After the investigation on partial remelting of thixotropic magnesium serial alloys （ZK60） by near non-equilibrium liquidus casting （NNLC）, the primary solid grains of ZK60-2Ca alloy spheroidized notably during pa...After the investigation on partial remelting of thixotropic magnesium serial alloys （ZK60） by near non-equilibrium liquidus casting （NNLC）, the primary solid grains of ZK60-2Ca alloy spheroidized notably during partial remelting processing, however, coarsening and polygonization as occurred holding time prolonged. The refining and globularity of the thixotropic alloys are promoted after further alloyed by Y, RE, Nd and/or Ag, and the results vary with those addition. The remelting structure of ZK60-2Ca-1Y alloy is finer than its base alloy. And the effect of RE, especially Ag, on the refinement of microstrueture is notable, but Nd does nothing on it. There is little impact of remelting temperature fluctuation on partial remelted microstrueture as holding time in general. On the contrary, it is more sensitive at longer holding time. The quality thixotropic silver-contained alloy can be achieved by remelted partially at 600℃ for 10 min.展开更多
In this study, reheating of liquidus semi-continuous cast billets of 7075 Al alloy was carried out in a resistance furnace, and the temperature contrast of the outer and the center of the reheated billets was investig...In this study, reheating of liquidus semi-continuous cast billets of 7075 Al alloy was carried out in a resistance furnace, and the temperature contrast of the outer and the center of the reheated billets was investigated, then the reheating microstructures were investigated. Results show that: the difference of temperature between the outer and center is small and the difference of their microstructures are also small. During reheating at 576℃ the spheroidization of grains is significant after 5min and no rosettes are visible after 20min by optical microscopy. Similar observations were madeon materials reheated at 596℃, but the ripening process is faster. The grains growup to 30-60μm, fine enough for thixoforming.展开更多
文摘After the investigation on partial remelting of thixotropic magnesium serial alloys （ZK60） by near non-equilibrium liquidus casting （NNLC）, the primary solid grains of ZK60-2Ca alloy spheroidized notably during partial remelting processing, however, coarsening and polygonization as occurred holding time prolonged. The refining and globularity of the thixotropic alloys are promoted after further alloyed by Y, RE, Nd and/or Ag, and the results vary with those addition. The remelting structure of ZK60-2Ca-1Y alloy is finer than its base alloy. And the effect of RE, especially Ag, on the refinement of microstrueture is notable, but Nd does nothing on it. There is little impact of remelting temperature fluctuation on partial remelted microstrueture as holding time in general. On the contrary, it is more sensitive at longer holding time. The quality thixotropic silver-contained alloy can be achieved by remelted partially at 600℃ for 10 min.
基金The National Natural Science Foundation of China (Grants No. 59974009) is greatly acknowledged for their financial support.
文摘In this study, reheating of liquidus semi-continuous cast billets of 7075 Al alloy was carried out in a resistance furnace, and the temperature contrast of the outer and the center of the reheated billets was investigated, then the reheating microstructures were investigated. Results show that: the difference of temperature between the outer and center is small and the difference of their microstructures are also small. During reheating at 576℃ the spheroidization of grains is significant after 5min and no rosettes are visible after 20min by optical microscopy. Similar observations were madeon materials reheated at 596℃, but the ripening process is faster. The grains growup to 30-60μm, fine enough for thixoforming.