granularity analysis, scanni...Lithium-ion battery cathode material Li3V2(PO4)3 was synthesized by sol-gel method using LiOH·H2O, NH4VO3, H3PO4 and citric acid as the raw materials. The samples were investigated by granularity analysis, scanning electron microscopy and X-ray diffraction. Results showed that sample synthesized by sol-gel procedure had a relatively smaller particle size compared with the products prepared by solid-state reaction, and had an ample surface. Electrochemical properties were investigated by charge/discharge cycle at 0.1 C rate with lithium as the anode. A high discharge specific capacity 122.42 mAh·g-1 was reached at the first cycle, with hardly capacity fading after 20 cycles.展开更多
文摘以柠檬酸为络合剂,聚乙二醇(PEG)为表面活性剂,偏钒酸铵、乙酸锰、磷酸二氢铵、氢氧化锂为原料,采用溶胶-凝胶法合成了xLiMnPO4·y Li3V2(PO4)3锂离子电池复合正极材料。采用X射线衍射(XRD)、扫描电镜(SEM)对其晶体结构和微观形貌进行表征,结果表明在700℃下烧结15 h合成的3LiMnPO4·Li3V2(PO4)3为结晶良好的两相结构,颗粒粒径相对较小且分布均匀。电化学性能研究表明,3LiMnPO4·Li3V2(PO4)3在室温0.2 C倍率下首次充放电容量分别为148.2 m Ah/g和141.5 m Ah/g,循环50次后放电容量为136.7 m Ah/g。
文摘Lithium-ion battery cathode material Li3V2(PO4)3 was synthesized by sol-gel method using LiOH·H2O, NH4VO3, H3PO4 and citric acid as the raw materials. The samples were investigated by granularity analysis, scanning electron microscopy and X-ray diffraction. Results showed that sample synthesized by sol-gel procedure had a relatively smaller particle size compared with the products prepared by solid-state reaction, and had an ample surface. Electrochemical properties were investigated by charge/discharge cycle at 0.1 C rate with lithium as the anode. A high discharge specific capacity 122.42 mAh·g-1 was reached at the first cycle, with hardly capacity fading after 20 cycles.